Study of A.C Electrical Properties of Aluminum–Epoxy Composites

Authors: A.Shawky --- N.A.Ali --- H.I.Jafar
Journal: Al-Nahrain Journal of Science مجلة النهرين للعلوم ISSN: (print)26635453,(online)26635461 Year: 2011 Volume: 14 Issue: 3 Pages: 77-82
Publisher: Al-Nahrain University جامعة النهرين

Loading...
Loading...
Abstract

Abstract
This work studies the electrical properties for pure epoxy (EP), and epoxy with (20%,30%,40%
and 50%)aluminum powder composites. The electrical conductivity [σ(w)a.c] for these materials
have been measured over the frequency range (102 -106)Hz at room temperature. It is found the A.C
conductivity increased when increased the concentration of aluminum.
It is found for all samples, the curves for real part of dielectric constant (ε) and dissipation factor
(tanδ). The dielectric constant increased smoothly with an increase in the concentration of
aluminum it was attributed to interfacial polarization and decrease with increased frequency. In
general, dissipation factor values for composites with higher concentrations of aluminum were
greater than those with lower volume content of aluminum. Also, the dissipation factor showed an
increase with a decrease in frequency. It was found that a.c electrical conductivity increases with
increasing frequency according to the relation s(w)=Aws has been observed , with values of
exponent (s) less than unity for all samples and decrease with the increase of frequency and lie
between (0.3 to 0.6) unit . Also, it was found that the correlated barrier hopping (CBH) is the
dominant conduction mechanism.

الخلاصة
يتناول هذا البحث دراسة خصائص العزل للايبوكسي
النقي والمتراكب المتكون من الإيبوكسي/ الالمنيوم .تم
للمتراكبات بنسبة [σ(w)a.c] قياس التوصيلية الكهربائية
٤٠ ٪، و ٥٠ ٪ وبمدى تردد بين ،٪ ٣٠ ،٪ ٢٠
١٠٦ ) هرتز في درجة حرارة الغرفة ووجد بان - ١٠٢)
التوصيلة تزداد بزيادة التركيز.
وعامل (ε ) لقد وجد لكل العينات ثابت العزل الحقيقي
يزداد بشكل (ε ) حيث ان ثابت العزل الحقيقي (tanδ) الفقد
H.I.Jafar
٨٢
قليل مع زيادة تركيز الالمنيوم المضاف والسبب يعود الى
بينية الاستقطاب ويقل مع زيادة التردد. بصورة عامة فان
للمتراكبات المحتوية على نسبة عالية (tanδ) قيم عامل الفقد
من الالمنيوم تكون اعلى من تللك التي تحتوي على نسبة
قليلة من الالمنيوم وقد لوحظ بان عامل الفقد يزداد مع
تناقص التردد. وجد بان التوصيلية المتناوبة تزداد مع زيادة
(s) وبقيم للعامل الاسي s(w)=Aws التردد وفق العلاقة
اقل من الواحد لكل العينات وتتناقص مع زيادة التردد وتقع
٠,٣ ) وحدة، وجد بان الية التوصيل السائدة هي - بين ( ٠,٦
.(CBH) نموذج القفز فوق حاجز التنطط

يتناول هذا البحث دراسة خصائص العزل للايبوكسي النقي والمتراكب المتكون من الإيبوكسي/ الالمنيوم .تم قياس التوصيلية الكهربائية[σ(w)a.c] للمتراكبات بنسبة 20 ٪، 30 ٪، 40 ٪، و 50 ٪ وبمدى تردد بين(102 -106) هرتز في درجة حرارة الغرفة ووجد بان التوصيلة تزداد بزيادة التركيز.لقد وجد لكل العينات ثابت العزل الحقيقي( (ε وعامل الفقد (tanδ) حيث ان ثابت العزل الحقيقي( (ε يزداد بشكل قليل مع زيادة تركيز الالمنيوم المضاف والسبب يعود الى بينية الاستقطاب ويقل مع زيادة التردد. بصورة عامة فان قيم عامل الفقد(tanδ) للمتراكبات المحتوية على نسبة عالية من الالمنيوم تكون اعلى من تللك التي تحتوي على نسبة قليلة من الالمنيوم وقد لوحظ بان عامل الفقد يزداد مع تناقص التردد. وجد بان التوصيلية المتناوبة تزداد مع زيادة التردد وفق العلاقة ()=Aws وبقيم للعامل الاسي (s) اقل من الواحد لكل العينات وتتناقص مع زيادة التردد وتقع بين (0.6-0.3) وحدة، وجد بان الية التوصيل السائدة هي نموذج القفز فوق حاجز التنطط (CBH).


