The Effect of the Solution Heat Treatment on the Mechanical Properties of Aluminum-Copper Alloy (2024-T3) Using Rolling Process
تأثير المعاملة الحرارية المحلولية على الخواص الميكانيكية لسبيكةألمنيوم- نحاس (2024-T3) باستعمال عملية الدرفلة

Loading...
Loading...
Abstract

The effect of solution heat treatment on the mechanical properties of Aluminum-Copper alloy. (2024-T3) by the rolling process is investigated. The solution heat treatment was implemented by heating the sheets to 480 C° and quenching them by water; then forming by rolling for many passes. And then natural aging is done for one month. Mechanical properties (tensile strength and hardness) are evaluated and the results are compared with the metal without treatment during the rolling process. ANSYS analysis is used to show the stresses distribution in the sheet during the rolling process. It has been seen that good mechanical properties are evident in the alloy without heat treatment due to the strain hardening and also the mechanical properties are improved after heat treatment and rolling process but with lower forces and stresses when compared with the untreated.

دراسة تأثير المعاملة الحرارية المحلولية على الخواص الميكانيكية لسبيكة ألمنيوم -نحاس 2024-T3 من خلال عملية الدرفلة . حيث تم إجراء معاملة حرارية تضمنت تسخين صفائح من هذه السبيكة إلى درجة حرارة (480°C) ثم التبريد السريع بالماء بعدها تم إجراء عملية التشكيل اللدن (بالدرفلة) على هذه الصفائح المقساة ثم إجراء عملية تعتيق طبيعي لمدة شهر بعدها تم دراسة الخواص الميكانيكية من مقاومة شد وصلادة حيث تم إجراء عملية التشكيل بواسطة عملية الدرفلة من خلال تمرير الصفائح بين درافيل وبنسب تشكيل متعددة ومقارنة النتائج للمعدن بدون تعامل. تم استخدام برنامج ANSYS لدراسة توزيع الاجهادات في عملية الدرفلة . لقد تبين أن الخواص الميكانيكية للسبيكة بدون تعامل حراري افضل بسبب ما يسمى بالاصلاد الانفعالي والخواص الميكانيكية للسبيكة بعد المعاملة الحرارية والدرفلة تحسنت ايضاً ولكن بجهد وقوى اقل مقارنة بتلك التي اجريت بدون معاملة


Article
Effect of Magnesium Addition on Corrosion Resistance of Aluminum -17%Silicon Alloy
تأثير أضافة المغنيسيوم على مقاومة االتآكل لسبيكة المينيوم – سيليكون 17%

Authors: Muna Khethier Abbass منى خضير عباس --- Khairia Salman Hassan خيرية سلمان حسن --- Kayser Aziz Ameen قيصر عزيز أمين
Journal: Al-Khwarizmi Engineering Journal مجلة الخوارزمي الهندسية ISSN: 18181171 23120789 Year: 2016 Volume: 12 Issue: 4 Pages: 50-58
Publisher: Baghdad University جامعة بغداد

Loading...
Loading...
Abstract

The electrochemical behavior of Al-17%Si alloy is investigated in 3.5wt% NaCl solution. Many alloys with addition of the different wt% magnesium metal of 1wt%, 2%, 3wt% ,4.5wt% ,and 9wt% were prepared by gravity die casting . The microstructures of prepared alloys were examined by optical and SEM microscopes. Corrosion behavior was investigated by using potentiostat instrument under static potentials test and corrosion current was recorded to determine corrosion resistance of all prepared samples. It was found that the addition of Mg metal improves the corrosion resistance of Al-17%Si alloy in 3.5%NaCl solution. The alloy containing 1%Mg shows less corrosion rate than the others while the alloys containing 4.5%Mg, 9%Mg content have the better pitting corrosion resistance than other alloys.

في هذا البحث تم دراسة السلوك الكهروكيمياوي لسبيكة (Al- 17%Si) في محلول (3.5 wt% NaCl)، وذلك باضافة معدن المغنيسيوم للسبائك وبنسب مختلفة (1wt%, 2wt%, 3wt%, 4.5wt%, 9wt%) حيث تم تحضير السبائك بواسطة قوالب الصب بالجاذبية.وقد تم استعمال المجهر الضوئي والمجهر الالكتروني الماسح لفحص التركيب المجهري للسبائك. وتم بحث اسلوب التآكل بواسطة استعمال جهاز المجهاد الساكن (Potentiostat) وتحت اختبار الجهد الساكن وتم تسجيل تيار التأكل وحساب مقاومة التأكل لكل النماذج المحضرة. وقد لوحظ انه عند اضافة معدن المغنيسيوم يزيد من مقاومة التأكل في سبائك (Al-17%Si) في محلول (3.5% NaCl). ولوحظ ايضاً ان السبائك الحاوية على (1% Mg) اظهرت اقل معدل تآكل من السبائك الاخرى بينما كانت السبائك الحاوية على (9% Mg, 4.5% Mg) تمتلك افضل مقاومة للتاكل النقري من باقي السبائك.