The casting ability of Non precious alloy used for ceramic restoration After remelting and treatment with new alloy
قابلية الصب لسبيكة من المعدن الغير ثمين والمستعمل لتعويضات السيراميك بعد إعادة تذويبها ومعاملتها مع معدن جديد

Author: Anaam sh.AL-hadad
Journal: journal of kerbala university مجلة جامعة كربلاء ISSN: 18130410 Year: 2011 Volume: 9 Issue: 1 Pages: 251-258
Publisher: Kerbala University جامعة كربلاء

Loading...
Loading...
Abstract

The high cost of gold and other noble metals over the past 25 years have necessitated the use of non precious alloy for the fabrication of fixed dental prosthesis . Castability is of great clinical signification since it is closely related to marginal fit, that in turn may effect the periodontal health because short margin may be more plaque retentive .This investigation for evaluating the castability of one type of non precious alloy after several remelting procedure with the addition of 50% and 35% by weight of new alloy . Three generation of remelting were performed , one without the addition of any new alloy , the second with the addition of 50% by weight of new alloy, and third with the addition of 35% by weight of new alloy.A test pattern composed of wax mesh section approximately 40 mm x 40 mm , attached to V-shaped sprue rods 5mm long . A castability value was obtained by counting complete segments of cast alloy grid to identify the quantitative and qualitative constituents of the alloy after several treatment procedure . Test results indicated that whenever remelting required for any type of dental alloy , it should be accomplished with the addition of 50% or at least 35% by weight of new alloy for remelting procedure to obtain a better castability performance .

إن ارتفاع أسعار الذهب والمعادن النبيلة خلال الخمسة والعشرون سنة الاخيرة أوجد ضرورة استعمال سبائك بديلة ذات نسبة قليلة من الذهب لتصنيع التعويضات السنية الثابتة Fixed dental prosthesis )). ان قابلية الصب للمعدن ذات أهمية كبيرة في العيادة لأنها تعود بشدة إلى انطباق حافة التعويضات الثابتة على الأسنان الساندة لتلك التعويضات والتي بدورها تؤثر على صحة اللثة , لان الحافات القصيرة هي الأكثر تجميعاً لمادة البلاك . أجريت هذه الدراسة لتقييم قابلية الصب لسبيكة من معدن غير ثمين بعد إعادة تذويبها لعدة مرات مع إضافة كمية من المعدن الجديد بنسبة 35% و 50% . ووفقاً لذلك تم تذويب المعدن على شكل ثلاث حالات، الأول إذابة المعدن بدون إضافة أي نسبة من المعدن الجديد , الثاني إضافة نسبة 50% من المعدن الجديد , والثالث اضاقة 35% من المعدن الجديد لقد تم اختيار نموذج الاختبار وفقاً لدراسات سابقة ويتكون من مقطع من شبكة شمعية حوالي 40 ملم × 40 ملم تتصل بمصب ( sprue rod ) على شكل حرف Vبطول 5 ملم . وتم تقييم قابلية الصب لكل نموذج بعد إضافة نسب مختلفة من المعدن الجديد (الذي لم يسبق إذابته) باحتساب عدد المقاطع الكاملة في المصبوبة .أظهرت النتائج بأنه عندما تكون هناك حاجة لإعادة صب أي معدن من المعادن يجب أن يكون مقروناً بإضافة 50% وعلى الأقل 35% من المعدن الجديد للحصول على أفضل مصبوبة ذات قابلية صب عالية (96.48 , 84.38) لكلا النسبتين

Keywords


Article
DISINFECTION OF ACRYLIC RESIN CURED BY CONVENTIONAL WATER BATH TECHNIQUE
تطهير مادة الاكريلك المبلمرة بواسطة الحمام المائي الاعتيادي

Author: Anaam sh.AL-hadad
Journal: AL-TAQANI مجلة التقني ISSN: 1818653X Year: 2012 Volume: 25 Issue: 2 Pages: 21-25
Publisher: Foundation of technical education هيئة التعليم التقني

