Effect of Nano SiO2 Particles on some Physical Properties of (UP/PU) Blend Composite
تأثير دقائق السيليكا النانوية على بعض الخصائص الفيزيائية لخليط متراكب (بولي يورثان /بولي أستر)

Author: Hanaa Sh. Mahmood
Journal: Engineering and Technology Journal مجلة الهندسة والتكنولوجيا ISSN: 16816900 24120758 Year: 2016 Volume: 34 Issue: 1 Part (B) Scientific Pages: 93-99
Publisher: University of Technology الجامعة التكنولوجية

Loading...
Loading...
Abstract

The effect of SiO2 physical properties (Shore D hardness, impact strength, 3 pts bending, thermal conductivity, and weight gain) after and before immersion in different liquid solution (water, HCL 0.2 N , and NaOH 0.2 N), of (UP/PU) blend was studied. Hand lay-up technique was applied using unsaturated polyester and polyurethane blend as a matrix and silicon oxide nano particles (Nano SiO2) as a filler with volume fraction (3% Vf ) .Results showed that liquids affected bending properties and thermal conductivity (k) by decreasing values, while the impact strength, and weight gain also studied for 4 weeks and it increase with increasing of immersion time in liquids.

تم دراسه تاثير دقائق السيليكا النانويه على بعض الخصائصالفيزيائيه ( صلاده شور , مقاومه الصدمه ، الانحناء، التوصيليه الحراريه والربح في الوزن ) فبل وبعد الغمر في سوائل ( الماء ، حامض الهيدروكلوريك بتركيز 0,2 مولاري ، هيدروكسيد الصوديوم , 0،2 مولاري) لمده (4) اسابيع على خليط من البولي يورثان والبولي استر الغير مشبعين ، استخدمت تقنيه القولبه اليدويه في تصنيع عينات الخليط المتراكب (بولي يورثان/ بولي استر ) كماده اساس ودقائق السيليكا كماده تقويه.اظهرت النتائج ان دقائق السيليكا تؤثر على جميع الخواص حيث تقل مقاومه الثني والتوصيليه الحراريه. ويزداد كل من الربح في الوزن والصلاده ومقاومه الصدمه بعد الغمر في السوائل المختلفه.


Article
Effect of gamma irradiation and ZnOnano particles on the A.C electrical conductivity of polyaniline
تأثير التشعيع بأشعة كاما وجسيمات اوكسيد الزنك النانوية على التوصلية الكهربائية المتناوبة لبولي انلين

Author: Hanaa Sh. Mahmood هناء شكر محمود
Journal: Iraqi Journal of Physics المجلة العراقية للفيزياء ISSN: 20704003 Year: 2017 Volume: 15 Issue: 32 Pages: 130-135
Publisher: Baghdad University جامعة بغداد

Loading...
Loading...
Abstract

Conducting polyaniline / ZnOnano composites are synthesized using a simplified cheap method with one step in –situ chemical polymerization, and AC conductivity (σac)of the prepared samples is studied in the range of frequency from 50 Hz to 15MHz.). The presence of polarons in the conjugated polymer chain are responsible for the ac conductivity is reliance on the frequency in these composites. The effect of increasing the ZnO nano particle concentration irradiation and gamma radiation on the electric conductivity was analyzed. The result showed that the nanocomposite prepared has the highest conductivity, from pure polyaniline and the exponential factor S was found increasing with ZnO content it was 0.739 for PANI pure and for 0.02 ZnO it was 1.415.

تم تحضير المتراكب النانوي اوكسيد الزنك / بوليمر موصل باستخدام طريقة بسيطة وغير مكلفة وبخطوة واحدة بالبلمرة الكيميائية للنظام, تم دراسة التوصلية المتناوبة σac للمتراكبات ضمن مدى الترددات(50 Hz-15MHz.) . ان وجود البولارون في سلسلة البوليمر المترافق هو المسؤول لاعتماد التوصلية المتناوبة على التردد. تم تحليل نتائج زيادة تركيز جسيمات اوكسيد الزنك النانوية والتشعيع كاما على التوصلية الكهربائية المتناوبة.أظهرت النتائج إن المتراكب النانوي المحضر يمتلك توصلية أعلى من البولي انلين النقي,والعامل الآسي s يزداد بزيادة محتوى، اوكسيد الزنك فقد كانت قيمته 0.739 للبولي انلين النقي والمتراكب ذو نسبة 0.02 اوكسيد الزنك أصبحت 1.415.


Article
Physical behavior of polypropylene/low density polyethylene blends

Authors: Balkees M. Aldabbagh --- Hanaa Sh. Mahmood
Journal: Journal of College of Education مجلة كلية التربية ISSN: 18120380 Year: 2015 Issue: 3 Pages: 289-300
Publisher: Al-Mustansyriah University الجامعة المستنصرية

Loading...
Loading...
Abstract

Blends of polypropylene (PP) and low-density polyethylene (LDPE) may contribute to make recycling more economically attractive. The aim of this work was to make LDPE /PP blends (0/100, 10/90, 25/75, 50/50 w/w) via injection molding carried out under 170 o C injection temperatures and to evaluate their physical properties including :(Shore D hardness, Density, Tensile strength , elongate to break , Fracture toughness ,impact strength, weight gain and thermal conductivity properties . The blend behavior dependent on its composition, especially regarding elongation at break and the presence of necking . The optimum sample was (10:90 w/w) (PP/LDPE).This sample has the optimum elongation to break, optimum fracture toughness, optimum thermal conductivity, and other properties.Increasing of PP contents over the optimum value leads to decreasing of the properties of blend.Weight gain of these samples increasing with increasing of the Immersion time in oil and benzene liquid but the sample not affected when exposed water.

