Study of Some Mechanical Properties for Polymeric Composite Material Reinforced by Fibers
دراسة بعض الخواص الميكانيكية لمادة مركبة بوليميرية مقواة بالألياف

Author: Ali I.Al-Mosawi علي إبراهيم الموسوي
Journal: Al-Qadisiyah Journal for Engineering Sciences مجلة القادسية للعلوم الهندسية ISSN: 19984456 Year: 2009 Volume: 2 Issue: 1 Pages: a14-a24
Publisher: Al-Qadisiyah University جامعة القادسية

Loading...
Loading...
Abstract

The objective of this research is to study the effect of changing the reinforcement percentage by fibers on Mechanical properties, for composite material consists of conbextra epoxy (EP-10) resin reinforced by biaxial woven roving kevlar fibers (°45-°0) with density (340 g/cm3) which included impact strength , tensile strength , flexural strength and hardness Where the Mechanical properties were extracted for phenol formaldehyde resin before reinforcement by fibers, then we reinforced the resin by different weight percentage from Kevlar fibers(20%,40%,60%) and studied the effect on the above mechanical properties as illustrated in the diagrams .

إن الهدف من هذا البحث هو دراسة تأثير تغيير نسبة التقوية بالألياف على الخواص الميكانيكية للمادة المركبة المكونة من راتنج الإيبوكسي نوع كونبكسترا (EP-10) المقوى بألياف كيفلار بشكل ظفائر محاكة ثنائية الإتجاه (°45-°0) ذات كثافة سطحية (340 g/cm3) وقد شملت هذه الخواص كل من مقاومة الصدمة ، مقاومة الشد ، مقاومة الإنثناء ، والصلادة حيث تم في البداية إستخراج الخواص الميكانيكية لراتنج الفينول فورمالدهيد قبل التقوية بالألياف بعدها تم تدعيم الراتنج بنسب وزنية مختلفة من ألياف كيفلار (%60, %40, %20) و دراسة تأثير ذلك على الخواص المذكورة وكما موضح في المخططات البيانية


Article
GEOMETRICALLY NONLINEAR ANALYSIS OF IMPERFECT LAMINATED COMPOSITE PLATES WITH A VARIABLE FIBER SPACING
تحليل اللآخطية الهندسية للصفائح المركبة المتطبقة والغير مضبطة مع تغير مسافات الألياف

Author: Ali I. Al-Mosawi علي إبراهيم الموسوي
Journal: Al-Qadisiyah Journal for Engineering Sciences مجلة القادسية للعلوم الهندسية ISSN: 19984456 Year: 2011 Volume: 4 Issue: 4 Pages: 439-455
Publisher: Al-Qadisiyah University جامعة القادسية

Loading...
Loading...
Abstract

The primary objective of research is to determine the improved structural efficiency of plates can be with variable fiber spacing. The Post-buckling of laminated composite plate with variable fiber spacing is obtained numerically, using eight node isoparametric quadrilateral elements (serendipity element) with five degree of freedom per node. The mathematical formulation is based on first-order shear deformation theory and von-Karman non-linearity. The effect of the initial geometric imperfection, fiber spacing, orientation fiber, and direction of in-plane loading were considered. Numerical results for boron/Epoxy fiber reinforced laminates are presented for the different effects of the composite plate under in-plane loading. This study showed that the post buckling behavior of composite plate very sensitive for type of distribution fiber and the seventh distribution equation gives maximum buckling load and smallest deformation.

الهدف الرئيسي للبحث هو لتحديد إمكانية تحسين الكفاءة الإنشائية للصفائح من خلال تغير مسافات الألياف. تم حصول النتائج العددية للإنبعاج اللاحق للصفائح المركبة والمطبقة مع ألياف متغيرة المسافات باستخدام عناصر رباعية الشكل ذات ثمانية عقد مع خمسة درجات الحرية للعقدة الواحدة. الصيغة الرياضية موضوعة على نظرية التشوهات القصية الأولى ولاخطية (von-Karman).تم الأخذ بنظر الإعتبار تأثير التشوهات الهندسية الابتدائية؛ مسافات الألياف؛ زاوية تدوير الألياف؛ وإتجاه الأحمال المحورية. النتائج العددية الخاصة بالـطبقات المسلحة بـ(البورون/إيبوكسي) تم تقديمها لمجمل من المؤثرات للصفائح المركبة تحت أحمال محورية. أظهرت هذه الدراسة إن الإنبعاج اللاحق للصفائح جدا حساس لنمط توزيع الألياف وان معادلة التوزيع السابعة تعطي أكبر حمل إنبعاج وأقل تشوه.


