Article
The effect of heat treatment on the optical properties of organic semiconductor (NiPc/C60) thin films
تأثير المعاملة الحرارية على الخواص البصرية لأغشية اشباه الموصلات العضوية (NiPc / C60) الرقيقة

Authors: Atheer M. Mkhaiber اثير مهدي مخيبر --- Ameer F. Abdulameer امير فيصل عبد الامير
Journal: Iraqi Journal of Physics المجلة العراقية للفيزياء ISSN: 20704003 Year: 2018 Volume: 16 Issue: 39 Pages: 33-41
Publisher: Baghdad University جامعة بغداد

Loading...
Loading...
Abstract

Thin films of the blended solution of (NiPc/C60) on glass substrates were prepared by spin-coated method for three different ratios (100/1, 100/10 and 100/100). The effects of annealing temperature and C60 concentration on the optical properties of the samples were studied using the UV-Vis absorption spectroscopy and FTIR spectra. The optical absorption spectrum consists of two main bands, Q and B band, with maxima at about (602-632) nm and (700-730) nm for Q1 and Q2 respectively, and (340-375) nm for B band. The optical energy gap were determined from optical absorption spectra, The variation of optical energy gap with annealing temperature was nonsystematic and this may be due to the improvement in crystal structure for thin films. While the energy gap decreased by increasing the concentration of C60 approaches from the energy gap of this compound.

تم تحضير الأغشية الرقيقة للمزيج من (NiPc / C60) على ركائز الزجاج بواسطة طريقة الطلاء البرمي لثلاث نسب مختلفة (100/1، 100/10 و 100/100). تمت دراسة تأثير درجة حرارة التلدين و تركيز C60 على الخواص البصرية للعينات باستخدام مطيافية الامتصاص UV-Vis و أطياف FTIR. يتكون طيف الامتصاص البصري من نطاقين رئيسيين، النطاقين Q و B، مع حد أقصى يبلغ حوالي (602-632) nm و (700-730) nm لـ Q1 و Q2 على التوالي، و (340-375) nm للنطاق B. تم تحديد فجوة الطاقة الضوئية من أطياف الامتصاص الضوئي، وكان تباين فجوة الطاقة الضوئية مع درجة حرارة التلدين غير نظامية، وقد يرجع ذلك إلى تحسن البنية البلورية للأغشية الرقيقة. في حين أن فجوة الطاقة انخفضت عن طريق زيادة تركيز C60 تقترب من فجوة الطاقة في هذا المركب.


Article
The structure and optical properties of organic semiconductor bulk hetrojunction blend (NiPcTs/Alq3) thin films
الخصائص التركيبيه والبصرية لاغشية الخليط المتباين الهجيني NiPcTs)/ِِAlq3) الرقيقة

Authors: Nada K. Abbas ندى خضير عباس --- Ameer F. Abdulameer امير فيصل عبد الامير --- Atyaf H. Kadhum أطياف حسين كاظم
Journal: Iraqi Journal of Physics المجلة العراقية للفيزياء ISSN: 20704003 Year: 2017 Volume: 15 Issue: 33 Pages: 40-48
Publisher: Baghdad University جامعة بغداد

Loading...
Loading...
Abstract

The effect of heat treatment on the optical properties of the bulk heterojunction blend nickel (II) phthalocyaninetetrasulfonic acid tetrasodium salt and Tris (8-hydroxyquinolinato) Aluminum (NiPcTs/Alq3) thin films which prepared by spin coating was described in this study. The films coated on a glass substrate with speed of 1500 rpm for 1.5 min and treated with different annealing temperature (373, 423 and 473) K. The samples characterized using UV-Vis, X ray diffraction and Fourier transform Infrared (FTIR) spectra, XRD patterns indicated the presence of amorphous and polycrystalline blend (NiPcTs/Alq3). The results of UV visible shows that the band gap increase with increasing the annealing temperature up to 373 K and decreases with increase the annealing temperature to (423, 473)K respectively.

في هذه الدراسة تم بيان تاثير المعاملة الحرارية على الخصائص التركيبية البصرية لاغشية المتغايير الهجيني(NiPcTs/Alq3),والمحضرة بطريقة الطلاء البرميعلى قواعد زجاجيه بسرعة دوران (1500)دورة خلال 1.5 دقيقة,اجريت المعاملة الحرارية باختلاف درجات الحرارة K(373, 423, 473). درست خصائص العينات باستخدام قياسات الاشعة السينية وUV-Vis وطيف فوربية للاشعة تحت الحمراء FTIR. طيف الاشعه السينية يشير الى خليط من العشوائية والمتعدد التبلور لاغشية المتغايير الهيجيني. نتائج UV-Vis توضح ان فجوة الطاقة تزداد بزيادة درجة الحرارة الى 373K ثم تتناقص مع زيادة درجة الحرارة الى (423,473)Kعلى التوالي.