Article
Effect of water on the properties of some polymeric composites

Authors: Balqees M.Dhyae --- Khansaa D.Salman
Journal: Engineering and Technology Journal مجلة الهندسة والتكنولوجيا ISSN: 16816900 24120758 Year: 2008 Volume: 26 Issue: 5 Pages: 528-535
Publisher: University of Technology الجامعة التكنولوجية

Loading...
Loading...
Abstract

The effect of water was studied on some physical and mechanical propertiesincluding (Roughness, Hardness, Compression Strength), and diffusion coefficientwas calculated using Ficks’ 2nd law for a polymeric composite materialsPVC+carbon black, Epoxy+Al powder, Epoxy + E-glass (chapped)), withvolume fraction Vf=30% reinforcement for all specimens, results showed thenegative effect of water on these properties which is differed between onespecimen and other, PVC+CB was affected more than Epoxy+E-glass thenEpoxy+Al powder and the diffusion coefficient (D) was less for Epoxy+Al thenPVC+CB and the less value was for Epoxy + E-glass .

تم في هذا البحث دراسة تأثير الماء على بعض الخصائص الفيزياوية والميكانيكية (الخشونة،الصلادة، متانة الانضغاط) اضافة الى حساب معامل الانتشار باستخدام قانون فك الثاني، لموادمتراكبة ذات اساس بوليمري مختلف (البولي كلوريد الفانيل مع اسود الكربون، الايبوكسي معمسحوق الالمنيوم والايبوكسي مع الياف الزجاج المتقطعة) وبكسر حجمي % 30 لكل منهم،اظهرت النتائج التأثير السلبي الواضح للماء على هذه الخواص وقد تفاوتت بين نموذج واخرتأثر بشكل اكبر يليه الايبوكسي مع الياف الزجاج ثم (PVC+C.B) حيث ان النموذج الاولفكان، نموذج (D) الايبوكسي مع مسحوق الالمنيوم وللخواص كافة. اما معامل انتشار الماءالايبوكسي مع مسحوق الالمنيوم اقل امتصاصية للماء يليه البولي كلوريد الفانيل مع اسودالكربون واقلهم تأثرًا كان الايبوكسي مع الياف الزجاج المتقطعة.

Keywords


Article
Comparative Study of Mechanical Properties of MWCNTS/Epoxyand SWCNTS/Epoxy Composites

Authors: Khansaa D. Salman --- Sameir A. Aziez --- Aqeel H. Alwan
Journal: Journal of University of Babylon مجلة جامعة بابل ISSN: 19920652 23128135 Year: 2018 Volume: 26 Issue: 5 Pages: 28-42
Publisher: Babylon University جامعة بابل

Loading...
Loading...
Abstract

The single – walled carbon nanotubes (SWCNTs) and multi – walled carbon nanotubes (MWCNTs) embedded into resin matrix with different weight concentrations ranging about (0.1, 0.3, 0.5 and 1 wt. %), the nanocomposites are synthesized by casting method. The main applications of this nanocomposites are in the sensors, actuators, radar. Mechanical tests were done for this study such as: tensile test, bending test and hardness test. Also many examinations were utilized to define the microstructure like scanning electron microscopy (SEM), X-ray diffraction and Raman spectroscopy.The results of this work showed that obviously an improvement in mechanical properties of the processed nanocomposites such as young’s modulus, ultimate tensile strength, bending strength and Shore hardness. Also the micrographs of SEM demonstrated that SWCNTs and MWCNTs homogeneously dispersed into epoxy. On the other hand Raman spectra and XRD revealed that same results for SEM.Finally all the results for mechanical properties and microstructure evaluation show that SWCNTs give extremely higher values and properties than MWCNTs.

تم دمج انابيب كاربونية نانوية احادية الطبقة وانابيب كاربونية نانوية متعددة الطبقات مع الايبوكسي وبتراكيز وزنية مختلفة تتراوح بحدود (0.1, 0.3, 0.5, 1 wt. %) وقد تم تصنيع هذه المادة النانوية بطريقة السباكة. من اهم التطبيقات لهذه المادة النانوية المركبة هي في المتحسسات, المشغلات والرادارولهذه الدراسة اجريت العديد من الاختبارات الميكانيكية مثل: اختبار الشد ، اختبار الانحناء والصلادة. كذلك تم استخدام العديد من الفحوصات لتحسين البنية المجهرية مثل الفحص بالمجهر الالكتروني الماسح ، الفحص بحيود الاشعة السينية والفحص بمطياف رامان. وقد اظهرت نتائج هذا العمل ان هناك تحسن واضح في الخواص الميكانيكية للمادة النانوية المركبة مثل معامل يونك ، مقاومة الشد القصوى ، مقاومة الانحناء وصلادة شور.وقد اظهرت الصور المجهرية المؤخوذة بالمجهر الالكتروني الماسح ان الانابيب الكاربونية احادية الطبقة والمتعددة الطبقات قد تم تشتيتها بشكل متجانس في الاليبوكسي. من ناحية اخرى اظهرت نتائج الفحص بمطياف رامان وحيود الاشعة السينية نفس النتائج المجهر الالكتروني الماسح. اخيرا قد اظهرت جميع نتائجالخواص الميكانيكية والبنية المجهرية بأن الانابيب الكاربونية احادية الطبقة تعطي نتائج افضل من نظيرتها ذات الانابيب الكاربونية المتعددة الطبقات.


