Using Autoclave Furnace to Improve Properties of Mixing an Autoclaved Aerated Concrete Waste with Window GlassWaste

Authors: Elham Abd AL-Majeed --- Ali Hassan Hadi
Journal: Journal of University of Babylon مجلة جامعة بابل ISSN: 19920652 23128135 Year: 2018 Volume: 26 Issue: 5 Pages: 258-271
Publisher: Babylon University جامعة بابل

Loading...
Loading...
Abstract

Autoclaved aerated concrete (ACC) or thermostone is now becoming increasingly used in constructions, building and partition works due to its properties such as a highly thermal insulating concrete-based material used for both internal and external construction, light weight and large size. However, its low compressive strength and high porosity affected its use.In this researchthe experimental part focused on mixing an autoclaved aerated concrete (AAC) in the form of powder with different ratios of window glass wastes powder, then study the influence of these additives onto properties of thermostone in terms of physical (absorption, porosity, density), mechanical (compressive and hardness), and thermal properties (thermal conductivity and thermal shock). The bulk densityincreased to about (1562Kg/m3), porosity and water absorption have been decreased to about (39.8 %, , 23.44%) respectively with the addition ratio (30) % by weight. of glass. Also the compressive strength has been getting good result (26.27 N/mm2) and hardness, improved (13.88) at the percentage of waste glass (30)% by weight compared to the sample with no-additive. Finally, thermal conductivity with the result (0.5311 watt/m.◦c) at the same percentage of waste glass, while thermal shock showed well result with the additives (10, 20, 30)% by weight at temperature 250 ◦C for 1 h, but failed at temperature of 350 ◦C for the same time.

إن كتل الخرسانة الخلوية أو ما يسمى بالثرمستون أصبح له استخدامات كثيرة في السنوات الأخيرة في عمليات البناء والإنشاءات والتقطيع في الدور و العمارات نظرا لتميزه بمواصفات مثل العزل الحراري الخاص للاستخدام في البنايات من الداخل والخارج, خفة وزنه و كبر حجم المقاطع المستخدمة. ومع ذلك فان له مقاومة انضغاطقليلة ومسامية قليلة عند استخدامه.في هذا البحث تركزت الدراسة العملية على خلط مسحوق الخرسانة الخلوية مع نسب مختلفة من الزجاج المتبقي حيثتم دراسة تأثير هذه النسب من الزجاج على خواص الثرمستون والتي تشمل الخواص الفيزيائية (الكثافة, الامتصاصية, المسامية) , الخواص الميكانيكية (مقاومة الانضغاط, الصلادة), والخواص الحرارية (التوصيلية الحرارية, الصدمة الحرارية). الكثافة تزدادالى (1583كغم/م3), والامتصاصية تنخفض الى ( 23.44 %) والمسامية ايضا تنخفض الى (% 39.8) عند نسبة وزنية (30)% من الزجاج المضاف. ايضا مقاومة الانضغاطتزدادالى (26.27 نيوتن/ملم2) والصلادةتتحسن الى (.13.88)عند نسبة وزنيةمن الزجاج المضاف (30 )% . وأخيرا التوصيلية الحرارية تبين تحسن جيد (0.5311 واط/ م. م◦) عندنفسالنسبةمنالزجاجالمضاف, فيحينانالصدمةالحراريةتبيننتائججيدةعندالاضافات (10, 20, 30)% عند درجة حرارة(250 م◦) لكنحصلالفشلعنددرجةحرارة (350 م◦) لنفسالفترةالزمنية.


Article
Glazing and Coloring of Cellular Concrete Blocks

Authors: Samir H. Awad --- Elham Abd Al-Majeed --- Mohammed Al-Issawi
Journal: Journal of University of Babylon مجلة جامعة بابل ISSN: 19920652 23128135 Year: 2015 Volume: 23 Issue: 3 Pages: 678-688
Publisher: Babylon University جامعة بابل

Loading...
Loading...
Abstract

Thermostone is one of the important materials which have been spraying glazed using different glass mixtures based on alkaline (A5), lead glasses (A4) and their composition at different glass/water (G/W) ratios using a special holder have been designed to keep the glazing on top of thermostone and thereby, protect the other surfaces from damage. Physical and mechanical properties, color, roughness and other properties have been investigated with the aid of microscopic analysis. Duplex layers of A5-glazed layer on pre-coated A4-layer (total thickness of 1.4mm) proved their superiority among A4-glazed layer (0.2mm) and unglazed surfaces, especially those glazed at G/W ratio of 30/70 where the standard thickness (1.5mm) for glazing of pours bodies due to the action of composition of A5- glaze mixture and its effects in sealing the pores and thereby, improving all the properties. The glazing process in this study introduced a glazed thermostone with improved properties using spray technique by means of compressive strength ,porosity, hardness , water absorption and bulk density aspects.

