Preparation and studying of some properties of polymer composites reinforced with natural and artificial fibers
تحضير ودراسة بعض الخواص لمتراكبات بوليمرية مسلحة بالياف طبيعية وصناعية

Authors: Awham M. Hameed أوهام محمد حميد --- Saad Ali Fouad سعد علي فؤاد
Journal: Iraqi Journal of Physics المجلة العراقية للفيزياء ISSN: 20704003 Year: 2016 Volume: 14 Issue: 31 Pages: 138-147
Publisher: Baghdad University جامعة بغداد

Loading...
Loading...
Abstract

This work concerns the thermal and sound insulation as well as the mechanical properties of polymer matrix composite reinforced with glass fibers. These fibers may have dangerous effect during handling, for example the glass fibers might cause some damage to the eyes, lungs and even skin. For this reason the present work, investigates the behavior of polymer composite reinforced with natural fibers (Plant fibers) as replacement to glass fibers. Unsaturated Polyester resin was used as matrix material reinforced with two types of fibers, one of them is artificial (Glass fibers) and the other type is natural (Jute, Fronds Palm and Reed Fibers) by hand lay-up technique. All fibers are untreated with any chemical solvent. The Percentage of mixing was (90 wt. %) of the matrix while the weight fraction of each type of fibers was fixed (10 wt. %). The mechanical tests included impact and flexural strength tests. The results showed that the impact strength and flexural strength of the composites reinforced with Jute fibers is higher than that of Glass fibers and other natural fibers. The coefficients of thermal conductivity of the composites were measured by Lee's disc apparatus, the results show that the thermal insulation of the composite reinforced with jute fibers is higher than that of glass fibers and other natural fibers.The acoustic insulation of the composites reinforced with Jute fibers showed excellent result in insulation compared with glass fibers and other natural fibers.

أهتمت العديد من البحوث في دراسة الخواص العزل الحراري والصوتي و الخواص الميكانيكية لمتراكبات بوليمرية مسلحة بالياف الزجاج علما بأن هذه الالياف لها مضار عند التعامل معها فهي قد تضر بالعينين والرئتين وكذلك الجلد لذا ارتأينا اجراء دراسة خواص لمتراكبات البوليمر المقواة بألياف طبيعية (نباتية) كبدائل عن الياف الزجاج ومقارنة خواص كليهما وتحديد النتائج.استخدم راتنج البولي استر غير المشبع كمادة اساس وتم تسلسحه مع نوعين من الالياف, صناعية (الياف الزجاج) وطبيعية (الياف الجوت, وسعف النخيل, والياف القصب) جميع الالياف استخدمت بدون معاملة كيميائية, بواسطة تقنية الصب اليدوي. الكسر الوزني للرتنج كانت 90% نسبة وزنية بينما كان الكسر الوزني لجميع للأياف ثابت وهو 10% نسبة وزنية, الاختبارات الميكانيكية الي تم اجرائها هي اختبار الصدمة بطريقة جاربي واختبار مقاومة الكسر لحساب قيمة مقاومة الصدمة ومقاومة الكسر لهذه المتراكبات, النتائج اضهرت ان المتراكبات المسلحة بالياف الجوت (الطبيعية) لها مقاومة صدمة ومقاومة كسر اعلى من الياف الزجاج والاياف الطبيعية الاخرى. كذلك تم اجراء فحص التوصيلية الحرارية لهذه المتراكبات باستخدام جهاز(قرص لي) واوضحت نتائج اختبار التوصيلية الحرارية بأن العزل احراري للمتراكبات المسلحة بألياف الجوت اعلى من المتراكبات المسلحة بألياف الزجاج وكذلك اعلى من الالياف الطبيعية الاخرى, بينما نتائج فحص العزل الصوتي للمتراكبات المسلحة بألياف الجوت كانت ممتازة مقارنة بالمتراكبات المسلحة بالياف الزجاج وكذلك المتراكبات المسلحة بالاياف الطبيعيه الاخرى.


Article
EFFECT OF PLASTIC WASTES AS LOW COST MATERIAL ON SOME PROPERTIES OF UNSATURATED POLYESTER.
تأثير المخلفات البلاستيكية كمادة واطئة الكلفة على بعض خصائص البولي استر غير المشبع.

