Annealing Effect on the Optical Properties of (CdO)1-x (Mg)x Thin Films
تأثير المعاملة الحرارية على الخصائص البصرية لأغشية (CdO)1-x (Mg)x الرقيقة

Author: Hadi Ahmed Hussin
Journal: journal of the college of basic education مجلة كلية التربية الاساسية ISSN: 18157467(print) 27068536(online) Year: 2014 Volume: 20 Issue: 84 / علمي Pages: 939-946
Publisher: Al-Mustansyriah University الجامعة المستنصرية

Loading...
Loading...
Abstract

(CdO)1-x (Mg)x thin films with (x = 0.06) deposited on perheated glass substrates at temperature 350°C by chemical spray pyrolysis technique. We have studied the effect of annealing temperature at (400, 450) °C. Optical absorption studies in the wavelength range 300–900 nm in order to calculate the optical constants such as refractive index, extinction coefficient, real and imaginary parts of dielectric constant. Results illustrate that the refractive index decreased at 600 nm while the extinction coefficient slightly increases after annealing, on the other hand, the values of real and imaginary parts of the dielectric are found to be decreases with increasing annealing. The skin depth is found to be decreases as the annealing temperature increased to 450 °C, so the skin depth is a transmittance related.

حضرت أغشية (CdO)1-x (Mg)x الرقيقة وبنسبة (x = 0.06) المرسبة على قواعد زجاجية مسخنة لدرجة حرارة 350 مئوية بطريقة التحلل الكيمياوي الحراري. درس تأثير التلدين وبدرجة حرارة 400 و450 درجه مئوية. تم دراسة طيف الامتصاصية في مدى الأطوال الموجية (900-300) نانومتر وذلك لغرض حساب الثوابت البصرية مثل معامل الانكسار، معامل الخمود، ثابت العزل بجزئية الحقيقي والخيالي. أوضحت النتائج بأن معامل الانكسار يقل عند الاطوال الموجية 600 نانومتر ومعامل الخمود يزداد بعد التلدين, بينما ثابت العزل بجزئية الحقيقي والخيالي وكذلك عمق القشرة جميعها تقل بزيادة درجة حرارة التلدين الى 400 درجه مئوية.


Article
Effect of Kaolin Clay Concentration and Irradiation on the Electronic Transitions of Polyvinyl Alcohol Films
تأثير تركيز الكؤلين والتشعيع على الأنتقالات الألكترونية لأغشية بولي فنايل الكحول

Author: Hadi Ahmed Hussin هادي أحمد حسين
Journal: Diyala Journal For Pure Science مجلة ديالى للعلوم الصرفة ISSN: 83732222 25189255 Year: 2014 Volume: 10 Issue: 4 Pages: 14-24
Publisher: Diyala University جامعة ديالى

Loading...
Loading...
Abstract

Pure and (1 and 3 wt%) kaolin doped PVA films were synthesized by solution casting method, and exposed to 60Co--rays, activity 2µCi for two weeks, The optical characterizations of the films were carried out using UV-Vis transmittance spectrophtometer in the wavelength range 300–900 nm. The results show that in the visible region the transmittance of the films increases as the kaolin concentration increase clearly as comared with the same film before irradiation. The dominant transmittance band of UV region increases after irradiation while the reverse is the case with the reflectance. Also results indicates that PVA films have an indirect band gap that decreased from 3.7 to 3.55 eV as the doping concentration increases to 3wt%. Also the energy band gap of the irradiated films appeared to be decreased from 3.9 eV down to 3.4 eV.

حضرت أغشية البولي فينايل الكحول غير المشوبة والمشوبة (1%, 3%) كاولين بطريقة الصب , وعرضت لأشعة كاما الناتجة من الكوبلت – 60 بنشاطة 2µCi لمدة اسبوعين, تم دراسة الخصائص البصرية باستخدام مطياف الأشعة فوق البنفسجية المرئية لمدى الاطوال الموجية 300 – 900 نانومتر. أثبتت النتائج ان النفاذية في المنطقة المرئية تقل بزيادة تركيز الكاولين عند مقارنتها مع الأغشيىة غير المشوبة. تزداد حزمة النفاذية المهيمنة في منطقة فوق البنفسجية بعد التشعيع بينما يحدث العكس في حالة الانعكاسية. كذلك فان النتائج تشير الى ان أغشية (PVA) ذات انتقال غير مباشر ويقل من 3.7 الى 3.55 eV بازدياد نسبة 3% . ان فجوة الطاقة المباشرة للأغشية المشععة تشير الى تناقص الفجوة من 3.9 الى3.4 eV .