Article
SYNTHESIS AND CHARACTERIZATIONS OF SILVER NANO PARTICLES USING CHEMICAL REACTION METHOD
تحضير وتشخيص الفضة النانوية بالطريقة الكيمياوية وبدرجات حرارية مختلفة

Author: Khitam S. Shaker ختام سالم شاكر
Journal: DIYALA JOURNAL OF ENGINEERING SCIENCES مجلة ديالى للعلوم الهندسية ISSN: 19998716/26166909 Year: 2016 Volume: 9 Issue: 1 Pages: 113-120
Publisher: Diyala University جامعة ديالى

Loading...
Loading...
Abstract

In the present investigation colloidal silver nanoparticles was prepared by chemical reaction method from silver nitrate (AgNO3) and sodium citrate (Na3C6H5O7) in water. The preparation method were achieved at three levels of temperature (100, 150 and 200℃) the produced silver nanoparticles characterize by UV-vis Visible Spectroscopy, Scanning Electron Microscopy (SEM) and Particle Size analyzer the result of particle size analyzer show that their size distribution to lie in the range of (58.9 -202) nm. The results show that silver nanoparticles are 58.9, 76.4 and 202 nm at temperatures of (100, 150, 200) ℃, respectively can be produced.

تم الحصول على الفضة النانوية الغروية من خلال طريقة التفاعل الكيميائي باختزال نترات الفضة من قبل سترات الصوديوم (Na3C6H5O7) في الماء .وشخصت الفضة النانوية التي حصل عليها بطريقة التحليل الطيفي للأشعة فوق البنفسجية ، المجهر الإلكتروني (SEM)، وقيست الفضة النانوية بواسطة استخدام جهاز محلل حجم الجسيمات وتوزيع حجمها لقد تبين ان الحجم الحبيبي يقع بين(58.9 -202) نانومتر. وتشير النتائج إلى أن معدل جزيئات الفضة المحضرة يتراوح ما بين (58.9، 76.4 و 202 ) نانومتر عند درجات حرارة (100، 150، 200) م∘ و على التوالي.


Article
Synthesis and Characterization Nano Structure of MnO2 via Chemical Method

Authors: Khitam S. Shaker --- Alyaa H. AbdAlsalm
Journal: Engineering and Technology Journal مجلة الهندسة والتكنولوجيا ISSN: 16816900 24120758 Year: 2018 Volume: 36 Issue: 9 Part (A) Engineering Pages: 946-950
Publisher: University of Technology الجامعة التكنولوجية

Loading...
Loading...
Abstract

In the current research, Magnesium oxide II (MnO2) nanostructures were prepared by chemical route from hydro manganese chloride salt using Potassium hydroxide as reducing agent. X-Ray diffraction (XRD), SEM and Fourier transformation infrared (FTIR) used to characterize both particle size and structure of MnO2 nanoparticles. XRD results confirmed impurity of synthesized powder with α-MnO2 as predominant phase. The average particle size of manganese dioxide was in the range 25- 30 nm. Photographs of scanning electron microscope (SEM) showed two hierarchical structures, cluster agglomeration and chain appearance.


Article
The Influence of Operation Conditions on the Permeative Flux of (PVC/PS) Hollow Fiber Membrane
تاثیر ظروف الغشاء على الجریان التنافذي للغشاء اللیفي المجوف ( PVC/PS)

Authors: Qusy F.Alsalhy --- Jamal M.Ali --- Khitam S.Shaker
Journal: Engineering and Technology Journal مجلة الهندسة والتكنولوجيا ISSN: 16816900 24120758 Year: 2012 Volume: 30 Issue: 16 Pages: 2767-2777
Publisher: University of Technology الجامعة التكنولوجية

Loading...
Loading...
Abstract

Membranes have gained an important place in chemical technology and are usedin a wide range of applications. This investigation has studied the effect of operatingconditions such as temperature, trans-membrane pressure and solute concentrationon the separation performance of (PVC/ PS) hollow fiber membrane, which wasprepared in the laboratory from 15% (PVC) and 2% (PS) using phase inversionmethod. An attempt was done to investigate the ability of PVC/PS hollow fibermembrane for ultrafiltration application. A (PVP) solute was used to measure (PVP)rejection of prepared membrane.The predicted flux was found to increase from (18.88 l/m2.hr) to 33.05 l/m2.hr)when the operation temperature was increased from (10Ž) to (30Ž).While itincreased from (28.57 l/m2.hr) to (263.36 l/m2.hr) when the operation pressure wasincreased from (1bar) to (3bar). It was also found to decrease from(17.97 l/m2.hr) to(12.20 l/m2.hr) with increase solute concentration from (1000ppm) to (2500ppm).The rejection efficiency was equal to (99.93%) when using (2500ppm) solute. Thisis considered within UF range.

