Study Torsion Capacity of Epoxy -Glass Fiber Composites

Authors: N. A. Abas --- H. I. Jafar --- F.T. Mohammed Noori
Journal: Al-Nahrain Journal of Science مجلة النهرين للعلوم ISSN: (print)26635453,(online)26635461 Year: 2011 Volume: 14 Issue: 1 Pages: 109-114
Publisher: Al-Nahrain University جامعة النهرين

Loading...
Loading...
Abstract

In this study, torsion test was performed in order to examine the mechanical behaviors of epoxy
and an epoxy reinforced by two types of glass fibers (chopped and yarn) composite rod. The stressstrain
curves were constituted and examined in order to show the elastic and plastic regions, the
yield point was 23.226o and 34.837o angle of twist for epoxy and epoxy /fibers respectively which
is the same for both chopped and yarn glass fibers epoxy, from this test it was found that the epoxy
rod initially yielded first, the cracks propagation in composite rod along the fibers direction, which
caused eventually the delimitation of composite chopped and yarn glass fibers from the epoxy
matrix. Then the white regions appear in composite rod and finally the fiber breakage and the
catastrophic failure took place.

تم في هذه الدراسة انجاز فحص عزم الالتواء لفحص السلوك الميكانيكي للايبوكسي ومتراكباته المدعمة بنوعين من الياف الزجاج (مقطع وخيوط), وتبين من انجاز منحيات الاجهاد- الانفعال كل من المناطق اللدنة والمرنة وكانت نقطة الخضوع23.2260و34.8370 للكل من الايبوكسي ومتراكباته على التوالي حيث انها متشابهة لايبوكسي-الياف زجاج مقطع وخيوط, ومن هذا الاختبار وجد ان قضيب الايبوكسي يخضع اولا وان الشقوق تاخذ بالانتشار على طول وباتجاه االالياف في القضيب المتراكب مما يتسبب انفصال الياف الزجاج المقطع والخيوط من الايبوكسي وبالتالي تظهر مناطق بيضاء في قضيب المتراكب ثم ينكسر الليف وبذلك يحل الفشل.


Article
Effect of Nanocomposites TiO2 addition on the Dielectric Properties of Epoxy resin
تأثير متراكبات النانو بإضافة TiO2¬ على خواص العزل لراتنج الأيبوكسي

Loading...
Loading...
Abstract

Sheets of Epoxy (EP) resin with addition of TiO2 of grain size (1.5μm, and 50nm) and weight percentage (1%, 3%, and 5%) were prepared. Discs of 20mm diameter and 3mm thickness were cut for dielectric measurements. Dielectric properties (dielectric constant, dispassion factor and electrical conductivity) over the frequency range 102 -106 Hz were measured.Comparison was made between the effect of micro and nano particles of TiO2 on the dielectric properties of EP composites with different weight percentage. Epoxy composites with micro sized particles of TiO2 were observed to have the better values of dielectric properties.

في هذا البحث تم تحضير صفائح راتنج الايبوكسي Ep باضافة ثنائي اوكسيد التيتانيوم TiO2 بمقاس حبيبي ((1.5μm, 50nm وبنسب وزنية مئوية مختلفة (1%, 3%, 5%). تم قطع اقراص بقطر 20mm وسمك 3mm من المادة المحضرة ولذلك لغرض القياسات العزلية. الخواص العزلية (ثابت العزل وعامل الفقد والتوصيلية الكهربائية) اجرت القياسات لمدى من الترددات بين 102 -106 Hz.تم كذلك مقارنة تأثير الجسيمات TiO2 من ابعاد النانومتر والمايكرمتر على الخصائص العزلية من متراكبات الايبوكسي وبنسب وزنية مختلفة. وتبين من النتائج ان الجسيمات TiO2 بابعاد المايكرو متر ذات خصائص عزلية افضل