The Effect of Weight Fraction and Grain Size of (Sio2) on the Thermal Conductivity of Epoxy
تاثير الكسر الوزني والحجم الحبيبي للـ (Sio2) على الموصلية الحرارية للايبوكسي

Author: Mena Faisal Khdeer مينا فيصل خضير
Journal: Al-Qadisiyah Journal for Engineering Sciences مجلة القادسية للعلوم الهندسية ISSN: 19984456 Year: 2011 Volume: 4 Issue: 4 Pages: a53-a64
Publisher: Al-Qadisiyah University جامعة القادسية

Loading...
Loading...
Abstract

This research deals with use of Lee's disc to measure the thermal conductivity and temperature change with respect to time through the thickness of the specimens of the unreinforced epoxy and reinforced epoxy by silica particles at different weight fraction and grain size. The results show that the thermal conductivity increased by increasing the weight fraction and reduced by increasing the grain size of silica particles by nonlinear relationship and the maximum difference between the unreinforced epoxy and reinforced epoxy was (0.445 W/m.ºc) at weight fraction (20 %) and grain size (20 µm) of silica particles, where at this value of weight fraction and grain size the thermal conductivity was maximum value (k= 0.61 W/m.ºc).

تم في هذا البحث استخدام جهاز قرص لي لقياس الموصلية الحرارية وتغير درجة الحرارة مع الزمن خلال سمك العينة للايبوكسي الغير مقوى والايبوكسي المقوى بدقائق السليكا عند كسر وزني وحجم حبيبي مختلف. حيث بينت النتائج بان الموصلية الحرارية تزداد بزيادة الكسر الوزني لمادة التقوية وتقل مع زيادة الحجم الحبيبي لدقائق السليكا بعلاقات لاخطية وان اقصى فرق بين الموصلية الحرارية بين الايبوكسي المقوى والغير مقوى كان بمقدار (0.445 w/m.ºc) عند كسر وزني (Wp=20 %) وعند حجم حبيبي (25 µm) لدقائق السليكا الذي بلغت عند هذا الكسر الوزني والحجم الحبيبي اعلى قيمة للموصلية الحرارية وكانت (k=0.61 w/m.ºc).