The study of the bending property of the epoxy (Ep / MgO) and (Ep/SiO2) composites in natural conditions and after immersion in chemical solution
دراسة خاصية الانحناء لمتراكب (Ep /MgO) و(Ep/SiO2) في الظروف الطبيعية وبعد الغمر في المحاليل الكيميائية

Authors: Baraa Khalil Ibrahim براء خليل إبراهيم --- Faik Hammad Antar فائق حماد عنتر
Journal: Iraqi Journal of Physics المجلة العراقية للفيزياء ISSN: 20704003 Year: 2018 Volume: 16 Issue: 39 Pages: 93-102
Publisher: Baghdad University جامعة بغداد

Loading...
Loading...
Abstract

In this paper, a polymer-based composite material was prepared by hand Lay-up method consisting of epoxy resin as a base material reinforced by magnesium oxide powder once and silicon dioxide powder again and with different weight ratios (3, 6, 9 and 12) wt %. The three-point bending test was performed in normal conditions and after immersion in sulfuric acid. The results showed that the bending value decreased with the increase of the weighted ratio of the reinforcement material (MgO, SiO2). The Bending of samples reinforced by SiO2 was found to be less than the bending of samples reinforced by particles (MgO). For example, the bending of the SiO2 sample (0.32 mm) at the weighted ratio (3%) and for the MgO (0.18mm) sample at the weight ratio were the same weighted load (100 g). It was found that the bending values of all samples exceeded the value after immersion in sulfuric acid. For example, the percentage of weight (6%) at the load level (500 g) was changed from 1.16 mm in normal conditions to 1.48mm for the same weight ratio after immersion. In sulfuric acid diluted with 0.3N for 10 days at the same applied load.

في هذا البحث تم تحضير مادة متراكبة ذات اساس بوليمري بطريقة القولبة اليدوية مكونة من راتنج الايبوكسي كمادة اساس مدعم بمسحوق اوكسيد المغنيسيوم مرة ومسحوق ثاني اوكسيد السليكون مرة اخرى وبنسب وزنية مختلفة 12, 9, 6, 3) %Wt). وتم اجراء اختبار الانحناء ثلاثي النقط في الظروف الطبيعية وبعد الغمر في حامض الكبريتيك. بينت النتائج ان قيمة الانحناء تقل مع زيادة النسب الوزنية لمادة التدعيم (MgO,SiO2). وجد ان الانحراف للعينات المدعمة بدقائق (SiO2) اقل من الانحراف للعينات المدعمة بدقائق (MgO) فمثلا كان الانحراف لعينة SiO2 (0.32 mm) عند الكسر الوزني (3%) و لعينة MgO (0.18mm) عند الكسر الوزني ذاتة عند مقدار الحمل المسلط ذاته (100 g). وتبين ان قيم الانحراف لجميع العينات قد زادت عن قيمتها بعد الغمر في حامض الكبريتيك فمثلا تغيرت عند النسبة المئوية الوزنية (6 %) عند مقدار الحمل (500 g) من (1.16 mm) في الظروف الطبيعية واصبحت (1.48 mm) للنسبة الوزنية ذاتها بعد الغمر بحامض الكبريتيك المخفف بعيارية 0.3 N لمدة 10ايام عند مقدار الحمل المسلط ذاته.

Keywords

MgO --- SiO2 --- Ep. --- bending property --- H2SO4 --- normal condition.


Article
Effect of sulfuric acid solution on thermal conductivity and impact strength of epoxy resin reinforced by silicon dioxide powder
تأثير محلول حامض الكبريتيك على التوصيلية الحرارية ومتانة الصدمة لراتنج الايبوكسي المدعم بمسحوق اوكسيد السلكون

Authors: Faik Hammad Antar فائق حماد عنتر --- Baraa Khalil Ibrahim براء خليل إبراهيم
Journal: Iraqi Journal of Physics المجلة العراقية للفيزياء ISSN: 20704003 Year: 2019 Volume: 17 Issue: 41 Pages: 82-90
Publisher: Baghdad University جامعة بغداد

Loading...
Loading...
Abstract

In this search, Ep/SiO2 at (3, 6, 9, 12 %) composites is prepared by hand Lay-up method, to measure the change in the thermal conductivity and Impact Strength of epoxy resin before and after immersion in H2SO4 Solution with a 0.3N for 10 days. The results before immersion decreases with the increase of the weight ratios of the reinforcement material (SiO2), It changed from (82.6×10-2 to 38.7×10-2 W/m.°C) with change weight ratios from (3 to 12) % respectively, but after immersion time in the chemical solution where it was (65.6×10-2 W/m.°C) at the weight ratios (6 %) and became (46.6 × 10-2 W/m.°C) after immersion in sulfuric acid. The results of the Impact strength decreased by increasing the percentage weight ratio, it changed from (1.48 to 0.87 kJ/m2) with change weight ratios from (3 to 12) % respectively, but found an increase in the value of Impact Strength after immersion in the chemical solution Where it was (1.28 kJ/m2) at the weight ratio of 6 % and became (1.82 kJ/m2) at the same weight ratio after immersion in sulfuric acid at normality of 0.3 for 10 days.

في هذا البحث تم تحضير متراكبات Ep/SiO2 عند (12, 9, 6, 3) % بطريقة القولبة اليدوية. لقياس التغير في التوصيلية الحرارية و متانة الصدمة لراتنج الايبوكسي قبل وبعد الغمر في محلول حامض H2SO4 بعيارية 0.3 ولمدة 10 ايام. اظهرت النتائج قبل الغمر تقل مع زيادة النسبة الوزنية لمادة التدعيم (SiO2), اذ تغيرت من 82.6×10-2 الى 38.7× 10-2 (W/m.°C) عند ( 3الى 12)% على التوالي. تبين من النتائج ايضا انه يزداد انخفاض التوصيلية الحرارية بزيادة مدة الغمر في المحلول الكيميائي حيث كانت65.6×10-2 (W/m. °C) عند النسبة الوزنية 6 % واصبحت 46.6×10-2 (W/m.°C) بعد الغمر في حامض الكبريتيك. نتائج مقاومة الصدمة تقل بزيادة النسب الوزنية المئوية , اذ تغيرت من (1.48 الى0.87 (kJ/m2مع تغير النسبة الوزنية من ( 3الى % (12 على التوالي, لكن وجد انه تزداد قيمة مقاومة الصدمة بعد الغمر في المحلول الكيميائي حيث كانت (1.28 kJ/m2) عند النسبة الوزنية 6 % واصبحت (1.83 kJ/m2) عند النسبة الوزنية ذاتها بعد الغمر في حامض الكبريتيك بعيارية0.3 لمدة 10ايام.