Article
The mechanical behavior of thermoplastic and thermosetting polymers in different aqueous environments
السلوك الميكانيكي لبوليمر مطاوع وآخر متصلد حراريا في بيئات مائية مختلفة

Author: Awham M. Hameed
Journal: Journal of College of Education مجلة كلية التربية ISSN: 18120380 Year: 2012 Issue: 1 Pages: 483-497
Publisher: Al-Mustansyriah University الجامعة المستنصرية

Loading...
Loading...
Abstract

The current investigation is interested by study the effect of some types of water (sea, river and rain) on the mechanical behavior for two polymeric materials (Epoxy resin (EP) and Polyvinyl Chloride (PVC) type U(Un plasticized PVC), the prepared specimens of two materials were tested under impact and bending loads at room temperature. The results showed that U-PVC has the higher impact strength comparing with (EP) resin before and after the immersion into three types of water for 4 weeks. The bending test results showed that the maximum deflection exhibits for both materials at the first stage of immersion except (U-PVC) sample which immersed in rain water, the maximum deflection exhibits in it after 2 weeks of immersion.The Young's modulus values vary (increase and decrease) for both materials under work depending on the nature of water, immersion time, the penetration amount of it into the structure of material as well as the plasticization case which causes it.

اهتم بحثنا الحالي بدراسة تأثير بعض انواع المياه التي شملت (ماء البحر, ماء النهر , ماء المطر) على السلوك الميكانيكي لمادتين بوليمريتين احدهما مطاوعة للحرارة وهي بولي كلوريد الفاينيل PVC نوع (U والاخرى متصلدة حراريا وهي (راتنج الايبوكسي EP) وبعد تحضير النماذج لكلا المادتين, جرى اختبارهما تحت تأثير حملي (الصدمة والانحناء) قبل وبعد غمرهما في المياه المذكورة اعلاه وقد تم ذلك عند درجة حرارة الغرفة.اظهرت النتائج ان مادة ((U-PVC لها مقاومة صدمة اعلى مقارنة براتنج الايبوكسي(Epoxy resin) وذلك في حالتي قبل وبعد الغمر في انواع المياه الثلاثة ولمدة اربعة اسابيع.اما نتائج اختبار الانحناء فقد بينت بان اقصى انحراف (maximum deflection) يظهر لكلا المادتين بعد الفترة الاولى من الغمر ((1week ما عدا نموذج ((U-PVC المغمور في ماء المطر الذي يحدث فيه اقصى انحراف بعد مدة اسبوعين من الغمر.اما قيم معامل المرونة (معامل يونك) فتتغير صعودا ونزولا لكلا المادتين قيد الدراسة وذلك حسب طبيعة الماء وفترة الغمرفيه ومقدار تغلغله الى داخل تركيب المادة علاوة على حالة التلدن التي يسببها للبوليمر.


Article
The Diffusion Coefficients of Different Types of Liquid Environments Into Binary Polymer Blend

Authors: Awham M. Hameed --- Raghad H. Helal
Journal: Al-Nahrain Journal of Science مجلة النهرين للعلوم ISSN: (print)26635453,(online)26635461 Year: 2013 Volume: 16 Issue: 3 Pages: 148-158
Publisher: Al-Nahrain University جامعة النهرين

Loading...
Loading...
Abstract

In this study, unsaturated polyester resin (UPE) and Natural rubber (NR) were used to prepared binary polymer blend (UPE/ NR) with weight ratio (95/5) %. The present paper investigates the diffusion behavior of three environmental groups , the first group is different types of water included (distilled water, tap water, rain water), the second is diluted solutions with same concentration (HCl , H2SO4, NaCl) and the third is solvents (ethanol, kerosene, benzene) and study their effects through (UPE/NR) polymer blend. Consequently, a set of specimens were immersed in various types of water, solutions and solvents for different periods of time. The diffusion coefficients (Dx) of these liquids were calculated based on Fick's law. The results of a series of experimental investigations showed that the values of (Dx) of all liquids are in the range (3.95- 9.1 *10-12 m2/s) except benzene which behaves another behavior called (non- Fickian diffusion) through the same time of immersion.

