Article
Effect of Carbon Black and Water Absorption on Dielectric behavior of EP-modified SiO2 composites
تأثير أسود الكاربون وامتصاصية الماء على سلوك العزل للايبوكسي المدعم بمتراكبات SiO2 إكرام عطا العجاج

Author: E.A.Al-Ajaj اكرام عطا العجاج
Journal: Iraqi Journal of Physics المجلة العراقية للفيزياء ISSN: 20704003 Year: 2010 Volume: 8 Issue: 11 Pages: 17-23
Publisher: Baghdad University جامعة بغداد

Loading...
Loading...
Abstract

Epoxy (EP) – Silica (SiO2) composites are well known composites used in microelectronic industry . So it is important to study their dielectric behavior under different conditions such as the presence carbon black (UV absorber) and immersion in the water for 30 days .Dielectric properties were calculated over the frequency range 102 – 106 Hz for epoxy composites with different weight % of micrometer 1.5μm SiO2 particles (60%, 65% and 70wt%) modified with 0.5wt% silane coupling agent to improve adhesion between EP and SiO2 phases . Similar dielectric constant ( ) behavior was observed for all composites , where values decrease slightly with increasing frequency . Dielectric loss behavior shows relaxation peak around 104Hz for composites with and without carbon black . 0.35% weight gain was observed for immersed composites in water and highest relaxation peaks intensity were observed at higher frequency (around 105 Hz) . Recovery study was performed on immersed composites and no chemical changes have taken place .

متراكبات الايبوكسي – سيليكا متراكبات معروفة في مجال صناعة المايكرو الكترونكس . لهذا من المهم تدقيق تصرف العازل تحت مختلف الظروف مثل وجود المضافات والتعرض الطويل المدى الى الرطوبة في المدى المطلو ب للترددات . . لهذا تم تدقيق خواص العزل باضافة اسود الكـاربون المعروف بامتصاصية للاشعة فوق البنفسجية (UV) وغمره في الماء لفترة 30 يوما.خواص العزل تم حسابها في مدى الترددات هرتز لمتراكبات الايبوكسي مع نسب وزنية مختلفة من حبيبات (60% ، 65% ، 70%) تم تحويرها باضافة رابط هو السايلين (0.5wt% Silane) الذي يعمل على تحسين الالتصاق بين اطوار EP و SiO2 . لوحظ تشابه في تصرف لكل المتراكبات حيث ان قيم تقل بشكل قليل جدا مع زيادة الترددات . ان تصرف يظهر ذروة استرخاء بحدود هرتز لكل المتراكبات بدون او مع وجود اسود الكاربون ولكن مع زيادة في شدة ذروة الاسترخاء للمتراكبات التي تحوي اسود الكاربون والتي تفسر بانها تعود الى الاسترخاء في الايبوكسي .لوحظ ان هناك 0.35% زيادة في الوزن للمتراكبات المغمورة في الماء . ان اعلى ذروة استرخاء لوحظت بحدود 105 هرتز للمتراكبات المغمورة في الماء (تأثير استقطاب واكييز – سيلرز) تم اعادة المعالجة عكسيا للمتراكبات المغمورة بالماء (تجفيف) ووجد انه لايوجد تغييرات كيميائية للمتراكبات المحورة المغمورة في الماء .


Article
Effect of Water Absorption on Some Electrical and Dielectrical Properties of Epoxy Resin Reinforced with Chopped Carbon Fibers

Authors: E.A.Al-Ajaj --- S.I.Husaen --- H.I.Jafar
Journal: Al-Nahrain Journal of Science مجلة النهرين للعلوم ISSN: (print)26635453,(online)26635461 Year: 2011 Volume: 14 Issue: 4 Pages: 87-94
Publisher: Al-Nahrain University جامعة النهرين

Loading...
Loading...
Abstract

In this research, we study a.c electrical conductivity (σa.c ( ) and dielectric properties (dielectric constant (έ), and dissipation factor ( tanδ) ), with frequency change (102 -107 Hz) for the epoxy resin and composites reinforced with chopped carbon fiber ,prepared by hand lay –up method (EP +5% CF), (EP +10% CF), (EP +15% CF), (EP +20% CF), Were measured electrical conductivity of epoxy and composites with frequency change and at room temperature the results showed a.c electrical conductivity dependence with frequency relationship σ (ω)=Aωs to the values of the exponential factor (s)of less than one all samples, and adopted the theory of filtration for the interpretation of data conductivity for composites reinforced with carbon fibers was selected epoxy+20% C.F showed a higher electrical conductivity (13.6 * 10-7 (ohm.cm)-1). The composites were immersed in water at room temperature for 6, 10,15,20,27 days.The results showed that the electrical conductivity of (σ (ω)) increasing with increasing weight gain(M%) due to water absorption. Itwas found that dielectric constant increases when the percentage moisture absorption increase, whereas dielectric constant (έ) is dependent on capacity of composite materials.

