Article
Effect of Unsaturated Polyester on Some Properties of Cement Mortar
تأثير البولي أستر غير المشبع على بعض خواص مونة السمنت

Author: Besma M. Fahad
Journal: Journal of Engineering and Sustainable Development مجلة الهندسة والتنمية المستدامة ISSN: 25200917 Year: 2017 Volume: 21 Issue: 3 Pages: 156-166
Publisher: Al-Mustansyriah University الجامعة المستنصرية

Loading...
Loading...
Abstract

Using polymers to modify mortar improve the workability, adhesion, strength, durability of the cement besides improving cure characteristics. Two mixtures of cement-sand were prepared without water. The first is 1:2 cement: sand and the other ratio was 1:1 cement: sand mixture. Unsaturated polyester was added to the two mixtures at different ratios (30:70, 40:60, and 50:50) polymer to cement- sand mixture. The effect of unsaturated polyester was studied on both mixtures by calculating the density besides measuring the hardness and compressive strength of specimens .The addition of unsaturated polyester showed an improvement in these properties and showed that the increase in the unsaturated polyester percent improve the mechanical properties

ان استخدام البوليمر لتحسين الملاط سيؤدي الى تحسين الخواص التشغيلية والألتصاقية والمتانة وكذلك المطيلية هذا الى 1:1 أسمنت:رمل والأخر بنسبة 1:1 جانب انه يتصلب بصورة اسرع. حضر مزيجان من الأسمنت- رمل بدون ماء، الاول بنسبة ) بوليمر الى خليط 03:03 و 03:03 و 03:03 أسمنت:رمل. اضيف الى المزيجان بوليمرالبولي أستر غير المشبع بنسب مختلفة ( السمنت والرمل. درس تأثير اضافة البولي استر غير المشبع على المزيجين وذلك بحساب الكثافة وقياس الصلادة ومقاومة الأنضغاط للعينات. وجد ان اضافة البولي أستر يظهرتحسن بالخواص بشكل ملحوظ ،كما ان زيادة نسبة البولي أستر غير المشبع تؤدي الى زيادة الخواص الميكانيكية


Article
MODIFICATION OF BAGHDAD POTABLE WATER BY USING RECYCLE WASTE GLASS

Authors: Besma M. Fahad --- Hyman Jafar Meerza
Journal: Al-Qadisiyah Journal for Engineering Sciences مجلة القادسية للعلوم الهندسية ISSN: 19984456 Year: 2016 Volume: 9 Issue: 1 Pages: 59-72
Publisher: Al-Qadisiyah University جامعة القادسية

Loading...
Loading...
Abstract

Modification or purification of potable water with the use of recycle waste glass reduces the drain on the natural resources of the raw materials, which is widely used in our daily life. However, the disposal of waste glass is not an easy matter, which is because glass is neither incinerated nor decomposed material.In this study, ten samples of potable water were collected from ten regions in Baghdad capital city in order to investigate their physical and chemical properties. Chemical and physical properties of water were identified. Several parameters of water quality were analyzed including: turbidity, electrical conductivity, and acidity function (pH) and total suspended solids according to Iraqi standards. The results of all water samples showed that the physical and chemical analysis tests were acceptable for drinking except the station of Madinat Alsadar. Using the waste glass to eliminate this problem, as low cost and inert material, was successful in potable water treatment. As a conclusion, the TSS was decreased after filtration process by waste glass especially for Althaalba and Alameria potable water which were disappeared (being zero).

