COMPARISON STUDY OF JOINING Ni-ALLOY WITH GRAPHITE

Author: Awfa Abdul-Rassol Abdullah
Journal: Al-Nahrain Journal of Science مجلة النهرين للعلوم ISSN: (print)26635453,(online)26635461 Year: 2010 Volume: 13 Issue: 4 Pages: 110-120
Publisher: Al-Nahrain University جامعة النهرين

Loading...
Loading...
Abstract

Modeling of diffusion bonding of Inconel 600 /Pyrolytic Graphite and Inconel 600/steelinterlayer/Pyrolytic Graphite is investigated in this research. Modeling implies utilization ofANSYS package to predict axisymmetric thermoelastic finite element analysis from the abovematerials. The model is used; to calculate thermal stresses induced across diffusion bonded joints.Investigating thermal stress levels along the potential failure interface for both joints is extremelyhelpful; these residual stresses are mostly the forces of joint failure for both joints. Axisymmetricfinite element analysis involves applying temperature along the whole joint as main parameter; thesecond parameter was changing the steel interlayer.

Keywords


Article
Transition Analysis to Study the Effect of Cooling Rates on Thermal Stresses for Diffusion Bonded Joints

Author: Awfa Abdul-Rassol Abdullah
Journal: Al-Nahrain Journal of Science مجلة النهرين للعلوم ISSN: (print)26635453,(online)26635461 Year: 2013 Volume: 16 Issue: 1 Pages: 91-97
Publisher: Al-Nahrain University جامعة النهرين

Loading...
Loading...
Abstract

In this work the analytical and numerical methods were used to calculate the residual stresses induced in the joint due to the deference in the physical and mechanical properties of the materials, cooling from bonding temperature to room temperature. The residual stresses induced in graphite may be become too high that the joint break down so it takes as major stress in the joint. It was found that the residual stress is affected by the joint geometry and the nickel interlayer thickness. The analytical calculation of the residual thermal stresses in graphite/Inconel 600 and Inconel 600/nickel interlayer/Graphite multilayered was done for bonding temperature Tbond=800oCwith various nickel foil thickness, it found that increasing nickel thickness reduce the thermal residual stresses inside the graphite. Numerical method by FEM was used to estimate the distribution of the maximum residual stresses (first principle stress) in the joint. The results indicate that increasing nickel thickness reduces the maximum tensile residual stress. So the joint thicknesses with graphite (5 mm) /Ni (0.1-0.2)mm/ Inconel600 (5 mm) are convenient.

يَتضمن البحث دِراسة الاجهادات المتبقية في وصلة اللحام وخاصة أثناء ااتبريد من أختلاف الخواص الفيزيائية والميكانيكية لمواد المزمع ربطها في الوصلة، وقد تكون هذه الاجهادات عالية لدرجة تؤدي الى تكسر الكرافيت وفشل وصلة اللحام بعد أنتهاء التبريد أو الى الفشل أثناء الأستخدام. لذا تم أعتماد قيم الأجهادات المتبقية في الكرافيت كأهم الأجهادات المتبقية في وصلة اللحام ولمقارنة تأثير المتغيرات المستخدمة في التحليل النظري للأجهادات الحراريـة الناتجـة عـن اللحـام في درجـة حـرارة (Tbond=800oC) لوصلة أنكونل مع الكرافيت بالأضافة الى أستخدام رقائق من النيكل النقي المختلفة السمك وجد أن قيم الأجهادات المتبقية تقل مع زيادة سمك النيكل. أستخدمت طريقة العناصر المحددة (FEM) في التحليل العددي لقيم الأجهادات المتبقية ولتخمين توزيعها فيوصلة اللحام. أستخدم الأجهاد الأساسي الأول (first principle stress) كقيمة مقارنة بين النتائج المستحصلة من هذه التحاليل. أظهرت النتائج أن أعلى قيمة للأجهاد الأساسي الأول في الكرافيت يقـل مع زيادة سمك النيكل لذا وصلة اللحام بالأبعاد graphite(5mm)Ni (0.1-0.2mm)(Inconel600 (5mm تعتبر مناسبة.

