Article
Study the surface hardness for (UPE/SiO2) composites
دراسة الصلادة السطحية لمتراكبات (UPE/SiO2)

Authors: Areej Hatam Fareed أريج حاتم فريد --- Faik Hammad Anter فائق حماد عنتر
Journal: Journal of university of Anbar for Pure science مجلة جامعة الانبار للعلوم الصرفة ISSN: 19918941 Year: 2017 Volume: 11 Issue: 2 Pages: 37-43
Publisher: University of Anbar جامعة الانبار

Loading...
Loading...
Abstract

In this work the effect of adding SiO2 powder on the hardness property for UPE was studied. Three groups of samples were prepared (UPE/(SiO2-Micro)), (UPE/(Nano-SiO2) and (UPE/(Micro+Nano)SiO2) with weight fraction of additives (%2، %4، %6، %8). The surface hardness for all samples was measured before and after irradiation with Ultraviolet at time interval (10) hours. The experimental results showed that the surface hardness of all samples increases with increasing the weight fraction of SiO2 in the composite in natural conditions, and that the nano samples has higher hardness than other samples. After UV irradiation, the hardness values also increase with increasing the weight fraction of SiO2 in the composite for all samples, and their value is higher than in normal conditions.

في هذا البحث تم دراسة تأثير اضافة مسحوق ثاني اوكسيد السيليكون على خاصية الصلادة لراتنج البولي استر غير المشبع. تم تحضير ثلاث مجاميع من العينات هي (UPE/(SiO2-Micro)), ((UPE/(Nano-SiO2) وSiO2)(UPE/(Micro +Nano) وبنسب وزنية للمواد المضافة (%2، %4، %6، %8). وتم قياس الصلادة السطحية للعينات قبل وبعد التشعيع بالاشعة فوق البنفسجية ولمدة (10) ساعات, لقد اظهرت النتائج العملية ان الصلادة للعينات كافة تزداد مع زيادة النسبة الوزنية لمادة SiO2 في المتراكب في الظروف الطبيعية, وان العينات النانوية تمتلك صلادة اعلى من بقية العينات. بعد تشعيع العينات ب(UV) تزداد قيم الصلادة ايضاً مع زيادة النسبة الوزنية لمادة SiO2 في المتراكب ولكافة العينات وتكون قيمتها اعلى مما في الظروف الطبيعية.


Article
The Effect of Ultraviolet Irradiation on the Electrical Breakdown and Hardness Properties of (Epoxy/Aluminum ,Nickel) Composites.
تأثير التشعيع بالأشعة فوق البنفسجية على خاصيتي الانهيار الكهربائي والصلادة لمتراكب (ايبوكسي/المنيوم ,نيكل)

Authors: Ahmed Jubair Jaffal أحمد جبير جفال --- Faik Hammad Anter فائق حماد عنتر
Journal: Journal of university of Anbar for Pure science مجلة جامعة الانبار للعلوم الصرفة ISSN: 19918941 Year: 2017 Volume: 11 Issue: 3 Pages: 92-97
Publisher: University of Anbar جامعة الانبار

Loading...
Loading...
Abstract

This work includes preparation particles composite materials by adding Aluminum particles (Al) , Nickel particles (Ni) and mixture of (Al +Ni) particles with grain size (40 m) to Epoxy resin with weight fractions (2%, 4%, 6%, 8%). Experimental results showed that, the values of electrical break down decrease with increasing of the weight fraction of additive particles for all samples in normal condition, the same case for other samples which reinforced with (Ni) particles or (Al+Ni) particles after irradiation the samples by (UV) , as well as the hardness value increases with increasing of the weight fraction of additive particles before and after (UV) irradiation .