في هذا البحث، أستخدم راتنج البولي استر غير المشبع (UPE) والمطاط الطبيعي (NR) لتحضير خليط بوليمري ثنائي (UPE/ NR) وبنسبة وزنية (95/5) %.الدراسة الحالية تبحث السلوك الانتشاري لثلاثة مجاميع بيئية , المجموعة الاولى هي انواع مختلفة من المياه شملت (الماء المقطر, ماء الحنفية, ماء المطر) والثانية هي محاليل مخففة وبنفس التركيز (HCl , H2SO4, NaCl) والثالثة هي مذيبات (الايثانول، النفط، البنزين) ودراسة تاثيراتها خلال الخليط البوليمري (UPE/NR). ولذلك غمرت مجموعة من النماذج في الانواع المختلفة من المياه والمحاليل والمذيبات لفترات زمنية مختلفة. معاملات الانتشار (Dx) لتلك السوائل تم حسابها على اساس قانون فك. اظهرت النتائج لسلسلة من البحوث التجريبية بأن قيم معاملات الانتشار ((Dx لجميع السوائل في المدى 3.95-9.1*10-12)m2/s.) ماعدا البنزين الذي يسلك سلوكا مغايرا حيث لايتبع سلوك فك في الانتشار خلال نفس الفترة من الغمر ويصطلح عليه (non- Fickian diffusion).


Article
Mechanism of Hybrid Reinforcement and its Effect on some Properties of Binary Polymer Blend
ألية التسليح الهجين وتأثيرها على بعض الخواص لخليط بوليمري ثنائي

Authors: Awham M. Hameed --- Entihaa G. Daway
Journal: Engineering and Technology Journal مجلة الهندسة والتكنولوجيا ISSN: 16816900 24120758 Year: 2014 Volume: 32 Issue: 2 Part (B) Scientific Pages: 287-301
Publisher: University of Technology الجامعة التكنولوجية

Loading...
Loading...
Abstract

The aim of current study is carrying out some modifying in properties of resin material (Unsaturated polyester, UPE) by adding thermoplastic material (polystyrene, PS) with different weight ratios included (0%, 5%, 10%, 15% and 20%) of (PS) to prepare binary polymer blend. The optimum ratio was selected in terms of the homogeneity case between the two polymers and studying the nature of the surfaces of the prepared materials using the optical microscope. Some mechanical tests were performed to determine the values of impact strength (I.S), ultimate tensile strength (UTS) for all prepared specimens. The ratio (80/20, weight/weight)% of (UPE/PS) blend was selected and reinforced with fibers volume fraction Фf = 10% using three types of fibers included(glass fibers (G.F), Carbon fibers (C.F) and hybrid from the two types (5% G.F and 5% C.F). All the above tests were repeated after the reinforcement for comparing the results and studying the behavior of materials under work. The results exhibited that the values of (I.S) increase with increasing of the blending ratio of (PS) while the values of (UTS) decrease at blending ratios (10, 15) % of (PS) and return to increase at the ratio 20% . After the reinforcement, it was found that the composite reinforced with carbon fibers records the highest values of impact strength for un notch specimens while the hybrid composite has the highest value of the ultimate tensile strength comparing with E-glass and carbon fibers composites.