الاغشیة تكسب مكانة مھمة في تقنیة الكیمیاویة وتستعمل في مدى واس ع م ن التطبیق ات . یتض منھذا البحث درسة تاثیر الظروف التشغیلیة مثل درجة الحرارة والضغط وتركیز المحل ول عل ى اداة% وبنسبة 15 (PVC) اللیفي المجوف والذي تم تحضیرة في المختبر من (PVC /PS) عمل اشغءةبسنب 2% باستخدام طریقة الطور الانعكاسي .وایضا في ھذا العمل تم دراسة قابلیةاستعمال (PS) وكم ادة مذاب ة لغ رض قی اس كف اءة PVP ت م اس تخدام . (UF ) الغشاء اللیفي المجوف في تطبیقات الاللیفي المجوف . لقد وجد ان نفاذی ة الت دفق ازداد (PVC /PS) من قبل غشاء (PVP) الارجاع لل 75 ) بزی ادة درج ة الح رارة م ن (℃ 10 ) ال ى (℃ L/m2.hr) 18.88 ) ال ى L/m2.hr) م ن263 ) م ع زی ادة . 36 L/m2.hr ) 28.57 ) ال ى L/m2.hr) 30 ) وك ذلك ازداد نفاذی ة الت دفق م ن17.54 ) ال ى L/m2.hr) 3 ) ولك ن نفاذی ة الت دفق یق ل م ن bar) 1 )ال ى bar) الض غط م ن25000 ( ) كفاءة الفصل ppm الى (ppm مع زیادة تركیز المذاب من )( 1000 (L/m2.hr) 12.20.(UF) 2500 ) وھذا یعتبر ضمن المدى التطبیقي لل ppm) تساوي (% 99.93 ) باستخدام


Article
Behavior of A.C conductivity and Complex dielectric constant of ZnS Thin Films
سلوك التوصيلية الكهربائية AC وثابت العزل الكهربائي للاغشية لكبريتيد الخارصين الرقيقة ZnS

Authors: Zainab Taha A --- Khitam S. Shaker --- Suaad S. Shaker --- Raghdaa Hameed Hani
Journal: Engineering and Technology Journal مجلة الهندسة والتكنولوجيا ISSN: 16816900 24120758 Year: 2015 Volume: 33 Issue: 4 Part (B) Scientific Pages: 745-752
Publisher: University of Technology الجامعة التكنولوجية

Loading...
Loading...
Abstract

The effect of temperature on dielectric properties of the prepared ZnS thin films by chemical bath deposition at film thickness (200) nm deposited at substrate temperature 333 K, was measured at frequency range (0.04-10 MHz) in the temperature range (298- 473) K .The temperature – dependent of electrical conductivity, the real and imaginary parts of the complex dielectric constant are calculated at the selected frequencies. The frequency exponent n, and the activation energy, Ea, are determined. The a.c. conduction mechanism of ZnS films has been explained on the basis of hopping of charge carriers.

تأثير درجة الحرارة على خصائص العازلة للكهربائيةللأغشية الرقيقة ZnSالمرسبة بطريقة الترسيب الحمام الكيميائيلغشاء ذات سماكة (200) نانومتر ومرسب على ركيزة في درجة حرارة 333 K، تم القياس في مدى التردد (0،04 حتي 10 ميغاهيرتز) في نطاق درجات الحرارة (298- 473 ) K. تم حساب درجة الحرارة -المعتمدةعلى التوصيلية الكهربائية، والأجزاء حقيقية والخيالية لثابت العزل الكهربائي المعقد في ترددات محددة. كما وتم تحديد مركبة التردد، وطاقة التنشيط،. تم توضيح ميكانكية التوصيل الكهربائي المتناوب للاغشية الرقيقة على أساس التنقل من حاملات الشحنة.

Listing 1 - 4 of 4
Sort by
Narrow your search

Resource type

article (4)


Language

English (4)


Year
From To Submit

2018 (1)

2016 (1)

2015 (1)

2012 (1)