Loading...
Loading...
Abstract

Performing a through disinfection of any dental prostheses before it is transferred to a dental laboratory is the key to prevention of accidental infection of the dentist and dental laboratory personal. This means that a dental prostheses must not only be disinfected on the surfaces but also on the interior material. 12 samples of acrylic plates of 48 mm × 25 mm × 3 mm in dimension were prepared by water bath curing method. The samples were immersed in broth culture of four identified bacteria for 24 hours.Later on, all the specimens were grouped and immersed in three or different disinfectant solution which were lodophor, chlorhexidine, and sodium hypochlorite. They were prepared and used in accordance with manufacturer's recommendations. The control group was normal saline solution. Cultures were made from smooth, rough and interior surface of acrylic samples. Any bacterial growth when existed, was identified by microbiological test. In this study the results demonstrated that bacteria can penetrate acrylic resin plates cured by this technique. However, the only effective disinfectant was 0.525% solution of sodium hypochlorite 10 minute immersion. It disinfect the exterior as well as the interior surfaces of acrylic resin plates of 3 mm thickness

ان تعقيم او تطهير أي من التعويضات السنية قبل تحويلها الى المختبر تعتبر هي المفتاح للحماية من التلوث واصابة الطبيب والعاملين في المختبر، وهذا يعني ان التعويضات السنية يجب ان تعقم في العمق وليس تطهيرا للسطوح الخارجية فقط. لقد تم تحضير 12 نموذجا من مادة الاكريلك على شكل صفائح ذات ابعاد483×25× ملم. كانت عملية البلمرة (curing) لتلك النماذج قد تمت باستخدام الحمام المائي الاعتيادي، ثم ان النماذج قد غطست في وسط مايكروبي لأربعة أنواع معروفة من البكتيريا لمدة 24ساعة، بعدها تم تقسيم النتائج الى مجاميع لتوضع في ثلاثة أنواع من المطهرات هي: ايودوفور ، كلورهيكسيدين، صوديوم هايبوكلورايت و وضعت المجموعة الرابعة من االنماذج بمحلول السلاين والتي استعملت بمثابة المجموعة الضابطة. كانت عينات زراعة البكتيريا تؤخذ من السطوح الملساء والخشنة والمناطق الداخلية والعميقة للنماذج. وعند ظهور أي نمو لأي نوع من البكتيريا كان يتم تشخيصه بواسطة الاختبارات المايكروبيولوجية.ان هذه الدراسة أثبتت أمكانية اختراق البكتيريا لمادة الاكريلك المبلمرة بواسطة الحمام المائي الاعتيادي، و أظهرت بان محلول الصوديوم هايبوكلورايت هو الأكثر فعالية لتطهير السطوح الخارجية والعميقة من الاكريلك ذات سمك 3ملم عند غمرها بها لمدة 10 دقائق

Keywords


Article
The Surface Hardness Measurement of Stone and Improved Die Stone After the Addition of a Mixture of Chemical Additives with Different Proportion

Loading...
Loading...
Abstract

Background: Incorporation of chemical additives has long been a technique used to improve properties of the gypsum products. The purpose of this work was to study the effects of adding a combination of gum Arabic and calcium hydroxide to a type III dental stone and type IV improved die stone with different proportion. The effect on water/powder ratio, and surface hardness was determined.Material and method: Both material stone and die stone were blended with two proportion of additives so that each material was mixed twice but with different proportion of gum Arabic (0.1% and 0.2%) and calcium hydroxide (0.5 % and 0.3%). Data for hardness were subjected to two-way analysis of variance.Results: The results revealed that the chemical additives were reduced the water requirements of gypsum products so that the reduction of water lead to increase the density of mixture that sets harder. For type III dental stone the additives significantly improved the surface hardness, while for type IV improved die stone the surface hardness was not enhanced except it was designed to be mixed at low water/powder ratio, and in some instances a reduction in hardness was observed, especially at the most reduced water / powder ratio (0.18)