Article
Experimental Investigation and Mathematical Modeling of Tensile Properties of Unsaturated Polyester Reinforced by Woven Glass Fibers
التقصي العملي والنمذجه الرياضيه لخصائص الشد للبولي استر الغير مشبع المقوى بالياف الزجاج الحصيرية

Authors: Jawad Kadhim Oleiwi --- Emad Saadi Al- Hassani --- Alaa Abd Mohammed
Journal: Engineering and Technology Journal مجلة الهندسة والتكنولوجيا ISSN: 16816900 24120758 Year: 2014 Volume: 32 Issue: 3 Part (A) Engineering Pages: 653-666
Publisher: University of Technology الجامعة التكنولوجية

Loading...
Loading...
Abstract

This research studied the tensile properties of glass fiber reinforced unsaturated polyester with different fiber volume fraction Vf, and angle of fibers for coarse and fine woven fibers reinforcement. The composite specimens were prepared by hand lay-up technique and cutting according to (ASTM D – 638) for tensile test to obtain modulus of elasticity, ultimate tensile strength and elongation percentage of the composite specimens. Mathematical models were done by using statistical analysis which shows the tensile properties of the composite specimens as a function of volume fraction and fiber angle.The results show that the maximum value of the modulus of elasticity was (11.5 GPA) and the maximum value of ultimate tensile strength was (240 MPa) which happed at (11% VF) for fine woven fibers and for (0º/90º) fibers angle, and vice versa for percentage elongation was (2.5%).

في هذا البحث تم دراسة خواص الشد للبولي استر غير مشبع مقوى بالياف الزجاج عند تغير كل من الكسر الحجمي وزاوية الليف لنوعين من التقوية الحصيرة الخشنه والناعمه. حضرت العينات المركبة بالطريقة اليدوية وقطعت وفق المواصفه (ASTM D – 638) لفحص الشد للحصول على معامل المرونة واقصى أجهاد شد والاستطالة النسبية لهذه العينات. تم عمل نماذج رياضية باستخدام التحليل الأحصائي الذي يبين خواص الشد كدالة لكسر الحجمي وزاوية الليف. بينت النتائج بان اقصى قيمة لمعامل المرونة كانت(11.5 GPa) واقصى اجهاد شد كان(240 MPa) يحصلان عند الكسر حجمي (11%) عند التقوية بالحصيرة الناعمة ولزاوية ليف (0º/90º) والعكس بالعكس للاستطاله النسبية حيث كانت 2.5%) ).


Article
Modeling and Buckling Analysis of Polymeric Composite Columns
نمذجة وتحليل الأنبعاج للأعمدة المتراكبة البوليمرية

Authors: Jawad Kadhim Oleiwi --- Emad Saadi Al- hassani --- Alaa Abd Mohammed
Journal: Engineering and Technology Journal مجلة الهندسة والتكنولوجيا ISSN: 16816900 24120758 Year: 2014 Volume: 32 Issue: 5 Part (A) Engineering Pages: 1180-1196
Publisher: University of Technology الجامعة التكنولوجية

Loading...
Loading...
Abstract

This research studied the buckling of composite columns made from glass fiber reinforced unsaturated polyester. The composite specimens were prepared by hand lay-up technique with different fiber volume fraction Vf, aspect ratio and angle of fibers when reinforced with coarse and fine woven fibers. Mathematical models were done by using statistical analysis which show the critical load of the composite column as a function of volume fraction, fiber angle and aspect ratio. The results show that the maximum value of the critical load can be observed at volume fraction Vf =11%, aspect ratio L/T = (3.5) and fiber angle θ = (0º/90º) for fine fiber was (500.72 N). Also its found the maximum critical load for coarse fiber can be observed at Vf =8%, L/T= (3.5) and θ = (0º/90º) was (400.4 N).

في هذا البحث تم دراسة الأنبعاج للأعمدة المركبة تتكون من البولي أستر الغير مشبع مقوى بالياف زجاج. حضرت العينات المركبة بالطريقة اليدوية عند تغير كل من الكسر الحجمي والنسبة الباعية وزاوية ليف لنوعين من التقوية الحصيرة الخشنة والناعمة. تم عمل نماذج رياضية باستخدام التحليل الأحصائي الذي بين الحمل الحرج للعمود المركب كدالة للكسر الحجمي وزاوية ليف والنسبة الباعية. بينت النتائج بأن أقصى قيمة للحمل الحرج حدثت عند الكسر الحجميVf =11%)) والنسبة الباعية (L/T=3.5) وزاوية ليف0º/90º)) عند التقوية باليف الناعم كانت (500.72N). أيضا وجد بأن أقصى قيمة للحمل الحرج عند التقوية بالحصيرة الخشنة حدثت عند الكسر الحجمي (Vf =8%) والنسبة الباعية L/T=3.5)) وزاوية ليف 0º/90º)) كانت (400.4 N) .