Article
Study the effect of volume fraction on thermal conductivity values for polyester particles composites
دراسة تأثير الكسر الحجمي على قيم الموصلية الحرارية لمتراكبات البولي أستر الدقائقية

Author: Ali I. Al-Mosawi علي إبراهيم الموسوي
Journal: Journal of Kufa - physics مجلة الكوفة للفيزياء ISSN: 20775830 Year: 2011 Volume: 3 Issue: 2 arabic Pages: 29-34
Publisher: University of Kufa جامعة الكوفة

Loading...
Loading...
Abstract

The objective of present research is to study the changing in thermal conductivity thermal of unsaturated polyester resin by additive the silica material (SiO2) as a filler with different Weight amount (10%,20%,30%) to resin and study the effect of this additive on thermal conductivity coefficient (k) of the resin . Fourier equation was used to calculate the changing in thermal conductivity coefficient (k) for unsaturated polyester resin before addition silica material and after ,where the results show increased thermal insulation of the resin by reduced thermal conductivity coefficient value after addition this material . Also the value of thermal insulation increased with increasing of additive percentage of silica as illustrated in diagrams which represent the relation between thermal conductivity coefficient with temperature.

يهدف البحث الحالي إلى دراسة التغير في الموصلية الحرارية لراتنج البولي أستر غير المشبع عند إضافة مادة السليكا (SiO2) كحشوة وبكميات وزنية مختلفة (10%،20%،30%) إلى هذا الراتنج ودراسة مدى تأثير هذه الإضافة على معامل التوصيل الحراري (k) لهذه المادة الراتنجية . ولتقويم مدى التغير في الخواص الحرارية لراتنج البولي أستر غير المشبع فقد إستخدمت معادلة فورير لحساب التغير في قيمة معامل التوصيل الحراري (k) للراتنج قبل إضافة مادة السليكا وبعدها ، إذ أظهرت النتائج زيادة العزل الحراري للراتنج عن طريق إنخفاض قيمة معامل التوصيل الحراري بعد إضافة هذه المادة . وإزدادت قيمة العزل الحراري مع زيادة نسبة السليكا المضافة كما موضح في المخططات البيانية التي تمثل العلاقة بين التوصيل الحراري و درجة الحرارة .


Article
دراسة بعض الخواص الميكانيكية لمادة مركبة مكونة من راتنج الفينول فورمالدهيد المقوى بألياف كيفلار
Study of Some Mechanical Properties for Composite Material Consist of Phenol Formaldehyde Resin Reinforced by Kevlar Fibers

Authors: مشتاق طالب البديري --- Ali I.Al-Mosawi علي إبراهيم الموسوي
Journal: Al-Qadisiyah Journal for Engineering Sciences مجلة القادسية للعلوم الهندسية ISSN: 19984456 Year: 2008 Volume: 1 Issue: 2 Pages: 56-66
Publisher: Al-Qadisiyah University جامعة القادسية

Loading...
Loading...
Abstract

The objective of this research is to study the effect of changed the reinforcement percentage by fibers on Mechanical properties for composite material consist of phenol formaldehyde resin reinforced by biaxial kevlar fibers (0o-90o))with (485g/cm3) density which included impact strength , tensile strength , and hardness where we extracted the Mechanical properties for phenol formaldehyde resin before reinforced by fibers, then we reinforced the resin by different weight percentage from Kevlar Fibers(20%,40%,60%) and studied its effect on the above Mechanical Properties as illustrated in the diagrams . Keywords:-Composite Material , Mechanical Properties, Phenol Formaldehyde Resin , Kevlar Fibers .

