Article
Effect of Micro Powder on Mechanical and Physical Properties of Glass Fiber Reinforced Epoxy Composite

Authors: Aseel Basim Abdul-Hussein --- Fadhel Abbas Hashim --- Tamara Raad Kadhim
Journal: Engineering and Technology Journal مجلة الهندسة والتكنولوجيا ISSN: 16816900 24120758 Year: 2016 Volume: 34 Issue: 7 Part (A) Engineering Pages: 1402-1414
Publisher: University of Technology الجامعة التكنولوجية

Loading...
Loading...
Abstract

In the present study, composites were prepared by Hand lay-up molding. The composites constituents were epoxy resin as the matrix, 3% volume fractions of Glass Fibers (G.F) as re enforcement and 2%, 4%, 6% volume fraction of micro powder (Aluminum Oxide Al2O3, Silicon Oxide SiO2 and Titanium Oxide TiO2) as filler. Studied the, hardness test, flexural strength, density, water absorption measurements and tests were conducted to reveal their values for each type of composite material. The results showed that the non – reinforced epoxy have lower properties than nano composites material. Measured density results had show an incremental increase with volume fraction increase and water absorption, hardness, and flexural strength had show an incremental increase with volume fraction increase and with smaller particle size.


Article
Comparison Study of Erosion Wear and Hardness of GF/EP with Nano and Micro SiO2 Hydride Composites
دراسة مقارنة بلى التعريه والصلاده لمتراكبات الايبوكسي والياف الزجاج المدعمه بنانو ومايكرو ثاني اوكسيد السليكون(SiO2)

Authors: Aseel Basim Abdul-Hussein --- Fadhel Abbas Hashim --- Tamara Raad Kadhim
Journal: Engineering and Technology Journal مجلة الهندسة والتكنولوجيا ISSN: 16816900 24120758 Year: 2015 Volume: 33 Issue: 9 Part (B) Scientific Pages: 1761-1774
Publisher: University of Technology الجامعة التكنولوجية

Loading...
Loading...
Abstract

The objective of this research is to study GF / EP nano and micro silicon dioxide (SiO2)composites were prepared with different volume percentage of nano and micro SiO2 powder (2,4,and 6 wt.% ). Atomic force microscopy techniques was used to measure the grain size of nano SiO2 powder (average diameter 38nm) and particle size analyzer techniques was used to measure the grain size of micro SiO2 powder (average diameter 6.069µm). Erosive wear behavior of this composite under three different impingement angles 30°, 60° and 90°and three angular silica sand abrasive particle sizes approximately 425, 600 and 850 μm and hardness (shore D) were study.In general the erosion wear of micro composites have lower resistance erosion than nanobased Materialcomposites other. Erosion resistance increase as the volume fraction increase. Nano composites of GF / EP with SiO2 have many advantages over micro composites from the view point of wear and hardness tests. The worn surface features of unfilled and filled G-E composites were examined using scanning electron microscopy (SEM) and results indicates more severe damage to matrix and glass fiber in unfilled composite system as compared to SiO2 filled composites.

الهدف من هذا البحث هو دراسة متراكبات الايبوكسي والياف الزجاج المدعمه بنانو ومايكرو ثاني اوكسيد السليكون (SiO2 ) مع نسبة حجمية مختلفة من نانو ومايكرو مسحوق SiO2(2و 4و6%). تم استخدام تقنيات مجهر القوة الذرية لقياس حجم مسحوق النانو SiO2 (متوسط قطرها nm38) وتقنيات تحليل حجم الجسيمات كان يستخدم لقياس حجم مسحوق المايكرو SiO2 (متوسط قطرها μm 6.069).سلوك بلى التعرية من هذا المركبة تحت ثلاثة زوايا مختلفة 30 درجة، 60 درجة و 90 درجة وثلاث احجام من رمل السيليكا حوالي 425 و 600 و 850 ميكرون. ودراسة صلاده شور (D) .بشكل عام بلى التعريةالمركبة المايكرو يكون أقل مقاومة للتعريه من النانو استنادا المركبة المواد الأخرى.مقاومة البلى تزداد مع زياده الكسر الحجمي . المركبات النانويه من الايبوكسي والياف الزجاج مع SiO2 لديها العديد من المزايا على المركبات المايكرويه من وجهة نظر من بلى التعريه واختبار الصلادة. تم فحص السمات السطحية البالية من المواد المركبة GE باستخدام المجهر الإلكتروني الماسح (SEM) والنتائج تشير إلى المزيد من الضرر الشديد إلى الاساس والألياف الزجاجية في نظام الغير مدعمه بالمقارنة مع المركبة الحاويه على مركب SiO2.