الهدف من الدراسة الحالية هو اجراء بعض التحوير في خواص مادة راتنجية ( البولي استر غير المشبع , UPE) بأضافة مادة ثرموبلاستيكية (البولي ستايرين ,PS) وبنسب وزنية مختلفة شملت0,5 10, 15, 20) )% من البولي ستايرين لتحضيرخليط بوليمري ثنائي.وقد تم اختيارالنسبة المثلى بدلالة حالة التجانس بين البوليمرين ودراسة طبيعة السطوح للموادالمحضرة بأ ستخدام المجهر الضوئي. أجريت بعض الاختبارات الميكانيكية لتحديد قيم مقاومة الصدمة (I.S) , مقاومة الشد القصوى (UTS) لجميع النماذج المحضرة. تم اختيارالنسبة الوزنية (80/20)% من خليط البولي استر غير المشبع/ البولي ستايرين وسلحت بالالياف وبكسرحجمي (Фf = 10%) باستخدام ثلاثة انواع من الالياف شملت (الياف الزجاج (G.F), الياف الكاربون ((C.F وهجين من نوعي الالياف (5% G.F) و(5% C.F). تم تكرار جميع الاختبارات اعلاه بعد التسليح لغرض مقارنة النتائج ودراسة سلوك المواد قيد البحث. أظهرت النتائج بأن قيم (I.S) تزداد مع زيادة نسبة الخلط للبولي ستايرين في حين قيم (UTS) تنخفض عند نسبتي الخلط (10, 15)% من البولي ستايرين وتعود لتزداد عند النسبة 20%. وبعد التسليح اظهرت النتائج بأن المتراكب المسلح بألياف الكاربون يسجل القيم الاعلى لمقاومة الصدمة لنماذج غير محزوزة في حين المتراكب الهجين يمتلك القيمة الاعلى لمقاومة الشد القصوى مقارنة مع متراكبات الياف الزجاج والكاربون.


Article
Investigation of the Mechanical Behavior of Binary and Ternary Polymer Blends

Authors: Awham M. Hameed --- Ryam E. Hawy
Journal: Iraqi Journal of Applied Physics المجلة العراقية للفيزياء التطبيقية ISSN: 18132065 23091673 Year: 2015 Volume: 11 Issue: 2 Pages: 19-24
Publisher: iraqi society for alternative and renewable energy sources and techniques الجمعية العراقية لمصادر وتقنيات الطاقة البديلة والمستجدة

Loading...
Loading...
Abstract

In this research, binary and ternary polymer blends were prepared by hand lay-up method with different weight ratios. The binary blends are epoxy/unsaturated polyester (EP/UPE) and epoxy/polysulfide rubber (EP/PSR) while the ternary blend is epoxy/unsaturated polyester/polysulfide rubber (EP/UPE/PSR). Impact, tensile and flexural characteristics for these blends were investigated at room temperature. The morphology of impact fracture surfaces for the prepared blends was examined by using the optical microscopy. The results revealed that the blending process of epoxy resin with UPE, PSR or both together within certain weight percentages forms compatible blends with improved toughness. The brittleness phenomenon of epoxy resin disappears with increasing the content of added polymer.


Article
Preparation and Studying the Fracture Toughness of Laminate Composites

Authors: Awham M. Hameed --- Mays Sabah Mahdi
Journal: Engineering and Technology Journal مجلة الهندسة والتكنولوجيا ISSN: 16816900 24120758 Year: 2016 Volume: 34 Issue: 4 Part (B) Scientific Pages: 451-461
Publisher: University of Technology الجامعة التكنولوجية

Loading...
Loading...
Abstract

Binary polymer blend was prepared by the mechanical mixing of epoxy resin (EP) with polycarbonate (PC) in different weight ratios of (0, 5, 10, 15 and 20%). Charpy impact test was carried out on these blends to determine the values of impact strength (I.S). It was found that the blend of the ratio (20wt. %) of PC has the highest (I.S) compared with other ratios. For this reason, this percentage of mixing was selected to fabricate the composite materials. Hand lay-up method was utilized to synthesize the (single and hybrid) laminate composites with fiber volume fraction (Ф=15%). Glass and Kevlar fibers were used to reinforce the epoxy and its polymer blend with different sequences of skin and core layers of the composite. The values of Young's modulus (E), impact characteristics (I.S, Gc, Kc) and hardness were determined for these composites. It is found that the values of (E) and hardness decrease while the values of material toughness (Gc) increase with increasing the blending ratio of the polymer blend. It can also be noticed that the composite reinforced with Kevlar fibers records the highest value of (Gc) compared with other composites.