إن الهدف من هذا البحث هو دراسة تأثير تغيير نسبة التقوية بالألياف على الخواص الميكانيكية للمادة المركبة المكونة من راتنج الفينول فورمالدهيد المقوى بألياف كيفلار ثنائية الإتجاه(0o-90o) ذات كثافة سطحية (485g/cm3)، وقد شملت هذه الخواص كل من مقاومة الصدمة ومقاومة الشد والصلادة حيث تم في البداية إستخراج الخواص الميكانيكية لراتنج الفينول فورمالدهيد قبل التقوية بالألياف بعدها تم تدعيم الراتنج بنسب وزنية مختلفة من ألياف كيفلار (%60,%40,%20) و دراسة تأثير ذلك على الخواص المذكورة وكما موضح في المخططات البيانية

Keywords


Article
STUDY THE EFFECT OF REINFORCING FIBERS ON SOME MECHANICAL PROPERTIES OF ADVANCED COMPOSITE MATERIALS
دراسة تأثير إضافة ألياف التقوية على بعض الخواص الميكانيكية للمواد المركبة المتقدمة

Authors: Ali J. Salaman علي جاهل سلمان --- Ali I. Al-Mosawi علي إبراهيم الموسوي
Journal: Al-Qadisiyah Journal for Engineering Sciences مجلة القادسية للعلوم الهندسية ISSN: 19984456 Year: 2010 Volume: 3 Issue: 4 Pages: a163-a169
Publisher: Al-Qadisiyah University جامعة القادسية

Loading...
Loading...
Abstract

This research aims to study some aspects and important properties in manufacturing of polymeric advanced composite materials reinforced by fibers will be studied ,these aspects show as introduction to some important properties of polymeric composite materials reinforced by fibers related with its composition and some mechanical properties (Tension ,Impact, Compression, Flexural, etc) .The objective of this research is to study the effect of using different reinforcement percentage of fibers on mechanical properties for composite material consist of vinyl ester resin reinforced by unidirectional Kevlar fibers with surface density (340 g/cm2) which included impact , tensile, compression , and flexural strength , where we extracted the mechanical properties for vinyl ester resin before reinforced by fibers, then we reinforced the resin by different weight percentage from kevlar Fibers (20%,40%,60%) and studied its effect on the above mechanical properties .

يهدف البحث الحالي إلى دراسة بعض المفاهيم والخواص المهمة في تصنيع المواد المركبة المتقدمة ذات أساس بوليميري والمقواة بالألياف ، حيث تعتبر المفاهيم مقدمة لبعض الخواص المهمة للمواد البولميرية المقواة بالألياف والمتعلقة بنسب مكوناتها من الألياف والمادة الأساس وبعض الخواص الميكانيكية (الشد ،الصدمة ،الإنضغاط ،الإنثناء ،الصلادة وغيرها) . يتناول هذا البحث إضافة نسب وزنية مختلفة من ألياف كيفلار أحادية الإتجاه ذات كثافة سطحية (340 g/cm2)والمستخدمة في تقوية راتنج الفنيل أستر وتأثير هذه الإضافة على الخواص الميكانيكية لهذا الراتنج وقد شملت هذه الخواص كل من مقاومة الصدمة والشد و الإنضغاط و الإنثناء والصلادة حيث تم في البداية إستخراج الخواص الميكانيكية لراتنج الفنيل أستر قبل تقويته بالألياف بعدها تم إضافة نسب وزنية مختلفة من ألياف كيفلار إلى الراتنج (%60,%40,%20) و دراسة تأثير ذلك على الخواص المذكورة


Article
Experimental Study of the Effect of Zinc Borate on Flame Retardancy of Carbon- Kevlar Hybrid Fibers Reinforced Composite Materials
دراسة عملية لتأثير بورات الخارصين على إعاقة اللّهب لمواد مركبة مقواة بألياف كاربون- كيفلار الهجينة

Loading...
Loading...
Abstract

This study aims to investigate possibility to increase the flame retardancy for composite materials by addition of a flame retardant material which represent the zinc borate as a coating layer of (4mm) thickness on the surface of composite material consist of araldite resin reinforced by hybrid fibers from carbon and kevlar fibers as a consecutive layers which be as a woven roving (º 90 - º 0). Then, this system (flame retardant material and composite material) was exposed to a direct flame which generated from oxyacetylene flame (up to 3000ºC) and gas flame (2000ºC) under different exposure distances (10,15, and 20mm), and study the range of resistance of flame retardant material layer to the flames and protected the substrate where we used the method of measuring the surface temperature opposite to the flame where we obtained the better results with large exposed distance and large percentage from protective layer which is zinc borate (30%) for both types of flames , as well as the flame resistance will be increased with decrease the flame temperature .

