Effect of the Addition Coconut Shell Powder on Properties of Polyurethane Matrix Composite
تأثير إضافة مسحوق قشور جوز الهند على خواص مادة متراكبة ذات أرضية بولي يورثان

Author: Hayder Abbas Sallal حيدر عباس صلال
Journal: AL-NAHRAIN JOURNAL FOR ENGINEERING SCIENCES مجلة النهرين للعلوم الهندسية ISSN: 25219154 / eISSN 25219162 Year: 2014 Volume: 17 Issue: 2 Pages: 203-210
Publisher: Al-Nahrain University جامعة النهرين

Loading...
Loading...
Abstract

This work focuses on the preparation of base polyurethane matrix composite materials by (Hand Lay-Up) method, and studying the effect of selected weight fractions (2, 4, 6, 8, and 10) % wt of (coconut shell powder) particles on some properties of the prepared composite. Some mechanical tests were used to evaluate the prepared system (Tensile, Compression, Impact, and Hardness) tests, and a physical test of (Water absorption %), and all tests were accomplished at room temperature. Maximum results of tensile strength, compression strength, impact energy, hardness and water absorption were (31.3 MPa),(53 MPa), ( 0.156 J), (82 Shor (D)), (0.345 %) at using (6% wt, 6% wt , 2% wt , 10% wt ,10% wt ) respectively. Improved properties of the samples reinforcing for the sample as pure, tensile strength increased to double almost and compressive strength by 12% and impact energy up to 4% and hardness by 17% and the percentage of water absorption into doubled.

يركز هذا العمل على تحضير مواد متراكبة ذات أساس بوليمري بطريقة (الصب اليدوي)، ودراسة تأثير الكسور الوزنية المختارة (2 , 4 , 6 , 8 ,10) % من (مسحوق قشور جوز الهند ) على خواص المواد المتراكبة المحضرة، حيث المادة المتراكبة من راتنج البولي يورثان (PU). عدد الاختبارات الميكانيكية التي أجريت لتقييم النظام المتراكب المحضر تتضمن (الشدّ، الانضغاط، الصدمة والصلادة)، بالإضافة إلى الاختبار الفيزيائي (النسبة المئوية لامتصاصية الماء)، وكل الاختبارات أجريت في درجة حرارة الغرفة.النتائج القصوى لمقاومة الشد ومقاومة الانضغاط وطاقة الكسر والنسبة المئوية لامتصاص الماء كانت ((MPa 31.3 (، (MPa 53( ، (156,0 J )،( 82Shor (D))،( (0.345%) عند (wt % 6 , wt % 6 , wt%2 , wt % 10 , wt % 10 ) على التوالي .تحسنت الخواص للعينات المقواة عن العينة النقية حيث أن مقاومة الشد ازدادت حوالي الضعف ومقاومة الانضغاط بمقدار 12% وطاقة الكسر بحدود 4% والصلادة بمقدار 17% والنسبة المئوية لامتصاص الماء الى الضعف.


Article
The Effect Of The Hybrid Additions on the Bending and Tensile Behavior for the Hybrid Composite Material Reinforced by Short Fibers and the Zeolite Particles by Multifarious Grain Size
تأثير الاضافات الهجينة على سلوك الشد والانحناء لمادة متراكبة هجينة مقوات بالياف قصيرة ودقائق الزيوليت باحجام حبيبية متنوعة

Author: Hayder Abbas Sallal حيدر عباس صلال
Journal: AL-NAHRAIN JOURNAL FOR ENGINEERING SCIENCES مجلة النهرين للعلوم الهندسية ISSN: 25219154 / eISSN 25219162 Year: 2017 Volume: 20 Issue: 1 Pages: 113-119
Publisher: Al-Nahrain University جامعة النهرين

Loading...
Loading...
Abstract

Consider polymers and polymer matrix composite are the basis of the most prevalent material in all industrial and medical fields because of its properties qualify to occupy an advanced position among other engineering materials because of its good properties. Therefore, This work focuses on the preparation of base polymer matrix composite materials and study non-saturated polyester as matrix has been strengthened by zeolite particles different grain sizes (25 - 65 - 75) µm and different volume fractions (1,5 - 3 - 4,5 - 6 - 7,5 - 10) % was strengthened by Carbon short fibers and constant volume fraction (8%),the tests tensile and bending according to ASTM specifications, respectively. Through the results it was observed that the maximum tensile strength improved through hybrid reinforcement when reached the maximum value when the grain size (25 µm ) and at volume fraction (7.5%), reaching ( 94 N/mm2 )compared with the rest of sizes and at the same volume fraction reaching (78 N/mm2 for 65 µm , 69 N/mm2 for 75 µm), As for the bending test has been getting maximum Flexural resistance at grain size (25 µm) at volume fraction ( 6%) reached to(111 N/mm2) ,if compared with the rest of sizes at the same volume fraction reaching (100 N/mm2 for 65 µm,79 N/mm2 for 75 µm) while was obtained on the maximum bending modulus at grain size (25 µm) and at volume fraction (10%) reach to (8099 N/mm2) if compared with the rest of sizes at the same volume fraction reaching (7466 N/mm2 for 65 µm, 6666 N/mm2 for 75 µm ). Through the results we note that for the particle size and fiber effect in improving the mechanical behavior of the composite material prepared.

