Article
Preparing Aluminum Alloys to Spot Welding by using immersion coating (Electrical Resistance Welding).

Author: Jaleel Kareem Ahmed
Journal: journal of kerbala university مجلة جامعة كربلاء ISSN: 18130410 Year: 2007 Volume: 5 Issue: 4 Pages: 164-172
Publisher: Kerbala University جامعة كربلاء

Loading...
Loading...
Abstract

It is the first time that immersion coating phenomenon used for preparing aluminum alloys surface for spot welding. Concentrated aqueous alkaline sodium zincate solution was used to deposit zinc at room temperature and replace an equivalent weight of aluminum from the alloy (G3/5052 or A5/3003) surface which is underneath the electrical insulator aluminum oxide layer which acts as inhibitor for spot welding results in destroying its link to the surface and fall down in the solution as visual white powder, it is similar to shaving process.Zinc coat is then removed by 50% nitric acid. The electrical resistance of the new conducting surface results from this treatment shows a linear relation ship against time up to 30 hours from the time of removal zinc coat according to the equation.Y= 0.6 X + 3.5and this indicates that the growth of aluminum oxide is regular during the first 30 hours from the time of exposure aluminum alloy surface to atmosphere. After this period (30 hours) the oxide film start to completion and its electrical resistance tends to be constant.The tensile strength of the welding spot shows a maximum value after 3 hours (19.3 kg/mm2) from the time of zinc coat removal (from the time of exposure of aluminum alloy to the atmosphere), but a linear relationship is found between tensile strength vs. time obeys the following equation:-Y= - 0.053X + 16.23 Where X between 6-48 hours after zinc coat removal.

لأول مرة في العالم تستخدم ظاهرة الطلاء بالغمر لتهيئة سطح سبائك الألمنيوم من نوع G3/5052و A5/3003للحام النقطي. تم استخدام محلول مائي قاعدي مركز من زنكات الصوديوم لترسيب الخارصين بدرجة حرارة الغرفة ليحل محل وزن مكافئ من الألمنيوم الذي يقع تحت غشاء اوكسيد الألمنيوم (Al2O3) العازل للكهربائية والمعرقل لعملية اللحام النقطي. تمت إزالة الخارصين المترسب بواسطة محلول حامض النتريك (50% حجما)ً. أظهرت المقاومة الكهربائية للسطح الجديد الموصل علاقة خطية مع الزمن لحد 30 ساعة الأولى من زمن إزالة الخارصين عن سطح سبيكة الألمنيوم حيث إن المعادلة التالية تعبر عن هذه العلاقة:-ص = 0.6 س + 3.5مما يدل على ان نمو اوكسيد الألمنيوم يكون منتظماً بحدود 30 ساعة من تعرض سطح السبيكة للجو بعدها يبدأ اوكسيد الالمنيوم بالاكتمال ومقاومته الكهربائية بالثبوتية.إن الحسابات أظهرت سمك الخارصين المترسب بحدود 21 مايكرون وهذا يعكس بأن مسامية الخارصين بهذا السمك بدأت تتلاشى وطاقة الإحلال غير كافية لاختراق ايونات الألمنيوم لجدار الخارصين المعرقل. أن الفقدان في سطح سبيكة الألمنيوم كان بحدود 6.4 مايكرون من كلا الجانبين حيث يمثل 0.32% من سمك سبيكة الألمنيوم الأصلي (2 ملم) حيث هذا الفقدان لا يؤثر على الصفات الميكانيكية للسبيكة (إبعاد النموذج 130×30×2 ملم).أظهرت النتائج إن أعلى قيمة لمتانة الشد عند نقطة اللحام هي 19.3كغم/ ملم2 وذلك بعد ثلاث ساعات من إزالة طبقة الخارصين إلا إن العلاقة الخطية بين متانة الشد والزمن والتي هي:ص = -0.053 س + 16.23أعطت قيما لـ س بين 6-48 ساعة بعد إزالة طبقة الخارصين.