تعديل او تنقية مياه الشرب مع استخدام نفايات الزجاج المعاد تدويرها يقلل من استنزاف الموارد الطبيعية من المواد الخام، و الذي يستخدم على نطاق واسع في حياتنا اليومية، ويرجع سبب ذلك كون الزجاج من المواد التي لا تحرق ولا تتحلل. في هذه الدراسة تم جمع عشر عينات من مياه الحنفية لعشرة مناطق في العاصمة بغداد من اجل التحقق من الخواص الفيزيائية والكيميائية للماء. وقد تم تحديد الخواص الفيزيائية و الكيميائية، وتم تحديد العديد من المعاملات المحددة لنوعية المياه بما في ذلك: العكورة، التوصيل الكهربائي، معامل الحموضة ( pH) و مجموع المواد الصلبة العالقة وفقا للمعايير العراقية.واظهرت نتائج جميع عينات المياه من خلال الاختبارات الفيزيائية و الكيميائية بانها مقبولة للشرب ماعدا محطة مدينة الصدر، واستخدمت نفايات الزجاج للقضاء على هذه المشكلة، كونها منخفضة التكلفة و تعتبر من المواد الخاملة، إذ كانت ناجحة في معالجة مياه الشرب. و كاستنتاج، فان (TSS ) قد انخفضت بعد عملية الترشيح باستخدام نفايات الزجاج و خاصة بالنسبة لمياه الشرب لمنطقتي الثعالبة و العامرية حيث اختفت و اصبحت (صفر).


Article
Effect of Particle Size of Sawdust on Behaviour of Sawdust/UPE Composites in Water

Authors: Nisreen S. Ali --- Besma M. Fahad
Journal: Iraqi Journal of Chemical and Petroleum Engineering المجلة العراقية للهندسة الكيمياوية وهندسة النفط ISSN: 19974884/E26180707 Year: 2015 Volume: 16 Issue: 4 Pages: 59-65
Publisher: Baghdad University جامعة بغداد

Loading...
Loading...
Abstract

The aim of the present work is to develop a new class of natural fillers based polymer composites with sawdust (S.D) which used two particle sizes (1.2 μm & 2.3 μm) and different weight percentage from sawdust (10%, 15%, and 20%). The mechanical properties studied include hardness (shore D) for all samples at normal conditions (N.C). The unsaturated polyester (UPE) and its composites samples were immersed in water for 30 days to find the effect of particle size of sawdust (S.D) on the weight gain (Mt %) by water for all the samples, also to find the effect of water on their hardness. The results show that the composite materials of sawdust (S.D) fillers which has particle size (1.2 μm) better than (2.3 μm) particle size before & after the immersion in water. Also the results show a decrease in the values of the hardness for the UPE and its composites samples after immersion in water. The results show that the UPE and its composites samples have relatively increased values of weight gain (Mt %) by water with time of immersion, for sawdust composite samples (1.2 μm) particle size the samples of (15%) weight percentage have relatively highest values of weight gain (Mt %) by water but for samples of (2.3 μm) particle size the samples of (20 %) weight percentage have relatively highest values of weight gain (Mt %). Finally results show that the value of weight gain (Mt %) increased with increasing of particle size of sawdust so that the composites samples have highest value of weight gain (Mt %) than UPE sample.


Article
Enhance Some Insulation Properties of Epoxy by Using Waste Materials

Authors: Besma M. Fahad --- Afaf Abdulhussein Naser
Journal: AL-NAHRAIN JOURNAL FOR ENGINEERING SCIENCES مجلة النهرين للعلوم الهندسية ISSN: 25219154 / eISSN 25219162 Year: 2018 Volume: 21 Issue: 2 Pages: 259-265
Publisher: Al-Nahrain University جامعة النهرين