Article
Comparing the Flexural Strength Values for Polymeric Material and other Fibrous Composite in 3 and 4 Point Bending Methods
مقارنة قيم متانة الانحناء لمادة بوليمرية واخرى متراكبة ليفية بطريقتي الانحناء ثلاثي ورباعي النقطة

Author: Awham M. Hameed اوهام محمد حميد
Journal: Journal of College of Education مجلة كلية التربية ISSN: 18120380 Year: 2017 Issue: 1 Pages: 163-178
Publisher: Al-Mustansyriah University الجامعة المستنصرية

Loading...
Loading...
Abstract

This research aims to determine the flexural strength (F.S) values for epoxy material before the reinforcement and after it by carrying out 3and 4 bending tests then comparing the results that obtained from the two mentioned test methods. For this purpose, the casts of materials under study were prepared by using molds prepared previously for this objective. Epoxy resin reinforced with chopped glass fibers with volume fraction is (20%). After the solidification process, the samples were cut with length (10cm), width (1cm) and thickness (0.5cm), and then some tests were performed at room temperature. It was found from the results of tests that epoxy reinforced with glass fibers has higher (F.S) with less strain than that for un reinforced epoxy. It can be also noticed in 4-point bending test, the force needed for the sample failure of pure epoxy is higher than that required for failing the same sample subjected to 3- point bending test. Optical microscope was used for imaging the fracture surfaces and failure regions of samples.

يهدف بحثنا هذا الى تحديد قيم متانة الانحناء لمادة الايبوكسي قبل وبعد تسليحها بالالياف وذلك باجراء اختباري الانحناء ثلاثي النقطة (3-point bending test) واختبار الانحناء رباعي النقطة (4-point bending test) ومن ثم مقارنة النتائج المستحصلة من طريقتي الاختبارالمذكورة.ولهذا الغرض تم تحضير مصبوبات المواد قيد الدراسة باستخدام قوالب اعدت لهذا الغرض مسبقا علما بان الكسر الحجمي للالياف قدره (%20) وتم تسليح الايبوكسي بالياف الزجاج المقطعة (chopped glass fibers) وبعد عملية التصلب تم تقطيع العينات بطول (10cm) ، عرض cm) 10 (وسمك (0.5cm) وقد تم اجراء الاختبارات عند درجة حرارة الغرفة ، ولوحظ من نتائج الفحوصات ان الايبوكسي المسلح بالياف الزجاج يمتلك متانة انحناء اعلى من تلك للايبوكسي غير المسلح وكذلك اقل انفعال وقد لوحظ في اختبار الانحناء رباعي النقطة ان القوة اللازمة لفشل العينة من الايبوكسي النقي تكون اعلى من تلك اللازمة لفشل نفس العينة المعرضة لاختبار الانحناء ثلاثي النقطة ، تم تصوير سطوح الكسر ومنطقة الفشل الحاصل للعينات باستخدام المجهر الضوئي .


Article
Reusing Iraqi Construction and Aggregates Waste to Manu-facturing Eco-Friendly Polymer Concrete

Authors: Awham M. Hameed --- Mohammad T. Hamza
Journal: Al-Mustansiriyah Journal of Science مجلة علوم المستنصرية ISSN: 1814635X Year: 2018 Volume: 29 Issue: 3 ICSSSA 2018 Conference Issue Pages: 63-69
Publisher: Al-Mustansyriah University الجامعة المستنصرية

Loading...
Loading...
Abstract

The recycling and reusing of waste materials to produce suitable materials is very important subjects to scientific research in world now, because the decrease natural resources and create a hole or risk in future of the world. The aim of our research to produce polymer concrete (PC) has high mechanical and physical characteristic. This PC was prepared by using the waste of aggregates and demolitions to make PC have good mechanical and physical characteristic with low cost as compared as cement concrete. In this research different types of construction and demolition waste were used as aggregates replacement (i.e. waste of cement/concrete debris, waste of ceramics and the waste of blocks) while the type of polymer resins (i.e. Epoxy) as cement replacements. The weight percentages of resin were changed within (20, 25 and 30) % to manufacture this polymer concrete. The tests we done like physical such as den-sity and mechanical such as compressive strength, flexural strength. Splitting tensile strength and Schmidt hammer rebound hardness.