Authors: Awham M. Hameed أوهام محمد حميد --- Ahmed Ali Talib احمد علي طالب
Journal: iraq journal of market research and consumer protection المجلة العراقية لبحوث السوق وحماية المستهلك ISSN: ISSN/ 20713894/ EISSN/25236180 Year: 2018 Volume: 10 Issue: 2 Pages: 1-13
Publisher: Baghdad University جامعة بغداد

Loading...
Loading...
Abstract

In this study, plastic wastes named (PET and PVC) were used to prepare polymer matrix composite (PMC) which can be used in different applications. Composite materials were prepared by mixing unsaturated polyester resin (UP) with plastic wastes, two types of plastic waste were used in this work included polyethylene-terephthalate (PET) and Polyvinyl chloride (PVC) with various weight fractions (0, 5,10,15, 20 and 25%) added as a filler in flakes form. In this work, some of the tests that were carried out included (tensile, bending, and compressive strength) as mechanical tests, in addition to (thermal conductivity and water absorption) as physical tests. The values of tensile, compressive strength and Young's modulus of UP increased after the reinforcement with PVC or PET. Thermal insulation of the composites is significantly higher than that of pure UP. Although the values of water absorption for composite are higher than pure UP due to the existence of the interface between matrix and filler material. Also, the low cost of plastic wastes recycling encourage preserving the environment.

في هذه الدراسة تم استخدام مخلفات بلاستيكية نوع (PVC و PET) لتحضير مادة متراكبة ذات اساس بوليمري (PMC) التي يمكن استخدامها في عدة تطبيقات. و تم تحضير المادة المتراكبة عن طريق خلط البولي استر غير المشبع مع المخلفات البلاستيكية بنوعيها و التي كانت بنسب وزنية مختلفة (0, 5, 10, 20 و 25%) والتي اضيفت على شكل رقائق. وكانت الاختبارات التي تم اجراؤها في هذا البحث هي (اختبار الشد, الانحناء والانضغاطية) كإختبارات ميكانيكية, في حين تم ايضا اجراء اختبارات (التوصيل الحراري و امتصاصية المياه) كإختبارات فيزيائية. قيم الشد والانضغاط ومعامل يونك للـUP والتي ازدادت بعد تدعيمها بالـ(PVC و PET). العزل الحراري للمادة المتراكبة وازداد بشكل ملحوظ بعد مقارنة بالـUP النقي. وأرتفعت ايضا القيم الامتصاصية للمياه بسبب وجود السطح البيني بين المادة الاساس والمادة المدعم بها. ان هذا البحث يسهم في الحث على اعادة تدوير المواد البلاستيكية حفاظا على البيئة وبتكلفة قليلة.


Article
Morphology and Mechanical Properties of (Epoxy/PVC) Blend
المورفولوجيا والخواص الميكانيكية لخليط (الايبوكسي/ بولي كلوريد الفاينيل)

Loading...
Loading...
Abstract

In this research, the morphology and mechanical properties of (Epoxy/PVC) blend were investigated. (EP/PVC) blend was prepared by manual mixing of epoxy resin with different weight ratios of (Poly vinyl chloride (PVC) after dissolving it in cyclohexanon). Five sheets of polymer blends in wt% included (0%, 5%, 10%, 15% and 20%) of PVC were prepared at room temperature. Tests were carried out to study some mechanical properties for these blends and compared with the properties of pure epoxy. The morphology of the prepared materials was examined to study the compatibility nature between the two polymers under work. It was found that the best ratio of addition is (20%) of PVC. This percentage gave the highest value of tensile strength compared with other percentages of mixing for (EP/PVC) blends.

في هذا البحث تم دراسة المورفولوجيا والخواص الميكانيكية لخليط بوليمري ثنائي. وقد حضر خليط من (الايبوكسي/ بولي كلوريد الفاينيل) بواسطة الخلط اليدوي لراتنج الايبوكسي مع نسب وزنية مختلفة من البولي كلوريد الفاينيل بعد اذابته في مذيب السايكلوهكسانون. وحضرت في هذه الدراسة خمسة الواح بنسب وزنية شملت (0،5،10،15،20) % من ال PVC عند درجة حرارة الغرفة. اجريت مجموعة من الاختبارات لدراسة الخواص الميكانيكية لتلك الخلائط وقورنت مع خواص الايبوكسي النقي . تم فحص المورفولوجيا للمواد المحضرة لغرض دراسة طبيعة التوافق بين البوليمرين قيد البحث. وقد وجد بان النسبة الافضل للاضافة هي (20%) من PVC علاوة على ان هذه النسبة المئوية تعطي القيمة الاعلى لمقاومة الشد مقارنة بنسب اخرى للخلط .

Listing 1 - 3 of 3
Sort by
Narrow your search

Resource type

article (3)


Language

English (2)

Arabic and English (1)


Year
From To Submit

2018 (1)

2016 (1)

2015 (1)