Article
Effect of Transformation Temperature on Microstructure andMechanical Properties of Bainite
دراسة تأثير درجة حرارة التحول على البنية المجهرية

Author: Hala Salman Hasan
Journal: Engineering and Technology Journal مجلة الهندسة والتكنولوجيا ISSN: 16816900 24120758 Year: 2012 Volume: 30 Issue: 13 Pages: 2165-2174
Publisher: University of Technology الجامعة التكنولوجية

Loading...
Loading...
Abstract

Fully bainitic microstructure can be obtained by isothermal transformation attemperatures within the range of bainite transformation. Both transformation temperatureand time determine the phase fraction, the scale of the resultant microstructure and thecarbone content of the retained austenite, which in turn determine the mechanicalproperties.In this study, the thermomechanical simulator was used to obtained the fully bainiticmicrostructure for the high carbon alloy steel (0.78%C) at a different bainitetransformation temperatures (200 to 350°C) in order to study the effect of the isothermaltransformation temperature on the resultant mechanical properties.It has been concluded from the detailed analysis of the microstructure, the dilatometricdata and the mechanical properties (hardness and tensile properties) that finer bainite andless retained austenite phase fraction can be obtained by transformation at lowertemperatures, and that leads to exceptional mechanical properties (Hardness ≈ 660 HV,and Tensile strength ≈ 2 Gpa).

يمكن الحصول على بنية مجهرية من البينايت عن طريق التحولات الايزوثيرمية ضمن مدى درجاتحرارة التحولات الطورية الباينايتية، ان درجة حرارة وزمن التحول الطوري يحددان الكسر الحجميودرجة نعومة البنية الناتجة وكذلك المحتوى الكاربوني للاوستنايت المتبقي والذي بدوره يحدد الخواصالميكانيكية الناتجة.تم في هذا البحث استخدام جهاز محاكي للتحولات الحرارية الميكانيكة للوصول الى البنية الباينايتية0.78% ) بدرجات حرارة تحول ايزوثيرمي مختلفة تتراوح من 200 C) للصلب العالي الكربونالى 350 م° وذلك لدراسة تأثير درجة حرارة التحول على الخواص الميكانيكية الناتجة. لقد تم التوصل من خلال التحليل الدقيق للبنية المجهرية الناتجة وبيانات التغيير في الابعاد وكذلك نتائجفحوصات الصلادة ومقاومة الشد الى امكانية الحصول على بينايت ناعم جدا مع انخفاض درجات حرارة2 مقاومة Gpa ≈ التحول الايزوثيرمي مما يقود الى خواص ميكانيكية عالية ( 660 صلادة فيكرز وشد).


Article
Effect of Alumina (Al2O3) Particles on The Mechanical Properties of Magnesium (Mg)
تأثير جزيئات الألومينا (Al2O3) على الخواص الميكانيكية للمغنيسيوم (Mg)

Authors: Hayder Muneam Abed Zaid حيدر منعم عبد زيد --- Abdul Rahman N. Abed عبد الرحمن نجم عبد --- Hala Salman Hasan هالة سلمان حسن
Journal: AL-NAHRAIN JOURNAL FOR ENGINEERING SCIENCES مجلة النهرين للعلوم الهندسية ISSN: 25219154 / eISSN 25219162 Year: 2019 Volume: 22 Issue: 2 Pages: 124-130
Publisher: Al-Nahrain University جامعة النهرين

Loading...
Loading...
Abstract

In the present study, magnesium-based composites reinforced with different volume fractions (3, 5, 10, and 15) vol.% of micro sized Al2O3 particulates were fabricated by powder metallurgy technique which involves mixed, compacted and sintered. Powders were mixed by ball milling (without balls) for 6 hours at rotation speed 60 rpm. Then powder was compacted at 550 MPa and sintered at 530˚C for 2 hours. Microstructures of sintered composites have been investigated by scanning electron microscopy (SEM), energy dispersive X-ray spectroscopy (EDX) and X-ray diffraction (XRD) energy dispersive. SEM image of sinter samples exhibit good bonding between the magnesium matrix and the alumina. The microhardness and wear resistance of micro composites has been improved significantly compared to that of pure magnesium. Highest value of microhardness is 97 HV at the volume fraction of 10 vol.% Al2O3.

في هذه الدراسة ، تم تصنيع مركبات أساسها المغنيسيوم معززة بكسور حجمية مختلفة (3، 5، 10، 15 %) كنسبة حجمية. من جسيمات الألومينا المايكروية الحجم والتي تم تصنيعها بواسطة ميتالورجيا المساحيق والتي تتضمن الخلط ، الضغط والتلبيد. تم خلط المساحيق عن طريق خلاط الأسطوانة (بدون كرات) لمدة 6 ساعات بسرعة دوران 60 دورة في الدقيقة. تم ضغط العينات عند 550 MPa وتم تلبيدها عند 530 م˚ لمدة 2 ساعة. تم فحص المجهرية عن طريق مسح المجهري الإلكتروني (SEM) ، تحليل العناصر المركبة للمركب باستخدام التحليل الطيفي للأشعة السينية المشتتة (EDS) و أجري تحليل حيود الأشعة .(XRD) تشير النتائج التجريبية لنتائج صورة SEM لمركبات العينات الملبدة إلى وجود ارتباط جيد بين ارضية المغنيسيوم والألومينا. تم تحسين صلادة و مقاومة البلى للمركبات بشكل ملحوظ عند مقارنةً بالمغنيسيوم النقي. أفضل القيم لتحسين 97 HV في الكسر الحجمي 10٪من.Al2O3 أظهر اختبار الضغط أن مقدار للمقاومة الانضغاطية القصوى (UCS) أفضل قيم للتحسين بنسبة حجمية 5% من Al2O3 هي حوالي 179MPa .