تهدف هذه الدراسة لبحث امكانية زيادة إعاقة اللّهب للمواد المركبة عن طريق إضافة مادة معيقة للّهب والتي تمثل بورات الخارصين بشكل طبقة طلاء بسمك (4mm) على سطح المادة المركبة المكونة من راتنج الإرلدايت المقوى بألياف هجينة من ألياف الكاربون وألياف كيفلار بشكل طبقات متتابعة والتي تكون بشكل ظفائر محاكة ثنائية الإتجاه (º 90 - º 0) . بعدها عرض هذا النظام (المادة المعيقة للّهب و المادة المركبة) إلى لّهب مباشر متولد من شُعلة أُوكسي أستيلينية بدرجة حرارة أكثر من (3000ºC) ولهب متولد من شُعلة غازية بدرجة حرارة(2000ºC) وبمسافات تعرض مختلفة (20mm,15mm,10mm) ودراسة مدى مقاومة طبقة المادة المعيقة للّهب لحرارة الشُعلتين ومدى حمايتها للمادة المركبة الواقعة تحتها حيث تم إعتماد طريقة قياس درجة حرارة السطح المقابل للشعلة في قياس درجة الحرارة المنتقلة خلال هذا النظام حيث تم الحصول على أفضل النتائج عندما تكون مسافة التعرض كبيرة و أكبر نسبة للطبقة الحامية والتي هي بورات الخارصين (نسبة %30) ولكلا الشعلتين إضافة إلى ذلك تزداد المقاومة للّهب كلما قلت حرارة الشُعلة


Article
MECHANICAL PROPERTIES OF ARALDITE MATRIX COMPOSITES REINFORCED WITH HYBRID CARBON - KEVLAR FIBERS
الخواص الميكانيكية لمادة مركبة ذات أساس من الإرلدايت مقواة بألياف الكاربون وألياف كيفلار الهجينة

Loading...
Loading...
Abstract

The mechanical properties of araldite matrix composites incorporated with hybrid carbon - kevlar fibers were evaluated . There are indications that the incorporation of both fibers into a single matrix which is araldite resin will stabilize mechanical properties and lowering manufacturing costs . In this research the impact strength , tensile strength ,flexural strength ,and hardness were studied for composite material reinforced with hybrid fibers as a woven roving (°90-°0) with density (225g/cm3) and (285g/cm3) for carbon and kevlar fibers respectively . These fibers were mixed with araldite resin in different reinforcement percentage (20%,40%,60%) and the effect on the above mechanical properties were studied , where we see Improves in these mechanical properties after reinforcement by fibers The value of mechanical properties will increase with increasing percentage of reinforcement .

تم في هذه الدراسة حساب قيم الخواص الميكانيكية للمادة المركبة ذات أساس من الإرلدايت المدمج مع ألياف الكاربون وألياف كيفلار الهجينة . حيث هنالك مؤشرات على إن دمج هذين النوعين من الألياف في أرضية واحدة يحافظ على الخواص الميكانيكية ويخفض تكاليف التصنيع . في هذا البحث تم دراسة مقاومة الصدمة ، مقاومة الشد ، مقاومة الإنثناء ، والصلادة للمادة المركبة المقواة بألياف هجينة بشكل حصيرة ثنائية (°0-°90) من ألياف الكاربون وألياف كيفلار بكثافة (225g/cm3) و(285g/cm3) على التوالي . حيث تم مزج هذه الألياف في أرضية من راتنج الإرلدايت وبنسب تقوية مختلفة (60%,40%,20%) ودراسة أثر ذلك على الخواص الميكانيكية ، حيث تم تحسين هذه الخواص بعد التقوية بالألياف إضافة إلى زيادة قيمة هذه الخواص مع زيادة نسبة التقوية بالألياف .