تم تحضير خليط من البولي اثلين الواطئ الكثافة والبولي بروبلين لعمل خليط بوليميري اقل كلفةمن الناحية الاقتصادية. الهدف من البحث هو عمل خليط بوليميري من البولي اثيلين بطريقة القولبةبدرجه حراره (0/100, 10/90, 25/75, 50/50 w/w) والبولي بروبلين الواطي الكثافة بنسب170 درجه مئويه بطريقة القولبة بالبثق لغرض دراسة الخواص الفيزيائية المتضمنة) الاستطالة صلاده شور ، الكثافة ، مقاومة الشد ، الزياده بالوزن والتوصيلية الحرارية ( ، افضل عينة كانتبنسبه ) 10 : 90 ( ) بولي بروبلين : بولي اثيلين ( واطئي الكثافة : اظهرت النتائج ان العينة التيتحتوي 10 % بولي بروبلين تظهر زيادة في جميع الخواص وبزياة نسبه البولي بروبلين يؤدي الىتدني الخواص الفيزيائية للخليط .الزيادة في وزن العينات اظهرت زيادة في مع زيادة زمن الغمرفي النفط والبنزين فيما اظهرت النتائج ان الماء لايؤثر على الخليط البوليميري .


Article
Effect of NaOH on some physical properties of Novalac /TiO2 composite
تأثير دقائق السليكا النانوية على بعض الخصائص الفيزيائية لخلط المتراكب بولي يورثان/بولي استر

Authors: Hanaa Sh. Mahmood هناء شكر محمود --- Balkees M. Al-Dabbagh بلقيس محمد ضياء
Journal: Iraqi Journal of Physics المجلة العراقية للفيزياء ISSN: 20704003 Year: 2015 Volume: 13 Issue: 27 Pages: 91-96
Publisher: Baghdad University جامعة بغداد

Loading...
Loading...
Abstract

Aim of present work is to evaluate the tensile strength, impact strength, and hardness of (Novalac/TiO2) composite with (Vf = 12% optimum value of volume fraction for calculating properties) of prepared by open molding (hand lay-up) technique. Thermal conductivity (k), and weight gain % after immersed in NaOH solution 0.5 M for 60 days were calculated. Results showed a decreasing in mechanical properties with different ratios, Diffusion coefficient (D) calculated (D=2.3 *10-12 m2/sec).

تم في هذا البحث دراسة خصائص متانة الشد، الصدمة، والصلادة لمتراكب (النوفالاك / اوكسيد التيتانيوم TiO2) بكسر حجمي (12 %)والذي يمثل أفضل قيمه للخواص المدروسة في هذا البحث بطريقه القولبة اليدوية، معامل التوصيل الحراري (K value) والربح في الوزن تم حسابه بعد الغمر في محلول NaOH 0.5 M ولفترة60 يوم.أظهرت النتائج التدني في الخواص الفيزيائية مع زيادة زمن الغمر، وتم حساب معامل الانتشار للمحلول D فوجد يساوي (2.3 *10-12m2/sec).


Article
Study the effect of mixing the Zirconium oxide ZrO2 powder ratios
دراسة تأثير نسب الخلط على مسحوق اوكسيد الزركونيوم ZrO2

Loading...
Loading...
Abstract

In this research , the electrical , physical and structure properties of Zirconium oxide ZrO2 have been studied as basic , Calcium and Yttrium oxides as dopped materials , By using hydraulic pressing we made the uniform disks of samples . these samples sintered at 800ºC and socking time 2hr.The XRD potteries of samples showed that the change of intensity of sample that, dopped with (0.15)wt Y2O3 .The dielectric constant of samples found the improvement in the value of sample (0.15)wt of Y2O3 doped.

في هذا البحث درُست الخصائص التركيبية والكهربائية و الفيزيائية لمادة اوكسيد الزركونيوم النقي والمشوب بأوكسيد الكالسيوم واوكسيد اليتريوم ، شكلت العينات باستعمال مكبس هيدروليكي وعوملت حراريا عند OC800 وبزمن انضاج ساعتين . بينت أنماط الحيود الاشعة السينية تغيير في الشدة مع بقاء موقع ثابت دون تغير بسب معاملتها عند درجة ºC800 لعينات اوكسيد الزركونيوم المشوبة ب 0.15 نسبة وزنية بمادة اوكسيد اليتريوم .ومن ملاحظة قيم الخصائص العزلية و الميكانيكية ،وجد التأثير الاعلى الزركونيا يعود لأوكسيد اليتريوم مقارنة بأوكسيد الكالسيوم.