A Comparison Between The Wear Rate Behavior Of Polyester Reinforced By Glass And Kevlar Fibers
مقارنة سلوك معدل البلى للبولي استر المقوى بألياف الزجاج والياف الكفلر

Author: Jamal Jalal Dawood
Journal: Engineering and Technology Journal مجلة الهندسة والتكنولوجيا ISSN: 16816900 24120758 Year: 2009 Volume: 27 Issue: 11 Pages: 2273-2285
Publisher: University of Technology الجامعة التكنولوجية

Loading...
Loading...
Abstract

In this research the wear rate of the polyester reinforced by chopped glassfibers and chopped Kevlar fibers with length (1-2.5 mm) and weight fraction (4, 8, 12,16 WT %) has been investigated. A Pin -on- Disc wear testing machine of variablespeed has been used. Flat against flat sliding surfaces under variable workingparameters conditions have been tested.The results of flat sliding surfaces show that the wear rate of the specimensdepends heavily on the working condition. It increases with the increase of the loadand sliding speed, and the wear rate decreases with the increase of the weight fraction.The results also show that the wear rate for polyester reinforced by Kevlarfiber was less than the polyester reinforced by glass fiber. The optimum value of wearrate was (2.75*10-6 mm3/mm) happened at weight fraction (16 WT %) when reinforcedby Kevlar fibers.

في هذا البحث تمت دراسة سلوك البليان للبولي أستر المقوى بألياف الزجاج وألياف الكفلر4, 8, 12 ) . لقد استخدم جهاز قياس , 16 WT %) 1-2.5 ) وكسر وزني mm) المتقطعة بطولالبلى ( المسمار - على - قرص ) ذو السرع المتغيرة. أجريت الدراسة على سطح مسمار مسطح –على قرص مسطح تحت معالم وضروف مختلفة.بينت نتائج الاسطح المنزلقة بان معدل البلى للعينات يعتمد بصورة كبيرة على ضروفالعمل. حيث يزداد معدل البلى مع زيادة الحمل المسلط والسرعة الانزلاقية ويقل مع زيادة الكسرالوزني.كذلك بينت النتائج بان معدل البلى للبولي أستر المقوى بألياف الكفلر اقل من المقوى بألياف( 2.75 ) حصلت عند كسر وزني 16 *10-6mm3/mm) الزجاج. وان أفضل قيمة لمعدل البلى كانتعند التقوية بألياف الكفلر. WT %)

Keywords


Article
Study The Effect Of The (Al) And (Al2O3) Particles Reinforcing On The Wear Volume Loss Characteristics Of Epoxy
دراسة تأثیر التقویة بدقائق (Al) و (Al2O3) على خصائص خسارة حجم البلى للأیبوكسي

Authors: Jamal Jalal Dawood --- Bassam Ali Ahmed
Journal: Engineering and Technology Journal مجلة الهندسة والتكنولوجيا ISSN: 16816900 24120758 Year: 2009 Volume: 27 Issue: 1 Pages: 116-126
Publisher: University of Technology الجامعة التكنولوجية

Loading...
Loading...
Abstract

This study investigated experimentally the wear volume loss of the epoxy reinforcedby (Al) and (Al2O3) particles of grain size ( £ 30 mm) with different four volumefractions of the reinforcements which are (3 %, 6 %, 9 %, and 12 % Vol.). Pin-on-Discwear test were conducted to exam the wear volume loss behavior of the compositespecimens. The wear test results indicated that the wear volume loss of the specimenincreases with the increase of the applied load and sliding time, while it decreases withthe increase of the volume fraction of the reinforcing material. Also the results show thatthe average volume loss of the epoxy reinforced by (Al) was higher than reinforced by(Al2O3) by the value was (45 % ) at volume fraction (= 6 %), sliding speed (Vs =2m/sec.) and sliding time ( T =300 sec.)

ذات الحجم (Al2O و ( 3 (Al) هذه الدراسة بحثت عمليا" خسارة حجم البلى للأيبوكسي المقوى بدقائق.(12 %, 9%, 6 %, 30 ) عند أربعة كسور حجميه مختلفة لمادة التقوية (% 3 mm ³) الحبيبيأستخدم جهاز البلى نوع ( مسمار – على – قرص ) للتوصل إلى طبيعة خسارة حجم البلى للعيناتالمتراكبة المستخدمة. بينت النتائج بان خسارة الحجم للعينات تزداد مع زيادة الحمل المسلط وزمن الانزلاق بينماتقل مع زيادة الكسر ألحجمي لمادة التقوية. كذلك بينت النتائج بان معدل خسارة حجم البلى للأيبوكسي المقوى ب(2 m/sec.) بنسبة (% 45 ) عند كسر حجمي (% 6) وسرعة أنزلاق (Al2O أعلى من المقوى ب ( 3 (Al).(300 sec.) وزمن أنزلاق

