Article
Tensile and Compressive Properties of Kaolin Rienforced Epoxy
خواص الشد والانضغاط للأيبوكسي المدعم بالكاؤولين

Author: Jabbar Hussein Mohmmed جبار حسين محمد
Journal: Al-Khwarizmi Engineering Journal مجلة الخوارزمي الهندسية ISSN: 18181171 23120789 Year: 2015 Volume: 11 Issue: 3 Pages: 96-101
Publisher: Baghdad University جامعة بغداد

Loading...
Loading...
Abstract

The toughening of epoxy resins with the addition of organic or inorganic compounds is of great interest nowadays, considering their large scale of applications. In the present work, composites of epoxy are synthesized with kaolin particles having different particle sizes as reinforcement. Composites of epoxy with varying concentration (0 to 40 weight %) of kaolin was prepared by using hand lay method. The variation of mechanical properties such as modulus of elasticity, yield, tensile, and compressive strength with filler content was evaluated. The composite showed improved modulus of elasticity and compressive properties on addition of filler. In contrast, the tensile and yield strength of the composites decreases with rising kaolin content. It is also observed that mechanical properties increase with decrease in particle size in all cases.

تقوية راتنجات الايبوكسي بإضافة مركبات عضوية أو لا عضوية هي ذات أهمية كبيرة في الوقت الحاضر نظرا للمدى الواسع من التطبيقات في العمل الحالي، تم عمل متراكبات من الايبوكسي مع حبيبات الكاؤولين بأحجام حبيبية مختلفة بوصفها مادة تقوية. تم تحضير متراكبات الايبوكسي بتراكيز مختلفة (0-40% من الوزن) من الكاؤولين باستخدام طريقة القولبة اليدوية. تم دراسة التغير في الخواص الميكانيكية مثل معامل المرونة، مقاومة الخضوع، الشد، والانضغاط مع محتوى التقوية. اظهرت المتراكبات تحسن في معامل المرونة وخواص الانضغاط مع إضافة مادة التقوية. من جانب آخر، انخفضت مقاومة الشد والخضوع للمتراكبات مع زيادة محتوى الكاؤولين. كذلك، لوحظ تحسن الخواص الميكانيكية مع تقليل حجم الحبيبات في جميع الحالات.


Article
Wear Rate and Hardness of Boride Low Carbon Steel
معدل البلى والصلادة للفولاذ الواطئ الكاربون المبورن

Author: Jabbar Hussein Mohmmed جبار حسين محمد
Journal: Journal of Engineering مجلة الهندسة ISSN: 17264073 25203339 Year: 2015 Volume: 21 Issue: 10 Pages: 90-99
Publisher: Baghdad University جامعة بغداد

Loading...
Loading...
Abstract

There are no single materials which can withstand all the extreme operating conditions in modern technology. Protection of the metals from hostile environments has therefore become a technical and economic necessity. In this work, for enhancing their wear-resistance, boride layers were deposited on the surface of low carbon steel by a pack cementation method at 850 °C for (2, 4, and 6) h using vacuum furnace. The boronizing process was achieved using different concentration of boron source (20, 25, and 30) % wt. into coating mixture to optimize the best conditions which ensure the higher properties with lower time. The coating was characteristic by X ray diffraction (XRD), and it is confirmed the presence of (Fe2B) and (FeB) in the coating. The wear rate, hardness and thickness of the boride layers were measured, and it was observed that they effected by concentration of boron and time holding of boronizing process. Experimental results show that the higher properties of coating layer were obtained with 30% wt. of boron concentration and 4 h time holding.

لا توجد مادة مفردة ممكن ان تتحمل ظروف التشغيل القاسية في التكنلوجيا الحديثة. لذلك, حماية المعدن من المحيط القاسي اصبح ضرورة تقنية واقتصادية. في هذا العمل، ولتحسين مقاومتها للبلى، تم ترسيب طبقات من البوريد على سطح الفولاذ المنخفض الكاربون باستخدام طريقة السمنتة الصلبة عند درجة حرارة 850 ْم ولازمان (2، 4، و6) ساعات باستخدام فرن مفرغ. تم اجراء عملية البورنة باستخدام تراكيز مختلفة لمصدر البورون (20، 25، و30) % من الوزن داخل خليط الطلاء للحصول على أفضل القيم لأفضل ظروف للحصول على أعلى خواص بأقل زمن. تم توصيف الطلاء باستخدام حيود الاشعة السينية وقد اثبتت وجود طوري (Fe2B) و(FeB) في الطلاء. تم قياس معدل البلى، الصلادة، وسمك طبقة البوريد، وقد لوحظ تأثرها بتركيز البورون وزمن الابقاء لعملية البورنة. اثبتت النتائج العملية ان افضل خواص ممكن الحصول عليها عند الطلاء ب 30 % من الوزن تركيز البورون مع زمن ابقاء 4 ساعات.


Article
Evaluation the Mechanical Properties of Kaolin Particulate Reinforced Epoxy Composites
تقييم الخواص الميكانيكية لمتراكبات الايبوكسي المقواة بدقائق الكاؤولين

Author: Jabbar Hussein Mohmmed جبار حسين محمد
Journal: Al-Khwarizmi Engineering Journal مجلة الخوارزمي الهندسية ISSN: 18181171 23120789 Year: 2018 Volume: 14 Issue: 1 Pages: 29-38
Publisher: Baghdad University جامعة بغداد

Loading...
Loading...
Abstract

Epoxy resin has many chemical features and mechanical properties, but it has a small elongation at break, low impact strength and crack propagation resistance, i.e. it exhibits a brittle behavior. In the current study, the influence of adding kaolin with variable particle size on the mechanical properties (flexural modulus E, toughness Gc, fracture toughness Kc, hardness HB, and Wear rate WR) of epoxy resin was evaluated. Composites of epoxy with varying concentrations (0, 10, 20, 30, 40 weights %) of kaolin were prepared by hand-out method. The composites showed improved (E, Gc, Kc, HB, and WR) properties with the addition of filler. Also, similar results were observed with the decrease in particle size. In addition, in this study, multiple regression models were developed by utilizing (SPSS) package to predict the properties of kaolin reinforced epoxy composites. Good agreement was obtained between the predicted and the experimental results. The accuracy of prediction was (89.71%, 80.58%, 85.82%, 92.27%, and 94.49%) for E, Gc, Kc, HB, and WR, respectively.

