Study of Annealing Effect on the Some Physical Properties of Nanostructured TiO2 films prepared by PLD
دراسة تأثير التلدين على بعض الخصائص الفيزيائية للأغشية TiO2التركيب النانوي المصنعة بتقنية PLD

Authors: Ali A.Yousif علي احمد يوسف --- Sarmad S. Al-Obaidi سرمد العبيدي
Journal: Journal of College of Education مجلة كلية التربية ISSN: 18120380 Year: 2013 Issue: 3 Pages: 139-160
Publisher: Al-Mustansyriah University الجامعة المستنصرية

Loading...
Loading...
Abstract

Nanostructured Titanium Dioxide (TiO2) thin films were prepared by pulsed laser deposition (PLD) on the glass substrates. The effects of different annealing temperature (400, 500 and 600 °C) towards the some physical properties such as structural, morphological and optical have been studied. From X-ray diffraction result, the crystallinity of TiO2 thin films improved at higher annealing temperature. It also could be observed that the rutile phase start to exist at annealing temperatures of 500 °C and 600 °C. The Full Width at Half Maximum (FWHM) of the (101) peaks of these films decreases from 0.450° to 0.301° with increasing of annealing temperature. AFM measurements confirmed that the films grown by this technique have good crystalline and homogeneous surface. The Root Mean Square (RMS) value of thin films surface roughness increased with increasing of the annealing temperature. From UV-VIS spectrophotometer measurements, the optical transmission results shows that theمجلة كلية التربية ............................................................. العدد الثالث 3102140transmission over than ~65% in the near-infrared region which decrease with the increasing of annealing temperatures. The allowed indirect optical band gap of the films was estimated to be in the range from 3.49 to 3.1 eV. The allowed direct band gap was found to decrease from 3.74 eV to 3.55 eV with the increase of annealing temperature. The refractive index of the films was found from 2.27 -2.98 at 550nm. The extinction coefficient, real and imaginary parts of the dielectric constant increase with annealing temperature.


Article
Gas sensitivity properties of TiO2/Ag nanocomposite films prepared by pulse laser deposition
خصائص المتحسس الغازي للغشاء المتراكب النانوي TiO2/Ag المحضر بطريقة الليزر النبضي

Loading...
Loading...
Abstract

In this study, a double frequency Q-switching Nd:YAG laser beam (1064 nm and λ= 532 nm, repetition rate 6 Hz and the pulse duration 10ns) have been used, to deposit TiO2 pure and nanocomposites thin films with noble metal (Ag) at various concentration ratios of (0, 10, 20, 30, 40 and 50 wt.%) on glass and p-Si wafer (111) substrates using Pulse Laser Deposition (PLD) technique. Many growth parameters have been considered to specify the optimum condition, namely substrate temperature (300˚C), oxygen pressure (2.8×10-4 mbar), laser energy (700) mJ and the number of laser shots was 400 pulses with thickness of about 170 nm. The surface morphology of the thin films has been studied by using atomic force microscopes (AFM). The Root Mean Square (RMS) value of thin films surface roughness increased with increasing of Ag contents, while the crystallite size was found to decrease with increase in different silver content. The sensitivity toward NO2 and NH3 gas has been measured under different ppm concentrations. TiO2 with noble metal has a sensitivity higher than pure TiO2 where as TiO2 with Ag metal deposited on glass substrate has maximum sensitivity to NO2 gas with a value of ~(50 %) at the nanocomposite 90%TiO2/10%Ag films with best operation temperature at 200 °C. In addition, noble metal like Ag to the titanium dioxide materials makes them sensitive to NO2 gas.

تم في هذه الدراسة استخدام حزمة ليزر النديميوم-ياك ذات التردد المضاعف و بتقنية المفتاح Q, ذات الطول الموجي 1064 نانومتر و ذات الطول الموجي 532 نانومتر و بمعدل تكرار 6 هيرتز, و زمن نبضة مقداره 10 نانو ثانية لترسيب الغشاء للمتراكب النانوي TiO2 النقي و المخلوط مع العنصر النبيل Ag بنسب تراكيز مختلفة (10, 20, 30, 40 and 50) % wt. على قواعد من الزجاج و الوفر سليكون (111) باستخدام تقنية الترسيب بالليزر النبضي (PLD). عدة معلمات انماء اخذت بنظر الاعتبار لتحديد الشروط المثلى كتحديد درجة حرارة القاعدة عند (300 oC), ضغط الاوكسجين (2.8x10-4), طاقة الليزر (700 mJ), عدد النبضات (400) نبضة و سمك الغشاء المرسب (170 nm). تم دراسة تضاريس السطح باستخدام مجهر القوة الذرية (AFM). و تظهر الدراسة بأن قيم RMS للاغشية الرقيقة و خشونة السطح ازدادت بزيادة محتوى الفضة, بينما الحجم البلوري قل بزيادة محتوى الفضة. تم قياس التحسسية لغاز NO2 و NH3 عند تراكيز مختلفة لكل جزء من المليون من الغاز (ppm). ان تحسسية اوكسيد التيتانيوم المخلوط مع العنصر النبيل الفضة اعلى مما في حالة اوكسيد التيتانيوم لوحده و المحضرة على قواعد من الزجاج و اعلى حساسية لغاز No2 استطاع الغشاء تحسسها كانت بحدود 50% تقريبا للغشاء المتراكب النانوي 90%TiO2/10%Ag عند افضل درجة حرارة تشغيل و كانت عند (200 oC). ان اضافة العنصر النبيل مثل الفضة جعل الاغشية المحضرة اكثر تحسسية لغاز NO2.