Article
Study the effect of sodium hydroxide solution on the thermal conductivity of nanocomposites
دراسة تأثير محلول هيدروكسيد الصوديوم على التوصيلية الحرارية لمادة متراكبة نانوية

Authors: Ayad Qabash Hameed اياد قباش حميد --- Faik Hammad Anter فائق حماد عنتر
Journal: Iraqi Journal of Physics المجلة العراقية للفيزياء ISSN: 20704003 Year: 2018 Volume: 16 Issue: 39 Pages: 48-54
Publisher: Baghdad University جامعة بغداد

Loading...
Loading...
Abstract

In this research, hand lay- up technique is used to prepare samples from epoxy resin reinforced with multi- walled carbon nanotubes in different weight fractions (0, 2, 3, 4, 5) wt%. The immersion effect by sodium hydroxide solution (NaOH) at normality (0.3N) for a period of (15 days) on the thermal conductivity of nanocomposites was studied, and compared to natural condition (before immersion). The thermal conductivity of epoxy nanocomposites specimens were carried out using Lee’s disk method. The experimental results showed that thermal conductivity increased with increase weight fraction before and after immersion for all specimens, while the immersion effect leads to decrease thermal conductive values compared to thermal conductivity values in natural condition.

في هذا البحث اُستخدمت تقنية القولبة اليدوية (Hand Lay – up) في تحضير عينات من راتنج الإيبوكسي المدعم بأنابيب الكربون النانوية متعددة الجدران (MWCNTs) بنسب وزنية مختلفة (0، 2، 3، 4، 5) wt%. تم دراسة تأثير الغمر في محلول هيدروكسيد الصوديوم (NaOH) ذو عيارية (0.3N) وبدرجة حرارة المختبر لمدة (15 يوم) على التوصيلية الحرارية للمتراكبات النانوية، ومقارنتها بالحالة الطبيعية (قبل الغمر). لقياس التوصيلية الحرارية لنماذج متراكبات الإيبوكسي استخدمت طريقة قرص لي (Lee’s disk). أظهرت نتائج الدراسة ان التوصيلية الحرارية تزداد بزيادة النسب الوزنية للمادة المضافة ولجميع العينات قبل وبعد الغمر في المحلول القاعدي. في حين لوحظ إن الغمر بالمحلول القاعدي يؤدي الى نقصان قيم التوصيلية الحرارية لكافة العينات مقارنة بقيم التوصيلية الحرارية في الحالة الطبيعية.


Article
Wear rate of epoxy resin reinforced with multi walls carbon nanotubes
معدل البلى لراتنج الايبوكسي المدعم بأنابيب الكربون النانوية متعددة الجدران

Authors: Ayad Qabash Hameed اياد قباش حميد --- Faik Hammad Anter فائق حماد عنتر
Journal: Iraqi Journal of Physics المجلة العراقية للفيزياء ISSN: 20704003 Year: 2019 Volume: 17 Issue: 40 Pages: 1-9
Publisher: Baghdad University جامعة بغداد

Loading...
Loading...
Abstract

In this study, nanocomposites have been prepared by adding multiwall carbon nanotubes (MWCNTs) with weight ratios (0, 2, 3, 4, 5) wt% to epoxy resin. The samples were prepared by hand lay-up method. Influence of an applied load before and after immersion in sodium hydroxide (NaOH) of normality (0.3N) for (15 days) at laboratory temperature on wear rate of Ep/MWCNTs nanocomposites was studied. The results showed that wear rate increases with increasing the applied load for the as prepared and immersed samples and after immersion. It was also found that epoxy resin reinforced with MWCNTs has wear rate less than neat epoxy. The sample (Ep + 5wt% of MWCNTs) has lower wear rate. The immersion effect in base solution led to increase in wear rate values for all samples compared to natural condition.

تم في هذا البحث تحضير عينات المتراكبات النانوية باستخدام تقنية القولبة اليدوية بإضافة نسب وزنية %(0، 2، 3، 4، 5) من أنابيب الكربون النانوية متعددة الجدران الى راتنج الإيبوكسي. حيث تمت دراسة تأثير الحمل المسلط قبل وبعد الغمر بمحلول هيدروكسيد الصوديوم ذو عيارية (0.3N) ولمدة (15) يوم على معدل البلى للمواد المتراكبة النانوية ومقارنتها بالحالة الطبيعية (قبل الغمر). بينت نتائج الدراسة ان معدل البلى يزداد مع زيادة الحمل العمودي المسلط ولجميع العينات. كما وُجد ان عينات الإيبوكسي المدعمة بأنابيب الكربون النانوية تمتلك معدل بلى اقل مقارنة بالإيبوكسي النقي. اقل قيمة لمعدل البلى سُجلت بالنسبة ل( Ep + 5wt% من MWCNTs). أدى تأثير الغمر بالمحلول القاعدي الى زيادة معدل البلى بالنسبة لجميع العينات مقارنة بالحالة الطبيعة.