Bi2-Xhgxsr2-Ybaycacu2o8/Ag Sheath HTSC Wires, (Hg, Ba) Substitution Effect on the Critical Temperature

Authors: Akram R. Jabur --- Matti N. Makadsi --- Mohammed S.Mehde
Journal: Engineering and Technology Journal مجلة الهندسة والتكنولوجيا ISSN: 16816900 24120758 Year: 2013 Volume: 31 Issue: 14 Part (A) Engineering Pages: 2650-2664
Publisher: University of Technology الجامعة التكنولوجية

Loading...
Loading...
Abstract

Bi2-xHgxSr2-yBayCaCu2O8 High Temperature Superconductor (HTSC) has beenprepared as a pellet by solid state reaction with a certain substitution percentages (0,0.05 ,0.1) of Hg and Ba substitution instead of Bi and Sr respectively . Then, HTSCwires were fabricated from the prepared superconductor pellets using powder in tube(PIT) method utilizing silver as the tube material. The prepared wires are of three types;with monofilament MOF, 9 multifilament core 9MF and 81 filaments core(81MF).Several cycles of mechanical drawing and rolling process performed to the startingsilver tube of 0.4 cm diameter and 5 cm length to minimize the filament diameter. Theaverage filament diameter with 81MFC wire was about 25μm measured with an opticalmicroscope.Tc critical temperature for superconductivity is measured for the pellets and wiresusing four point probes techniques. These results show that the substation Bi by Hggive a rise to the superconductor to improve highly Tc , while substitution Sr with Balowers Tc .substitution of 0.05 , 0.1 Hg to the composition Bi2-xHgxSry-2BayCa1Cu2O8will raise the transition temperature (Tc) . Also substitution of Sr by Ba decreases thetransition temperature (Tc), Hg( 0.05 – 0.1 ) substitution still raise Tc after substitutionof Ba with (0.05 – 0.1). low – Tc phase (2212) , 2201 phase in B-2212 system and theaddition of Ag to silver sheaths and a small amount of impurity phases appear in theresult of XRD analysis.


Article
Optical Investigations of CdSe1-x Tex Thin Films
الاستقصاء البصري لاغشيةCdSe1-xTex الرقيقة

Loading...
Loading...
Abstract

The alloys of CdSe1-xTex compound have been prepared from their elements successfully with high purity (99.9999%) which mixed stoichiometry ratio (x=0.0, 0.25, 0.5, 0.75 and 1.0) of (Cd, Se and Te) elements. Films of CdSe1-xTex alloys for different values of composition with thickness(0.5m) have been prepared by thermal evaporation method at cleaned glass substrates which heated at (473K) under very low pressure (4×10-5mbar) at rate of deposition (3A˚/s), after that thin films have been heat treated under low pressure (10-2mbar) at (523K) for two hours.The optical studies revealed that the absorption coefficient (α) is fairly high. It is found that the electronic transitions in the fundamental absorption edge tend to be allowed direct transition. It was also found that the optical energy gap vary non-linearly with composition (x) and have a minimum value at x=0.5 and increases after heat treatment.It is found that the optical constants vary non-linearly with composition, and the behavior inverse at x=0.5, and affected by heat treatment. The behavior of 1 is similar to the behavior of n, while the behavior of 2 is similar to the behavior of k.

تم تحضير سبائك المركب CdSe1-xTex بنجاح من عناصرها الأولية بنقاوة عالية (%99.9999) بخلط نسب العناصر (x = 0.0, 0.25, 0.5, 0.75, 1.0) من (Cd, Se, Te)، واستخدم تحليل مطياف الامتصاص الذري لمعرفة تركيز العناصر في السبيكة. وكذلك أجريت فحوصات حيود الأشعة السينية ولوحظ أن السبائك تملك تركيباً متعدد البلورات. حضرت أغشية رقيقة من سبائك CdSe1-xTex لقيم مختلفة من التراكيز بسمك (0.5μm) بطريقة التبخير الحراري على قواعد نظيفة من الزجاج المسخن بدرجة حرارة 473K تحت ضغط واطئ جدا (4×10-5mbar) بمعدل تبخير (ِs 3 A) وبعد ذلك تمت معاملة الأغشية حراريا تحت ضغط واطئ (10-2mbar) بدرجة حرارة 523K لمدة ساعتين.من الدراسة البصرية تبين أن قيم معامل الامتصاص (α) عالية بعض الشيء، ووجد ان الانتقالات الإلكترونية عند حافة الامتصاص الأساسية كانت من نوع الانتقال المباشر المسموح، وان فجوة الطاقة البصرية تتغير بشكل غير خطي مع التركيز (x) وتملك أوطأ قيمة لها عند x=0.5، وكذلك وجد أن فجوة الطاقة البصرية تزداد قليلا بعد المعاملة الحرارية.استخدم طيف النفاذية في إيجاد الثوابت البصرية (n, k, ε1, ε2)التي تم حسابها بوساطة طريقة سوانبل (Swanepoel) باستخدام النفاذية العظمى TM والنفاذية الصغرى Tm في تقنية الغلاف.وتبين ان الثوابت البصرية جميعها تتغير بشكل غير خطي مع التركيز وان انقلاب السلوك يكون دائما عند x=0.5، وجد انها تبدي تأثرا بعد معاملة الأغشية حراريا. وكان تصرف الجزء الحقيقي لثابت العزل مشابها لتصرف معامل الانكسار، بينما الجزء الخيالي لثابت العزل كان مماثلا لتصرف معامل الخمود.