Article
Tensile and Buckling Analysis of Polymeric Composite Columns

Authors: Jawad Kadhim Oleiwi --- Emad Saadi Al- hassani --- Alaa Abd Mohammed
Journal: Basrah Journal for Engineering Science مجلة البصرة للعلوم الهندسية ISSN: Print: 18146120; Online: 23118385 Year: 2014 Volume: 14 Issue: 2 Pages: 176-188
Publisher: Basrah University جامعة البصرة

Loading...
Loading...
Abstract

This research studied the critical load of composite columns theoretical and numerical by using ANSYS14 package depended on experimental tensile properties of composite specimens. The composite specimens were prepared by hand lay-up technique made from unsaturated polyester reinforced with glass fibers with different fiber volume fraction Vf, aspect ratio (L/T), and angle of fibers for coarse and fine woven fibers.The critical load that obtained by using program (ANSYS 14) have also shown a good agreement with results that were obtained theoretically and the maximum difference was (0.7%).The results show that the maximum value of the critical load can be observed at Vf =11%, L/T = (3.5) and θ = (0º/90º) for fine woven fibers was (622.115N). Also its found the maximum critical load for coarse woven fibers can be observed at Vf %=8%, L/T=(3.5) and θ = (0º/90º) was (486.887N). Also the observed values of tensile properties and predicated values are scattered close to the (45˚) line.


Article
Effect of Nature Materials Powders on Mechanical and Physical Properties of Glass Fiber / Epoxy Composite
تأثير مساحيق اساسها مواد طبيعية على الخواص ميكانيكية وفيزياوية لمواد مركبة من ايبوكسي والياف زجاج

Authors: Aseel Basim Abdul-Hussein --- Emad Saadi AL-Hassani --- Reem Alaa Mohammed
Journal: Engineering and Technology Journal مجلة الهندسة والتكنولوجيا ISSN: 16816900 24120758 Year: 2015 Volume: 33 Issue: 1 Part (A) Engineering Pages: 175-197
Publisher: University of Technology الجامعة التكنولوجية

Loading...
Loading...
Abstract

In the present study composites were prepared by Hand lay-up molding. The composites constituents were epoxy resin as the matrix, 6% volume fractions of Glass Fibers (G.F) as reinforcement and 3%, 6% of nature material (Rice Husk Ash, Carrot Powder, and Sawdust) as filler. Density, water absorption, hardness test, flexural strength, shear stress measurements and tests were conducted to reveal their values for each type of composite. True density results had shown an incremental increase with volume fraction increasing and water absorption, hardness, flexural strength and shear stress results had shown an incremental increase with volume fraction increasing with smaller particle size.

تم في هذا البحث تحضير مواد متراكبه بواسطة طريقة القولبة اليدوية. المواد المتراكبة مكونة من راتنج الايبوكسي كماده اساس وبألياف الزجاج بكسر حجمي 6% وكذلك 3% و 6 % كحشوة من المواد الطبيعية ( رماد قشور الارز , مسحوق الجزر , بودرة خشب جاوي ) . تم اجراء قياسات وفحوصات الكثافة وامتصاصية الماء وفحص الصلادة, مقاومة الانحناء , اجهاد القص للكشف عن قيمها لكل نوع من المواد المتراكبة . عند اجراء اختبارات الكثافة فان النتائج اظهرت بان الكثافة تزداد مع زيادة الكسر الجحمي والنتائج اظهرت بان امتصاصية الماء والصلادة ومقاومة الانحناء واقصى اجهاد قص يزداد مع زياد الكسر الجحمي و مع اصغر حجم حبيبي .