Keywords


Article
Cross Linking Condensation Polymerization of Rayon Fiber

Author: Jaleel Kareem Ahmad جليل كريم احمد
Journal: Iraqi National Journal Of Chemistry المجلة العراقية الوطنية لعلوم الكيمياء ISSN: 22236686 Year: 2007 Issue: 26 Pages: 270-283
Publisher: Babylon University جامعة بابل

Loading...
Loading...
Abstract

AbstractThe degree of cross linking condensation polymerization of rayon molecule under argon atmosphere is a function of temperature in the range (200 – 230)C with liberation of 10%, 10.5%, and 10.9% water respectively from the fiber weight. Elemental analyses show increasing of carbon % on the expense of hydrogen and oxygen percents in the same order. Above 230C self-carbon dioxide is generated. The fiber resulted from the polymerization shows fire resistance and insoluble in sulfuric acid which is in opposite behavior to the untreated fiber. Also treated fiber shows color change from white  yellow brown black depending on temperature degree and duration of heating with smooth and oily surface appearance due to the new bonding system and more close rayon molecules upon polymerization, accompanied with what is called chemiluminescence phenomenon.Polymerization under nitrogen atmosphere shows early liberation of carbon dioxide gas beside water due to the presence of oxygen even in trace amount in the nitrogen gas which attacks the rayon molecules at the above temperature.

الخلاصةإن درجة البلمرة التكثيفية التشابكية لجزيئة الحرير تحت جو من غاز الاركون تزداد مع زيادة درجة الحرارة وعلى النحو التالي 200ْم، 215ْم، 230ْم مع تحرر 10%، 10.5% و10.9 ماء على التوالي. التحاليل الكيمياوية اظهرت زيادة في نسبة الكاربون على حساب نسبة الهيدروجين والاوكسجين بنفس الترتيب. بعد درجة 230ْم يبدأ تحرر غاز ثاني اوكسيد الكاربون الذاتي.الجزيئة الكبيرة الناتجة من البلمرة اظهرت مقاومة عالية ضد حامض الكبريتيك المركز وعلى مقاومة اللهب وكذلك اظهرت الياف الحرير تغير في لونها وكما يلي:ابيض اصفر  قهوائي  اسود معتمداً على درجة الحرارة وعلى زمن التعريض لها كما اظهرت سطح املس دهني بسبب نظام التآصر الجديد وتقارب جزيئات الحرير نتيجة البلمرة التشابكية العرضية المصحوبة بظاهرة ما يسمى بالتألق الكيميائي.البلمرة تحت جو من غاز النتروجين اظهرت التحرر الذاتي لغاز ثاني اوكسيد الكاربون مبكراً اضافة الى الماء ويعود السبب الى تواجد نسبة قليلة من الاوكسجين في غاز النتروجين والذي يهاجم جزيئة الحرير في تلك الدرجات الحرارية.

Keywords


Article
Prevent Intravenous Therapy (IV) Contamination by Addition of Magnesium Oxide Nanoparticles to Silicone Rubber

Authors: Auda Jabbar --- Braihi Jaleel Kareem --- Jaleel Kareem Ahmed --- Rami Sattar Jabbar
Journal: Journal of University of Babylon مجلة جامعة بابل ISSN: 19920652 23128135 Year: 2019 Volume: 27 Issue: 1
Publisher: Babylon University جامعة بابل

Loading...
Loading...
Abstract

Antibacterial material nanocomposites are prepared to manufacture intravenous therapy (IV). These composites prepared by adding Magnesium oxide nano powder (MgO NPs)with a different percent (3, 6, and 9 wt %) to Silicone rubber (SR). The activity of this antibacterial material was inspected againstS. aureus and E.coli microorganisms byusing Agar Well Diffusion method.Results showed that the addition of MgO NPs to SiR causes the following enhancement the antibacterial activity against E.coli and S.aureus by 7.1% and 27.1% respectively, increasing tensile strength by 65.5%, increasing the hardness by11.25%, increasing the wear resistance by 84.5%,increasing surface bearing index (Sbi) by 80.5% , increasing in core fluid retention (Sci) by 8.5%, decreasingsurface roughness (Sa) by 65%, decreasingcore roughness depth (Sk) by 67% and enhancement the wettability by decreases contact angle to minimum value.

