Factors Affecting the Relationship Between Total Porosity and Electrical Resistivity for Concrete Repair Materials
العوامل المؤثره على العلاقه بين المساميه الكليه والمقاومه الكهربائيه في مواد اصلاح الخرسانه.

Author: Maan Salman Hassan
Journal: Engineering and Technology Journal مجلة الهندسة والتكنولوجيا ISSN: 16816900 24120758 Year: 2008 Volume: 26 Issue: 8 Pages: 1016-1024
Publisher: University of Technology الجامعة التكنولوجية

Loading...
Loading...
Abstract

The paper examines the properties of five different types of repair and substratematerials, including conventional mortar, fly ash mortar, silica fume mortar, conventionalconcrete substrate, and high-performance concrete substrate materials. Assessment wascarried out on the basis of some physical properties (total porosity, and electrical resistivity).These properties were measured at early age and later after 14 weeks of exposure conditionsto 6 % (by weight) of sodium chloride solution to simulate typical marine environment.The results show that the electrical resistivity and total porosity measurements appearto be related and the measurements obtained are affected by the pore structure of thematerials. It is also expresses that if a material has grater proportion of coarse aggregates (e.g.the substrate concrete in this study) it will appear to have a lower porosity although theporosity of mortar surrounding the aggregates could be higher. This makes comparisonsbetween materials containing different aggregates proportions and size difficult.

تهتم هذه الدراسه باختبار صفات خمسة مواد مختلفه بعضها يستخدم كمونه في اصلاح الاضرار فيالمنشات الخرسانيه وبعضها يمثل الخرسانه المتضرره ذاتها. أشتملت المواد قيد الدراسه على مونه تقليديه ,مونه باستعمال رماد وقود متطاير, مونة السليكا, خرسانه تقليديه , وخرسانه عالية الاداء . أن الصفاتالفيزيائيه التي تم اختبارها هي المساميه والمقاومه الكهربائيه. وقد تم حساب قيم هذه الصفات في عمر مبكروكذلك بعد 14 اسبوع من التعرض الى السائل الملحي الذي يحتوي على 6% وزنا من كلوريد الصوديوموذلك لمحاكاة الظروف البحريه.بينت النتائج وجود علاقه واضحه بين المساميه والمقاومه الكهربائيه, وان هذه النتائج تتأثر بالهيكلالمسامي للمواد. كما بينت النتائج ايضا ان المواد التي تحتوي على نسبة ركام خشن اكثر (حصى) كما هوالحال في الخرسانه تكون قيم المساميه فيها اقل على الرغم من ان المسافات البينيه المحيطه بحبيبات الركامالخشن تكون اكثر مساميه وهذا يجعل المقارنه بين المواد الخرسانيه التي تحتوي على تدرجات ونسب مختلفهمن الركام الخشن صعبه.


Article
Mechanical Performance of CO2 and Autoclave Cured Date Palm Fiber Reinforced eco-mortar Composites

Authors: Maan Salman Hassan --- Wahad Marwan Salih
Journal: Engineering and Technology Journal مجلة الهندسة والتكنولوجيا ISSN: 16816900 24120758 Year: 2016 Volume: 34 Issue: 14 Part (A) Engineering Pages: 2754-2765
Publisher: University of Technology الجامعة التكنولوجية

Loading...
Loading...
Abstract

Using nature waste fibers in construction industries had shown important character "environmental friendly" which paid a great interest around the world. The aim of this paper was to investigate the suitability of agriculture waste date palm fibers as lignocellulosic materials for the production of wood-cement composite, in addition to enhance their compatibility with cement using accelerated curing like carbonation or autoclave.Three percentages of date palm fibers were used (2, 6, and 10)% by weight of cement in cement composites specimens. Compressive, flexural and direct tension strengths were examined as strength properties and X-ray diffraction (XRD) as microstructure properties. The results show that carbonation curing was the most effective curing for compressive strength property while autoclave curing leads to better performance in flexural strengths. Curing type effects on direct tension property were fluctuated. This could be attributed to the variation in cellulose fiber roles with respect to each property evaluated. X-ray diffraction confirmed that CO2-curing led to increased CaCO3 content compared with autoclaved composites.


Article
Strength Evaluation of CO2-Cured Cellulose Date Palm Fiber Reinforced Cementitious Boards

Authors: Maan Salman Hassan --- Shakir Ahmed Salih --- Isam Mohamad Ali
Journal: Engineering and Technology Journal مجلة الهندسة والتكنولوجيا ISSN: 16816900 24120758 Year: 2016 Volume: 34 Issue: 6 Part (A) Engineering Pages: 1029-1046
Publisher: University of Technology الجامعة التكنولوجية

Loading...
Loading...
Abstract

In recent years there has been an increasing demand to recycle wastes produced by the agricultural and industrial processing. The aim of this paper is to investigate the suitability of date palm (Phoenix dactylifera) as lignocellulosic materials for the production of wood-cement composite boards, in addition to enhance their compatibility with cement using physical pretreatment processes and accelerated carbonation curing. Experiments were performed to assess the physical properties (as density, flexural strength, toughness and E-modulus), and micro structural properties (as determined by scanning electron microscopy) of the produced cement boards. The results show an improvement in the physical and microstructural properties of cellulosic fiber-cement composites by using accelerated CO2 curing method. In addition, excessive carbonation rate associated with pure gas carbonation does not necessarily lead to high strength and even detrimental strength development was found, which was shown by cement paste.


