Article
The combined effect of rapid solidification and phosphor addition on the microstructure of hypereutectic A390 alloys.

Author: Lamyaa Mahde Asaad
Journal: Journal Of Wassit For Science & Medicine مجلة واسط للعلوم والطب ISSN: 58161992 Year: 2012 Volume: 5 Issue: 1 Pages: 190-199
Publisher: Wassit University جامعة واسط

Loading...
Loading...
Abstract

The influence of the combined effect of rapid solidification and phosphor addition on the morphology of primary silicon particles in A390 Al-Si alloy has been investigated by using light optical microscope (LOM). The P as modifier element was added in the shape of copper phosphor (Cu3P) master alloy.The results show that as the solidification rate increases, the size of primary silicon particles in A390 alloy reduces and the morphology of these particles evolve from plate-like to the fine nodular shape. The rapid solidification has a significant improvement on the refining performance of P to modify and refine the primary Si particles in A390 alloy. It is suggested that the refining performance of P in Cu3P master alloy is related to the formation the AlP particles which act as a heterogeneous nucleation. This affects the solidification rate and restricts the Si phase's growth.

تم في هذاالبحث دراسة التاثير المشترك للتصلب السريع مـع اضافةالفسفور في تركيبة جزيئات السليكون الاولية في سبيكةالالمنيوم- سليكون A390 Ai _SI))باستخدام المجهرالضوئـي (LOM)تم اضافةالفسفور كعنصر معدل بشكل سبيكة نحاس- فسفـور (Cu3P)القياسية.اظهرت النتائج بان عندزيادةمعدل التصلب فان حجم جزيئات السليكون الاولية يقل وان تركيبة هذه الجزيئات تتحول من الشكل الصفائحي الى الشكل الكروي .كما ان للتصلب السريع تحسين افضل في اداء تنعيم الفسفورلتعديل وتنعيم جزيئات السليكون الاولية في سبيكة A390 .واقترح ان كفاءة تنعيم الفسفور في سبيكة Cu3Pالقياسية تعودالى تكوين جزيئات (AlP)التي تقوم بالتنويةالغيـر متجانسة وهذايؤثرعلى معدل التصلب ويحدد من نموطور السليكون.

Keywords


Article
Influence of Titanium & Carbon Additions on the Phosphorous Modification Efficiency in Near Eutectic Al–14Si alloy

Authors: Talib Abdulameer Jasim --- Lamyaa Mahde Asaad
Journal: Journal of University of Babylon مجلة جامعة بابل ISSN: 19920652 23128135 Year: 2013 Volume: 21 Issue: 3 Pages: 919-926
Publisher: Babylon University جامعة بابل

Loading...
Loading...
Abstract

The influence of Titanium (Ti) & Carbon (C), as gray cast iron master alloy, additions on the structure modification efficiency of the phosphorous (P) in near eutectic Al–14Si alloy and the nucleating mechanism was studied in this work. The results show that the phosphorous modification efficiency can be significantly affected by this addition and the sizes of the primary Si particles can be obviously refined after the addition of trace Ti&C. Micro probe Analyzer (MPA) shows there is a coupling of aluminium phosphides (AlP) and Al4C3 particles in the center of primary Si. Moreover, the nucleation mechanism of primary Si by like-peritectic coupling of AlP and Al4C3 was presented. The formation mechanism of like-peritectic coupling of these particles was also discussed.

في هذا البحث تمت دراسة تاثير اضافة التيتانيوم والكربون،على شكل حديد الزهر الرمادي كسبيكة اشابة، على كفائة الفوسفور في تعديل البنية البلورية لسبيكة الالمنيوم- %14سليكون، كما تم ايضا دراسة سلوك التنوية لهذه السبيكة. لقد اظهرت النتائج بان كفائة تعديل الفوسفور للبنية البلورية تتاثر كثيرا بهذه الاضافة وان الحجم الحبيبي لدقائق السليكون الاولي تاثر هو الاخر بشكل ملحوظ باضافة التيتانيوم والكربون. ويظهرمجس التحليل المايكروي (MPA) ان هناك ارتباط بين دقائق فوسفيد الالمنيوم ودقائق كربيد الالمنيوم في مركز حبيبة السليكون الاولي. علاوة على ذلك فقد تم عرض الية تخليق دقائق السليكون الاولي بواسطة مزدوج شبه بيرتكتك لفوسفيد وكربيد الالمنيوم (AlP and Al4C3. تم ايضا مناقشة الية تكوين مزدوج شبيه البيرتكتك لتلك الدقائق.