Article
Study the Effect of Some Solutions on Epoxy Resin & Calculate Diffusion Coefficient of Solution.
دراسة تأثير بعض المحاليل على راتنج الايبوكسي وحساب معاملات الانتشار لهذه المحاليل.

Author: Khalil T. Hassan خليل ثابت حسان
Journal: Journal of university of Anbar for Pure science مجلة جامعة الانبار للعلوم الصرفة ISSN: ISSN: 19918941 Year: 2010 Volume: 4 Issue: 1 Pages: 65-71
Publisher: University of Anbar جامعة الانبار

Loading...
Loading...
Abstract


Abstract: Specimen of Epoxy resin have surface area (1cm*1cm) immersed in several individual solvent (0.5% NaoH), (1% NaOH),(2.5% H2SO4), (5%H2SO4),(2.5%HCl), (5% HCl). For long time (three years). The specimen's masses were measured before and after immersion in solutions. Diffusivity and diffusion coefficient of solutions in epoxy resin measured from the relation of the change of specimen weight and the square rout of time.Photograph of the specimen surface have taken by using optical microscope and digital camera. Shoor Hardness test was used to obtain the change of Hardness properties after pot in solvent. The result obtained illustrate the different effect of these solution in the surface of specimen that effect in hardness and diffusion coefficient.

الخلاصة:-في هذا البحث تم غمر عینات مصنوعة من ا رتنج الایبوكسي ذات أبعاد مساحة مقطع ( ١سم* ١سم) في محالیل مختلفةكل على حدة وبت ا ركیز مختلفة وهي( ٠.٥ % هیدروكسید الصودیوم)و( ١% هیدروكسید الصودیوم)و ( ٢.٥ %وحامضالكبریتیك)و( ٥%وحامض الكبریتیك) و( ٢.٥ %حامض الهیدوكلوریك)و( ٥%حامض الهیدوكلوریك) لفترة زمنیة طویلة ( ثلاث سنوات)وتم وزن النماذج قبل وبعد الغمر بفت ا رت زمنیة مختلفة .تم إیجاد الانتشاریة للمحالیل وحساب معامل الانتشار لها من خلال رسم العلاقةبین التغیر في وزن العینات والجذر ألتربیعي للزمن .تم التقاط صور لأسطح العینات باستخدام المجهر الضوئي والكامی ا ر الالكترونیة.لقدأظهرت النتائج التأثیر المختلف للمحالیل على العینات هذا التأثیر ظهر بشكل واضح عل سطوح العینات وعلى قیم معامل الانتشارلهذه المحالیل.


Article
Growth Nanostructured CdO Thin Film via Solid-Vapor Deposition
تحضير اغشية الكادميوم اوكسايد النانويه باستخدام طريقة التبخير الحراري

Loading...
Loading...
Abstract

Cadmium Oxide ( CdO ) thin films have been prepared by vacuum evaporation method on Si (111) substrate at room temperature using CdCl2 as a source of Cd. Detailed structural properties of the films are presented using XRD and SEM. The films was pure polycrystalline CdO phase with high crystallinity. The lattice constant average crystallite size of the nanocrystalline CdO thin films were calculated. SEM image confirm the formation nanostructure. Energy dispersive X-ray analysis spectra of CdO thin films shows the presence of Cd and O peaks only, no additional peaks attributed to impurities or contamination are observed.

اغشية الكادميوم اوكسايد تم تحضيرها باستخدام طريقة التبخير الحراري على قواعد من السيلكون باستخدام كادميوم كلورايد كمصدر للكادميوم. دُرست الخصائص التركيبيه, طوبوغرافية السطح بواسطة حيود الاشعه السينيه (XRD), المجهر الالكتروني الماسح (SEM) . اظهرت قياسيات حيود الاشعه السينيه ان غشاء الكادميوم اوكاسايد المرسب كان متعدد التبلور ومتبلور بصوره جيده . تم حساب ثابت الشبيكه و الحجم الحبيبي النانوي. اكدت نتائج المجهر الالكتروني الماسح طبيعية التركيب النانوي للفلم. بينت نتائج تحليل الاطياف للطاقة والتشتت للاشعه السينه ان الفلم يحتوي على قمم الكادميوم والاوكسجين فقط من غير ظهور لاية قمم تعود للشوائب او التلوث .