Article
Effect of Nature Materials Powders on Mechanical and Physical Properties of Glass Fiber / Epoxy Composite
تأثير مساحيق اساسها مواد طبيعية على الخواص ميكانيكية وفيزياوية لمواد مركبة من ايبوكسي والياف زجاج

Authors: Aseel Basim Abdul-Hussein --- Emad Saadi AL-Hassani --- Reem Alaa Mohammed
Journal: Engineering and Technology Journal مجلة الهندسة والتكنولوجيا ISSN: 16816900 24120758 Year: 2015 Volume: 33 Issue: 1 Part (A) Engineering Pages: 175-197
Publisher: University of Technology الجامعة التكنولوجية

Loading...
Loading...
Abstract

In the present study composites were prepared by Hand lay-up molding. The composites constituents were epoxy resin as the matrix, 6% volume fractions of Glass Fibers (G.F) as reinforcement and 3%, 6% of nature material (Rice Husk Ash, Carrot Powder, and Sawdust) as filler. Density, water absorption, hardness test, flexural strength, shear stress measurements and tests were conducted to reveal their values for each type of composite. True density results had shown an incremental increase with volume fraction increasing and water absorption, hardness, flexural strength and shear stress results had shown an incremental increase with volume fraction increasing with smaller particle size.

تم في هذا البحث تحضير مواد متراكبه بواسطة طريقة القولبة اليدوية. المواد المتراكبة مكونة من راتنج الايبوكسي كماده اساس وبألياف الزجاج بكسر حجمي 6% وكذلك 3% و 6 % كحشوة من المواد الطبيعية ( رماد قشور الارز , مسحوق الجزر , بودرة خشب جاوي ) . تم اجراء قياسات وفحوصات الكثافة وامتصاصية الماء وفحص الصلادة, مقاومة الانحناء , اجهاد القص للكشف عن قيمها لكل نوع من المواد المتراكبة . عند اجراء اختبارات الكثافة فان النتائج اظهرت بان الكثافة تزداد مع زيادة الكسر الجحمي والنتائج اظهرت بان امتصاصية الماء والصلادة ومقاومة الانحناء واقصى اجهاد قص يزداد مع زياد الكسر الجحمي و مع اصغر حجم حبيبي .


Article
Erosion Wear Behavior of Industrial Material Reinforced Epoxy Resin Composites and its Coating with Natural Based Material
سلوك بلى التعرية لمواد الصناعية المدعمة براتتج الايبوكسي وطلائها مع مادة اساسها طبيعي

Authors: Aseel Basim Abdul-Hussein --- Emad Saadi AL-Hassani --- Reem Alaa Mohammed
Journal: Engineering and Technology Journal مجلة الهندسة والتكنولوجيا ISSN: 16816900 24120758 Year: 2015 Volume: 33 Issue: 4 Part (A) Engineering Pages: 902-918
Publisher: University of Technology الجامعة التكنولوجية

Loading...
Loading...
Abstract

In the present study, composites were prepared by Hand lay-up molding The composites constituents were epoxy resin as a matrix, 6% volume fractions of Glass Fibers (G.F) as reinforcement and 3%, 6% volume fractions of preparation industrial powder (calcium carbonate CaCO3, potassium carbonate K2CO3 or sodium carbonate Na2CO3) as filler. The erosion wear behavior and coating by natural wastes (Rice Husk Ash) with epoxy resin after erosion were studied. The results showed that the non – reinforced epoxy have lower resistance erosion than industrial based Material composites and the specimen (Epoxy+6%glass fiber+6% CaCO3) has higher resistance erosion than composites reinforced with sodium carbonate and potassium carbonate at 25cm, angle 30°, grin size of sand 850µm, temperature 25Ċ, 200 gm salt content in 3liter of water and 15 hour. Coating specimen with mixed epoxy resin -RHA with particles size in the range (1.4-4.2) µm improves erosion wear resistance characteristics of the coated specimen, coating thickness was (16 ± 1) μm and after erosion in (15 hours) the thickness was (10) μm .Application of the work protection of pipes from erosion, these pipes include the sewage water , drainage pipe laboratory (hot water, chemicals and mineral oil) , pipeline transportation of petroleum products and pipeline transportation of gas products