يتضمن هذا البحث تحضير مادة متراكبة دقائقية عن طريق إضافة دقائق الالمنيوم (Al) ودقائق النيكل (Ni) او مزيج من دقائق الالمنيوم والنيكل (Al+Ni) بحجم حبيبي (40 m) الى راتنج الايبوكسي وبنسب مئوية وزنية (8%,6%,4%,2%)، وتم دراسة اختبار الانهيار الكهربائي والصلادة. أظهرت النتائج العملية بأن قيم الانهيار الكهربائي تقل مع زيادة النسب المئوية الوزنية للدقائق المضافة لكافة العينات في الحالة الطبيعية، وكذا الحال لبقية العينات المدعمة بدقائق النيكل أو مزيج الألمنيوم مع النيكل بعد التعرض الى الاشعة فوق البنفسجية وكذلك تزداد قيمة الصلادة لكافة العينات بزيادة النسبة المئوية الوزنية للدقائق المضافة في الحالة الطبيعية وبعد التعرض للأشعة فوق البنفسجية .


Article
The Effect of Additive Particulate on same Physical and Electrical Properties of Polymeric Composites
تأثير الإضافات الدقائقية على بعض الخواص الفيزيائية والكهربائية لمتراكب بوليمري

Authors: Ahmed Jubair Jaffal أحمد جبير جفال --- Faik Hammad Anter فائق حماد عنتر
Journal: Journal of university of Anbar for Pure science مجلة جامعة الانبار للعلوم الصرفة ISSN: 19918941 Year: 2017 Volume: 11 Issue: 3 Pages: 98-103
Publisher: University of Anbar جامعة الانبار

Loading...
Loading...
Abstract

This work includes adding Aluminum particles (Al) , Nickel particles (Ni) and mixture of (Al +Ni) particles of grain size (40 m) to Epoxy resin with weight fractions ratio (2%, 4%, 6%, 8%). Tests which were studied dielectric constant and thermal conductivity . Experimental results showed that, the values of dielectric constant increases with increasing the weight fraction ratio of additive particles before and after (UV) irradiation.Thermal conductivity increases slowly with increasing weight fraction ratio of additive particles before and after (UV) irradiation. The maximum value of thermal conductivity was for samples reinforced with for (Al) particle followed by samples reinforced with (Ni) and particle mixture of (Al+Ni) particles.

يتضمن هذا البحث إضافة دقائق الالمنيوم (Al) ودقائق النيكل (Ni) او مزيج من دقائق الالمنيوم والنيكل (Al+Ni) بحجم حبيبي (40 m) الى راتنج الايبوكسي لتحضير مادة متراكبة بنسب مئوية وزنية (8%,6%,4%,2%) . تم دراسة اختبار ثابت العزل الكهربائي والتوصيلية الحرارية، وقد أظهرت النتائج بان قيمة ثابت العزل الكهربائي تزداد بزيادة النسبة المئوية الوزنية ولكافة العينات قبل وبعد التشعيع بالأشعة فوق البنفسجية، التوصيلية الحرارية تزداد بصورة بطيئة مع زيادة النسب المئوية الوزنية للدقائق المضافة قبل وبعد التشعيع بالأشعة فوق البنفسجية واعلى قيمة للتوصيلية الحرارية كانت للعينات المدعمة بدقائق الالمنيوم تليها العينات المدعمة بمزيج من دقائق الالمنيوم والنيكل ثم العينات المدعمة بدقائق النيكل


Article
Layer Exchange Effect of Different Fibers on Modulus of Elasticity and Dielectric Constant For Some Fibrous Composites.
تأثير تبادل الطبقات للألياف المختلفة على معامل المرونة وثابت العزل الكهربائي لبعض المتراكبات الليفية

Authors: Faik Hammad Anter فائق حماد عنتر --- Noor Sadi Saleh نور سعدي صالح
Journal: Journal of university of Anbar for Pure science مجلة جامعة الانبار للعلوم الصرفة ISSN: 19918941 Year: 2017 Volume: 11 Issue: 3 Pages: 104-110
Publisher: University of Anbar جامعة الانبار

Loading...
Loading...
Abstract

The aim of this research is to prepare materials overlays way the molding hand of strengthening the epoxy resin fiber glass type (E-glass) fibers and carbon fiber (chopped carbon) section and fractures volumetric (20%, 30%, 40%) were measured modulus of elasticity and the dielectric constant and explained the practical consequences that the modulus of elasticity decreases with increasing volume fraction as well as the dielectric constant

ان الهدف من هذا البحث هو تحضير مواد متراكبه بطريقه القولبة اليدوية ( Hand – ray up method) من تدعيم راتنج الايبوكسي بألياف الزجاج من نوع (E-glass) والالياف الكاربون المقطع (chopped carbon) و بكسور حجمية (%40,%30,%20) تم قياس معامل المرونة و ثابت العزل الكهربائي وأوضحت النتائج العملية ان معامل المرونة يقل بزيادة الكسر الحجمي وكذلك ثابت العزل الكهربائي .


