Influence of Coating with Some Natural Based Materials on the Erosion Wear Behavior of Glass Fiber Reinforced Epoxy Resin
تأثير الطلاء لبعض المواد المتراكبة التي اساسها مواد طبيعية على سلوك بلى التعرية لراتنج الايبوكسي المدعم بالالياف الزجاجية

Loading...
Loading...
Abstract

In the present study, composites were prepared by Hand lay-up molding. The composites constituents were epoxy resin as a matrix, 6% volume fractions of glass fibers (G.F) as reinforcement and 3%, 6% volume fractions of preparation natural material (Rice Husk Ash, Carrot Powder, and Sawdust) as filler. Studied the erosion wear behavior and coating by natural wastes (Rice Husk Ash) with epoxy resin after erosion. The results showed the non – reinforced epoxy have lower resistance erosion than natural based material composites and the specimen (Epoxy+6%glass fiber+6%RHA) has higher resistance erosion than composites reinforced with carrot powder and sawdust at 30cm , angle 60°, grin size of sand 425µm , temperature 30Ċ , 300 gm salt content in 2liter of water and 15 hour. Coating specimen with mixed epoxy resin -RHA with particles size in the range (1.4-4.2) µm improves erosion wear resistance characteristics of the coated specimen, coating thickness was (16 ± 1) μm and after erosion at (15 hour) the thickness was (10) μm .

تم في هذا البحث تحضير المواد المتراكبة بوساطة طريقة القولبة اليدوية . تتكون المواد المتراكبة من راتنج الايبوكسي ماده اساس والياف الزجاج مادة تقوية بكسر حجمي 6% و مساحيق طبيعية محضرة ( رماد قشور الرز و مسحوق الجزر و بودرة الخشب ) بكسر حجمي (3% , 6% ) . دراسة سلوك بلى التعرية والطلاء بوساطة النفايات الطبيعية (رماد قشور الرز) مع راتنج الايبوكسي بعد التعرية . النتائج اظهرت بان الايبوكسي غير المقوى يمتلك مقاومة للتعرية قليلة من المواد المتراكبة التي اساسها مواد طبيعة والعينة (الايبوكسي + 6%الالياف زجاج + 6% رماد قشور الرز) تملك مقاومة للتعرية من المواد المتراكبة المدعمة بمسحوق الجزر وبودرة الخشب عند25 سم ، زاوية 30º، حجم دقائق تعرية 850 مايكرون , ودرجة حرارة 25Ċ ,200 غم ملح في 3 لتر من ماء 15 ساعة . طلاء العينات براتنج الايبوكسي مع رماد قشور الرز مع حجم حبيبي ضمن المدى (1.4-2.4) مايكرون لتحسين خواص مقاومة التعرية للعينات التي تم طلائها , وسمك الطلاء كان (16 ± 1) مايكرون وبعد التعرية عند 15 ساعة اصبح سمك الطلاء (10) مايكرون .


Article
Mechanical and physical properties of carbon nanotubes with Kevlar fiber reinforced with polyester resin
الخواص الميكانيكية و الفيزيائية لانابيب الكاربون النانوية مع الياف الكفلر المقواة مع راتنج البولي استر

Loading...
Loading...
Abstract

In this research study Hardness (shore D), Water absorption, Flexural, Impact Test, and Fracture Toughness of polymer nano composites.The polymer nano composites based on unsaturated polyester resin reinforced with Kevlar fibers (K.F). The samples are attended by hand lay – up method according to (Rule mixture) for various volume fractions of unsaturated polyester resin, fiber and carbon nanotube. The polyester resin was matrix strengthened with 3% volume fraction from Kevlar fiber and (0.5%, 1%, 1.5%, 2%( volume fractions of carbon nanotube. The water absorption, hardness (shore D), flexural test, impact testand toughness fracture properties were studied. Results showed that the water absorption increase with volume fraction increase of fiber with Carbon Nanotube, the sample (polyester+3%K.F+0.5% CNTs) has lower water absorption than other samples. The hardness (shore D), flexural test, impact testand toughness fracture for the sample (polyester+3%C.F+0.5% CNTs) has higher value for Nano- composites. Nano composites, Carbon nanotube, Kevlar fiber, Hardness (shore D), Water absorption, Flexural Strength, Impact Test, Toughness Fracture.

تم في هذا البحث دراسة الصلادة (شورD), امتصاصية الماء, مقاومة الكسر, اختبار الصدمة و متانة الكسر لمتراكبات نانوية ذات اساس راتنج البولي استر غير المشبع مقواة بألياف الكفلر. العينات جهزت بطريقة الصب اليدوي وفقالقاعدة الخلط لكسور حجمية مختلفة من راتنج البولي استر غير المشبع والالياف وانابيب الكاربون النانوية. راتنج البولي استر كان ارضية مقواة مع 3%كسر حجمي من الياف الكفلر و (0.5 ,1 ,1.5 , 2 ) % كسر حجمي لانابيب الكاربون النانوية. تم دراسة خواص امتصاصية الماء, صلادة (شور(D, اختبار الصدمة ومقاومة الكسر. اظهرت النتائج بان امتصاصيه الماء تزداد مع زيادة الكسر الحجمي للالياف مع انابيب الكاربون النانوية, العينه (بولي استر + 3% الياف كفلر + 0.5 % انابيب اكاربون النانوية) تمتلك اقل امتصاصية ماء من العينات الاخرى. الصلادة (شورD), فحص الكسر, فحص الصدمة ومتانة الكسر للعينه (بولي استر +3% الياف كفلر + 0.5 %انابيب الكاربون انانوية) تمتلك اعلى قيمه للمتراكبات النانوية.