Article
STUDYING THE MECHANICAL PROPERTIES OF UNSATURATED POLYESTERS - B4C SYSTEM
دراسة الخواص الميكانيكية لنظام بولي استر غير المشبع - كاربيد البورون

Loading...
Loading...
Abstract

In this investigation, the composite material was prepared which was consist of polyester as the matrix and B4C as additive material with grain size equal to25μm with different weight fractions (10%,20%,30%,40%,50%). This investigation was done into two stages: the first stage is to produce the composite material, while the second stage is to test the new material which includes tensile test, hardness and microstructure evaluation. Also photomicrographs were taken by ordinary microscope. The results showed that obviously improvement in properties of the new composite material especially at weight fraction of (40% , 50%).

تم في هذا البحث تحضير مادة متراكبة هجينية ذات اساس بوليميري بطريقة الصب.تتكون المادة المتراكبة من راتنج البولي استر غير المشبع كمادة اساس وكاربيد البورون كمادة مدعمة وبحجم حبيبي mμ25 وبكسور وزنية 50%,40%, 30%, 20%, 10%)). تم اجراء البحث على مرحلتين: المرحلة الاولى: تصنيع المادة المتراكبة اما المرحلة الثانية فقد أجريت اختبارات عديدة على المادة الجديدة تضمنت اختبار الشد والصلادة والبنية المجهرية. كذلك تم تصوير العينات باستخدام المجهر الضوئي الاعتيادي. أظهرت النتائج تحسناً واضحاً في خواص المادة المتراكبة الجديدة وخاصة عند الكسور الوزنية %40 و%50.


Article
Effect of Laser Surface Treatment on Some Mechanical Properties of Low Carbon Steel
أثرالمعاملة السطحية الليزرية على بعض الخواص الميكانيكية للفولاذ منخفض الكاربون

Authors: Asaad K. Hamza اسعد خضير حمزة --- Enaam O.Hasuon انعام عبيد حسون --- Khansaa D. Salman خنساء داؤود سلمان
Journal: Engineering and Technology Journal مجلة الهندسة والتكنولوجيا ISSN: 16816900 24120758 Year: 2012 Volume: 30 Issue: 12 Pages: 271-283
Publisher: University of Technology الجامعة التكنولوجية

Loading...
Loading...
Abstract

This research aims to study the effect of localized laser surface treatment onmechanical behavior of low carbon steel. Laser Cw Nd : YAG was used in thetreatment hardening of the specimens for different laser energy (2.7,3.3,4.37100J ),with time interval for the beam (10-2 sec) and the laser intensity(4500,5500,7100Watt/mm2) . Different mechanical tests were achieved Static and Dynamic on thespecimens which were surface treated .Static tests included ( Tensile test,Microhardness test) ,While the dynamic test included (Impact test ).The results show that the mechanical properties for low carbon steel H[.hxstrength by(0.9,10,25.5%) , ultimate tensile strength by(6.4,16.24,24.59%),while theincrement fracture stress by (12,17.28,34.87%),also increment in microhardness by(3.4, 5 , 23% )and toughness by (4.3,10.86,20.8 %). Some of mechanical propertiesfor low carbon steel reduce with increasing in laser energy which show in Youngmodulus (26.06,40.89,50.8%), Rigidity modulus by (25,40.5,48.99 %) , Poisson s,ratio (1.29,2.34,3.69%) .

يهدف البحث الى دراسة تأثير المعاملة الموقعية (السطحية ) بأستخدام الليزر على الخواصCw Nd : YAG الميكانيكية للفولاذ منخفضالكاربون . وقد تم أستخدام ليزرنيديميوم - ياك المستمرفي معالجة العينات المستخدمة في البحث مستخدمين متغيرات تضمنت طاقة ليزرية مختلفة.( 10-2 ) وشدة ليزرية 4500,5500,7100 Sec) 2.7,3.3,4.3 ) وفترة زمنية لكل حزمة ليزرية J)وقد أجريت اختبارات ميكانيكية ساكنة ومقترنة بالحركة تضمنت الساكنة Watt/mm 2)منها فحصي الشد والصلادة أما المقترنة بالحركة فتركزت على فحص الصدمة .وقد أظهرت النتائجأن الخواص المیكانیكیة للفولاذ منخفض الكاربون تطورت بزی ادة قیم ة طاق ة اللیزرحی ث س جلتمق اومة الخض وع ارتفاع ا بمق دار (% 0.9,10,25.5 ) ومقاوم ة الش د القص وى6.4,16.24,24.59% )أما أجھاد الكسر فقد سجل أرتفاعا بمقدار(% 12,17.28,34.87 )، كما )حقق ت الص لادة الدقیق ة أرتفاع ا بمق دار (% 3,4,5.23 ) والمتان ة بمق دار , 4.3,10.86 20.8% ) وتق ل بع ض الخ واص المیكانیكی ة للف ولاذ منخف ض الكارب ون بزی ادة طاق ة )، ( اللی زرحیث أتض ح ذل ك ف ي معام ل المرون ة, (% 26.06,40.89,50.8( معامل الجساءة (% 25,40.5,48.99 ) ،نسبة بواصون(% 1.29,2.34,3.69

Keywords

Listing 1 - 4 of 4
Sort by
Narrow your search

Resource type

article (4)


Language

Arabic (2)

English (2)


Year
From To Submit

2018 (1)

2014 (1)

2012 (1)

2008 (1)