Article
Effect of number of Kevlar fiber layers on bending property of thermoplast blend
تأثير عدد طبقات ألياف الكفلر على خاصيه الانحناء لخليط متصلد حرارياً

Authors: Faik Hammad Anter فائق حماد عنتر --- Khamees Dhari Mahmoud خميس ضاري محمود
Journal: Journal of university of Anbar for Pure science مجلة جامعة الانبار للعلوم الصرفة ISSN: 19918941 Year: 2017 Volume: 11 Issue: 3 Pages: 111-116
Publisher: University of Anbar جامعة الانبار

Loading...
Loading...
Abstract

This research includes preparation hybrid material by reinforcing the blend (EP80%+UPE20%) with number of Kevlar fiber layers by hand lay-up method and volume fraction 30% . Bending property was studied at room temperature before and after (UV) irradiation Expermental results showed that ,the value of deflection decreases with increasing the number of reinforcing Kevlar fiber layers while modulus of elasticity increases with increasing the number of reinforcing layers before and after UV irradiation .

يتضمن هذا البحث تحضير مادة هجينه من بتدعيم الخليط (EP80%+UPE20%) بعدد من طبقات ألياف الكفلر بطريقة القولبة اليدوية وبكسر حجمي 30% . تمت دراسة خاصية الانحناء عند درجة حرارة الغرفة قبل وبعد التشعيع بالأشعة فوق البنفسجية، أظهرت النتائج العملية بأن قيمة الانحراف تقل مع زيادة عدد طبقات التدعيم بألياف الكفلر بينما معامل المرونة يزداد مع زيادة عدد طبقات التدعيم قبل وبعد التشعيع بالأشعة فوق البنفسجية.


Article
Study the effect of sodium hydroxide solution on the thermal conductivity of nanocomposites
دراسة تأثير محلول هيدروكسيد الصوديوم على التوصيلية الحرارية لمادة متراكبة نانوية

Authors: Ayad Qabash Hameed اياد قباش حميد --- Faik Hammad Anter فائق حماد عنتر
Journal: Iraqi Journal of Physics المجلة العراقية للفيزياء ISSN: 20704003 Year: 2018 Volume: 16 Issue: 39 Pages: 48-54
Publisher: Baghdad University جامعة بغداد

Loading...
Loading...
Abstract

In this research, hand lay- up technique is used to prepare samples from epoxy resin reinforced with multi- walled carbon nanotubes in different weight fractions (0, 2, 3, 4, 5) wt%. The immersion effect by sodium hydroxide solution (NaOH) at normality (0.3N) for a period of (15 days) on the thermal conductivity of nanocomposites was studied, and compared to natural condition (before immersion). The thermal conductivity of epoxy nanocomposites specimens were carried out using Lee’s disk method. The experimental results showed that thermal conductivity increased with increase weight fraction before and after immersion for all specimens, while the immersion effect leads to decrease thermal conductive values compared to thermal conductivity values in natural condition.