Article
Using Polyethylene Glycol to Produce Self Cured Cement Mortar

Authors: Rasha R. Rawdhan --- Awham M. Hameed --- Shakir A. Salih
Journal: Engineering and Technology Journal مجلة الهندسة والتكنولوجيا ISSN: 16816900 24120758 Year: 2018 Volume: 36 Issue: 4 Part (A) Engineering Pages: 401-409
Publisher: University of Technology الجامعة التكنولوجية

Loading...
Loading...
Abstract

The capacity of self-curing admixture is to reduce the evaporation of water from mortar, and subsequently they increase the ability of water retention from mortar contrasted with those traditionally cured mortar. Polymeric phase is disperse in cement causing diminish in water absorption and Likewise its connection with hydrating cement create further bond formation which lead to the increment in strength. In this study two group of mortar samples were prepared, first group consist reference and fly ash mortar, second group prepare with admixtures of polymer were PEG 400 used as self-curing agent in this study. Flow test and setting time performed on fresh mortar to reach to the optimum standard specifications. Two mechanical test were carried out include compressive, tensile strength tests, the effect of PEG 400 on bulk density of polymer-modified hardened mortar also studied. The optimum results observed at the age of curing 28 days for PEG wt% 1and 3 were 39.4 and 37.7 MPa for compressive strength tests respectively, and the tensile strength at the age of curing 28 days for PEG wt% 1and 3 were 3.67 and 4.1 MPa respectively, bulk density decrease when increasing the percentage of PEG.


Article
Preparation and studying of some properties of polymer composites reinforced with natural and artificial fibers
تحضير ودراسة بعض الخواص لمتراكبات بوليمرية مسلحة بالياف طبيعية وصناعية

Authors: Awham M. Hameed أوهام محمد حميد --- Saad Ali Fouad سعد علي فؤاد
Journal: Iraqi Journal of Physics المجلة العراقية للفيزياء ISSN: 20704003 Year: 2016 Volume: 14 Issue: 31 Pages: 138-147
Publisher: Baghdad University جامعة بغداد

Loading...
Loading...
Abstract

This work concerns the thermal and sound insulation as well as the mechanical properties of polymer matrix composite reinforced with glass fibers. These fibers may have dangerous effect during handling, for example the glass fibers might cause some damage to the eyes, lungs and even skin. For this reason the present work, investigates the behavior of polymer composite reinforced with natural fibers (Plant fibers) as replacement to glass fibers. Unsaturated Polyester resin was used as matrix material reinforced with two types of fibers, one of them is artificial (Glass fibers) and the other type is natural (Jute, Fronds Palm and Reed Fibers) by hand lay-up technique. All fibers are untreated with any chemical solvent. The Percentage of mixing was (90 wt. %) of the matrix while the weight fraction of each type of fibers was fixed (10 wt. %). The mechanical tests included impact and flexural strength tests. The results showed that the impact strength and flexural strength of the composites reinforced with Jute fibers is higher than that of Glass fibers and other natural fibers. The coefficients of thermal conductivity of the composites were measured by Lee's disc apparatus, the results show that the thermal insulation of the composite reinforced with jute fibers is higher than that of glass fibers and other natural fibers.The acoustic insulation of the composites reinforced with Jute fibers showed excellent result in insulation compared with glass fibers and other natural fibers.

أهتمت العديد من البحوث في دراسة الخواص العزل الحراري والصوتي و الخواص الميكانيكية لمتراكبات بوليمرية مسلحة بالياف الزجاج علما بأن هذه الالياف لها مضار عند التعامل معها فهي قد تضر بالعينين والرئتين وكذلك الجلد لذا ارتأينا اجراء دراسة خواص لمتراكبات البوليمر المقواة بألياف طبيعية (نباتية) كبدائل عن الياف الزجاج ومقارنة خواص كليهما وتحديد النتائج.استخدم راتنج البولي استر غير المشبع كمادة اساس وتم تسلسحه مع نوعين من الالياف, صناعية (الياف الزجاج) وطبيعية (الياف الجوت, وسعف النخيل, والياف القصب) جميع الالياف استخدمت بدون معاملة كيميائية, بواسطة تقنية الصب اليدوي. الكسر الوزني للرتنج كانت 90% نسبة وزنية بينما كان الكسر الوزني لجميع للأياف ثابت وهو 10% نسبة وزنية, الاختبارات الميكانيكية الي تم اجرائها هي اختبار الصدمة بطريقة جاربي واختبار مقاومة الكسر لحساب قيمة مقاومة الصدمة ومقاومة الكسر لهذه المتراكبات, النتائج اضهرت ان المتراكبات المسلحة بالياف الجوت (الطبيعية) لها مقاومة صدمة ومقاومة كسر اعلى من الياف الزجاج والاياف الطبيعية الاخرى. كذلك تم اجراء فحص التوصيلية الحرارية لهذه المتراكبات باستخدام جهاز(قرص لي) واوضحت نتائج اختبار التوصيلية الحرارية بأن العزل احراري للمتراكبات المسلحة بألياف الجوت اعلى من المتراكبات المسلحة بألياف الزجاج وكذلك اعلى من الالياف الطبيعية الاخرى, بينما نتائج فحص العزل الصوتي للمتراكبات المسلحة بألياف الجوت كانت ممتازة مقارنة بالمتراكبات المسلحة بالياف الزجاج وكذلك المتراكبات المسلحة بالاياف الطبيعيه الاخرى.


