Copper Etching In Air RegeneratedCupric Chloride Solution

Author: Baseem H. Fadhil
Journal: Journal of Engineering مجلة الهندسة ISSN: 17264073 25203339 Year: 2010 Volume: 16 Issue: 3 Pages: 5771-5777
Publisher: Baghdad University جامعة بغداد

Loading...
Loading...
Abstract

One of the most important steps in the world of printed circuit board manufacturing (PCB) is the copper etching process. Because of its low cost, environment aspects, and simple regeneration techniques, cupric chloride was chosen to be the most attractive etchant. Etching of copper from standard single-sided copper boards used usually for printed circuit board fabrication was conducted in a cell containing cupric chloride solution. Average etching rates were recorded as a function of time, etchant specific gravity, free acid concentration, and temperature. Air was injected continuously in the etching cell during the process enabling mixing and solution regeneration. It is found that best operating conditions to obtain maximum etching rate is at 45-55C, specific gravity of 1.3-1.4, and free acid concentration of 1.3-1.4 M.

ان التأكل الموجّه للنحاس يعد احد العمليات المهمة في عالم صناعة الدوائر الالكترونية المطبوعة (PCB). وانتخب محلول كلوريد النحاس ليكون احد اهم المحاليل المسببة لعملية التأكل الموجه نظراً لرخص ثمنه، وسهولة استرجاع فعاليته بعد استعماله، ولاعتبارات بيئية.دُرس تأكل النحاس عبر عينات قياسية لالواح نحاس ذات وجه واحد تستخدم عادةً للطباعة الالكترونية في خلية تحوي محلول كلوريد النحاس، وسُجلت معدلات التأكل للعينات بالنسبة للزمن، ولدرجة الحرارة، وكثافة المحلول، وتركيز الحامض الحر. حُقن هواء بشكل مستمر في داخل الخلية بهدف مزج المحلول واسترجاع فعاليته. وجد ان افضل الظروف لتحقيق اعلى المعدلات للتاكل تكون بدرجة حرارة 45-55م، وكثافة نوعية بحدود 1.3-1.4، وتركيز الحامض الحر بحدود 1.3-1.4 مولاري.


Article
Electrochemical Decolorization Of Direct Black Textile Dye Wastewater
الازالة الكهروكيمياوية للصبغة السوداء المباشرة من الماء المطروح من الصناعات االنسيجية

Authors: Baseem H. Fadhil --- Atheer M. Ghalib
Journal: Journal of Engineering مجلة الهندسة ISSN: 17264073 25203339 Year: 2011 Volume: 17 Issue: 3 Pages: 441-447
Publisher: Baghdad University جامعة بغداد

Loading...
Loading...
Abstract

Electrochemical decolorization of direct black textile dye was studied in the presence of sodium hydroxide (NaCl). Electrochemical cell occupy about 1 liter of working electrolyte supplied with graphite electrodes for both anode and cathode was constructed for this purpose. Decolorization percent, treatment time, power consumption, and pH were studied as a function of the applied voltage and salt concentration. Results show that decolorization increase with increasing salt concentration and applied voltage. Best decolorization of 86% can be achieved after 17 min at 7 volt and 5 g/l salt concentration. Further decolorization can be achieved but this will be accompanied with a sharp increase in power consumption. No significant decrease in pH value was observed at the end of each experiment

دُرست الازالة الكهروكيمياوية للصبغة السوداء المباشرة المستخدم في الصناعات النسيجية من الماء المطروح الحاوي على هذه الصبغة بالطريقة الكهروكيمياوية بوجود ملح هيدروكسيد الصوديوم. تم بناء مفاعل كهروكيمياوي يتالف من قطبي كرافيت وتم دراسة العوامل المؤثرة من فرق جهد قطبي الخلية، وتركيز الملح، على نسبة الازالة وزمن المعالجة ودرجة الحموضة فضلا عن الطاقه المستخدمة. اظهرت النتائج زيادة في نسبة الازالة اللونية بزيادة جهد الخلية وتركيز الملح وان افضل ازالة تكون بحدود 86% عند فرق جهد 7 فولت وتركيز الملح عند 5 غملتر وزمن معالجة 17 دقيقة. الازالة اللونية يمكن زيادتها ولكن على حساب زيادة حادة في الطاقة المستخدمة.كما لوحظ انخفاض طفيف بدرجة الحموضة عند نهاية التجربة.

Listing 1 - 2 of 2
Sort by
Narrow your search

Resource type

article (2)


Language

English (2)


Year
From To Submit

2011 (1)

2010 (1)