Article
Erosion Wear Behavior of Industrial Material Reinforced Epoxy Resin Composites and its Coating with Natural Based Material
سلوك بلى التعرية لمواد الصناعية المدعمة براتتج الايبوكسي وطلائها مع مادة اساسها طبيعي

Authors: Aseel Basim Abdul-Hussein --- Emad Saadi AL-Hassani --- Reem Alaa Mohammed
Journal: Engineering and Technology Journal مجلة الهندسة والتكنولوجيا ISSN: 16816900 24120758 Year: 2015 Volume: 33 Issue: 4 Part (A) Engineering Pages: 902-918
Publisher: University of Technology الجامعة التكنولوجية

Loading...
Loading...
Abstract

In the present study, composites were prepared by Hand lay-up molding The composites constituents were epoxy resin as a matrix, 6% volume fractions of Glass Fibers (G.F) as reinforcement and 3%, 6% volume fractions of preparation industrial powder (calcium carbonate CaCO3, potassium carbonate K2CO3 or sodium carbonate Na2CO3) as filler. The erosion wear behavior and coating by natural wastes (Rice Husk Ash) with epoxy resin after erosion were studied. The results showed that the non – reinforced epoxy have lower resistance erosion than industrial based Material composites and the specimen (Epoxy+6%glass fiber+6% CaCO3) has higher resistance erosion than composites reinforced with sodium carbonate and potassium carbonate at 25cm, angle 30°, grin size of sand 850µm, temperature 25Ċ, 200 gm salt content in 3liter of water and 15 hour. Coating specimen with mixed epoxy resin -RHA with particles size in the range (1.4-4.2) µm improves erosion wear resistance characteristics of the coated specimen, coating thickness was (16 ± 1) μm and after erosion in (15 hours) the thickness was (10) μm .Application of the work protection of pipes from erosion, these pipes include the sewage water , drainage pipe laboratory (hot water, chemicals and mineral oil) , pipeline transportation of petroleum products and pipeline transportation of gas products

تم في هذا البحث تحضير المواد المتراكبة بواسطة طريقة القولبة اليدوية. تتكون المواد المتراكبة من راتنج الايبوكسي كماده اساس والياف الزجاج كمادة تقوية بكسر حجمي 6% و مساحيق طبيعية محضرة (كاربونات الكالسيوم , كاربونات الصوديوم اوكاربونات البوتاسيوم ) بكسر حجمي (3% , 6% ) دراسة سلوك بلى التعرية والطلاء بواسطة النفايات الطبيعية (رماد قشور الرز) مع راتنج الايبوكسي بعد التعرية . النتائج اظهرت بان الايبوكسي غير المقوى يمتلك مقاومة للتعرية قليلة من المواد المتراكبة التي اساسها مواد طبيعة والعينة (الايبوكسي + 6%الالياف زجاج + 6% كاربونات الكالسيوم) تملك مقاومة للتعرية من المواد المتراكبة المدعمة بمسحوق الجزر وبودرة الخشب عند25 سم ، زاوية 30º، حجم دقائق تعرية 850 مايكرون , ودرجة حرارة 25Ċ ,200 غم ملح في 3 لتر من ماء 15 ساعة . طلاء العينات براتنج الايبوكسي مع رماد قشور الرز مع حجم حبيبي ضمن المدى (1.4-2.4) مايكرون لتحسين خواص مقاومة التعرية للعينات التي تم طلائها , وسمك الطلاء كان (16 ± 1) مايكرون وبعد التعرية عند 15 ساعة اصبح سمك الطلاء (10) مايكرون. تطبيق هذا الدراسة هو حماية الانابيب من التعرية , وهذة الانابيب تتضمن انابيب الصرف الصحي ,انابيب الصرف لمختبرات (الماء الساخن ، المواد الكيمياوية والزيوت ) وانابيب نقل المنتجات النفطية والغازية .


Article
Influence of Coating with Some Natural Based Materials on the Erosion Wear Behavior of Glass Fiber Reinforced Epoxy Resin
تأثير الطلاء لبعض المواد المتراكبة التي اساسها مواد طبيعية على سلوك بلى التعرية لراتنج الايبوكسي المدعم بالالياف الزجاجية

Loading...
Loading...
Abstract

In the present study, composites were prepared by Hand lay-up molding. The composites constituents were epoxy resin as a matrix, 6% volume fractions of glass fibers (G.F) as reinforcement and 3%, 6% volume fractions of preparation natural material (Rice Husk Ash, Carrot Powder, and Sawdust) as filler. Studied the erosion wear behavior and coating by natural wastes (Rice Husk Ash) with epoxy resin after erosion. The results showed the non – reinforced epoxy have lower resistance erosion than natural based material composites and the specimen (Epoxy+6%glass fiber+6%RHA) has higher resistance erosion than composites reinforced with carrot powder and sawdust at 30cm , angle 60°, grin size of sand 425µm , temperature 30Ċ , 300 gm salt content in 2liter of water and 15 hour. Coating specimen with mixed epoxy resin -RHA with particles size in the range (1.4-4.2) µm improves erosion wear resistance characteristics of the coated specimen, coating thickness was (16 ± 1) μm and after erosion at (15 hour) the thickness was (10) μm .