تـم في هـذا البحث دراسـة التوصيليـة الكهربائيـة المتناوبـة ()(σa.c وخـواص العـزل الكهربائـي (έ,tan (مـع تغيـر التردد (102 -107 Hz) لراتنـج الايبوكسي ومتراكباته المدعمة بالياف الكاربون المقطعة والمحضرة بطريقة التشكيل اليدوية(EP+5%C.F)، (EP+10%C.F)، (EP+15%C.F)، (EP+20%C.F) تم قياس التوصيلية المتناوبة للايبوكسي ومتراكباته في مدى التردد وفي درجة حرارة المختبر اظهرت النتائج اعتماد التوصيلية على التردد وفق العلاقة σ(ω)=Aωs بقيم للعامل الاسي اقل من الواحدلكل العينات, واعتمدت نظرية الترشيح لتفسير بيانات التوصيلية لمتراكبات الايبوكسي المدعم بالالياف الكاربون. كما تم دراسة تأثير التردد في قيمة ثابت العزل الكهربائي وفقد العزل فقد وجد بان السماحية ( ( έتقل في حالة التقوية بالياف الكاربون المقطعة، تم اختيار المتراكب ايبوكسي -20% الياف الكاربون المقطعة الافضل من بين المتراكبات باعتبـاره اظهـر اعلـى توصيليـة كهربائيـة( (ohm.cm )-1 13.6*10-7 ). تم تغطيس المتراكبات في الماء بدرجة حرارة الغرفة لمدة 20,1510,6, 7, 2 يوم، اظهـرت النتائـج العمليـة ان التوصيليـة الكهربائيـة((ω)σ) تزداد بزيادة التردد وزيادة النسبة المئوية لامتصاصية الماء بينما ثابت العزل (έ) يزداد عند زيادة النسبة المئوية لامتصاصية الماء اعتمادا على السعة الكهربائية للمواد المتراكبة.


Article
Nano-SiO2 Addition Effect on Flexural Stress and Hardness of EP/MWCNT
تاثير مضافات السليكا النانوية على اجهاد الانحناء والصلادة لمتراكب الايبوكسي/ انابيب الكاربون النانوية

Authors: E.A.Al-Ajaj --- A.Sh. Alguraby --- M.K. Jawad
Journal: Engineering and Technology Journal مجلة الهندسة والتكنولوجيا ISSN: 16816900 24120758 Year: 2015 Volume: 33 Issue: 7 Part (B) Scientific Pages: 1248-1257
Publisher: University of Technology الجامعة التكنولوجية

Loading...
Loading...
Abstract

Nano-SiO2 with different weight percentage (1,2 ,3, 4 and 5) % wt. , and 3% MWCNT were usedto fabricate nano-SiO2/MWNT/epoxy composite samples by hand layup method. Ultrasonic mixing processwas used to disperse the nano additives into the resin system. scanning electron microscopy (SEM)where usedto carry out the characteristic of fracture surface. By both the high aspect ratio and the very high modulus ofnano fillers. The mechanical properties of the composite with different weight percentages of nano-SiO2 havebeen investigated and After examine, the Scanning Electron Microscopy (SEM) explains well dispersednanotubes and SiO2 nano particles in the matrix. No evidence of agglomeration of the nanotubes can be foundin this micrographs. By adding SiO2 nano particles to epoxy/MWCNT composite, this would dramaticallyimprove the bending properties and The Young’s modulus has been doubled and quadrupled for compositeswith respectively 2 and 4 wt.% nano SiO2, compared to the pure resin matrix samples (3.36 ,4.06 ,and 1.59 )GPa respectively .While flexural strength has been increased in random manner with maximum value for 2 wt%(111 MPa). The hardness of nano composite increased with increase of SiO2 filler loading, it can be seen thatthe SiO2 filler greatly increased the hardness, which can be attributed to the higher hardness and moreuniform dispersion of SiO2 filler. The higher hardness is exhibited by the 5 wt% SiO2 filled compared to othernanocomposites. The results show that at 5wt% nano SiO2 content there is 11% increase in hardness