Article
Some Durability Characteristics of Micro Silica and Nano Silica Contained Concrete

Authors: Mohammed Salah Nasr --- Shakir Ahmed Salih --- Maan Salman Hassan
Journal: Journal of University of Babylon مجلة جامعة بابل ISSN: 19920652 23128135 Year: 2016 Volume: 24 Issue: 4 Pages: 980-990
Publisher: Babylon University جامعة بابل

Loading...
Loading...
Abstract

This paper aims to investigate the influence of replacement of cement with nano and micro silica admixtures on some durability properties of concrete such as water absorption, chloride content and pH tests. Three replacement ratios (5%,10%,15%) of micro silica and four replacement proportions (0.5%,1.5%,3%,5%) for nano silica were used in this study. Two exposure conditions were considered for chloride content test: wetting-drying and full immersing exposure in 6% of chloride ions solution, NaCl type.Results showed that mixes of %5 micro silica and 5% nano silica had lower content of chloride (about 0.19% and 0.18%) for wetting-drying and full immersing exposure respectively. For water absorption test, all mixes incorporated micro and nano silica, except for %5 micro silica mix, showed lower absorption than control mixes. For pH test, results indicated that the adding of nano and micro silica didn’t affect adversely the alkalinity of concrete

تهدف هذه الدراسة الى التحري عن تأثير استبدال السمنت بمضافات النانو والمايكرو سليكا على بعض خواص الديمومة للخرسانة مثل امتصاص الماء، محتوى الكلوريد و فحص القاعدية. تم استخدام ثلاث نسب استبدال (%5،10%،15%) للمايكرو سليكا واربع نسب استبدال (%0.5،%1.5،%3،5%) للنانو سليكا. تم اعتماد اسلوبي تعرض لفحص محتوى الكلوريد: تجفيف-ترطيب وغمر كلي في محلول 6% ايونات الكلوريد، نوع كلوريد الصوديوم.اظهرت النتائج بان الخلطات 5% مايكرو سليكا و5% نانو سليكا امتلكت اقل محتوى كلوريد ( حوالي 0.19% و 0.18 %) لأسلوبي التعرض تجفيف-ترطيب وغمر كلي على التوالي. بالنسبة لفحص الامتصاص، فان نتائج جميع الخلطات الحاوية على مايكرو ونانو سليكا، عدا الخلطة 5% مايكرو سليكا, اظهرت امتصاص اقل من الخلطات المرجعية. بالنسبة لفحص درجة القاعدية, فقد اشارت النتائج بان اضافة النانو والمايكرو سليكا لم تؤثر سلبيا على قاعدية الخرسانة.


Article
“Effect of Polypropylene Fibers on Producing Sustainable Accelerated Hardened Cementitious Materials”
تأثير ألياف البولي بروبلين في أنتاج مواد أسمنتية مستدامة سريعة التصلب

Authors: Ziyad Majeed Abed --- Maan Salman Hassan --- Rana Hameed Faisal
Journal: journal of kerbala university مجلة جامعة كربلاء ISSN: 18130410 Year: 2018 Volume: 16 Issue: 2 Pages: 150-159
Publisher: Kerbala University جامعة كربلاء

Loading...
Loading...
Abstract

The aim of this research is to produce environmental friendly cementitious materials using polypropylene fibers as recyclable reinforcement materials and silica fume (side-product in manufacturing of ferro-silicon alloys and silicon metal) material. The manufacturing process includes using accelerating curing with carbon dioxide for the fresh cementitious mixtures to decrease setting time and improve hardening, particularly in precast concrete plants.Mix proportions used in this research were cement: silica fume: Sand (1: 0.75: 1.3) and 0.5 w/c ratio. Also, four percentages of polypropylene fibers are used (0, 0.3, 0.9, and 1.5%) by weight of cement. All specimens are exposed to 100% of carbon dioxide gas concentration for 2 hours. Compressive, flexural, and direct tensile strengths have been tested at 7 and 28 days. The results show a significant improvement of flexural strength and direct tension for specimens. The increasing percentages of flexural strength and direct tension with (1.5% polypropylene) compared with control mixture at age 28 days were about (+ 28%) and (+ 117%) respectively.

ان الهدف الرئيسي في هذا البحث هو انتاج مواد سمنتية صديقة للبيئة باستعمال الياف البولي بروبلين كمواد تسليح قابلة لاعادة الاستعمال وكذلك مادة غبار السيليكا (منتج ثانوي في صناعة سبائك الحديد والسيليكون ومعدن السليكون). ان عملية التصنيع تتضمن الانضاج المعجل باستعمال ثنائي اوكسيد الكربون للخلطات السمنتية الطازجة من اجل تقليل زمن التجمد وتحسين التصلب وخصوصا في معامل الخرسانة مسبقة الصب .نسب الخلط المستعملة في هذا البحث هي سمنت: سيليكا فيوم :رمل ( 1.3 : 0.75 : 1) ونسبة الماء الى السمنت هي 0.5 .اضافة الى ذلك، تم استعمال اربع نسب من الياف البولي بروبلين هي (0,0.3,0.9,1.5 )% من وزن السمنت. تم تعريض كل النماذج الى غاز ثنائي اوكسيد الكربون وبتركيز 100% ولمدة ساعتين . تم فحص مقاومة الانضغاط , الانثناء, والشد المباشر بعمر 7 و 28 يوم . بينت النتائج تحسن ملحوظ في مقاومة الانثناء والشد المباشر للنماذج .نسب الزيادة في مقاومة الانثناء والشد المباشر باستخدام نسبة (1.5% بولي بروبلين) مقارنة مع الخلطة المرجعية وبعمر 28 يوم كانت حوالي (+28%)و(+117%) على التوالي .

Listing 1 - 5 of 5
Sort by
Narrow your search

Resource type

article (5)


Language

English (5)


Year
From To Submit

2018 (1)

2016 (3)

2008 (1)