ان الكتل الخرسانية الخلوية او ما يسمى بالثرمستون اصبح له استخدامات كثيرة في السنوات الاخيرة في عمليات البناء والانشاءات والتقطيع في الدور و العمارات نظرا لتميزه بمواصفات مثل العزل الحراري الخاص للاستخدام في البنايات من الداخل والخارج , خفة وزنه و كبر حجم المقاطع المستخدمة.ان مقاومة الانضغاط لهذه المادة والمسامية العالية تحد من استخدام الثرمستون لبعض التطبيقات علاوة على ان سطوح الثرمستون بعد البناء تحتاج عمليات تشطيب وانهاء باستخدام السمنت او السيراميك والمواد الاخرى لحماية السطوح ولغرض الحصول على الديكور والمنظر المناسب. تم في هذا البحث تزجيج سطوح عينات من الثرمستون المجهز من قبل معمل ثرمستون كربلاء بطريقة الرش وباستخدام خلطات زجاجية مختلفة ,قلوية (خلطة A5 بدرجة 920C°) , وزجاج الرصاص (خلطة A4 بدرجة 550C°) وخلطات اخرى مركبة من مزيجهما عند نسب زجاج/ماء (G/W) مختلفة وباستخدام حواضن خاصة لغرض تزجيج السطح العلوي فقط وحماية بقية السطوح من التلف.المواصفات الفيزيائية والميكانيكية ,اللون ,خشونة السطح وفحوصات بصرية تم دراستها بمساعدة الفحص المجهري باستخدام المجهر الضوئي لتقيم الطبقات الناتجة بعد التزجيج. النتائج اظهرت امكانية استخدام عملية التزجيج الثنائي الطبقة (طبقة من زجاج A4 ثم طبقة من زجاج A5 بسمك اجمالي 1.4ملم) في خلق طبقة زجاجية ملتصقة بالسطح الاساس وبسمك ضمن السمك القياسي للتزجيج (1.5ملم) وتحسين مواصفات الثرمستون وتحقيق الديكور والجمالية والتلوين المطلوبة. البحث في هذا الموضوع يحتاج الكثير من الدراسات المستقبلية لدعم هذه المحاولة.هذه الطبقة الثنائية وبالخصوص عند نسبة G/W مساوية 30/70 حققت مواصفات افضل من كل الخلطات ومن مواصفات الثرمستون بدون تزجيج نفسه بسبب خاصية مكونات الطبقة A5 القلوية في غمر المسامات وتحسين الصفات بوجود الطبقة الزجاجية. النتائج اوضحت ان مقاومة الانضغاط و الصلادة قد تحسنت بعد التزجيج. كذلك المسامية ,امتصاصية الماء ,الكثافة و خشونة السطح قد تحسنت بعد التزجيج ايضا بالوان جذابة اختلفت باختلاف تركيب الزجاج. نتائج الفحص المجهري اثبتت تأثير التزجيج في الحصول على اجسام قليلة المسامية خصوصا تلك المزججة عند نسبة G/W مساوية الى 30/70 .


Article
Properties Improvement of Cast Stone Produced Using Recycled Glass Waste and Lightweight Aggregates

Authors: Elham Abd AL-Majeed --- Samir Hamid --- Laith Kazum
Journal: Journal of University of Babylon مجلة جامعة بابل ISSN: 19920652 23128135 Year: 2018 Volume: 26 Issue: 2 Pages: 253-264
Publisher: Babylon University جامعة بابل

Loading...
Loading...
Abstract

Cast stone (CS) is a form of pre-cast concrete widely, used in architectural applications for decorating and building face in place of natural stone due its superior features. The present study was an attempt in using of local lightweight aggregate materials (LWAM) as an alternative to percentage of coarse aggregate, and glass wastes as alternatives to percentages of fine aggregate in cast stone normal mixtures with white cement and plasticizer admixture. The CS products were cured after 24 hrs using of two different processes: water curing (at 23 C° for 3 days) and steam curing (at 60 C° for 14 hrs). Then the products were characterized by tests of compressive strength, design, absorption, flexure strength and liner drying shrinkage. The addition of alternative materials was done by trial mixes (M0-M3) through 3 groups (A, B, and C) according to standards. Group A: design of reference mixtures of CS with compressive strength of 46.3 MPa and the absorption of 6.19%, Group B: design of mixtures containing 50% LWA were 16% lighter than those of Group A with compressive strength of 43.6 MPa and 11% improvement in the absorption, Group C: design of mixtures containing (50 and 75%) glass waste with compressive strength of (47.5-44.3 MPa) and the absorption of (5.3-4.7%), respectively. The modified steam curing process (curing after 24 hrs casting) done in this study could prove its effectiveness in the achievement of the required compressive strength in comparison with the normal process (direct curing after casting) due to the effect of such new process in providing the more uniform distribution of the cement gel with good physical properties. Results from the flexural strength test could prove the achievement of the required levels (6.9 – 6.3 at 50 – 75% glass waste addition) recorded in the standard.