Article
Using Computer Techinques to Study the Effect of Type And Direction Loading on Stress Concentrations
إستخدام تقنيات الحاسوب لدراسة تأثير نوع وإتجاه التحميل على ممركزات الإجهاد

Authors: Mustafa A. Rigab مصطفى أحمد رجب --- Ali I. Al-Mosawi علي إبراهيم الموسوي --- Mona A. Rigab منى أحمد رجب
Journal: Al-Ma'mon College Journal مجلة كلية المامون ISSN: 19924453 Year: 2013 Issue: 21 Pages: 189-202
Publisher: AlMamon University College كلية المامون الجامعة

Loading...
Loading...
Abstract

The objective of this paper is to study the effect of loading system and direction on stress concentration around a square hole in an infinite plate using (FEM) . The study involves the effect of uniaxial and biaxial loading on stress concentration factor ( Kt ) in an infinite steel plate that contains a central square hole(6)mm a side , beside the type of loading (tension and compression (, the effect on stress concentration factor is also considered. Results have indicated that under uniaxial tensile loading , stress concentration occurs at the four corners of the hole, however under uniaxial compression loading, results were similar excepts for the sing of stress in biaxial loading (tension)results showed that (Kt) was higher than in uniaxial loading and when biaxial loading(tension and compression( stress concentration is still higher than that due to uniaxial loading .

أوضحت النتائج إنه عندما يكون التحميل بإجهاد شدي فقط على شريحة تحتوي على ثقب مربع فإنّ تركيز الإجهادات يكون عند حواف الزوايا الأربعة للثقب في حين يكون تركيزها اقل شدة عند منتصف حواف الثقب (العمودية والموازية لمحور التحميل). أما في حالة التحميل بإجهاد ضغط فقط فستكون النتائج مماثلة لما سبق إلا أن قيمة الإجهادات الرئيسة تكون معكوسة بالمقدار والإتجاه . من ناحية أخرى بينت النتائج إنه عند التحميل الثنائي المحور وبإجهاد شدي وبالقيمة بنفسها فأن قيم الإجهادات المتركزة عند حواف الثقب الأربعة تكون اكبر مما لو كان التحميل أحادي المحور (Uniaxial) . أما لو كان التحميل الثنائي المحور بإجهاد شدي وبقيم مختلفة لكل محور فإنّ قيمة الإجهادات المتركزة هي عبارة عن محصلة قيم الإجهادات الرئيسة المتركزة والناتجة من كل تحميل على انفراد , في حين لو كان التحميل الثنائي المحور بإجهاد شدي لأحد المحاور وبإجهاد ضغط للمحور الآخر وقيمة الإجهاد نفسها فإنّ قيمة الإجهادات الرئيسة المتركزة عند حواف الثقب الأربعة تكون بقيمة أعلى مما لو كان التحميل أحادي المحور (Uniaxial) , بينما لو كان التحميل الثنائي المحور بإجهاد شدي لأحد المحاور وبإجهاد ضغط للمحور الآخر وبقيم مختلفة للإجهاد فإنّ قيمة الإجهادات الرئيسة أو الإجهادات القص المتركزة عند حواف الثقب المربع تكون عبارة عن محصلة قيم الإجهادات الناتجة عن كل تحميل على انفراد .


Article
Using of Coating Technique by Inorganic Flame Retardants to Protect Civil and Industrial Foundations from Fires
استعمال تقنية الطلاء بمعيقات اللّهب لحماية المنشآت المدنية والصناعية من الحرائق

Loading...
Loading...
Abstract

تم في هذا البحث زيادة إعاقة اللّهب لأجزاء المنشآت المدنية والصناعية المصنعة من المواد المتراكبة البولميرية المتقدمة المقواة بالألياف بطلائها بطبقة سطحية مكونة من مادة معيقة للّهب . إستعمل رابع أُوكسيد الأنتيمون كطبقة طلاء بسمك (3mm) لإعاقة اللّهب ومنع إنتشاره لطلاء سطح راتنج البولي أستر (SIROPOL 8340-PI) المقوى بألياف هجينة مكونة من حصيرة ألياف الكاربون وألياف كيفلار(49) (&#186; 0 -&#186; 45) ، وتعريضها إلى لهب مباشر متولد من شُعلة غازية درجة حرارتها (2000&#186;C) وبمسافات تعرض مختلفة(20mm,15,10) ودراسة مدى مقاومة هذه الطبقة للحرارة ومدى قدرتها على حماية المادة المتراكبة التي تحتها .لقد أظهرت النتائج العملية التي تم التوصل إليها من إختبار التعرية الحرارية تحسن مقاومة المادة المتراكبة للحرارة العالية بعد إضافة طبقة رابع أُوكسيد الأنتيمون وتزداد هذه المقاومة مع زيادة مسافة التعرض لحرارة اللّهب .