تم في هذا البحث تحضير المواد المتراكبة بوساطة طريقة القولبة اليدوية . تتكون المواد المتراكبة من راتنج الايبوكسي ماده اساس والياف الزجاج مادة تقوية بكسر حجمي 6% و مساحيق طبيعية محضرة ( رماد قشور الرز و مسحوق الجزر و بودرة الخشب ) بكسر حجمي (3% , 6% ) . دراسة سلوك بلى التعرية والطلاء بوساطة النفايات الطبيعية (رماد قشور الرز) مع راتنج الايبوكسي بعد التعرية . النتائج اظهرت بان الايبوكسي غير المقوى يمتلك مقاومة للتعرية قليلة من المواد المتراكبة التي اساسها مواد طبيعة والعينة (الايبوكسي + 6%الالياف زجاج + 6% رماد قشور الرز) تملك مقاومة للتعرية من المواد المتراكبة المدعمة بمسحوق الجزر وبودرة الخشب عند25 سم ، زاوية 30º، حجم دقائق تعرية 850 مايكرون , ودرجة حرارة 25Ċ ,200 غم ملح في 3 لتر من ماء 15 ساعة . طلاء العينات براتنج الايبوكسي مع رماد قشور الرز مع حجم حبيبي ضمن المدى (1.4-2.4) مايكرون لتحسين خواص مقاومة التعرية للعينات التي تم طلائها , وسمك الطلاء كان (16 ± 1) مايكرون وبعد التعرية عند 15 ساعة اصبح سمك الطلاء (10) مايكرون .


Article
Mechanical and physical properties of carbon nanotubes with Kevlar fiber reinforced with polyester resin
الخواص الميكانيكية و الفيزيائية لانابيب الكاربون النانوية مع الياف الكفلر المقواة مع راتنج البولي استر

Loading...
Loading...
Abstract

In this research study Hardness (shore D), Water absorption, Flexural, Impact Test, and Fracture Toughness of polymer nano composites.The polymer nano composites based on unsaturated polyester resin reinforced with Kevlar fibers (K.F). The samples are attended by hand lay – up method according to (Rule mixture) for various volume fractions of unsaturated polyester resin, fiber and carbon nanotube. The polyester resin was matrix strengthened with 3% volume fraction from Kevlar fiber and (0.5%, 1%, 1.5%, 2%( volume fractions of carbon nanotube. The water absorption, hardness (shore D), flexural test, impact testand toughness fracture properties were studied. Results showed that the water absorption increase with volume fraction increase of fiber with Carbon Nanotube, the sample (polyester+3%K.F+0.5% CNTs) has lower water absorption than other samples. The hardness (shore D), flexural test, impact testand toughness fracture for the sample (polyester+3%C.F+0.5% CNTs) has higher value for Nano- composites. Nano composites, Carbon nanotube, Kevlar fiber, Hardness (shore D), Water absorption, Flexural Strength, Impact Test, Toughness Fracture.

تم في هذا البحث دراسة الصلادة (شورD), امتصاصية الماء, مقاومة الكسر, اختبار الصدمة و متانة الكسر لمتراكبات نانوية ذات اساس راتنج البولي استر غير المشبع مقواة بألياف الكفلر. العينات جهزت بطريقة الصب اليدوي وفقالقاعدة الخلط لكسور حجمية مختلفة من راتنج البولي استر غير المشبع والالياف وانابيب الكاربون النانوية. راتنج البولي استر كان ارضية مقواة مع 3%كسر حجمي من الياف الكفلر و (0.5 ,1 ,1.5 , 2 ) % كسر حجمي لانابيب الكاربون النانوية. تم دراسة خواص امتصاصية الماء, صلادة (شور(D, اختبار الصدمة ومقاومة الكسر. اظهرت النتائج بان امتصاصيه الماء تزداد مع زيادة الكسر الحجمي للالياف مع انابيب الكاربون النانوية, العينه (بولي استر + 3% الياف كفلر + 0.5 % انابيب اكاربون النانوية) تمتلك اقل امتصاصية ماء من العينات الاخرى. الصلادة (شورD), فحص الكسر, فحص الصدمة ومتانة الكسر للعينه (بولي استر +3% الياف كفلر + 0.5 %انابيب الكاربون انانوية) تمتلك اعلى قيمه للمتراكبات النانوية.

Listing 1 - 7 of 7
Sort by
Narrow your search

Resource type

article (7)


Language

English (6)

Arabic and English (1)


Year
From To Submit

2016 (1)

2015 (3)

2014 (3)