Investigation of Flexural Properties and Thermal Conductivity for Wood Dust Filled Epoxy.

Author: Ban M. Al-Shabander
Journal: Al-Nahrain Journal of Science مجلة النهرين للعلوم ISSN: (print)26635453,(online)26635461 Year: 2013 Volume: 16 Issue: 3 Pages: 104-109
Publisher: Al-Nahrain University جامعة النهرين

Loading...
Loading...
Abstract

This paper presents the flexural properties and thermal conductivity of composites made from wood dust filler particles and epoxy resin. The flexural tests of composites, based on wood dust filler particles at different filler contents viz. (0, 1, 3, 5, 7 and 10) Wt%, were carried out using an Instron universal testing machine according to ASTM D790 and their results were presented. Experimental results showed that the flexural strength of the composites decreased with the increase of the filler particle content. Concerning the relation between the Young’s modulus and percentage of filler for flexural tests, it was found to be directly proportional at low concentrations of wood dust, at concentrations of 7 Wt% and 10 Wt% wood dust, the Young’s modules decreases with increasing wood dust, with values of (1.870) and (1.824) GPa respectively.Thermal tests were done using Lee’s disk to determine the coefficient of thermal conductivity. The results obtained showed that the increasing weight percentage of wood dust in the composite leads to decreasing the thermal conductivity.

يعنى هذا البحث بدراسة خواص الالتواء والتوصيلية الحرارية لمتراكبات مكونه من جسيمات غبار الخشب والايبوكسي. وقد قمنا بأختبار متراكبات تحوي نسب مختلفه من جسيمات غبار الخشب و قدرها (0, 1, 3, 5, 7, 10) Wt% وذلك بأجراء اختبارات عالمية طبقا لتوصيف محدد ASTM D 790. وقد اظهرت هذه الاختبارات ان متانة الانحناء تتناقص مع زياده نسبة الجسيمات الممزوجة. اما بخصوص العلاقه بين معامل يونك والنسبة المئوية للمادة الممزوجة فأنها تزداد بزيادة نسبه جسيمات الخشب عند التراكيز الواطئة اما عند التراكيز العالية (7) Wt% و (10) Wt%فأن معامل يونك يتناقص مع زيادة نسبه جسيمات الخشب وتساوي (1.870) و (1.824) GPa على الترتيب. اجريت اختبارات حرارية تضمنت استخدام قرص لي لحساب معامل التوصيل الحراري واظهرت النتائج المستحصلة انخفاض التوصيلية الحرارية مع زيادة نسبة جسيمات الخشب.


Article
Urea Modified TiO2 Nanoparticles Prepared by Sol-Gel Method to enhance the Photocatalytic Activity under Sunlight
اليوريا لتحسين جسيمات ثاني اوكسيد التيتانيوم النانوية والمحضرة بطريقة السول جل لتعزيز فعالية التحفيز الضوئي تحت ضوء الشمس

Authors: Ban M.Al-Shabander --- Ekram A. Ajaj
Journal: Engineering and Technology Journal مجلة الهندسة والتكنولوجيا ISSN: 16816900 24120758 Year: 2015 Volume: 33 Issue: 9 Part (B) Scientific Pages: 1591-1598
Publisher: University of Technology الجامعة التكنولوجية

Loading...
Loading...
Abstract

Pure and urea (5wt %) doped titanium dioxide nanoparticles were prepared by sol–gel method. The preparation of pure and urea doped TiO2 nanoparticles were achieved by titanium tetraisopropoxide, hydrochloric acid and ethanol as starting materials and the products were annealed at 600°C to get anatase phase. The prepared materials were characterized by X-ray diffraction analysis (XRD), Fourier transform infra-red spectroscopy (FT- IR), Scanning electron microscopy (SEM) with Energy dispersive X-ray analysis (EDX)and Photoluminescence (PL) spectroscopy. Thephotocatalytic activity of the samples was evaluated by degradation of Methyl Orange (MO) in aqueous solution at concentration (10ppm) under sunlight irradiation. The experimental results reveal that the urea doped TiO2 nanoparticles exhibit an enhanced photocatalytic activity in sunlight compared with that of pure TiO2 nanoparticles.

تم تحضير تاني اوكسد التيتانيوم النقي والمطعم باليوريا بنسبة وزنية (%5)بطريقة السول جل. والمواد التي استخدمت في التحضير هي التيتانيوم تترا ايزوبربكسايد وحامض الهيدروكلوريك وكحول الاثيل والناتج تم تلدينه بدرجة حرارة 600 درجة مئوية للحصول على طور الآنتاس. شخصت المواد الناتجة باستخدام حيود الاشعة السينية ومطياف الاشعة تحت الحمراء ومطياف الاشعة المتفلورة والمجهر الالكتروني الماسح.وتم حساب فعالية التحفيز الضوئي للنماذج من خلال تحلل المحلول المائي لصبغة المثيل البرتقالي بتركيز 10 جزء من المليون تحت اشعة ضوء الشمس .واظهرت النتائج العملية ان ثاني اوكسبد التيتانيوم المطعم باليوريا عززمن فعالية التحفيز الضوئي تحت اشعة الشمس مقارنة بثاني اوكسيد التيتانيوم النقي .