حجر الصب أو الحجر الصناعي هو نوع من انواع الخرسانه مسبقه الصب الواسعه الاستخدام في التطبيقات المعماريه لغرض الديكور و تغليف واجهات المباني بدل الحجر الطبيعي نظرآ لمواصفاته المتميزه. الدراسه الحاليه هي محاوله في استخدام مواد محليه مثل الركام خفيف الوزن كبديل عن نسبه من الركام الخشن, و مخلفات الزجاج كبديل عن نسبه من الركام الناعم في خلطات حجر الصب التقليديه مع الاسمنت البيض و الملدنات. حجر الصب المنتج من الخلطه المرجعية تم معالجته بعد 24 ساعه من الصب باستخدام طريقتين مختلفتين: المعالجه بالماء (عند 23مᵒ لثلاثه ايام) و المعالجه بالبخار (عند 60مᵒ لمده 14 ساعه). تم توصيف منتجات حجر الصب باختبارات مقاومه الانضغاط, الكثافه, الامتصاصيه, مقاومه الانحناء, و التقلص الجاف الخطي. تمت اضافه المواد البديله بنظام الخلطات التجريبيه (M0-M3) باستخدام 3 مجاميع (A,B وC) تبعآ للمعايير. مجموعه A: تصميم الخلطه المرجعيه لحجر الصب مع مقاومه انضغاط 46.3 مغا باسكال و امتصاصيه 6.19%, مجموعه B: تصميم خلطات تحتوي على 50% من الركام الخفيف الوزن وكان أخف وزنا بنسبة 16٪ من حجر المجموعة A مع مقاومة انضغاط 43.6 ميجا باسكال وتحسن 11٪ في الامتصاص, مجموعه C: تصميم خلطات تحتوي 50% و 75% مخلفات الزجاج مع مقاومه انضغاط (47.5-44.3 مغا باسكال) و امتصاصيه (5.3-4.7%), على التوالي. إن عملية المعالجة بالبخار المعدلة (المعالجة بعد الصب 24 ساعة) التي أجريت في هذه الدراسة قد اثبتت فعاليتها في تحقيق مقاومة الانضغاط المطلوبة بالمقارنة مع العملية العادية (المعالجة المباشرة بعد الصب) نتيجة لتأثير هذه العملية في توفير توزيع أكثر انتظام لعجينه الاسمنت مع الخصائص الفيزيائية جيدة. اثبتت نتائج اختبار قوة الانحناء تحقيق المستويات المطلوبة (6.9 - 6.3 عند 50 - 75٪ من إضافة النفايات الزجاجية) المسجلة في المعايير المعتمده.


Article
EFFECT OF GLASS WASTE ON PROPERTIES OF CELLULAR CONCRETE WASTE POWDER
تأثير مخلفات الزجاج على خواص مسحوق مخلفات الخرسانة الخلوية

Loading...
Loading...
Abstract

The research includes making mixtures of cellular concrete (thermostone) waste powder with different percentages of glass waste powder and measuring some mechanical and physical properties of the resulting composite material of glass and thermostone waste. The properties (porosity, absorption, density, compression, and hardness) were tested on two types samples, first type without addition of glass (standard sample) and the second with addition of glass (10, 20, 30)% by weight of thermostone waste.The results showed that both of porosity and absorption of thermostat waste powder are decreasing with increasing of a glass percent, where porosity decrease from 63.38% to 28.74% and absorptions from 46.88% to 16.78%. Density, compression and hardness were increased with increasing of glass percent, where density increased from 1.351 to 1.712 gm/cm3, compression from 9.7 to 13.8 Mpa, and hardness from 22.7 to 99.7.

يتضمن البحث عمل خلطات من مخلفات الخرسانة الخلوية (الثرمستون) الحاوية على نسب مختلفة من مخلفات الزجاج وتقييم سلوك بعض الخواص الميكانيكية والفيزيائية للمادة المركبة لمخلفات الثرمستون والزجاج. تم قياس كل من المسامية ، الامتصاصية ، الكثافة ، الانضغاطية والصلادة على نوعين من نماذج مخلفات الثرمستون, الاول بدون اضافة مخلفات الزجاج والثاني بإضافة الزجاج بنسب )30, 20, 10 ) % من وزن مخلفات الثرمستون.اظهرت النتائج ان كل من المسامية والامتصاصية للعينات تنخفض مع زيادة نسبة الزجاج المضافة ، حيث انخفضت المسامية من 73,62% الى 28,74% والامتصاصية من 58,25% الى 16,78% . وازدادت كل من الكثافة والانضغاطية والصلادة مع زيادة نسبة الزجاج، حيث زادت الكثافة من 1,351 الى 1,712 والانضغاطية من 2,93 الى 4,88 والصلادة من 22,75 الى 99,7 .

Listing 1 - 4 of 4
Sort by
Narrow your search

Resource type

article (4)


Language

English (4)


Year
From To Submit

2018 (2)

2017 (1)

2015 (1)