استخدم في هذا البحث سيليكا نانوية بنسب مختلفة (1,2,3,4,5) % وزن و اضيفت الى 3% من مادة الانابيب الكاربونية النانوية لتصنيع مادة متراكبة متكونة من ( nano-Sio2/MWNT/epoxy ) باستخدام طريقة ( hand lay up ) . تم استخدام الموجات الفوق الصوتية لنشر و توزيع المادة الممزوجة النانوية باضافة المواد اللاصقة . و استخدم المجهر الالكتروني الماسح لمعاينة كسر السطح و تعين النسبة الباعية . و درست الخصائص الميكانيكية بعدفحص طوبوغرافية السطح , اذ لوحظ نشر جيد للمادة MWCNT مع السيليكا النانوية , و لا يوجد اي تجمعات للمادة النانوية عند الخلط .وجد ان اضافة المواد النانوية الى الايبوكسي حسن الكثير من الخصائص الميكانيكية و خصوصاً خصائص الثني و معامل يونك لمرتين و اربع مرات عند نسبة 2% و 4% للمادة Sio2 مقارنة بالمادة الرابطة النقية دون اضافة . و لوحظ ايضاً زيادة قوة الصلادة للمادة المتراكبة بزيادة نسبة Sio2 و يعطي انتظامية اكثر . و اعلى صلادة ظهرت عند نسبة 5% من Sio2 مقارنة مع النسب الاخرى . اذ اظهرت النتائج زيادة الصلادة الى 11% عند نسبة 5% من Sio2 .


Article
Photocatalytic Characterization of TiO2 Nanorods and Nanotubes Synthesized by Sol Gel Template Method

Authors: Ban M. Al-Shabander --- Asma Sh. Khalil --- E. A. Al-Ajaj
Journal: Engineering and Technology Journal مجلة الهندسة والتكنولوجيا ISSN: 16816900 24120758 Year: 2018 Volume: 36 Issue: 2 Part (C) Pages: 153-158
Publisher: University of Technology الجامعة التكنولوجية

Loading...
Loading...
Abstract

Titanium dioxide nanorods (TNR) and nanotubes (TNT) wereprepared by sol gel method using anodic aluminium oxide (AAO)membrane as template and calcined at 550°C. The structural of TiO2nanorods and nanotubes investigated by X-ray diffraction (XRD), thesurface topography and the morphology of the samples werecharacterized by atomic force microscopy (AFM), and scanning electronmicroscopy (SEM). The photocatalytic activity of the TiO2 nanostructureswere evaluated by the photodegradation of methyl orange (MO) solutionat different concentrations 10, 20 and 35 ppm under UV irradiation. Thecrystallinity and anatase phase of the TiO2 nanorods and nanotubes areconfirmed by XRD measurements. Average diameter size of TiO2nanorods and TiO2 nanotubes obtained from AFM histogram were 96.14,132.34 nm respectively. A high photocatalytic activity of TiOR2Rnanostructures were obtained at the three different concentrations underUV irradiation.


Article
Effect of Nanocomposites TiO2 addition on the Dielectric Properties of Epoxy resin
تأثير متراكبات النانو بإضافة TiO2¬ على خواص العزل لراتنج الأيبوكسي

Loading...
Loading...
Abstract

Sheets of Epoxy (EP) resin with addition of TiO2 of grain size (1.5μm, and 50nm) and weight percentage (1%, 3%, and 5%) were prepared. Discs of 20mm diameter and 3mm thickness were cut for dielectric measurements. Dielectric properties (dielectric constant, dispassion factor and electrical conductivity) over the frequency range 102 -106 Hz were measured.Comparison was made between the effect of micro and nano particles of TiO2 on the dielectric properties of EP composites with different weight percentage. Epoxy composites with micro sized particles of TiO2 were observed to have the better values of dielectric properties.

في هذا البحث تم تحضير صفائح راتنج الايبوكسي Ep باضافة ثنائي اوكسيد التيتانيوم TiO2 بمقاس حبيبي ((1.5μm, 50nm وبنسب وزنية مئوية مختلفة (1%, 3%, 5%). تم قطع اقراص بقطر 20mm وسمك 3mm من المادة المحضرة ولذلك لغرض القياسات العزلية. الخواص العزلية (ثابت العزل وعامل الفقد والتوصيلية الكهربائية) اجرت القياسات لمدى من الترددات بين 102 -106 Hz.تم كذلك مقارنة تأثير الجسيمات TiO2 من ابعاد النانومتر والمايكرمتر على الخصائص العزلية من متراكبات الايبوكسي وبنسب وزنية مختلفة. وتبين من النتائج ان الجسيمات TiO2 بابعاد المايكرو متر ذات خصائص عزلية افضل

Listing 1 - 5 of 5
Sort by
Narrow your search

Resource type

article (5)


Language

English (5)


Year
From To Submit

2018 (1)

2015 (1)

2011 (1)

2010 (1)

2009 (1)