في هذا البحث اُستخدمت تقنية القولبة اليدوية (Hand Lay – up) في تحضير عينات من راتنج الإيبوكسي المدعم بأنابيب الكربون النانوية متعددة الجدران (MWCNTs) بنسب وزنية مختلفة (0، 2، 3، 4، 5) wt%. تم دراسة تأثير الغمر في محلول هيدروكسيد الصوديوم (NaOH) ذو عيارية (0.3N) وبدرجة حرارة المختبر لمدة (15 يوم) على التوصيلية الحرارية للمتراكبات النانوية، ومقارنتها بالحالة الطبيعية (قبل الغمر). لقياس التوصيلية الحرارية لنماذج متراكبات الإيبوكسي استخدمت طريقة قرص لي (Lee’s disk). أظهرت نتائج الدراسة ان التوصيلية الحرارية تزداد بزيادة النسب الوزنية للمادة المضافة ولجميع العينات قبل وبعد الغمر في المحلول القاعدي. في حين لوحظ إن الغمر بالمحلول القاعدي يؤدي الى نقصان قيم التوصيلية الحرارية لكافة العينات مقارنة بقيم التوصيلية الحرارية في الحالة الطبيعية.


Article
Effect of the type of reinforcing for Hardness properties for (Thermoset – fibers) composite .
تأثير نوع مادة التقوية على خاصية الصلادة لمتراكب ثرموسيت– ألياف

Loading...
Loading...
Abstract

This research included preparation of two types of fiber composites and the the basis as ato break the stereotypes and manual volumetric rate of 25% . The characterization of the fiber is divided into two types:Overlapping material composed of epoxy resin as a subsidized two layers and four layers , six layers of fiber glass basis of the type (E-Glass) is woven mat.Overlapping material composed of epoxy as supported by two layers and four layers , six layers of caors rock wool fibers basis . In this paper the hardness characteristic study of the above complexes in natural conditions and after immersion normal water for different time periods is (5,10,15) days at room temperature . The results showed the process that the value of surface hardness for both types of specimens in natural conditions increases with the number of layers of reinforcement and that the value of the complexes fiberglass higher than the value of the complex rock wool fibers , after immersion the samples with water usual noticed that the surface hardness decreases with increasing duration of water immersion and with increasing number of reinforcement layers and both types of complexes , but their value in the complexes, fiberglass largest of its value for the characterization of rock wool fibers .

تضمن هذا البحث تحضير نوعين من متراكبات الألياف ولنفس الأساس بطريقة القولبة اليدوية وبكسر حجمي مقداره (%25) . تم تقسيم متراكبات الألياف إلى نوعين :مادة متراكبة مكونة من راتنج الايبوكسي كمادة أساس مدعمة بطبقتين وأربع طبقات وست طبقاتمن الألياف الزجاجية نوع (E–Glass) المحاكة بشكل حصيرة .مادة متراكبة مكونة من الايبوكسي كمادة أساس مدعمة بطبقتين وأربع طبقات وست طبقات من ألياف الصوف الصخري الخشن .في هذا البحث تم دراسة خاصية الصلادة للمتراكبات أعلاه في الظروف الطبيعية وبعد الغمر بالماء الاعتيادي لفترات زمنية مختلفة هي (15, 10, 5) يوما وبدرجة حرارة الغرفة .أظهرت النتائج العملية بأن قيمة الصلادة السطحية لكلا النوعين من العينات في الظروف الطبيعية تزداد بزيادة عدد طبقات التدعيم وان قيمتها لمتراكبات الالياف الزجاجية اعلى من قيمتها لمتراكبات ألياف الصوف الصخري , وبعد غمر العينات بالماء الاعتيادي لاحظنا ان الصلادة السطحية تقل مع زيادة مدة الغمر بالماء ومع زيادة عدد طبقات التدعيم ولكلا النوعين من المتراكبات , ولكن قيمتها في متراكبات الالياف الزجاجية اكبر من قيمتها لمتراكبات ألياف الصوف الصخري .


Article
Wear rate of epoxy resin reinforced with multi walls carbon nanotubes
معدل البلى لراتنج الايبوكسي المدعم بأنابيب الكربون النانوية متعددة الجدران

Authors: Ayad Qabash Hameed اياد قباش حميد --- Faik Hammad Anter فائق حماد عنتر
Journal: Iraqi Journal of Physics المجلة العراقية للفيزياء ISSN: 20704003 Year: 2019 Volume: 17 Issue: 40 Pages: 1-9
Publisher: Baghdad University جامعة بغداد