Article
Study Torsion Capacity of Epoxy -Glass Fiber Composites

Authors: N. A. Abas --- H. I. Jafar --- F.T. Mohammed Noori
Journal: Al-Nahrain Journal of Science مجلة النهرين للعلوم ISSN: (print)26635453,(online)26635461 Year: 2011 Volume: 14 Issue: 1 Pages: 109-114
Publisher: Al-Nahrain University جامعة النهرين

Loading...
Loading...
Abstract

In this study, torsion test was performed in order to examine the mechanical behaviors of epoxy
and an epoxy reinforced by two types of glass fibers (chopped and yarn) composite rod. The stressstrain
curves were constituted and examined in order to show the elastic and plastic regions, the
yield point was 23.226o and 34.837o angle of twist for epoxy and epoxy /fibers respectively which
is the same for both chopped and yarn glass fibers epoxy, from this test it was found that the epoxy
rod initially yielded first, the cracks propagation in composite rod along the fibers direction, which
caused eventually the delimitation of composite chopped and yarn glass fibers from the epoxy
matrix. Then the white regions appear in composite rod and finally the fiber breakage and the
catastrophic failure took place.

تم في هذه الدراسة انجاز فحص عزم الالتواء لفحص السلوك الميكانيكي للايبوكسي ومتراكباته المدعمة بنوعين من الياف الزجاج (مقطع وخيوط), وتبين من انجاز منحيات الاجهاد- الانفعال كل من المناطق اللدنة والمرنة وكانت نقطة الخضوع23.2260و34.8370 للكل من الايبوكسي ومتراكباته على التوالي حيث انها متشابهة لايبوكسي-الياف زجاج مقطع وخيوط, ومن هذا الاختبار وجد ان قضيب الايبوكسي يخضع اولا وان الشقوق تاخذ بالانتشار على طول وباتجاه االالياف في القضيب المتراكب مما يتسبب انفصال الياف الزجاج المقطع والخيوط من الايبوكسي وبالتالي تظهر مناطق بيضاء في قضيب المتراكب ثم ينكسر الليف وبذلك يحل الفشل.


Article
Effect of Water Absorption on Some Electrical and Dielectrical Properties of Epoxy Resin Reinforced with Chopped Carbon Fibers

Authors: E.A.Al-Ajaj --- S.I.Husaen --- H.I.Jafar
Journal: Al-Nahrain Journal of Science مجلة النهرين للعلوم ISSN: (print)26635453,(online)26635461 Year: 2011 Volume: 14 Issue: 4 Pages: 87-94
Publisher: Al-Nahrain University جامعة النهرين

Loading...
Loading...
Abstract

In this research, we study a.c electrical conductivity (σa.c ( ) and dielectric properties (dielectric constant (έ), and dissipation factor ( tanδ) ), with frequency change (102 -107 Hz) for the epoxy resin and composites reinforced with chopped carbon fiber ,prepared by hand lay –up method (EP +5% CF), (EP +10% CF), (EP +15% CF), (EP +20% CF), Were measured electrical conductivity of epoxy and composites with frequency change and at room temperature the results showed a.c electrical conductivity dependence with frequency relationship σ (ω)=Aωs to the values of the exponential factor (s)of less than one all samples, and adopted the theory of filtration for the interpretation of data conductivity for composites reinforced with carbon fibers was selected epoxy+20% C.F showed a higher electrical conductivity (13.6 * 10-7 (ohm.cm)-1). The composites were immersed in water at room temperature for 6, 10,15,20,27 days.The results showed that the electrical conductivity of (σ (ω)) increasing with increasing weight gain(M%) due to water absorption. Itwas found that dielectric constant increases when the percentage moisture absorption increase, whereas dielectric constant (έ) is dependent on capacity of composite materials.

تـم في هـذا البحث دراسـة التوصيليـة الكهربائيـة المتناوبـة ()(σa.c وخـواص العـزل الكهربائـي (έ,tan (مـع تغيـر التردد (102 -107 Hz) لراتنـج الايبوكسي ومتراكباته المدعمة بالياف الكاربون المقطعة والمحضرة بطريقة التشكيل اليدوية(EP+5%C.F)، (EP+10%C.F)، (EP+15%C.F)، (EP+20%C.F) تم قياس التوصيلية المتناوبة للايبوكسي ومتراكباته في مدى التردد وفي درجة حرارة المختبر اظهرت النتائج اعتماد التوصيلية على التردد وفق العلاقة σ(ω)=Aωs بقيم للعامل الاسي اقل من الواحدلكل العينات, واعتمدت نظرية الترشيح لتفسير بيانات التوصيلية لمتراكبات الايبوكسي المدعم بالالياف الكاربون. كما تم دراسة تأثير التردد في قيمة ثابت العزل الكهربائي وفقد العزل فقد وجد بان السماحية ( ( έتقل في حالة التقوية بالياف الكاربون المقطعة، تم اختيار المتراكب ايبوكسي -20% الياف الكاربون المقطعة الافضل من بين المتراكبات باعتبـاره اظهـر اعلـى توصيليـة كهربائيـة( (ohm.cm )-1 13.6*10-7 ). تم تغطيس المتراكبات في الماء بدرجة حرارة الغرفة لمدة 20,1510,6, 7, 2 يوم، اظهـرت النتائـج العمليـة ان التوصيليـة الكهربائيـة((ω)σ) تزداد بزيادة التردد وزيادة النسبة المئوية لامتصاصية الماء بينما ثابت العزل (έ) يزداد عند زيادة النسبة المئوية لامتصاصية الماء اعتمادا على السعة الكهربائية للمواد المتراكبة.

Listing 1 - 3 of 3
Sort by
Narrow your search

Resource type

article (3)


Language

English (3)


Year
From To Submit

2011 (3)