المواد النانوية المتراكبة المضادة للبكتيريا تم تحضيرها لاستخدامها كأنابيب لادخال العلاج عن طريق الوريد (IV). حيث حضرت هذه المركبات بإضافة مسحوق أكسيد المغنيسيوم النانوي (MgO NPs) بنسب وزنية مختلفة (3،6،و9) وزن% إلى مطاط السيليكون (SR) وتم فحص فعالية هذه المادة المتراكبة المضادة للبكتيريا ضد بكتيريا S. aureus وE. coli باستخدام طريقة Agar Well Diffusion.أظهرت النتائج أن إضافة MgO NPs إلى SR يؤدي إلى تحسين الفعالية المضادة للبكتيريا ضدE. coli و S.aureus بنسبة 7.1 ٪ و 27.1 ٪ على التوالي ، وزيادة قوة الشد بنسبة 65.5 ٪ ، وزيادة الصلابة بنسبة 11.25 ٪ ، وزيادة مقاومة البلى بنسبة 84.5 ٪ ، وزيادة مؤشر تحمل السطح (Sbi) بنسبة 80.5 ٪ ، وزيادة في قابلية خزن السوائل (Sci) بنسبة 8.5 ٪ ، وخفض خشونة السطح (Sa) بنسبة 65 ٪ ، وخفض عمق الخشونة الأساسية (SK) بنسبة 67 ٪ و تحسين قابلية الترطيب للسطوح من خلال تقليل زاوية التلامس إلى اقل قيمة.


Article
Development and Evaluation of Chromium- Modified Aluminide Diffusion Coating

Author: Ahmed Ali Moosa,Jaleel Kareem Ahmed, Ali Hubi Haleem
Journal: Journal of University of Babylon مجلة جامعة بابل ISSN: 19920652 23128135 Year: 2009 Volume: 17 Issue: 1 Pages: 308-321
Publisher: Babylon University جامعة بابل

Loading...
Loading...
Abstract

AbstractIn this work nickel superalloy Inconel 600 was coated with two different types of coatings Cr modified aluminide coating this is called(Aluminizing- Chromizing) and Y-doped Cr modified aluminide coating this is called (Aluminizing- Chromizing- Yttriumizing) using pack cementation method. Diffusion coating was carried out in one step process by simultaneous aluminizing –chromizing process and by simultaneous aluminizing- chromizing- yttriumizing process using the conversion reaction of 10 wt.% Cr2O3, 10 wt.% Al, 2 wt.% NH4Cl, 4 wt% NaCl and 72 wt.% Al2O3 and 2% Y2O3 when required. The diffusion coating processes were carried out at 1050 oC for 8hrs. After diffusion coating the coating layer was found to be consisted of: -NiAl.Cyclic oxidation test in air was conducted on the Inconel 600 coated with Cr-modified aluminide coating and on the Inconel 600 alloy coated with Y-doped Cr modified aluminide coating in the temperature range 700- 1100 oC. The oxidation cycles include 10 hrs. at furnace temperature. The results indicate that Y-doped Cr modified aluminide coating is more effective in increasing the oxidation resistance of Inconel 600 alloy. The role of yttrium can be attributed to an improvement of the adherence of the oxide scales.

الخلاصة تم في هذا البحث طلاء سبيكة ذات أساس نيكل ( الانكونل 600) بنوعين من الطلاء : الأول طلاء الألمنيوم المدعم بالكروم و يدعى ( الألمنه – الكرمنة) والثاني طلاء الألمنيوم المدعم باليتريوم والكروم ويدعـى ( الألمنه – الكرمنة- التطعيم باليتريوم) بتقنية السمنته . جرى الطلاء الانتشاري آنيا لنوعي الطلاء من خلال التفاعل للمكونات التالية : 10 wt.% Cr2O3, 10 wt.% Al, 2 wt.% NH4Cl , 4 wt% NaCl ,72 wt.% Al2O3أما بالنسبة للنوع الثاني من الطلاء فيتم بإحلال فقط 2 wt.% Y2O3 من الألومينا. تمت عملية الطلاء الانتشاري بدرجة حرارة 1050 oC ولمدةhr. 8 . لقد وجد إن طبقة الطلاء الانتشاري تتكون من الطور -NiAl . جرى اختبار الأكسدة الدوري لسبيكة الانكونل 600 قبل وبعد الطلاء في مدى من درجات الحرارةoC ( 700 - 1100) وبمعدل 10hr للدورة الواحدة. أشارت النتائج إن تدعيم الألمنيوم باليتريوم والكروم أكثر كفاءة في زيادة مقاومة التأكسد لسبيكة الانكونل 600 , ويرجع ذلك إلى دور اليتريوم في تحسين التصاقية طبقة الأوكسيد الواقية.