تعتبر البوليمرات والمواد المتراكبة ذات اساس بوليمر من اكثر المواد انتشارا في كافة المجالات الصناعية والطبية لما تتمتع به من خواص تؤهلها لاحتلال مركز متقدم من بين المواد الهندسية الاخرى لما تتمتع به من خواص جيدة . لذلك , في هذا العمل ركز على دراسة مادة متراكبة ذات اساس بوليمري حيث تم دراسة البولي أستر الغير مشبع كأرضية وتم تقويته بدقائق الزيوليت بأحجام حبيبية مختلفة ( 25 – 65 – 75 µm( وكسور حجمية مختلفة ( 1,5 – 3 – 4,5 – 6 – 7,5 – 10 )% وتم تقويته بالياف كاربون قصيرة وبكسر حجمي ثابت مقداره ( 8% ) , وتم اجراء اختبار الشد والانحناء حسب المواصفات الامريكية على التوالي .ومن خلال النتائج لوحظ ان مقاومة الشد القصوى تحسنت من خلال التقوية الهجينة الماخوذة وبلغت قيمتها القصوى عند الحجم الحبيبي (25 µm( وعند كسر حجمي (7,5 %) حيث بلغت (94N/mm2 ) مقارنة مع باقي الاحجام وعند نفس الكسر الحجمي حيث بلغت ( 78 N/mm2 للحجم 65 µm – 69 N/mm2 للحجم 75( µm , اما بالنسبة لاختبار الانحناء فقد تم الحصول على اقصى مقاومة انحناء عند الحجم الحبيبي (25 µ) وعند كسر حجمي (6%) حيث بلغت ( 111( N/mm2 اذا ماقورن مع باقي الاحجام عند نفس الكسر الحجمي حيث بلغت ( 100 N/mm2 للحجم 65 µm 79 N/mm2, للحجم 75( µm بينما تم الحصول على اعلى معامل انحناء عند الحجم الحبيبي (25( µm وعند كسر حجمي (10%) حيث بلغت ( 8099( N/mm2 اذا ماقورن مع باقي الاحجام عند نفس الكسر الحجمي حيث بلغت (7466 N/mm2 للحجم 65 6666 N/mm2, µm للحجم 75 µm ) من خلال النتائج نلاحظ ان للحجم الحبيبي والالياف تاثير في تحسين السلوك الميكانيكي للمادة المتراكبة المحضرة.


Article
Study the Effect of Adding Pharmaceutical Rennie Particles to Composite Materials with Polyester Matrix to be used in Medical Purposes
دراسة تأثير أضافة دقائق Rennie الصيدلانية على مواد متراكبة ذات اساس بولي استر لاستخدامها في الاغراض الطبية

Authors: Hayder Abbas Sallal حيدر عباس صلال --- Ismail Ibrahim Marhoon إسماعيل ابراهيم مرهون
Journal: AL-NAHRAIN JOURNAL FOR ENGINEERING SCIENCES مجلة النهرين للعلوم الهندسية ISSN: 25219154 / eISSN 25219162 Year: 2014 Volume: 17 Issue: 2 Pages: 56-67
Publisher: Al-Nahrain University جامعة النهرين

Loading...
Loading...
Abstract

The study carried out on the Rennie filled unsaturated polyester composites of varying size and different filler concentration reveals changes of the mechanical and physical properties of the composites, these changes in the properties of the Rennie filled polymer composites make them suitable for their use in medical, biomedical and pharmaceutical applications on large extent. This work focuses on the preparation of base polymer matrix (unsaturated polyester) composite materials by (Hand Lay-Up) method, and studying the effect of selected grain size (25, 53, and 90) µm of (Rennie) particles on some properties of the prepared composite. Some mechanical tests were used to evaluate the prepared system (Tensile, Compression, Impact, and Hardness) tests, and a physical test of (Water absorption %), and all tests were accomplished at room temperature. Maximum results of tensile strength, elongation at brake, young’s module, compression strength, flexural strength, flexural modulus, impact strength, hardness and water absorption were ((55.6 MPa),( 2.36 %), (2550 MPa), (51.5 MPa), (77.33 MPa), (6072.8 MPa),( 4.48 KJ/m2), (87.5 Shore (D)) and (0.321%)) respectively at using (25µm) except for flexural modulus and water absorption at (90 µm).