Keywords


Article
Study on Bond Strength of Bonded Gray Cast Iron

Authors: Awfa Abdul-Rassol Abdullah --- Rasha Rahman Rawhdan
Journal: Al-Nahrain Journal of Science مجلة النهرين للعلوم ISSN: (print)26635453,(online)26635461 Year: 2014 Volume: 17 Issue: 2 Pages: 94-100
Publisher: Al-Nahrain University جامعة النهرين

Loading...
Loading...
Abstract

In the present study, two gray cast iron specimens were diffusion bonded at the temperatures of 700, 750, 800, 850, and 900 °C, the furnace used atmosphericexperiment under a pressing load of 1 and 2 ton for 15, 30 and 60min. After diffusion bonding, shear test measurements of interface region were made. As a result, from the microstructural observations, a good bonding along the interface of the bonded couples were detected since the interface is free from voids and microcracks. To evaluate the bond strength, the shear test investigation was used. The actual bonded area was calculated by using a computer package called (Auto Cad 2006). The results shows that the bond strength increases with increasing the temperature and holding time. Fracturography of the interface was carried out by using optical microscope before and after the experiments. The microstructure results shows the formation of carbide. Its precipitation increases with increasing the bonding temperature and time.

يتضمن البحث دراسة الربط الانتشاري لحديد الزهر الرمادي بالظروف الجوية باستخدام طرق تسخن مختلفة 900,850,800,750,700°م، وباستخـدام قـوة كبـس2,1 طن بأزمان مختلفة 60,30,15 دقيقة لإيجاد الظروف العملية المناسبه التي تؤثر على متانة الربط. قيمت متانة الربط باستخدام فحص القص وأظهرت النتائج إن متانة الربط تزداد مع ازدياد درجات الحرارة وكذلك متانةالربـط تـزداد مع ازدياد الوقـت. استخدم برنامج(Auto Cad 2006) لحساب مساحه التماس. لوحظ عند استخدام غاز الاركون انه لم تتكون وصله ربط بسبب الاكسده. بعد استبيان النتائج التي تم الحصول عليها من الدراسة ألمختبريه تبين إن الوصلات المربوطة وجدت مقاومة قص قصوى تساوي 155.7 ميكاباسكال عند ربطها في درجه حرارة 900°م تحت قوة كبس 1 طن ولفترة تسخين 30 دقيقة. وتبين من اختبارات الفحص المجهري تكون أطواركاربيدية (Carbides) وترسيبها على سطح العينة وداخل السطح البيني.


Article
Microstructure Characteristics in the Interface Zone of Gray Cast Iron Solid State Bonds
دراسة البنية الدقيقة للاسطح البينية لمنطقه ربط الحديد الزهر الرمادي

Authors: Awfa Abdul-Rassol Abdullah --- Rasha Rahman Rawhdan
Journal: Engineering and Technology Journal مجلة الهندسة والتكنولوجيا ISSN: 16816900 24120758 Year: 2014 Volume: 32 Issue: 1 Part (B) Scientific Pages: 15-22
Publisher: University of Technology الجامعة التكنولوجية

Loading...
Loading...
Abstract

In the present study, gray cast iron was diffusion bonded under air atmosphere and in inert environment (argon). In air it was carried out at the temperatures of 700, 750, 800, 850, and 900 °C under UN pressing load of 1 and 2 ton for 15, 30 and 60min. After diffusion bonding, experimental studies were adopted. As a result, Vickers micro hardness testing was carried out to measure hardness distribution in gray cast iron joint. The results observed from Vickers micro hardness test show that the hardness increases with increasing bonding temperature due to formation of hard phased iron carbides (Fe3C)the maximum value were observed at 850°C for 60 min holding time under 2 ton is 310 HV. The microstructure results show the formation of carbide and the carbide precipitation increases with increasing the bonding temperature and time.

يتضمن البحث دراسة الربط الانتشاري لحديد الزهرالرمادي بالظروف الجوية وبوجودغاز خامل(أركون).تحت ظروف جوية عادية تم الربط باستخدام درجات تسخين مختلفة900,850,800,750,700°م, وباستخدام قوة كبس 2,1طن بأزمان مختلفة 60,30,15 دقيقة لإيجاد الظروف العملية المناسبه التي تؤثر على مقاومة الربط. أجريت دراسات باستخدام قياسات الفحص المجهري والصلادة الدقيقة(Micro hardness) .حيث اجريت فحوصات الصلادة على السطح الفاصل للوصلة.حيث تبين إن الصلادة تزداد مع زيادة درجه الحرارة حيث أعلى قيمه للصلادة تم الحصول عليها عند درجه حرارة 850°م لفترة 60 دقيقه تحت ضغط 2 طن هي310(HV).وتبين من اختبارات الفحص المجهري تكون أطواركاربيدية (Carbides)وترسيبها على سطح العينة وداخل السطح البيني.