Loading...
Loading...
Abstract

In this study, nanocomposites have been prepared by adding multiwall carbon nanotubes (MWCNTs) with weight ratios (0, 2, 3, 4, 5) wt% to epoxy resin. The samples were prepared by hand lay-up method. Influence of an applied load before and after immersion in sodium hydroxide (NaOH) of normality (0.3N) for (15 days) at laboratory temperature on wear rate of Ep/MWCNTs nanocomposites was studied. The results showed that wear rate increases with increasing the applied load for the as prepared and immersed samples and after immersion. It was also found that epoxy resin reinforced with MWCNTs has wear rate less than neat epoxy. The sample (Ep + 5wt% of MWCNTs) has lower wear rate. The immersion effect in base solution led to increase in wear rate values for all samples compared to natural condition.

تم في هذا البحث تحضير عينات المتراكبات النانوية باستخدام تقنية القولبة اليدوية بإضافة نسب وزنية %(0، 2، 3، 4، 5) من أنابيب الكربون النانوية متعددة الجدران الى راتنج الإيبوكسي. حيث تمت دراسة تأثير الحمل المسلط قبل وبعد الغمر بمحلول هيدروكسيد الصوديوم ذو عيارية (0.3N) ولمدة (15) يوم على معدل البلى للمواد المتراكبة النانوية ومقارنتها بالحالة الطبيعية (قبل الغمر). بينت نتائج الدراسة ان معدل البلى يزداد مع زيادة الحمل العمودي المسلط ولجميع العينات. كما وُجد ان عينات الإيبوكسي المدعمة بأنابيب الكربون النانوية تمتلك معدل بلى اقل مقارنة بالإيبوكسي النقي. اقل قيمة لمعدل البلى سُجلت بالنسبة ل( Ep + 5wt% من MWCNTs). أدى تأثير الغمر بالمحلول القاعدي الى زيادة معدل البلى بالنسبة لجميع العينات مقارنة بالحالة الطبيعة.


Article
Study of effect acidic solution (HCl) and (EP/Al2O3 & EP/ TiO2) hybrid on thermal conductivity of epoxy resin.
دراسة تاثير المحلول الحامضي (HCl) والهجين (EP/Al2O3 & EP/ TiO2) على التوصيلية الحرارية لراتنج الايبوكسي

Loading...
Loading...
Abstract

This research studies the effect of adding micro, nano and hybrid by ratio (1:1) of (Al2O3,TiO2) to epoxy resin on thermal conductivity before and after immersion in HCl acid for (14 day) with normality (0.3 N) at weight fraction (0.02, 0.04, 0.06, 0.08) and thickness (6mm). The results of thermal conductivity reveled that epoxy reinforced by (Al2O3) and mixture (TiO2+Al2O3) increases with increasing the weight fraction, but the thermal conductivity (k) a values for micro and Nano (TiO2) decrease with increasing the weight fraction of reinforced, while the immersion in acidic solution (HCl) that the (k) values after immersion more than the value in before immersion.

تم في هذا البحث دراسة تأثير إضافة الدقائق المايكروية والنانوية والهجين بنسبة (1:1) من (Al2O3، TiO2) على راتنج الايبوكسي في اختبارات التوصيل الحراري قبل وبعد الغمر في المحلول الحامضي (HCl ) لمدة (14 يوم) بتركيز (N 0.3) وبكسر وزني (0.02، 0.04، 0.06، 0.08) وسمك (6 mm). أظهرت نتائج اختبار التوصيل الحراري في الحالة الطبيعية أن الايبوكسي المقوى بدقائق المايكروية والنانوية (Al2O3) و الهجين (TiO2 + Al2O3) يزداد مع زيادة النسبة الوزنية، ولكن قيم التوصيل الحراريk) ) لدقائق المايكروية والنانوية (TiO2) تتناقص مع زيادة النسبة الوزنية في حين تكون قيم (k) في حالة الغمر في المحلول الحامضي (HCl) اكبر من القيمة قبل الغمر.

Listing 1 - 9 of 9
Sort by
Narrow your search

Resource type

article (9)


Language

Arabic (6)

English (3)


Year
From To Submit

2019 (1)

2018 (2)

2017 (6)