Synthesis of Fibrous Hydroxyapatite through Sol-Gel Route
تصنيع مادة الهيدروكسي ابتايت الشعيرية باستخدام طريقة السائل الهلامي

Loading...
Loading...
Abstract

The sol-gel route using an agar gel with calcium nitrate and phosphate solution as starting materials for producing hydroxyapatite (HAP). The product formed were needle like, zigzag and straight fibres. The fibrous products on sintering transformed into stoichiometric HAP with a biological Ca/P ratio of 1.67. The influences of pH, temperature, nature of base and phosphate solution on the growth of fibrous HAP were studied. The pH of the solution was found to greatly influence the growth rate and morphology of the resultant product. The optimum gel temperature was found to be 60oC and sintering temperature of 900oC for 1 hour. The crystalline, thermal, functional and morphological characteristics of the fibrous HAP were investigated.

أن العمل المعروض في هذا البحث يتضمن طريقة جديدة لتصنيع مادة الهيدروكسي ابتايت (هاب) الشعيرية ذات الاستخدام البايولوجي. محلول نترات الكالسيوم ]المخلوط بنسبة محسوبة لمادة (agar) الهلامية[ وفوسفات الامونيوم تمثلان المواد الرئيسية في التحضير، والتي ينتج عنها مادة (هاب) وبالاشكال (الابري، المتعرج والمستقيم) مع الاخذ بنظر الاعتبار المحافظة على البنية الاساسية لمادة الهاب وبالنسبة المعتمدة بايولوجيا (1.67). لاجل الحصول على تلك المادة وبالمواصفات البايولوجية الدقيقة، يجب السيطرة على المتغيرات الحاكمة وبمنتهى الدقة (الدالة الحامضية، درجة حرارة التفاعل، طبيعة المادة القاعدية وتركيز محلول الفوسفات). الفحوصات الطورية والحرارية والصور المجهرية بينت بان المادة المحضرة مطابقة للمواصفات القياسية.

Listing 1 - 1 of 1
Sort by
Narrow your search

Resource type

article (1)


Language

English (1)


Year
From To Submit

2009 (1)