In this work, Soda Lime Glass (S.L.G.) powder was used ,as fluxe in traditional porcelain instead of feldspar. Two ceramics porcelain were compared; commercial or traditional porcelain that content of 50wt % kaolin, 25wt % quartz, and 25wt % feldspar. Feldspar mass was substituted by scraps soda lime glass yielding a new porcelain composition, to determine the softening points and then the effect of glass addition on porcelain firing process.
Eight samples, for each patch, were prepared and 8wt % water was added. The resulting composite blends were then die pressed at 2N, to produce disk specimens with diameter of 1.5 cm, and then they were sintered at (1000, 1100, 1200, 1250,1300,1350,1400 and 1450) ˚C, for 2 hours in an electric furnace with a digital controller. Physical parameters, such as density, water absorption, and shrinkage were measured. It was concluded that the sintering process and physical properties were improved by heat treatment. However, the firing results showed that the addition of S.L.G. replacing feldspar lowers the melting points of porcelain and the addition of scrap powder has a positive effect on the quartz dissolution.
The purpose of the present work is to replace 25wt% of feldspar by soda lime glass in a standard porcelain composition and evaluate their differences in physical properties at different firing temperatures.

في هذا العمل ،استخدم مسحوق زجاج الصودا لايم (S.L.G) كمصهر في البورسلين التقليدي بدل الفلدسبار،حيث تم مقارنة نوعين من البورسلين السيراميكي. البورسلين التجاري او التقليدي والذي يحتوي على 50% كاؤلين, 25% كوارتز, 25% فلدسبار. عوضت كمية الفلدسبار بمخلفات زجاج الصودا لايم لأنتاج تركيب جديد من البورسلين وحساب درجة انصهاه ثم حساب تأثير اضافة الزجاج على عملية حرق البورسلين.تم تحضير ثماني عينات من كل خلطة باضافة 8% من الماء ثم كبس المخلوط المركب بضغط مقداره 2 نيوتن للحصول على عينة قرصية بقطر 1,5 سم بعدها تم تلبيد العينات بدرجات حرارة (1000, 1100, 1200, 1250, 1300, 1350, 1400, 1450) مº لمدة ساعتين في فرن كهربائي. تم قياس المعاملات الفيزيائية مثل الكثافة, امتصاصية الماء, والتقلص. تم الاستنتاج ان عملية التلبيد والخصائص الفيزيائية قد تحسنت بالمعاملة الحرارية ,حيث اظهرت نتائج الحرق ان اضافة زجاج الصودا لايم بدل الفلدسبار قد خفض درجة انصهار البورسلين وان اضافة المسحوق المتخلف له تأثير ايجابي في ذوبان الكوارتز. الغرض من هذا العمل, هو استبدال 25% من الفلدسبار بمخلفات زجاج الصودا لايم في تركيب البورسلين القياسي ثم تقييم الاختلاف في الخصائص الفيزيائية بدرجات حرارية مختلفة.

scrap glass --- new porcelain --- S.L.G

ABSTRACT The influence of SiC particles on the physical and mechanical properties for MgO/SiC composites was investigated. MgO matrix was reinforced with (2 wt%,4 wt%,6 wt% and 8 wt% ) of SiC particles which synthesized using powder technology technique. Five samples of each patch have been prepared and supplied to physical properties (green density (G.D) and bulk density (B.D)) and mechanical properties (hardness and compressive strength) were measured. It was observed that the green density of all samples were decreases with increasing SiC particles content. This due to the lower density of SiC than MgO particles. Prepared samples were sintered at different temperatures (800 ˚C, 1100 ˚C, and 1450 ˚C). The bulk density reviled the unaffecting property for samples sintered at 800C and 1100˚C, but it was observed a significant increasing in B.D for samples sintered at higher temperature (1450˚C). It has been found that Vickers hardness, compressive strength and diametrical strength values increases with increasing sintering temperature and decreasing with SiC particles content. The purpose of this study was to confirm the influence of SiC addition on some physical and mechanical properties of MgO matrix.

الخلاصةتم دراسة تأثير إضافة دقائق كاربيد السليكون على الخواص الفيزيائية والميكانيكية لمتراكب اوكسيد المغنيسيوم/كاربيد السليكون وبنسب مئوية مضافة من كاربيد السليكون هي 2%،4%،6%،8% والتي تم تصنيعها بطريقة تكنولوجيا المساحيق. تم تحضير العينات وقياس الخصائص الفيزيائية (الكثافة قبل الحرق والكثافة الحجمية) والخصائص الميكانيكية( الصلادة ومتانة الانضغاط). لقد تم ملاحظة أن الكثافة الطرية لكل العينات تقل بازدياد دقائق كاربيد السليكون المضافة وهذا نتيجة انخفاض كثافة كاربيد السليكون مقرنة باوكسيد المغنيسيوم. أظهرت الكثافة الحجمية عدم تأثرها بالعينات الملبدة بدرجات الحرارة 800م، 1000م وتأثرها الواضح بدرجة التلبيد1450م. لوحظ أيضا آن صلادة فيكرز ومتانة الانضغاط والمتانة القطرية تزداد بازدياد درجة حرارة التلبيد وتقل بازدياد كمية الدقائق المضافة.الغرض من البحث هو لتوضيح تأثير إضافة دقائق كاربيد السليكون على الخواص الفيزيائية والميكانيكية لقالب اوكسيد المغنيسيوم.

MgO/SiC composite --- strength --- heat treatment --- mechanical properties --- MgO/SiO متراكب --- معاجة حرارية --- خصائص ميكانيكية