Synthesis of calcium hydroxyapatite powder from hen’s eggshell
تحضير مسحوق الهايدروكسي أبتايت من قشور بيض الدجاج

Authors: Ahmed M. Saeed أحمد محمد سعيد --- Raaed A. Hassan رائد عبد العباس حسن --- Khalid M. Thajeel خالد مهدي ثجيل
Journal: Iraqi Journal of Physics المجلة العراقية للفيزياء ISSN: 20704003 Year: 2011 Volume: 9 Issue: 16 Pages: 24-28
Publisher: Baghdad University جامعة بغداد

Loading...
Loading...
Abstract

The interest in calcium phosphates arises from the fact that bones contain a high percentage of mineralized calcium phosphate . In this study, pure and biocompatible hydroxyapatite (HAP) powder was successfully synthesized using hen’s egg shell as calcium source and phosphoric acid by precipitation method.The precipitate obtained was subjected to ripenning process for 24 hours, filtered, air dried, and calcined at temperatures of 400,800,900,and 1000 ºC.X-Ray diffraction(XRD) technique was used to investigate the formation of HAP powder, XRD results revealed the HAP formation and also indicate no occurrence of secondary phases. Fourier Transform Infrared(FT-IR) spectrum shows the characterstic peaks for phosphate and hydroxyl groups .The measured Ca/P ratio in HAP powder was 1.67 .

تدخل مركبات الكالسيوم فسفور في تركيب العظام والأسنان بنسب مئوية عالية، وهي تعد من المواد ذات الفعالية المتميزة بايولوجيا،مما يجعل منها ملائمة للأستخدام كبدائل عظمية و في حقل الزوارع الجراحية . حضر في هذه الدراسة مسحوق الهايدروكسي أبتايت النقي بخلط معلق من هيدروكسيد الكالسيوم- المحضر أصلا من قشور بيض الدجاج- مع حامض الفسفوريك ،واخضع الراسب المتكون الى عمليات : انضاج لمدة 24ساعة، وترشيح، وتجفيف، ومن ثم الى تلبيد بدرجات حرارية تراوحت من 400 الى 1000 درجة سلليزية . للتحقق من تحضير هذا المسحوق ، استخدمت تقنية حيود الأشعة السينية ، وقد أكدت نتيجة الفحص تكون طور الهايدروكسي أبتايت الخالي من الأطوار الثانوية . من جانب آخر أظهرت نتائج الفحص بتقنية التحليل بالأشعة تحت الحمراء تواجد قمم مميزة لمجاميع الفوسفات والهيدروكسيل . اضافة الى ذلك فأن التحاليل الكيميائية التقليدية أظهرت ان نسبة الكالسيوم الى الفسفور في المسحوق المحضر هي 1,67.

Keywords


Article
The Effect of SiC Particles on the Physical Properties of MgO Ceramic Matrix Composites
تأثير دقائق كاربيد السليكون على الخصائص الفيزيائية لمتراكب ذات الأساس السيراميكي لأوكسيد المغنيسيوم

Loading...
Loading...
Abstract

ABSTRACT The influence of SiC particles on the physical and mechanical properties for MgO/SiC composites was investigated. MgO matrix was reinforced with (2 wt%,4 wt%,6 wt% and 8 wt% ) of SiC particles which synthesized using powder technology technique. Five samples of each patch have been prepared and supplied to physical properties (green density (G.D) and bulk density (B.D)) and mechanical properties (hardness and compressive strength) were measured. It was observed that the green density of all samples were decreases with increasing SiC particles content. This due to the lower density of SiC than MgO particles. Prepared samples were sintered at different temperatures (800 ˚C, 1100 ˚C, and 1450 ˚C). The bulk density reviled the unaffecting property for samples sintered at 800C and 1100˚C, but it was observed a significant increasing in B.D for samples sintered at higher temperature (1450˚C). It has been found that Vickers hardness, compressive strength and diametrical strength values increases with increasing sintering temperature and decreasing with SiC particles content. The purpose of this study was to confirm the influence of SiC addition on some physical and mechanical properties of MgO matrix.

الخلاصةتم دراسة تأثير إضافة دقائق كاربيد السليكون على الخواص الفيزيائية والميكانيكية لمتراكب اوكسيد المغنيسيوم/كاربيد السليكون وبنسب مئوية مضافة من كاربيد السليكون هي 2%،4%،6%،8% والتي تم تصنيعها بطريقة تكنولوجيا المساحيق. تم تحضير العينات وقياس الخصائص الفيزيائية (الكثافة قبل الحرق والكثافة الحجمية) والخصائص الميكانيكية( الصلادة ومتانة الانضغاط). لقد تم ملاحظة أن الكثافة الطرية لكل العينات تقل بازدياد دقائق كاربيد السليكون المضافة وهذا نتيجة انخفاض كثافة كاربيد السليكون مقرنة باوكسيد المغنيسيوم. أظهرت الكثافة الحجمية عدم تأثرها بالعينات الملبدة بدرجات الحرارة 800م، 1000م وتأثرها الواضح بدرجة التلبيد1450م. لوحظ أيضا آن صلادة فيكرز ومتانة الانضغاط والمتانة القطرية تزداد بازدياد درجة حرارة التلبيد وتقل بازدياد كمية الدقائق المضافة.الغرض من البحث هو لتوضيح تأثير إضافة دقائق كاربيد السليكون على الخواص الفيزيائية والميكانيكية لقالب اوكسيد المغنيسيوم.