أن هذه الدراسة التي تم أجرائها على مسحوق مادة Rennie المقوي لمتراكبات البولي أستر الغير مشبع باستخدام أحجام وتراكيز مختلفة من هذا المسحوق حيث أظهرت تغيراً في الخواص الميكانيكية والفيزياوية لهذه المتراكبات , وأن هذا التغير بالخواص كان مناسباً لاستخدام هذه المواد المتراكبة في المجالات الطبية بشكل كبير. يركز هذا العمل على تحضير مواد متراكبة ذات اساس بوليمري من مادة (البولي أستر غير المشبع) بطريقة (الصب اليدوي)، ودراسة تأثير الحجوم الحبيبة المختارة (25 , 53 ,90) مايكرون من مادة (Rennie) (وبكسور وزنية مختلفة (4%, 8%, 12%, 16%, 20%) على خواص المادة المتراكبة المحضرة. عدد الاختبارات الميكانيكية التي أجريت لتقييم النظام المتراكب المحضر تتضمن (الشدّ، الانضغاط ، الانحناء ,الصدمة والصلادة)، بالإضافة الى الاختبار الفيزيائي (النسبة المئوية لامتصاصية الماء)، وكل الاختبارات اجريت في درجة حرارة الغرفة. النتائج القصوى لمقاومة الشد والاستطالة عند الكسر ومعامل يونك ومقاومة الانضغاط ومقاومة الانحناء ومعامل الانحناء ومقاومة الصدمة والصلادة والنسبة المئوية لامتصاص الماء كانت مرتبة كالتالي ((55.6(MPa, (2.36%), (2550 MPa), (51.5(MPa, (77.33MPa), (6072,8 MPa ), (4.48 KJ/m2), (87.5 Shore (D)), (0.321 %)) عند الحجوم ( 25 ) مايكرون ما عدا معامل الانحناء و الامتصاصية كانت عند الحجم (90 ) مايكرون.


Article
Effect the Grain Size on the Polymer Matrix Composites Reinforced by Reenia Particles
تأثير الحجم الحبيبي على مادة متراكبة ذات أساس بوليمري مقواة بدقائق من مادة (Reenia)

Loading...
Loading...
Abstract

Synthetic polymers such as polyurethane are used widely in the field of biomedical applications such as implants or part of implant systems.This paper focuses on the preparation of base polymer matrix composite materials by (Hand Lay-Up) method, and studying the effect of selected grain size (32, 53, 63, 75, and 90) µm of (Reenia) particles on some properties of the prepared composite.Mechanical tests were used to evaluate the prepared system (Tensile, Compression, Impact, and Hardness) tests, and a physical test of (Water absorption %), and all tests were accomplished at room temperature.Where results showed tensile test (maximum tensile strength and modulus of elasticity) high at small grain size while the percentage of elongation decreased with increasing size. As the compressive strength increased with small grain size. And also the values of hardness and fracture energy affected by particle size where the hardness and fracture energy increased at small particles size of compared to larger particles size. While the percentage of water absorption increased at large particle size.In general the results showed clear improvement in properties and maximum values which get it of tensile strength, Modulus of elasticity, elongation percentage, compression strength, fracture energy, hardness and water absorption were as follows ((34.8 MPa), (10%), (268 N/mm2), ( 54.2 MPa),( o.408 J), (78.9 Shor (D)), (0.2668 %)) at using (32µm)) except water absorption was at (90µm) .

يركز هذا البحث على تحضير مادة متراكبة ذات اساس بوليمري بطريقة (الصب اليدوي)، ودراسة تأثير الحجوم الحبيبة المختارة (32 , 53 , 63 , 75 ,90) مايكرون من مادة (Reenia) (وبكسر وزني ثابت 12% ) على خواص المادة المتراكبة المحضرة، حيث أن مادة الاساس المستخدمة هي راتنج البولي يوريثان (PU).عدد الاختبارات الميكانيكية التي أجريت لتقييم النظام المتراكب المحضر تتضمن (الشدّ، الانضغاط، الصدمة والصلادة)، بالإضافة الى الاختبار الفيزيائي (النسبة المئوية لامتصاصية الماء)، وكل الاختبارات اجريت في درجة حرارة الغرفة.حيث اظهرت نتائج اختبار الشد (اقصى مقاومة شد ومعامل المرونة ) ارتفاع عند الحجوم الدقائقية الصغيرة بينما قلت النسبة المئوية للأستطالة مع زيادة الحجم الدقائقي .كما ان مقاومة الانضغاط ازدادت مع الحجوم الدقائقية الصغيرة .وأيضا قيم الصلادة و طاقة الكسر تأثرت بالحجم الدقائقي حيث ارتفعت الصلادة وطاقة الكسر عند الحجوم الصغيرة للدقائق مقارنة بالحجوم الأكبر. بينما النسبة المئوية لامتصاص الماء ازدادت مع ارتفاع الحجوم الدقائقية .بشكل عام أظهرت النتائج تحسن واضح بالخواص وكانت القيم القصوى التي تم الحصول عليها لمقاومة الشد والنسبة المئوية للأستطالة ومعامل يونك ومقاومة الانضغاط وطاقة الكسر والنسبة المئوية لامتصاص الماء كانت مرتبة كالتالي ((34.8(MPa (10%) ,(268 نت/ملم2), (54.2(MPa ، (0.408 J) ،( Shor (D) 78.9)، (0.2668%) عند الحجوم ( 32) مايكرون ماعدى الامتصاصية كانت عند الحجم (90) مايكرون.

Listing 1 - 4 of 4
Sort by
Narrow your search

Resource type

article (4)


Language

English (2)

Arabic (1)

Arabic and English (1)


Year
From To Submit

2017 (1)

2014 (2)

2013 (1)