Electrical and dielectric properties of kevlar - carbon hybrid fiber / epoxy laminated composites
الخصائص االعزلية والكهربائية لمتراكبات الطبقية الايبوكسي - الياف هجينية الكفلر والكاربون

Authors: Ekram A. Al-ajaj اكرام عطا العجاج --- Farah T. Mohammed Noori فرح طارق محمد نوري --- Harith I. Jafer حارث ابراهيم جعفر
Journal: Baghdad Science Journal مجلة بغداد للعلوم ISSN: 20788665 24117986 Year: 2011 Volume: 8 Issue: 1 Pages: 148-154
Publisher: Baghdad University جامعة بغداد

Loading...
Loading...
Abstract

This paper reports a.c., d.c. conductivity and dielectric behavior of Ep-hybrid composite with12 Vol.% Kevlar-Carbon hybrid . D.C. conductivity measurements are conducted on the graded composites by using an electrometer over the temperature range from (293-413) K. It was shown then that conductivity increases by increasing number of Kevlar –Carbon fiber layers (Ep1, Ep2, Ep3), due to the high electrical conductivity of Carbon fiber. To identify the mechanism governing the conduction, the activation energies at low temperature region (LTR) and at high temperature region (HTR) have been calculated. The activation energy values for hybrid composite decrease with increasing number of fiber layers. The a.c. conductivity was measured over frequency range 100 Hz-1MHz. It was found that σ(ω) values increase with increasing frequency according to the relation σ (ω)=Aws . The values of frequency exponent (s) were found to increase with number of layers.

تم في هذا البحث دراسة التوصيلية المتناوبة والمستمرة وسلوك العزل للمتراكب الهجيني المكون من الايبوكسي المقوى بالالياف الهجينية الكفلر والكاربون، بكسر حجمي 0.12قد وجد ان التوصيلية المستمرة لمدى درجات الحرارة ( 293-413 ) K تزداد بزيادة عدد الطبقات من الالياف الهجينيه الكفلر والكاربون: (Ep1, Ep2, Ep3) بسبب وجود ألياف الكاربون التي تمتلك معامل توصيل كهربائي عال، ولتفسير ميكانيكية التوصيل تم حساب طاقة التنشيط عند منطقة درجات الحرارة الواطئة والعالية وجد ان قيم طاقة التنشيط تتناقص بزيادة عدد الطبقات. تم قياس التوصيلية المتناوبة ضمن مدى تردد من 100Hz-1MHz.وجد انها تزداد مع زيادة التردد على وفق العلاقة σ(ω)=Aws .وجد ان قيم المتغير الاسي(s) يزداد مع زيادة عدد الطبقات.


Article
A.C Conductivity and Dielectric Properties of Epoxy - TiO2 Nanocomposites
الخصائص العزلية والتوصيلية المتناوبة لمتراكبات الايبوكسي- TiO2 النانوية

Loading...
Loading...
Abstract

In this paper, A.C conductivity of micro and nano grain size- TiO2 filled epoxy composites is measured. The dielectric material used is epoxy resin, while micro and nano-sized titanium dioxide (TiO2) of grain size (1.5μm, and 50nm) was used as filler at low filler concentrations by weight (3%, and 5%). Additionally the effect of annealing temperature range (293-373)º K and at a frequency range of 102-106 Hz on the A.C conductivity of the various specimens was studied. The result of real permittivity for micro and nanocomposite show that the real permittivity increases with decreasing frequency at range of 102-106Hz. The micron-filled material has a higher real relative permittivity than the nano-filled this is true at all the temperatures measured.The variation of the A.C conductivity with frequency for micro and nanocomposites shows that A.C conductivity for all samples increase with increasing frequency and the temperature dependence on the A.C conductivity increases as the frequency decrease.

في هذا البحث تم قياس التوصيلية المتناوبة لمتراكبات الايبوكسي مع ثاني اوكسيد التيتانيوم ذو الحجم الحبيبي مايكروونانو. المادة العزلية المستخدمة هي راتنج الايبوكسي بينما ثاني اوكسيد التيتانيوم ذو الحجم الحبيبي (1.5μm, and 50nm) تم استخدامه بتراكيز قليلةand 3%) (5% . إضافة لذلك تم دراسة تأثير الحرارة لمدى293-373)º K (ولمدى من الترددات (102-106 Hz ( على التوصيلية المتناوبة لمختلف العينات .تظهرنتائج ثابت العزل الحقيقي للمتراكبات المايكروية ولمتراكبات النانوية الزيادة مع نقصان التردد. كما ان العزلية لمتراكبات الميكرو اعلى مما لمتراكبات النانو وهذا واضح عند كل درجات الحرارة.يوضح تغير التوصيلية المتناوبة مع التردد لمتراكبات الميكروية والنانوية ان التوصيلية المتناوبة تزداد مع زيادة التردد وان التوصيلية المعتمدة على درجات الحرارة تزداد مع نقصان التردد.