Article
Structural and Optical Characterization of Nickel Oxide Thin Films Prepared by Spray Pyrolysis Technique
الخصائص التركيبية والبصرية لأغشية اوكسيد النيكل الرقيقة المحضرة بطريقة الرش الحراري

Author: Fadheela H. Oleiwe
Journal: Engineering and Technology Journal مجلة الهندسة والتكنولوجيا ISSN: 16816900 24120758 Year: 2015 Volume: 33 Issue: 8 Part (B) Scientific Pages: 1503-1512
Publisher: University of Technology الجامعة التكنولوجية

Loading...
Loading...
Abstract

In this research, Nickel oxide (NiO) thin film were prepared by using nickel chloride ( NiCl2.6H2O) on glass substrate by using Spray Pyrolysis technique. The Structural and optical properties were studied for the growth thin films under influence different molarities (0.5,1,2 M) by XRD , SEM . The optical properties studied in the wavelength range from 200-1100nm measured by UV-VIS Spectrometer device. The X-ray diffraction studies indicated that intensity was increased with molarities increase and had cubic structure , these films has grain size values (4.13-11.95 nm) with different molarities (0.5, 1 , 2M) , SEM found the films has smooth surface with grains scattered throughout the surface and the surface the films filled with the clusters of the larger grains the at increase molarities and AFM it is found the (RMS) of NiO films increased from 7.77 to 20.7 nm and the roughness average increased from 5.73-15.6 nm with the increase of molarities from 0.5-2 M . From the optical studies it is found the film thickness increased with molarities increase, while the transmittance decreased from approximately 75% to approximately 54% and the energy gap for the NiO films varies from ( 3.65 to 3.1eV) as the molarities increase.

في هذا البحث حضر اوكسيد النيكل باستخدام كلوريدات النيكل على قاعدة زجاجية باستخدام تقنية الرش الحراري , درست الخصائص التركيبية والبصرية للاغشية النامية تحت تأثير المولارية بواسطة فحص حيود الأشعة السينية والمجهر الالكتروني الماسح ومجهر القوة الذرية , الخصائص البصرية درست عند طول الموجي من 200-1100 نانومتر مقاسه بواسطة استخدام جهاز مطياف UV -VIS .ان فحص حيود الاشعة السينية اشار الى ان الشدة تزداد بزيادة المولارية وتمتلك تركيب مكعب , هذه الاغشية لها حجم حبيبي قيمته تتغير من (4.13-11.95) مع تغيير التركيز (0.5,1,2) مولارية , وجد المجهر الالكتروني الماسح الاغشية تمتلك سطح ناعم مع انتشار الحبوب في كافة انحاء السطح , وسطح الاغشية ملأت بعناقيد بالحبوب الكبيرة بزيادة المولارية , ومجهر القوة الذرية وجد ان قيمة مربع متوسط الجذر تزداد من (7.77 الى 20.7) ومعدل الخشونة يزداد من( 5.73 الى 15.6 ) عندما تتغير قيمة المولارية من ( 0.5 الى 2 ). من دراسة الخصائص البصرية وجد ان السمك يزداد مع زيادة المولارية بينما النفاذية قلت تقريباَ من 75% الى 54% وفجوة الطاقة لاغشية اوكسيد النيكل تتغير من( 3.65 الى 3.1 ) الكترون فولت عند زيادة المولارية


Article
Preparation and Characterization of Tin Oxide Thin Films by Using Spray Pyrolysis Technique
تحضير وخصائص أغشية ثنائي اوكسيد القصدير الرقيقة بواسطة استخدام تقنية الرش الحراري

Authors: Selma M. H. Al-Jawad --- Fadheela H. Oleiwe --- Jabbar .H. Khulaef
Journal: Engineering and Technology Journal مجلة الهندسة والتكنولوجيا ISSN: 16816900 24120758 Year: 2015 Volume: 33 Issue: 3 Part (B) Scientific Pages: 528-538
Publisher: University of Technology الجامعة التكنولوجية

Loading...
Loading...
Abstract

In this work, tin oxide thin films have been prepared by Spray pyrolysis technique, using tin chloride over soda – lime glass. Structural and optical properties were studied under different conditions like substrate temperatures of 300, 350 and 400°C, and annealing in air at temperature 300°C for 1 hr. The films were characterized by XRD, SEM, AFM, and UV-VIS analysis. The optical spectra of the films were measured in the wavelength range of 300 –900 nm by UV-VIS Spectrometer device. The X-ray diffraction studies confirmed the films have the orthogonal structure at low substrate temperature change to a tetragonal structure at high substrate temperature. Films prepared with different substrate temperatures were correspond to preferential orientation along the plane (132) and (110) planes for structural orthogonal, tetragonal respectively. The grain size founded( 25.2-9.77nm) for different substrate temperatures range ( 300- 400°C) after annealing , from the (SEM) images the grain size values of the SnO2 thin films are found to be in the range of (32.3-24.2 nm) corresponding to the substrate temperature (350 and 400°C) after annealing and from the AFM the root mean square (RMS) values for the thin film at substrate temperature 350C was found to be 10.4 nm, the surface roughness 8.86 nm. The maximum value of transmittance was found to be 78 % around the wavelength of 900nm at substrate temperatures 300°C also have energy gap (2.9-3.4eV) at substrate temperatures range ( 300- 400°C) after annealing in air at temperature 300°C for 1 hr.

في هذا العمل حضر ثنائي أوكسيد القصدير بطريقة الرش الحراري , باستخدام كلوريد القصدير على قاعدة زجاجية , درست الخصائص التركيبية والبصرية تحت شروط مختلفة مثل درجة حرارة القاعدة (400,350,300) درجة سيلزية ولدنت في الهواء عند درجة حرارة (300) درجة سيلزية ولمدة ساعة . شخصت خصائص الاغشية بواسطة فحص حيود الأشعة السينية والمجهر الالكتروني الماسح ومجهر القوة الذرية وقياسات الأطياف للأشعة المرئية وفوق البنفسجية , الأطياف البصرية للأغشية حسبت عند الطول الموجي (من 300الى900) نانومتر . أكدت دراسة حيود الأشعة السينية ان الاغشية تمتلك تركيب متعامد عند درجات الحرارة الواطئة للقاعدة وتتغير الى تركيب رباعي الزاوية عند درجات الحرارة العالية للقاعدة , وجدت قيمة الحجم الحبيبي تتغير (من 9.77 الى25.2 ) نانومتر عندما تتغير درجة حرارة القاعدة بين ( 300 الى 400) درجة سيلزية بعد التلدين , كذلك وجدت من صور المجهر الالكتروني الماسح قيمة الحجم الحبيبي لأغشية اوكسيد القصدير تساوي (24.2- 32.3) نانومتر الذي يقابل درجة حرارة القاعدة ( 350 و 400) درجة سيلزية بعد التلدين , اظهرت نتائج مجهر القوة الذرية ان قيمة مربع متوسط الجذر تساوي (10.4) نانومتر ومعدل الخشونة يساوي 8.86 نانومتر عندما تكون درجة حرارة القاعدة 350 درجة سيلزية . بالاضافة الى ذلك وجد ان أعلى قيمة للنفاذية تساوي 78% عند الطول الموجي ( 900) نانومتر عند درجة حراة القاعدة 350 درجة سلزية , وتمتلك فجوة طاقة (2.9-3.4) الكترون فولت لاغشية اوكسيد القصدير عندما درجة الحرارة تتغير بين (300- 400) درجة سليزية بعد التلدين لمدة ساعة.