Article
Oxidation of Ni – Al Electrodeposited Composite Coating of Inconel 600 Alloys

Authors: Newal Mohammed --- Ali Hubi Haleem --- Jaleel Kareem Ahmed
Journal: journal of kerbala university مجلة جامعة كربلاء ISSN: 18130410 Year: 2009 Volume: 7 Issue: 1 Pages: 129-140
Publisher: Kerbala University جامعة كربلاء

Loading...
Loading...
Abstract

The oxidation behavior of nickel matrix/ aluminum particle composite coatings in air at (600-800°C) for 25 hrs. was studied. The composite coatings were applied to Inconel 600 alloy by the electrodeposition technique and heat treated under argon atmosphere for three hours at 800 °C prior to oxidation testing. During heat treatment, coating morphological development was found to occur by the exothermic reaction Ni +Al = NiAl. For all samples, weight gain kinetics was obtained from furnace exposure and the composition and morphology of the oxidation products were examined using XRD analysis and light optical microscopy. An outer Al2O3 layer was formed on the composite coating surface. At test temperatures such as 800 °C, the coatings benefits from a small grain size that enhances Al diffusion to the surface to form the protective alumina layer.

تم دراسة آلية التأكسد لسبيكة الانكونل 600 المكتسية بالطلاء المركب ألمنيوم –نيكل عند درجات حرارة (600-800 ºC ) ولفترة (25 hrs.) . تم إجراء عملية الطلاء بتقنية الترسيب الكهربائي والمتبوعة بمعالجة حرارية في جو من الآركون لفترة ( 3 hrs. ) عند (800 ºC ). حصل أثناء المعاملة الحرارية تفاعل باعث للحرارة (Ni + Al = NiAl). جرت اختبارات التأكسد لجميع النماذج وكذلك تم تحديد صفات ومكونات طبقة الأوكسيد باستخدام المجهر الضوئي وحيود الأشعة السينية, لوحظ عند درجة حرارة الاختبار( 800 ºC) إن الحجم الحبيبي الناعم للطلاء يعزز من انتشار الألمنيوم إلى السطح مكونا طبقة الألومينا الواقية.


Article
FORMATION OF NI-SB PHASES BY ELECTRO-CODEPOSITION DIFFUSION COATING
تكوين أطوار Ni-Sb بطريقة الترسيب الكهربائي _ الانتشاري للطلاء

Loading...
Loading...
Abstract

Electrodeposited metal matrix/metal particle composite coatings (EMMC’s) were deposited, heat treated and characterized. Nickel matrix/ antimony particulate coatings deposited on Inconel 600 substrate (Ni-base superalloy) was chosen as a model system. The microstructure of the plated and heat treated coatings was characterized using light optical microscope (LOM) and X-ray diffraction analysis (XRD).Results showed that Ni5Sb2, Ni3Sb, and NiSb phases are presented in the coated layer. Further NiSb is a good source for Sb2O4 compound formation under open heating. This oxide has good stability at high temperatures.

تم في هذا البحث إجراء ترسيب كهربائي مزدوج لأرضية معدنية / دقائق معدنية وهذا ما يصطلح عليه ( EMMC’s ) ثم تلى ذلك إجراء معاملة حرارية . حيث تم ترسيب أرضية نيكل / دقائق الانتيمون على سطح سبيكة الانكونيل 600 وهي احد أنواع السبائك الفائقة ذات أساس نيكل والتي تتمتع باستخدامات واسعة وقد تم تحديد التركيب المجهري لطبقة الطلاء المعالجة حرارياً باستخدام المجهر الضوئي ، حيود الأشعة السينية .أظهرت النتائج تكون الأطوار NiSb, Ni3Sb, Ni5Sb2 عند سطح الطلاء. كما بينت النتائج إن طور NiSb مصدر جيد لتكوين Sb2O4 عند تسخينه في الهواء. هذا الأوكسيد يتمتع باستقرارية جيدة عند درجات الحرارة المرتفعة.