Keywords


Article
Modelling of Carburization Parameters Process for Low Carbon Steel

Authors: Abbas Khammas Hussein --- Laith Kais Abbas --- Jamal Jalal Dawood --- Nadeen Jaafar Ismae
Journal: Engineering and Technology Journal مجلة الهندسة والتكنولوجيا ISSN: 16816900 24120758 Year: 2016 Volume: 34 Issue: 6 Part (A) Engineering Pages: 1069-1079
Publisher: University of Technology الجامعة التكنولوجية

Loading...
Loading...
Abstract

This paper representsthe carburization parameters for steel (1020) using Desirability Function Analysis-DFA. The experiments were conducted using Taguchi (L9) orthogonal array. Carburization parameters such as carburization temperature, carburization time and tempering temperature were optimized by multi - response considerations depending onmicrohardnessand were rate measurements. The optimal carburizing parameters had been determined by composite desirability value obtained from desirability function analysis while significant contribution of parameter was determined by analysis of variance (ANOVA). The analyses results showed that optimal combination for higher hardness and lower wear rate were at (A2=920 oC, B2= 3 hours and C3=120 oC). Confirmation test was also conducted to validate the test results. Mathematical models for composite desirability, microhardness and rate wear were determined. Experimental results showed that the carburization performance can be improved effectively through desirability approach.


Article
MULTIPLE OBJECTIVE OPTIMIZATION OF WELD GEOMETRY OF DISSIMILAR METALS
تحديد العوامل المثلى المتعددة الاستجابة للشكل الهندسي لوصلة لحام المعادن المختلفة

Loading...
Loading...
Abstract

The parameters affecting on bead geometry of the dissimilar welding between stainless steel (AISI-304) and Low carbon steel (ASTM A516 Grade 70) using (Gas Metal Arc Welding-GMAW) technique were studied in this paper. A multi-response optimization approach to determine the optimal process parameters in (GMAW) was used. Three process parameters were used in the experiments: welding current, welding speed and wire diameter, in three levels for obtaining the responses on bead width, reinforcement and penetration of the weldments. Taguchi (L9) orthogonal array was used to gather information regarding the welding process with less number of the experimental runs. A multi criteria decision making method (TOPSIS) passive was applied in the present study to approve a significant Taguchi approach in solving multi response optimization problem. In order to consider experimental uncertainty, the responses are expressed in linguistic terms rather than crisp values. In additional the (ANOVA) test was passive also applied to identify most the significant factors. The results of (ANOVA) showed that optimum bead geometry can be reached by a control on the parameters mentioned above. Also it was found that the welding current factor contributed the highest percentage (88.14%) to the factor effects, followed by (wire diameter) which equal (8.92%) and (welding speed) which equal (2.94%). Confirmation experiments showed that developed models are accurate.

يتضمن هذا البحث دراسة تاثيرالعوامل على الشكل الهندسي لدرز لحام المعادن المختلفة المكونة من الفولاذ المقاوم للصدا نوع(AISI-304) والفولاذ منخفض الكاربون نوع (ASTM A516 Grade 70) باستخدام طريقة لحام القوس.(GMAW) تم استخدام اسلوب الامثلية متعددة الاستجابة لتحديد العوامل المثلى لطريقة (GMAW) حيث استخدمت ثلاث عوامل تجريبية (تيار اللحام، سرعة اللحام، وقطر سلك اللحام) بثلاث مستويات للحصول على استجابة لكل من عرض الدرز، التقوية، والاختراق في الوصلات الملحومة. استخدمت مصفوفة (Taguchi) نوع (L9) لتجميع بيانات عملية اللحام عند اقل عدد ممكن من التجارب ، بالاضافة الى ذلك استخدمت طريقة صنع القرار المتعدد المعيار (TOPSIS) في هذه الدراسة لغرض تطبيق طريقة (Taguchi) لحل الامثلية المتعددة الاستجابة. لغرض تلافي الغموض التجريبي فقد تم التعبير عن الاستجابة من خلال المصطلحات النصية بدلاً من القيم العددية . أضافة الى ذلك تم تطبيق طريقة تحليل التباين (ANOVA) لتحديد العوامل الاكثر تاثير على الاستجابة المتعددة. واظهرت نتائج تحليل (ANOVA) ان الشكل الهندسي الامثل لدرز اللحام يمكن الحصول عليه من خلال السيطرة على العوامل اعلاه ، ووفقاً لنتائج (ANOVA) فان تيار اللحام كان له التأثير الأكبر على الاستجابة وبنسبة (88.14%) يليه قطر السلك بنسبـة (8.92%) وثم سرعة اللحام بنسبة (2.94%)، واخيرا اضهرت نتائج تجارب الاثبات دقة الأنموذج الرياضي المعتمد.

Listing 1 - 4 of 4
Sort by
Narrow your search

Resource type

article (4)


Language

English (4)


Year
From To Submit

2016 (2)

2009 (2)