تم في هذا البحث تحضير المواد المتراكبة بواسطة طريقة القولبة اليدوية. تتكون المواد المتراكبة من راتنج الايبوكسي كماده اساس والياف الزجاج كمادة تقوية بكسر حجمي 6% و مساحيق طبيعية محضرة (كاربونات الكالسيوم , كاربونات الصوديوم اوكاربونات البوتاسيوم ) بكسر حجمي (3% , 6% ) دراسة سلوك بلى التعرية والطلاء بواسطة النفايات الطبيعية (رماد قشور الرز) مع راتنج الايبوكسي بعد التعرية . النتائج اظهرت بان الايبوكسي غير المقوى يمتلك مقاومة للتعرية قليلة من المواد المتراكبة التي اساسها مواد طبيعة والعينة (الايبوكسي + 6%الالياف زجاج + 6% كاربونات الكالسيوم) تملك مقاومة للتعرية من المواد المتراكبة المدعمة بمسحوق الجزر وبودرة الخشب عند25 سم ، زاوية 30º، حجم دقائق تعرية 850 مايكرون , ودرجة حرارة 25Ċ ,200 غم ملح في 3 لتر من ماء 15 ساعة . طلاء العينات براتنج الايبوكسي مع رماد قشور الرز مع حجم حبيبي ضمن المدى (1.4-2.4) مايكرون لتحسين خواص مقاومة التعرية للعينات التي تم طلائها , وسمك الطلاء كان (16 ± 1) مايكرون وبعد التعرية عند 15 ساعة اصبح سمك الطلاء (10) مايكرون. تطبيق هذا الدراسة هو حماية الانابيب من التعرية , وهذة الانابيب تتضمن انابيب الصرف الصحي ,انابيب الصرف لمختبرات (الماء الساخن ، المواد الكيمياوية والزيوت ) وانابيب نقل المنتجات النفطية والغازية .


Article
EFFECT OF CARBON NANO TUBES ON EROSION WEAR OF CARBON FIBER, GLASS FIBER & KEVLAR FIBER REINFORCED UNSATURATED POLYESTER COMPOSITES

Authors: Marwa Subhi Atallah --- Emad Saadi Abdel Kareem --- Aseel Basim Abdul-Hussein
Journal: Journal of Engineering and Sustainable Development مجلة الهندسة والتنمية المستدامة ISSN: 25200917 Year: 2018 Volume: 22 Issue: 4 Pages: 74-89
Publisher: Al-Mustansyriah University الجامعة المستنصرية

Loading...
Loading...
Abstract

In the present study, nano composites were prepared by Hand lay-up molding. The nano composites component of the unsaturated polyester resin (UP) as a matrix, 3% volume fractions of Carbon Fiber (C.F), Glass Fibers (G.F), Kevlar Fiber (K.F) as reinforcement and (0.5%,1%, 1.5% and 2%) volume fractions of Carbon Nanotubes (CNTs) as filler. The erosion wear behavior of this nano composite at four different impingement angles 30°, 45°, 60° and 90° and four angular silica sand abrasive particle sizes 400, 500 , 600 and 800 μm and density were studied. The results showed that the specimens (UP + 3% (GF, CF, KF) +2% CNTs) have the maximum density when compared with the other volume fractions. The non – reinforced unsaturated polyester have lower erosion resistance than nano composites and the specimen (polyester +3% carbon fiber + 0.5% CNTs) has higher erosion resistance than other nano composites at 15cm, angle 30°, grin size of sand 400µm and 15 hour. Application of this work in protection of aircraft structure, turbine blades and pipes from erosion. The Taguchi experimental design ANOVA shows that the filler content factor has great effect on erosion rate of CNTs filled carbon, glass and Kevlar fibers reinforced unsaturated polyester resin.


Article
Effect of Nano Powder on Mechanical and Physical Properties of Glass Fiber Reinforced Epoxy Composite
تأثير المساحيق النانويه على الخواص الميكانيكية والفيزيائية للمواد المركبة المدعمة بالالياف الزجاج

Authors: Tamara Raad Kadhim تماره رعد --- Fadhel Abbas Hashim فاضل عباس هاشم --- Aseel Basim Abdul-Hussein اسيل باسم عبد الحسين
Journal: Al-Khwarizmi Engineering Journal مجلة الخوارزمي الهندسية ISSN: 18181171 23120789 Year: 2016 Volume: 12 Issue: 3 Pages: 72-79
Publisher: Baghdad University جامعة بغداد

Loading...
Loading...
Abstract

Fiber reinforced polymer composite is an important material for structural application. The diversified application of FRP composite has taken center of attraction for interdisciplinary research. However, improvements on mechanical properties of this class of materials are still under research for different applications. In this paper we have modified the epoxy matrix by Al2O3, SiO2 and TiO2 nano particles in glass fiber/epoxy composite to improve the mechanical and physical properties. The composites are fabricated by hand lay-up method. It is observed that mechanical properties like flexural strength, hardness are more in case of SiO2 modified epoxy composite compare to other nano modifiers, were physical properties like density, water absorption are more in case of TiO2 modified epoxy composite. This may be because of smaller particle size of silica compare to others.