Article
Copolymer Production From Poly(Vinyl Alcohol)

Authors: Jaleel Kareem --- Auda Jabbar Braihi --- Dalal abbass Kadham
Journal: Journal of University of Babylon مجلة جامعة بابل ISSN: 19920652 23128135 Year: 2018 Volume: 26 Issue: 5 Pages: 199-208
Publisher: Babylon University جامعة بابل

Loading...
Loading...
Abstract

The treatment of PVA with concentrated hydrochloric acid using a reflex technique for several days to transfer some of PVA to PVC as co-polmer. Black material formed with very high ability to absorb water (approximately 220%) which indicates large voids formed in the new structure which confirmed by many tests. The new structureis a good water storage which is interested in agriculture applications

علاج بولي فنيل الكحول مع حمض الهيدروكلوريك المركزة باستخدام تقنية رد الفعل لعدة أيام لتحويل بعض بولي فنيل الكحول إلى بولي فينيلكلوريدكبوليمر مشارك. حيث تكون مادة سوداء لها قدرة عالية جدا على امتصاص الماء (حوالي 220٪) مما يدل على الفراغات الكبيرة التي تشكلت في الهيكل الجديد الذي أكده العديد من الاختبارات. الهيكل الجديد يحزن الماء بشكل جيد وهذا مثير للاهتمام في تطبيقات الزراعة.


Article
Polymer Biomedical Films

Authors: Salah Mahdi Abdullah --- Jaleel Kareem Ahmed --- Nizar Jawad Hadi
Journal: Journal of University of Babylon مجلة جامعة بابل ISSN: 19920652 23128135 Year: 2018 Volume: 26 Issue: 6 Pages: 220-233
Publisher: Babylon University جامعة بابل

Loading...
Loading...
Abstract

Composite films ofboth Poly (vinyl alcohol)/nano silica-nano zinc oxide (PVA/SiO2- ZnO) andPoly (methyl methacrylate) / nano silica-nano zinc oxide -chlorophyll (PMMA/SiO2-ZnO-Ch) are prepared by usingcasting method and their medical applications areevaluated. In this study Nano, silica and Nano zinc oxide are used as filler with thefollowing percentagesof (1,2 and 3) to improve the biological and mechanical properties of the composite films. Many tests are carried on the composite films such as Fouriertransform infrared spectroscopy (FTIR), antibacterial activity, and tensile test. Their results show that zinc oxide hasan excellent antibacterial activity andthis activity increases in composite films with the increasing concentrationof the zinc oxide .PMMA composite films show a better healing power than that of the PVA composite films. To avoid cracking on the produced PMMA film, chlorophyll as a bio natural pigment, is added it acts as a plasticizer and as a result it removes film stresses.All mechanical and physical tests show that the PVA composite has higher values than those of PMMA.This is due to the fact that PVA can build a hydrogen bond with ZnO or SiO2 additives while PMMA has no tendency for H-bonding.

الافلام المركبة لكل من بولي فنيل الكحول مع السليكا النانوية - اوكسيد الزنك النانوي. بولي مثيل ميثا اكريليت مع السليكا النانوية - اوكسيد الزنك النانوي- الكلوروفيل يتم تحضيرها باستخدام طريقة الصب ويتم تقييم تطبيقاتها الطبية. في هذه الدراسة السليكا النانوية واوكسيد الزنك النانوي تستخدم كماده ماله لتحسين الخواص البيولوجية والميكانيكه للأفلام المركبة. يتم اجراء العديد من الاختبارات على الافلام المركبة مثل مطياف الأشعة تحت الحمراء والفعالية المضادة للبكتريا واختبار الشد.اضهرت النتائجأنأوكسيدالزنكلديهنشاطمضادللجراثيمممتازوهذاالنشاطيزدادفيالأفلامالمركبةمعزيادةتركيزاوكسيدالزنك. الافلام المركبة البولي مثيل ميثا اكريليت اضهرت قوة شفاء أفضل من لأفلام المركبة لبولي فنيل الكحول. ولتجنب الشقوق على افلام بولي مثل ميثا اكريلت المنتجة، الكلوروفيل كصبغه طبيعية حيوية تضاف حيث انها تعمل كملدن وبذالك تزال الشقوق من الافلام المركبة. جميع الاختبارات الميكانيكية والفيزيائية تظهر ان لأفلام المركبة لبولي فنيل الكحول لها قيم اعلى من قيم الافلام المركبة البولي مثيل ميثا اكريليت وهذا يرجع الى حقيقة ان بولي فنيل الكحول يمكن ان يبني اواصر هيدروجينية مع اضافات اوكسيد الزنك النانوي او السليكا النانوية بينما بولي مثيل ميثا اكريليت لا يمتلك ميل لعمل اواصر هيدروجينية.

Listing 1 - 8 of 8
Sort by
Narrow your search

Resource type

article (8)


Language

English (8)


Year
From To Submit

2019 (1)

2018 (2)

2009 (3)

2007 (2)