يمتلك راتنج الايبوكسي العديد من الخواص الميكانيكية والكيميائية المهمة جداً، لكنه في الوقت نفسه يمتلك مطيلية محدودة ومقاومة ضعيفة للصدمة ولتوسع الشق، بمعنى آخر يبدي سلوكاً هشاً. في هذا البحث تم تقويم تأثير اضافة الكاؤولين بأحجام حبيبية مختلفة على الخواص الميكانيكية ) معامل الانحناء، المتانة، متانة الكسر، الصلادة، ومعدل البلى( لراتنجات الايبوكسي. تم تحضير متراكبات من الايبوكسي بتراكيز مختلفة (0، 10، 20، 30، 40% من الوزن) من الكاؤولين باستخدام طريقة القولبة اليدوية. اظهرت المتراكبات تحسنا في خواص (معامل الانحناء، المتانة، متانة الكسر، الصلادة، ومعدل البلى) عند اضافة حشوة الكاؤولين. وتمت ملاحظة النتائج نفسها بتقليل الحجم الحبيبي. كما تم ايضا في هذا البحث تطوير موديل انحدار متعدد باستعمال برنامج (SPSS) من اجل التنبؤ بخواص متراكبات الايبوكسي المقواة بالكاؤولين وتم الحصول على توافق جيد عند مقارنة القيم العملية والمتنبئة. فقد كانت دقة التنبؤ حوالي (89.71%، 80.58%، 85.82%، 92.27%، و94.49%) لمعامل الانحناء، المتانة، متانة الكسر، الصلادة، ومعدل البلى على التوالي.


Article
Evaluation the Mechanical Properties of Shot Peened TIG Welded Aluminum Sheets
تقييم الخواص الميكانيكية لصفائح الالمنيوم الملحومة بطريقة قطب التنكستن المحمي بالغاز الخامل والمعاملة بطريقة القذف بالكرات

Loading...
Loading...
Abstract

A tungsten inert gas (TIG) welding is one of the most popular kinds of welding used to join metals mainly for aluminum alloys. However, many challenges may be met with this kind of joining process; these challenges arise from decay of mechanical properties of welded materials. In the present study, an attempt was made to enhancing the mechanical properties of TIG weld joint of 6061-T6 aluminum alloy by hardening the surfaces using shoot peening technique. To optimize the shoot peening process three times of exposure (5, 10, and 15) min. was used. All peened and unpeened, and welded and unwelded samples were characterized by metallographic test to indicate the phase transformation and modification in microstructure occurring during welding process. Tensile test and Vickers micro-hardness measurements were performed for all samples to investigate the effect of shoot peening on mechanical properties of welded aluminum. The results indicated a significant improvement in properties for peened welded and unwelded samples compared with those unpeened one. Also, the results showed that the tensile and micro-hardness properties were increased with increasing the time of exposure to 15 min. due to generation of compressive residual stresses at surface.

تعتبر عملية اللحام بقطب التنكستن المحمي بالغاز الخامل (TIG) من اكثر انواع اللحام انتشارا والمستخدمة لربط المعادن وخصوصا سبائك الالمنيوم. رغم هذا فهناك العديد من التحديات والتي ممكن مواجهتها عند استخدام هذا النوع من عمليات الربط. هذه التحديات ناشئة من انخفاض الخواص الميكانيكية للمواد الملحومة. في الدراسة الحالية تم عمل محاولة لتحسين الخواص الميكانيكية لوصلة من سبائك الالمنيوم (6061-T6) ملحومة بطريقة اللحام بقطب التنكستن المحمي بالغاز الخامل (TIG) من خلال تصليد السطح باستخدام تقنية القذف بالكرات. وللوصول الى الاسلوب الامثل في عملية القذف بالكرات تم استخدام ثلاث ازمان للتعرض (5,10,15) دقيقة. تم توصيف جميع العينات المعاملة بالقذف بالكرات وغير المعاملة، الملحومة وغير الملحومة من خلال فحص سطح المعدن لبيان التحولات الطورية والتغيرات الحاصلة خلال عملية اللحام. تم اجراء فحص الشد وقياس صلادة فيكرز المجهرية لجميع العينات لدراسة تاثير القذف بالكرات على الخواص الميكانيكية لملحومات الالمنيوم. بينت النتائج تحسن ملموس في خواص العينات المعاملة بالقذف بالكرات الملحومة وغير الملحومة مقارنة بالعينات الغير معاملة. بينت النتائج ايضا ان خواص الشد والصلادة المجهرية قد ازدادت مع زيادة زمن التعرض الى 15 دقيقة نتيجة لتوليد مستويات اعلى من اجهادات الضغط المتبيقية عند السطح.

Listing 1 - 4 of 4
Sort by
Narrow your search

Resource type

article (4)


Language

Arabic and English (2)

English (2)


Year
From To Submit

2018 (1)

2017 (1)

2015 (2)