Loading...
Loading...
Abstract

Particles filled polymer composites started to be essential because of their wide applications in addition to reducing the cost of polymer, which is a main problem. The aim of this work is studying the insulation of particulate composites resulting from the addition of filler (glass or porcelain) waste powder to reinforced epoxy matrix. Samples with and without filler were exposed to some tests to decide the influence of the filler contents on the characteristics of epoxy. Epoxy is synthesized with filler particles having (90 micron) particle sizes as reinforcement. Composites of epoxy with varying percentage (0 to 40 weights %) of filler were prepared by using hand lay-up method. The nondestructive tests consist of thermal conductivity; ultrasonic test and water absorption test have been investigated. The composite showed an improvement in physical properties with the addition of filler according to their percentages. The result show the addition of the filler in all proportions to the epoxy increased the density of the composite, leading to the ultrasonic pulses velocity ranges between 2100 m/s and 2800 m/s. Increase glass and porcelain percentage cause increase in density which increases the acoustic impedance. While the thermal conductivity decrease with glass powder percentages in the composite increase, unlike the increase in porcelain percentage which causes an increase in thermal conductivity. The 40% percentage of glass in the epoxy had higher effect on reduce the thermal conductivity. As well as from the results the epoxy reinforced by porcelain powder would have lower water absorption than epoxy reinforced by glass powder.


Article
Enhancing the Compressive Strength and Density of Cement Mortar by the Addition of Different Alignments of Glass Fibers and Styrene Butadiene Rubber
تحسين مقاومة الانضغاط للملاط باستخدام توزيع مختلف من الياف الزجاج ومستحلب الستايرين بيوتادايين

Authors: Besma M. Fahad بسمة محمد فهد --- Mustafa M. Hamza مصطفى محمد حمزة
Journal: Al-Khwarizmi Engineering Journal مجلة الخوارزمي الهندسية ISSN: 18181171 23120789 Year: 2017 Volume: 13 Issue: 3 Pages: 108-119
Publisher: Baghdad University جامعة بغداد

Loading...
Loading...
Abstract

In the field of construction materials the glass reinforced mortar and Styrene Butadiene mortar are modern composite materials. This study experimentally investigated the effect of addition of randomly dispersed glass fibers and layered glass fibers on density and compressive strength of mortar with and without the presence of Styrene Butadiene Rubber (SBR). Mixtures of 1:2 cement/sand ratio and 0.5 water/cement ratio were prepared for making mortar. The glass fibers were added by two manners, layers and random with weight percentages of (0.54, 0.76, 1.1 and 1.42). The specimens were divided into two series: glass-fiber reinforced mortar without SBR and glass-fiber reinforced mortar with 7% SBR of mixture water. All specimens were tested after curing for 7 and 28 days, glass-fiber reinforced mortar exhibited better properties than control mortar in improvement of compressive strength and lowering the density after curing for 28 days due to the completion of cement hydration reaction.. For compressive strength the best results were achieved with 1.42 wt.% layers glass-fiber reinforced mortar with 7% SBR which gave 41.56 MPa. On the other hand, the addition of 1.42 wt.% random glass-fiber without SBR addition caused the beast reduction in density by 10.6% and produced lighter structure than control sample.

الملاط المدعم بألياف الزجاج والمضاف لها مستحلب ستايرين بيوتادايين (SBR) تعد من المواد الحديثة في مجال المواد الإنشائية. يهدف هذا البحث لدراسة تأثير اضافة الياف الزجاج العشوائية وطبقات الياف الزجاج على كثافة و مقاومة انضغاط الملاط مختبرياً في حالة وجود او عدم وجود مادة (SBR). تم تحضير خلطات من الملاط بنسبة خلط وزنية 1:2 ) اسمنت- رمل ( ونسبة الماء الى الإسمنت (0.5). تم اضافة الياف الزجاج بطريقتين عشوائية وطبقات بنسب وزنية (0.54, 0.76, 1.1, 1.42). قسمت العينات الى سلسلتين احداهما مدعمة بألياف الزجاج بدون اضافة (SBR) والأخرى مدعمة بألف الزجاج مع اضافة 7% (SBR) من ماء الخلطة. تم فحص العينات بعد غمرها بالماء لمدة 7 و 28 يوماً. الملاط المدعم بألياف الزجاج أظهر تحسينا في مقاومة الانضغاط مقارنة مع عينات القياس. اما افضل النتائج كانت مع العينات المدعمة بألياف الزجاج والمضاف لها 7% (SBR). الإنضاج بعمر 28 يوماً اظهر افضل النتائج بسبب اكتمال تفاعل الماء مع الإسمنت.


