Effect of Laser Irradiation on the Optical Properties of SnO2 films Deposited by Post Oxidation of metal Films
تأثير أشعة الليزر على الخصائص البصرية لأغشية SnO2 المرسبة بطريقة الأكسدة اللاحقة لأغشية المعدن

Authors: Najwa J. Jubier نجوى جاسم جبر --- Majida A.Ameen ماجدة علي أمين --- Souad G. Khalil سعاد غفوري خليل
Journal: Baghdad Science Journal مجلة بغداد للعلوم ISSN: 20788665 24117986 Year: 2011 Volume: 8 Issue: 4 Pages: 962-967
Publisher: Baghdad University جامعة بغداد

Loading...
Loading...
Abstract

Tin oxide films (SnO2) of thickness (1 m) are prepared on glass substrate by post oxidation of metal films technique. Films were irradiated with Nd:YAG double frequency laser of wavelength (532 nm) pulses of three energies (100, 500, 1000) mJ. The optical absorption, transmission, reflectance, refractive index and optical conductivity of these films are investigated in the UV-Vis region (200-900) nm. It was found that the average transmittance of the films is around (80%) at wavelength (550 nm) and showed high transmission ( 90 %) in the visible and near infrared region. The absorption edge shifts towards higher energies, which is due to the Moss-Burstien effect and it lies at (4 eV). The optical band gap increased with increasing of energy.

حضرت أغشية أوكسيد الخارصين (SnO2) بسمك (1 m) على قواعد من الزجاج بطريقة الأكسدة اللاحقة لأغشية المعدن Sn. تم تشعيع الأغشية بنبضات ليزر Nd:YAG ذو التردد المزدوج عند الطول الموجي (532 nm) وبثلاث طاقات (100, 500, 1000)mJ. درست الامتصاصية البصرية، النفاذية، الانعكاسية، معامل الانكسار و التوصيلية البصرية لهذه الأغشية في منطقة UV-VIS ذو المدى (200-900) nm. وجد ان معدل النفاذية لهذه الأغشية تقترب من (80 %) عند الطول الموجي (550 nm) وان اعلى نفاذية تقترب من (90 %) في المدى المرئي وتحت الحمراء القريبة. حافة الامتصاص تزحف نحو الطاقات العالية التي تعزى الى تأثير بيرشتاين-موس وتقع في المدى (4 eV). ان فجوة الطاقة البصرية تزداد عند زيادة طاقة اشعاع الليزر.


Article
Annealing Effect on the phase Transformation in
دراسة تأثير التلدين في التحولات الطورية لأوكسيد التيتانيوم

Authors: Anwar A. Baker أنوار علي باقر --- Asmaa J. Khadum أسماء جواد كاظم --- Majida A. Ameen ماجدة علي أمين
Journal: Baghdad Science Journal مجلة بغداد للعلوم ISSN: 20788665 24117986 Year: 2011 Volume: 8 Issue: 2عدد خاص بمؤتمر الفيزياء Pages: 503-508
Publisher: Baghdad University جامعة بغداد

Loading...
Loading...
Abstract

This work describes the effect of temperature on the phase transformation of titanium dioxide (TiO2) prepared using metal organic precursors as starting materials. X-ray diffraction (XRD) was used to investigate the structural properties of TiO2 gels calcined at different temperatures (300, 500, 700) C. the results showed that the samples have typical peaks of TiO2 polycrystalline brookite nanopowders after calcined at (300 C), which confirmed by (111), (121), (200), (012), (131), (220), (040), (231), (132) and (232) diffraction peaks. Also, XRD diffraction spectra showed the presence of crystallites of anatase with low proportion of rutile phase where calcined at (500 C), while rutile phase domains at (700 C). The crystallite size of TiO2 nanopowders was calculated by Scherer's formula and showed that the crystallite size decreased and then increased with increasing the annealing temperature.

يدرس هذا البحث تأثير درجة الحرارة في التحول الطوري لأوكسيد التيتانيوم المحضر باستعمال المواد العضوية الفلزية كمواد أولية. أُستعملت تقنية حيود الأشعة السينية (XRD) لدراسة الخصائص التركيبية لجل TiO2 بعد حرقها بدرجات حرارة مختلفة (300, 500, 700) C. بينت النتائج بأن للعينات التركيب المتعدد التبلور لمادة TiO2 وبطور البروكايت عند حرقها بدرجة (300 C)، تمثلت بقمم الانعكاس (111)، (121)، (200)، (012)، (131)، (220)، (040)، (231)، (132) و (232). أظهرت أطياف حيود الأشعة السينية ايضاً وجود بلورات من الاناتيس مع نسبة قليلة من طور الروتايل بعد حرقها بدرجة (500 C)، بينما يسود طور الروتايل على التركيب البلوري عند درجة حرارة (700 C). حُسب الحجم البلوري لحبيبات TiO2 الدقيقة التركيب بواسطة معادلة شرر (Scherer) وتبين ان الحجم البلوري يقل ثم يزداد بزيادة درجة حرارة التلدين.