Article
Using the plastic wastes in fabrication of composite materials for different applications
استخدام النفايات البلاستيكية في تصنيع مواد متراكبة متعددة التطبيقات

Authors: Awham M. Hameed اوهام محمد حميد --- Ahmed Ali Talib احمد علي طالب
Journal: Iraqi Journal of Physics المجلة العراقية للفيزياء ISSN: 20704003 Year: 2018 Volume: 16 Issue: 36 Pages: 123-133
Publisher: Baghdad University جامعة بغداد

Loading...
Loading...
Abstract

This study suggests using the recycled plastic waste to prepare the polymer matrix composite (PMCs) to use in different applications. Composite materials were prepared by mixing the polyester resin (UP) with plastic waste, two types of plastic waste were used in this work included polyethylene-terephthalate (PET) and Polyvinyl chloride (PVC) with varies weight fractions (0, 5, 10, 15, 20 and 25 %) added as a filler in flakes form. Charpy impact test was performed on the prepared samples to calculate the values of impact strength (I.S). Flexural and hardness tests were carried out to calculate the values of flexural strength and hardness. Acoustic insulation and optical microscope tests were carried out. In general, it is found that UP/PVC composite exhibit the optimum values compared to UP/PET composite in all properties under test. From the experimental results, it can be concluded that the prepared composites from the waste could be utilized as precast or partitions inside the buildings with improved mechanical properties.

يقترح هذا البحث اعادة التدوير للمخلفات البلاستيكية لغرض استعمالها في تصنيع متراكبات ذات اساسات بوليمرية (PMCs) من الممكن استخدامها في تطبيقات متعددة. حضرت المواد المتراكبة بخلط راتنج البولي استر غير المشبع مع المخلفات البلاستيكية وقد استخدم نوعين من المخلفات اضيفت كحشوة بشكل قشور في هذه الدراسة شملت البولي اثيلين ترفثاليت (PET) والبولي كلوريد الفاينيل ((PVC وبكسوروزنية مختلفة (0، 5، 10،15 ، 20 و (25%. نفذ اختبار صلادة نوع جاربي على النماذج المحضرة لتحديد قيم مقاومة الصدمة لها. كما اجري اختباري الانحناء والصلادة لتحديد قيم مقاومة الانحناء والصلادة. اختبار العزل الصوتي والفحص بالمجهر البصري تمت على النماذج القياسية. بشكل عام، وجد ان المتراكب المدعم بمخلفات الPVC يظهرقيم مثلى مقارنة بالمتراكب المدعم بمخلفات الPET في جميع الخواص قيد الدراسة. ومن النتائج التجريبية يمكن الاستنتاج بان المتراكبات المحضرة من التدعيم بالمخلفات يمكن استخدامها كمصبوبات اولية جاهزة أو كقوطع داخل المباني وبخواص ميكانيكية محسنة.

Listing 1 - 10 of 12 << page
of 2
>>
Sort by
Narrow your search

Resource type

article (12)


Language

English (10)

Arabic and English (2)


Year
From To Submit

2018 (4)

2017 (1)

2016 (2)

2015 (2)

2014 (1)

More...