Article
The Mechanical Properties of Polymer-Mortar Composites
الخصائص الميكانيكية مركبات البوليمر- ملاط

Loading...
Loading...
Abstract

The polymer-mortar composites have several benefits, including corrosion resistance, high strength and modulus values compared to their low density, acceptable deformability, tailored design and excellent formability. This enables the fabrication of new elements and the structural rehabilitation of the existing parts made of traditional materials. In this work two sets of mixtures were prepared that consist of mortar and polymer to fabricate the polymer-mortar composite. The first set include mortar with ratio (1:1) (cement-sand) without water, while the other set include mortar with ratio (1:2) (cement-sand) without water. The polymer was epoxy which is added to the mortar after mixing the resin with the hardener in proportion of (1:3). Each set consists of different percentage of polymer (50:50, 40:60 and 30:70). to obtain Several results were obtained such as density, were the highest value was about 1906.4 kg/m3 for (1:1). The behavior of non-destructive test (UPV) was differ from that of density were the highest value was about 3521.12 m/sec for (1:2). The highest hardness of composites was 98.2 for (1:1). The destructive tests as compressive and flexural strength, the highest compressive strength was about 102.889MPa and the highest value of flexural strength was about 57.648MPa for (1:1).

مركبات البوليمر – ملاط لها فوائد عدة، بما في ذلك مقاومة للتآكل، متانة عالية ومعامل المقاومة عالي مقارنة مع كثافتها الواطئة، التشوه الحاصل يكون مقبول، دقة التصميم, قابليه التشكيل ممتازة. هذا يمكن من تصنيع عناصر جديدة وإعادة تأهيل هياكل الأجزاء المصنعة من مواد تقليدية. تم في هذا البحث أخذ مجموعتين من الخلطات التي أعدت من الملاط والبوليمر لتكوين مركب البوليمر- ملاط. المجموعة الأولى تشمل ملاط بنسبة (1:1) (الأسمنت-الرمل) بدون ماء،و أخرى تشمل ملاط بنسبة (1:2) (الأسمنت-الرمل) بدون ماء. البوليمر الذي أضيف إلى الملاط هو ايبوكسي يضاف بعد خلط الراتنج مع المصلد بنسبة (1:3). أضيف البوليمر الى كل مجموعة من الملاط بنسب مختلفة (50:50، 40:60 و 30:70). حيث تم الحصول على عدة نتائج منها، نسبة البوليمر التي يضاف إلى الملاط يؤثر على الخصائص. تجانس الخليط يلعب دورا رئيسيا في سلوك المركب ويمكن تحقيق خصائص مختلفة وفقا لنسبة الاسمنت- رمل . و يزيد من مقاومة الشد والانحناء من الملاط وأيضا يقلل من طبيعتها الهشة. وتم الحصول على العديد من النتائج فعند قياس الكثافة كانت أعلى قيمة حوالي 1906.4 كغ / م3 لنسبة (1:1). هذا السلوك يختلف عند فحصه بالاختبارات اللاأتلافية (UPV) لقياس سرعة الموجة في النماذج حيث أعلى قيمة كانت حوالي 3521.12 متر / ثانية لنسبة (1:2). أما عند اختبار الصلادة فإن هي 98.2 لنسبة (1:1). عند فحصه بالاختبارات الأتللافية أعلى قيمة لمقاومة الانضغاط حوالي 102.889MPa و أعلى قيمة لمتانة الانحناء حوالي 105 57.648MPa لنسبة (1:1).

Listing 1 - 6 of 6
Sort by
Narrow your search

Resource type

article (6)


Language

English (5)

Arabic and English (1)


Year
From To Submit

2018 (1)

2017 (2)

2016 (1)

2015 (2)