تم في هذا البحث زيادة إعاقة اللّهب لأجزاء المنشآت المدنية والصناعية المصنعة من المواد المتراكبة البولميرية المتقدمة المقواة بالألياف بطلائها بطبقة سطحية مكونة من مادة معيقة للّهب . إستعمل رابع أُوكسيد الأنتيمون كطبقة طلاء بسمك (3mm) لإعاقة اللّهب ومنع إنتشاره لطلاء سطح راتنج البولي أستر (SIROPOL 8340-PI) المقوى بألياف هجينة مكونة من حصيرة ألياف الكاربون وألياف كيفلار(49) (º 0 -º 45) ، وتعريضها إلى لهب مباشر متولد من شُعلة غازية درجة حرارتها (2000ºC) وبمسافات تعرض مختلفة(20mm,15,10) ودراسة مدى مقاومة هذه الطبقة للحرارة ومدى قدرتها على حماية المادة المتراكبة التي تحتها .لقد أظهرت النتائج العملية التي تم التوصل إليها من إختبار التعرية الحرارية تحسن مقاومة المادة المتراكبة للحرارة العالية بعد إضافة طبقة رابع أُوكسيد الأنتيمون وتزداد هذه المقاومة مع زيادة مسافة التعرض لحرارة اللّهب .


Article
Fire retardancy characteristics of polymeric composite materials
صفات تثبيط اللهب للمواد المركبة البوليميرية

Authors: Naser A.Alwash نصر عبد الأمير علوش --- Ali J.Salaman علي جاهل سلمان --- Mustafa A. Rijab مصطفى أحمد رجب** --- Ali I .Al-Mosawi علي إبراهيم الموسوي
Journal: Baghdad Science Journal مجلة بغداد للعلوم ISSN: 20788665 24117986 Year: 2013 Volume: 10 Issue: 3عدد خاص بموتمر الكيمياء Pages: 828-831
Publisher: Baghdad University جامعة بغداد

Loading...
Loading...
Abstract

Fire retardancy characteristics of polymeric composite material reinforced by fibers using coating by a fire retardant layer represent antimony tetroxide was studied. A coating layer (4mm) thickness from antimony tetroxide was used as a surface layer to react and prevent spread of flame on surface of epoxy resin reinforced by carbon – Kevlar fibers and exposed this coating layer to direct flame generated from oxyacetylene flame with different exposure distances (10,15,20mm) and study how it can protect the substrate . The experimental results showed that a great increment in thermal resistance and flame retardancy after coating by antimony tetroxide as well as rising flame resistance increased exposure distances to flame. .

الخلاصة :صفات تثبيط اللهب لمادة مركبة بوليمرية مقواة بالألياف بإستخدام الطلاء بطبقة مثبط لهب متمثلة برابع أوكسيد الأنتيمون قد تم دراستها . تم إستخدام طبقة طلاء بسمك (4mm) من رابع أوكسيد الأنتيمون كطبقة طلاء سطحية لمقاومة ومنع إنتشار اللهب على سطح راتنج الإيبوكسي المقوى بألياف الكربون - كيفلار ، وتعريض هذه الطبقة للهب مباشر الناتج متولد من شعلة أوكسي أستيلينية مع مسافات تعرض مختلفة (mm10،15،20) ودراسة كيف تستطيع حماية الطبقة التحية. أظهرت النتائج العملية زيادة كبيرة في المقاومة الحرارية وتثبيط اللهب بعد طلاء برابع أوكسيد الأنتيمون وكذلك إرتفاع مقاومة اللهب مع زيادة مسافات التعرض .

Listing 1 - 10 of 11 << page
of 2
>>
Sort by
Narrow your search

Resource type

article (11)


Language

Arabic (5)

English (5)

Arabic and English (1)


Year
From To Submit

2013 (3)

2011 (3)

2010 (2)

2009 (1)

2008 (2)