تم في هذا البحث تحضير مواد متراكبه بواسطة طريقة القولبة اليدوية ودراسة خصائصها. تتكون المواد المتراكبة من راتنج الايبوكسي كماده اساس و3% كسر حجمي من ألياف الزجاج كمادة تقوية و 2% و4% و 6% لمساحيق نانويه ( اوكسيد الالمنيوم Al2O3, اوكسيد السليكون SiO2 , اوكسيد التيتانيوم TiO2 ). فحص الصلاده ومقاومة الانحناء والكثافه والامتصاصيه للكشف عن قيمها لكل نوع من المواد المتراكبة النانويه. اظهرت النتائج ان الايبوكسي غير المقوى يمتلك خواص اقل من المواد المتراكبة . عند اجراء اختبارات الكثافة فان النتائج اظهرت بان الكثافة تزاد مع زياد الكسر الحجمي وامتصاصية الماء والصلادة ومقاومة الانحناء بانها تزداد مع زيادة الكسر الحجمي مع اصغر حجم حبيبي .


Article
Effect of industrial powder on mechanical properties of glass fiber reinforced epoxy composite
تأثير المساحيق الصناعية على الخواص الميكانيكية للمواد المركبة المدعمة بألياف الزجاج

Loading...
Loading...
Abstract

In the present study, composites were prepared by Hand lay-up molding and investigated. The composites constituents were epoxy resin as the matrix, 6% volume fractions of Glass Fibers (G.F) as reinforcement and 3%, 6% of industrial powder (Calcium Carbonate CaCO3, Potassium Carbonate K2CO3 and Sodium Carbonate Na2CO3) as filler. Density, water absorption, hardness test, flexural strength, shear stress measurements and tests were conducted to reveal their values for each type of composite material. The results showed that the non – reinforced epoxy have lower properties than composites material. Measured density results had show an incremental increase with volume fraction increase and water absorption, hardness, flexural strength and shear stress results had show an incremental increase with volume fraction increase and with smaller particle size.

تم في هذا البحث تحضير مواد متراكبه بواسطة طريقة القولبة اليدوية ودراسة خصائصها. تتكون المواد المتراكبة من راتنج الايبوكسي كماده اساس وبألياف الزجاج بكسر حجمي6% وكذلك 3%و 6% مساحيق صناعية تدعيم من (كاربونات الكاليسوم CaCO3, كاربونات البوتاسيوم K2CO3, كاربونات الصوديوم Na2CO3). تم اجراء فحوصات الكثافة وامتصاصية الماء، فحص الصلادة, مقاومة الانحناء و اجهاد القص للكشف عن قيمها لكل نوع من المواد المتراكبة. اظهرت النتائج ان الايبوكسي غير المقوى يمتلك خواص اقل من المواد المتراكبة. عند اجراء اختبارات الكثافة فان النتائج اظهرت بان الكثافة تزاد مع زياد الكسر الحجمي وامتصاصية الماء والصلادة ومقاومة الانحناء واقصى اجهاد قص بانها تزداد مع زيادة الكسر الحجمي مع اصغر حجم حبيبي.


Article
Influence of Coating with Some Natural Based Materials on the Erosion Wear Behavior of Glass Fiber Reinforced Epoxy Resin
تأثير الطلاء لبعض المواد المتراكبة التي اساسها مواد طبيعية على سلوك بلى التعرية لراتنج الايبوكسي المدعم بالالياف الزجاجية

Loading...
Loading...
Abstract

In the present study, composites were prepared by Hand lay-up molding. The composites constituents were epoxy resin as a matrix, 6% volume fractions of glass fibers (G.F) as reinforcement and 3%, 6% volume fractions of preparation natural material (Rice Husk Ash, Carrot Powder, and Sawdust) as filler. Studied the erosion wear behavior and coating by natural wastes (Rice Husk Ash) with epoxy resin after erosion. The results showed the non – reinforced epoxy have lower resistance erosion than natural based material composites and the specimen (Epoxy+6%glass fiber+6%RHA) has higher resistance erosion than composites reinforced with carrot powder and sawdust at 30cm , angle 60°, grin size of sand 425µm , temperature 30Ċ , 300 gm salt content in 2liter of water and 15 hour. Coating specimen with mixed epoxy resin -RHA with particles size in the range (1.4-4.2) µm improves erosion wear resistance characteristics of the coated specimen, coating thickness was (16 ± 1) μm and after erosion at (15 hour) the thickness was (10) μm .

