Article
Compressive Strength and Physical Properties Behavior of Cement Mortars with addition of Cement Klin Dust

Author: Auday A. Mehatlaf
Journal: Journal of University of Babylon مجلة جامعة بابل ISSN: 19920652 23128135 Year: 2018 Volume: 26 Issue: 1 Pages: 114-121
Publisher: Babylon University جامعة بابل

Loading...
Loading...
Abstract

Cement Klin Dust (CKD) was the waste of almost cement industry factories, so that in this paper utilization of CKD as filler in cement and/or concrete was the main objective. CKD from the Karbala cement factory had been used and analysis to know the chemical composition of the oxides was done. In this paper cement mortars with different weight percentages of CKD (0,5,10,20,30,40) had been prepared. Physical properties such as density and porosity were done in different age curing (3, 7, 28) day. In addition, mechanical properties included the coefficient of thermal conductivity and compressive strength had also observed with different age (3,7, and 28) for all prepared specimens. From the obtained the experimental results and their discussion, it was clear that the addition (20%) of CKD had the good results in cement mortars.

غبار فرن السمنت هو مخلفات من معامل صناعة السمنت، لذلك في هذا البحث استخدام غبار فرن السمنت كمادة مالئة في السمنت والخرسانة هو الهدف الرئيسي . استخدم فرن غبار السمنت من معمل سمنت كربلاء وتم تحليله لمعرفة التركيب الكيميائي للأكاسيد.في هذا البحث حضرت مونة السمنت مع اضافة نسب وزنية مختلفة من فرن غبار السمنت (0،5،10،20،30،40). الخواص الفيزياوية مثل الكثافة والمسامية تم حسابها عند اعمار تقسية مختلفة (3،7،28) يوم. بالأضافة الى ذلك الخواص الميكانيكية المتضمنة معامل التوصيل الحراري و مقاومة الأنضغاط تم قياسها بأعمار مختلفة (3،7،28) ولكل العينات المحضرة . من نتائج العملي المستحصلة ومناقشتها تبين ان الأضافة 20% من غبار فرن السمنت اظهر نتائج جيدة في مونة السمنت.


Article
Synthesis and Studying SomeMechanical Properties of Nanocomposite
تصنيع متراكب نانوي ودراسة بعض خواصه الميكانيكية

Authors: Fadhil A. Chyad --- Abdul-Raheem K.Abid Ali --- Auday A. Mehatlaf
Journal: Engineering and Technology Journal مجلة الهندسة والتكنولوجيا ISSN: 16816900 24120758 Year: 2013 Volume: 31 Issue: 7 Part (A) Engineering Pages: 1221-1228
Publisher: University of Technology الجامعة التكنولوجية

Loading...
Loading...
Abstract

This study aims to synthesis a nanocomposite from Al2O3 – Cr2O3 and studying some of its mechanical properties like microhardness and fracture strength. X-Ray diffraction patterns shows a good crystallinity of the composite with very sharp and neat peaks. TEM photographs shows the good distribution of the particles which have an average particle size of (3-6 nm). The microhardness is increased with the increasing of sintering temperatures having the height value at 15% chromia while the fracture strength behaves as a bell shape having again the height value at 15% chromia.

الخلاصةيهدف البحث الى تحضير متراكب نانوي من الألومينا والكروميا ودراسة بعض الخواص الميكانيكية مثل الصلادة المجهرية ومتانة الكسر. أظهرت فحوصات حيود الأشعة السينية ببلورية جيدة لهذا المتراكب حيث القمم الحادة والنظيفة. أما صور المجهر الألكتروني الخارق اظهر ان توزيع الحجم الحبيبي جيد ومعدل الحجم الحبيبي(6-3)نانومتر. أزدادت قيم الصلادة بزيادة درجة حرارة التلبيد وكانت اعلى صلادة لنسبة 15% من الكروميا. اما متانة الكسر ايضا ازدادت مع نسبة الكروميا وايضا نسبة 15% هي الأعلى ومن ثم تبدأ بالنزول.