Article
Photocatalytic Characterization of TiO2 Nanorods and Nanotubes Synthesized by Sol Gel Template Method

Authors: Ban M. Al-Shabander --- Asma Sh. Khalil --- E. A. Al-Ajaj
Journal: Engineering and Technology Journal مجلة الهندسة والتكنولوجيا ISSN: 16816900 24120758 Year: 2018 Volume: 36 Issue: 2 Part (C) Pages: 153-158
Publisher: University of Technology الجامعة التكنولوجية

Loading...
Loading...
Abstract

Titanium dioxide nanorods (TNR) and nanotubes (TNT) wereprepared by sol gel method using anodic aluminium oxide (AAO)membrane as template and calcined at 550°C. The structural of TiO2nanorods and nanotubes investigated by X-ray diffraction (XRD), thesurface topography and the morphology of the samples werecharacterized by atomic force microscopy (AFM), and scanning electronmicroscopy (SEM). The photocatalytic activity of the TiO2 nanostructureswere evaluated by the photodegradation of methyl orange (MO) solutionat different concentrations 10, 20 and 35 ppm under UV irradiation. Thecrystallinity and anatase phase of the TiO2 nanorods and nanotubes areconfirmed by XRD measurements. Average diameter size of TiO2nanorods and TiO2 nanotubes obtained from AFM histogram were 96.14,132.34 nm respectively. A high photocatalytic activity of TiOR2Rnanostructures were obtained at the three different concentrations underUV irradiation.


Article
Effect of Fiber Volume on The Flexural Strenght of Steel Fiber Reinfored Polyester Resin Composite
تأثير الكسر الحجمي في متانة الالتواء لمتراكبات البولي استير المدعم بالياف الحديد

Authors: Harith I.Jaffer حارث ابراهيم جعفر --- Awattif A Mohammed عواطف عذاب محمد --- Ban M.Al-Shabander بان مازن الشابندر
Journal: Iraqi Journal of Science المجلة العراقية للعلوم ISSN: 00672904/23121637 Year: 2013 Volume: 54 Issue: 1 Pages: 105-109
Publisher: Baghdad University جامعة بغداد

Loading...
Loading...
Abstract

The aim of this study is to determine the flexural properties of steel fiber as a metal fiber and polyester resin as a matrix. The steel fibers were added to polyester resin at the various fiber volume fractions of 5, 10, and 15% steel fiber, and with different fiber orientations such as woven steel fiber type (0-45) ° and woven steel fiber type (0-90) ° indicate. Hand layup processes in these experiments were used to produce specimens test with the curing time of 24 hr. for the composite at room temperature. The results show that the flexural strength and flexural modulus values for 15 % vol.of woven steel fiber composite type (0-90) ° are (210MPa) and (2.29GPa( respectively. The results above indicate that the woven steel fiber (0-90) ° has a better bonding between its fiber and matrix compare to woven steel fiber type (0-45) °.

الهدف من هذه الدراسة هو تحديد خواص الالتواء لالياف الحديد كالياف معدنية وراتنج البولي استير كمادة اساس . الياف الحديد اضيفت الى راتنج البولي استير بكسور حجمية مختلفة هي 10,5و15% , مع اختلاف في اتجاه الالياف مثل حصيرة الالياف نوع (0-45) ° وحصيرة الالياف نوع (0-90) ° .تم تصنيع الواح من المتراكبات بطريقه التصنيع اليدوي مع زمن تصلب مقداره 24 ساعه بدرجه حرارة الغرفة.اظهرت النتائج قيم متانه الالتواء ومعامل الالتواء للكسر الحجمي 15% لمتراكبات حصيرة الياف الحديد نوع (0-90) °هي (210MPa)و((2.29GPa على التوالي.وبينت النتائج اعلاه ان حصيرة الالياف من نوع (0-90) ° تمتلك اليافها ترابط افضل مع المادة الاساس مقارنه لحصيرة الالياف نوع ° (0-45) .


Article
Preparation of TiO2 nanorods by Sol–Gel template method and measured its photo- catalytic activity for degradation of methyl orange
تحضير قضبان نانوية من ثاني اوكسيد التيتانيوم بطريقة السول-جل وحساب فعالية التحفيز الضوئي لها من خلال تحلل المثيل البرتقالي

Authors: Ban M.Al-Shabander بان مازن مزاحم --- Zainab R.Musleem زينب رحيم مسلم --- Ekram A. Ajaj اكرام عطا عجاج
Journal: Iraqi Journal of Physics المجلة العراقية للفيزياء ISSN: 20704003 Year: 2015 Volume: 13 Issue: 26 Pages: 171-177
Publisher: Baghdad University جامعة بغداد

Loading...
Loading...
Abstract

Titanium dioxide nanorods have been prepared by sol-gel template method. The structural and surface morphology of the TiO2 nanorods was investigated by X-ray diffraction (XRD) and atomic force microscopy (AFM), it was found that the nanorods produced were anatase TiO2 phase. The photocatalytic activity of the TiO2 nanorods was evaluated by the photo degradation of methyl orange (MO). The relatively higher degradation efficiency for MO (D%=78.2) was obtained after 6h of exposed to UV irradiation.

تم تحضير ثاني اوكسيد التيتانيوم قضبان نانوية بطريقة السول-جل. درس التركيب البلوري و طبيعة السطح لاوكسيد التيتانيوم نوع قضبان نانوية باستخدام حيود الاشعة السينية ومطياف القوة الذرية. لقد وجد ان ثاني اوكسيد التيتانيوم من نوع قضبان نانوية هو من طور الانتاس. كما تمت دراسة التحفيز الضوئي لثاني اوكسيد التيتانيوم من خلال التحلل الضوئي لصبغة المثيل البرتقالي، ان مقدار التحلل العالي لصبغة المثيل البرتقالي 78.2% حدث بعد مرور6 ساعات من التعرض للاشعة فوق البنفسجية.

Listing 1 - 5 of 5
Sort by
Narrow your search

Resource type

article (5)


Language

English (5)


Year
From To Submit

2018 (1)

2015 (2)

2013 (2)