تم في هذا البحث تحضير المواد المتراكبة بوساطة طريقة القولبة اليدوية . تتكون المواد المتراكبة من راتنج الايبوكسي ماده اساس والياف الزجاج مادة تقوية بكسر حجمي 6% و مساحيق طبيعية محضرة ( رماد قشور الرز و مسحوق الجزر و بودرة الخشب ) بكسر حجمي (3% , 6% ) . دراسة سلوك بلى التعرية والطلاء بوساطة النفايات الطبيعية (رماد قشور الرز) مع راتنج الايبوكسي بعد التعرية . النتائج اظهرت بان الايبوكسي غير المقوى يمتلك مقاومة للتعرية قليلة من المواد المتراكبة التي اساسها مواد طبيعة والعينة (الايبوكسي + 6%الالياف زجاج + 6% رماد قشور الرز) تملك مقاومة للتعرية من المواد المتراكبة المدعمة بمسحوق الجزر وبودرة الخشب عند25 سم ، زاوية 30º، حجم دقائق تعرية 850 مايكرون , ودرجة حرارة 25Ċ ,200 غم ملح في 3 لتر من ماء 15 ساعة . طلاء العينات براتنج الايبوكسي مع رماد قشور الرز مع حجم حبيبي ضمن المدى (1.4-2.4) مايكرون لتحسين خواص مقاومة التعرية للعينات التي تم طلائها , وسمك الطلاء كان (16 ± 1) مايكرون وبعد التعرية عند 15 ساعة اصبح سمك الطلاء (10) مايكرون .


Article
Mechanical and physical properties of carbon nanotubes with Kevlar fiber reinforced with polyester resin
الخواص الميكانيكية و الفيزيائية لانابيب الكاربون النانوية مع الياف الكفلر المقواة مع راتنج البولي استر

Loading...
Loading...
Abstract

In this research study Hardness (shore D), Water absorption, Flexural, Impact Test, and Fracture Toughness of polymer nano composites.The polymer nano composites based on unsaturated polyester resin reinforced with Kevlar fibers (K.F). The samples are attended by hand lay – up method according to (Rule mixture) for various volume fractions of unsaturated polyester resin, fiber and carbon nanotube. The polyester resin was matrix strengthened with 3% volume fraction from Kevlar fiber and (0.5%, 1%, 1.5%, 2%( volume fractions of carbon nanotube. The water absorption, hardness (shore D), flexural test, impact testand toughness fracture properties were studied. Results showed that the water absorption increase with volume fraction increase of fiber with Carbon Nanotube, the sample (polyester+3%K.F+0.5% CNTs) has lower water absorption than other samples. The hardness (shore D), flexural test, impact testand toughness fracture for the sample (polyester+3%C.F+0.5% CNTs) has higher value for Nano- composites. Nano composites, Carbon nanotube, Kevlar fiber, Hardness (shore D), Water absorption, Flexural Strength, Impact Test, Toughness Fracture.

تم في هذا البحث دراسة الصلادة (شورD), امتصاصية الماء, مقاومة الكسر, اختبار الصدمة و متانة الكسر لمتراكبات نانوية ذات اساس راتنج البولي استر غير المشبع مقواة بألياف الكفلر. العينات جهزت بطريقة الصب اليدوي وفقالقاعدة الخلط لكسور حجمية مختلفة من راتنج البولي استر غير المشبع والالياف وانابيب الكاربون النانوية. راتنج البولي استر كان ارضية مقواة مع 3%كسر حجمي من الياف الكفلر و (0.5 ,1 ,1.5 , 2 ) % كسر حجمي لانابيب الكاربون النانوية. تم دراسة خواص امتصاصية الماء, صلادة (شور(D, اختبار الصدمة ومقاومة الكسر. اظهرت النتائج بان امتصاصيه الماء تزداد مع زيادة الكسر الحجمي للالياف مع انابيب الكاربون النانوية, العينه (بولي استر + 3% الياف كفلر + 0.5 % انابيب اكاربون النانوية) تمتلك اقل امتصاصية ماء من العينات الاخرى. الصلادة (شورD), فحص الكسر, فحص الصدمة ومتانة الكسر للعينه (بولي استر +3% الياف كفلر + 0.5 %انابيب الكاربون انانوية) تمتلك اعلى قيمه للمتراكبات النانوية.

Listing 1 - 9 of 9
Sort by
Narrow your search

Resource type

article (9)


Language

English (7)

Arabic and English (2)


Year
From To Submit

2018 (1)

2016 (3)

2015 (4)

2014 (1)