Agent Based Monitoring For Investigation Process And Maintenance Improvement

Authors: Soroor K.Hussain --- Zouhair I. Ahmed --- Ameer Hussein Ali
Journal: Journal of Engineering مجلة الهندسة ISSN: 17264073 25203339 Year: 2011 Volume: 17 Issue: 5 Pages: 1269-1288
Publisher: Baghdad University جامعة بغداد

Loading...
Loading...
Abstract

Agent technology has a widespread usage in most of computerized systems. In this paper agent technology has been applied to monitor wear test for an aluminium silicon alloy which is used in automotive parts and gears of light loads. In addition to wear test monitoring, porosity effect on wear resistance has been investigated. To get a controlled amount of porosity, the specimens have been made by powder metallurgy process with various pressures (100, 200 and 600) MPa. The aim of this investigation is a proactive step to avoid the failure occurrence by the porosity.A dry wear tests have been achieved by subjecting three reciprocated loads (1000, 1500 and 2000)g for three periods (10, 45 and 90)min. The weight difference after each test is immediately measured to find the losing weight and wear rate for each specimen. Wear test was monitored online by two sensors, force sensor to control the applied load, find friction force and coefficient of friction. The sensor is an acoustic emission to detect crack initiations of the worn surface by transfers the emitted ultrasonic waves from crack initiations to electric signals. Scanning electron microscope has been used to examine the worn surfaces. The overall results include that the effect of pores depends on pore shapes, sizes and concentrations.

تقنية العميل لها استخدام واسع في معظم الأنظمة المسيطر عليها بواسطة الحاسوب. في هذا البحث تم تطبيق تكنلوجيا العميل لمراقبة فحص البليان لسبيكة الأمنيوم سليكون التي تدخل في صناعة اجزاء السيارات ومنتجات اخرى كتروس اللأحمال الخفيفة. بالاضافة الى مراقبة فحص البلي, تم التحقيق من تأثير المسامية على مقاومة البليان. للحصول على كمية مسيطر عليها من المسامية تم تصنيع العينات بواسطة عملية مساحيق المعادن مع ضغوطات متغيرة (100, 200 و600) ميكا باسكال. الهدف من هذا الفحص هو الخطوة الاستباقية لتجنب حدوث الفشل الناتج من المسامية.اختبارات البلي الجاف قد انجزت عن طريق تسليط ثلاثة احمال تبادلية (1000, 1500 و2000) غم لثلاث فترات (10, 45 و 90) دقيقة. تم قياس الفارق بالوزن مباشرة بعد اختبارات البلي الجاف قد انجزت عن طريق تسليط ثلاثة احمال تبادلية (1000, 1500 و2000) غم لثلاث فترات (10, 45 و 90) دقيقة، وتم قياس الفارق بالوزن مباشرة بعد كل عملية فحص لإيجاد فقدان الوزن ومعدل البلي لكل عينة. اما فحوصات البلي تم مراقبتها بصورة مباشرة بواسطة متحسسين، احدهما متحسس القوى واستخدم لضبط الحمل المسلط ، ايجاد قوة الإحتكاك و معامل الاحتكاك. اما المتحسس الاخر هو متحسس الانبعاثا ت الصوتية لكشف بدايات التصدع في السطح المبلي عن طريق تحويل الموجات فوق الصوتية المنبعثة من بداية التصدع الى اشارة كهربائية. تم استعمال المجهر الماسح الألكتروني لفحص السطوح البالية. تضمنت النتائج بشكل اساس ايجاد تأثير المسامية على مقاومة البليان الذي يعتمد على شكل وحجم وتراكيز المسامات على في المعدن


Article
Study of the effect of non-thermal plasma on the structural properties of pure Cadmium Oxide thin Films (CdO) prepared by Pulsed laser Deposition Technique ( PLD )
دراسة تأثير البلازما الباردة على الخواص التركيبية لأغشية اوكسيد الكادميوم النقية المحضرة بتقنية الترسيب بالليزر النبضي

Authors: Abdul Ameer Hussein Ali عبد الامير حسين علي --- Hussain Ali Noor حسين علي نور --- SaleemAzaraHussain سليم عزاره حسين
Journal: Journal of Kufa - physics مجلة الكوفة للفيزياء ISSN: 20775830 Year: 2019 Volume: 11 Issue: 01 Pages: 63-70
Publisher: University of Kufa جامعة الكوفة

Loading...
Loading...
Abstract

In this research, the preparation of pure ( CdO ) films on a glass substrate was conducted using pulsed laser deposition method (PLD) .The deposition of the films was done at different times ( 5 , 10 , 15 , 20 ) minutes at room temperature . The effect of non-thermal plasma on these prepared films in two exposure times of (30, 60) minutes was studied. The results of X-ray diffraction (XRD) of the prepared pure (CdO) films showed that the films have polycrystalline structure of cubic phase with preferred orientation (111) . It was noted that the increasing of deposition time of (Nd : YAG) laser , reduces the intensity of diffraction peaks at (111 ) , (200) , (220) . The results of (XRD) have also showed that when the prepared pure ( CdO ) films are exposed to non-thermal plasma , their crystalline structure was not affected . The tests also showed that the increasing of the exposure time to non-thermal plasma causes a decrease in the intensity of the diffraction peaks. The (AFM) tests also demonstrated that the changing in ( RMS ) of the surface roughness is irregular and it was found that the ( RMS ) increases by increasing the deposition time

في هذه الدراسة تم تحضير ودراسة الخصائص التركيبية لأغشية اوكسيد الكادميوم النقية على قواعد زجاجية والمحضرة بتقنية الترسيب بالليزر النبضي (PLD) وبأزمان ترسيب مختلفة (20,15,10,5) دقيقة , وبدرجة حرارة الغرفة وتأثير البلازما الباردة على هذه الأغشية المحضرة بحالتين للتعرض (60,30) دقيقة , واظهرت نتائج حيود الأشعة السينية (XRD) لأغشية (CdO) النقية المحضرة أن تركيب الأغشية كان متعدد التبلور (Polycrystalline) من النوع المكعب (Cubic), وأن الاتجاه المفضل للنمو هو (111) للأغشية المحضرة قبل وبعد التعرض للبلازما الباردة , وتبين ان بزيادة زمن الترسيب بالليزر نيدميوم–ياك(Nd:YAG) قلل من شدة قمم الحيود بشكل قليل جداً للذروات (220) ,(200) ,(111), كما تبين من نتائج (XRD) عند تعرض أغشية (CdO) النقية المرسبة للبلازما الباردة لا تؤثر على طبيعة التركيب البلوري , وتبين ان بزيادة زمن التعرض للبلازما الباردة ادى الى انخفاض في شدة قمم الحيود بشكل قليل , واظهرت نتائج فحوصات (AFM) ان التغير في (RMS) غير منتظم الا انهُ بزيادة زمن التعرض للبلازما الباردة يصبح التغير في (RMS)الى حد ما منتظم ونلاحظ زيادة (RMS) بزيادة زمن الترسيب