Abstract | Keywords | Fulltext | Export | TOC

In this Research, four high-copper amalgam alloys have been prepared by melting at 1050oC in an inert atmosphere, with copper content ranging from (14 to 26wt. %). Heat treatment processes were carried out to increase phases homogeneity and to reduce residual stresses, then, the alloys were mixed with mercury with a ratio of (1:1.2). Several structural measurements were carried out such as x-ray diffraction and microstructure analysis and some mechanical tests such as micro-hardness and compressive strength. X-ray diffraction results show that the amalgams and amalgams alloys have a variety of phases which depends on the copper content in the alloys. On the other hand, results of micro-hardness and compressive strength show that there is a linear increment in the mechanical properties with increasing copper in the amalgam, the results of D (Cu 26%) amalgam was comparable to those measured for the commercial amalgam of ANA that have high mechanical properties.

حضرت أربع سبائك ملغم عالية النحاس بصهرها عند درجة حرارة 1050oC في أجواء خاملة. وقد تراوحت نسب النحاس في السبائك بين (14~26wt.%) , تم إجراء معالجات حرارية لتحسين التجانس الطوري في السبائك وإزالة الإجهادات، أُجريت عملية الملغمة بخلط السبائك مع الزئبق بنسبة (1:1.2) ,أُجري عدد من القياسات التركيبية مثل تحليلات حيود الأشعة السينية وتحليلات البنية الدقيقة وبعض الخواص الميكانيكية المهمة مثل الصلادة ومقاومة الأنضغاط. وبينت تحليلات حيود الأشعة السينية وجود عدد من الأطوار الرئيسية في السبائك والملاغم تعتمد نسبها وتوزيعها على محتوى النحاس في السبيكة. بينما أظهرت نتائج قياسات الصلادة ومقاومة الانضغاط حصول زيادة خطية في الخصائص الميكانيكية مع زيادة النحاس في الملاغم. وكانت نتائج الملغم D (%26 Cu) مقاربة للقيم المقاسة للملغم التجاري ANA والذي يمتلك خصائص ميكانيكية عالية

Dental Amalgam --- Microstructure --- Hardness and Compressive Strength --- ملغم الاسنان --- البنية الدقيقة --- الصلادة ومقاومة الانضغاط