Effect of MnO-4 Anion Inhibition on Corrosion of (70%Cu-30%Zn) Brass in Salt and Basic Solutions

Author: Mervit M. Al-Jnabi
Journal: Engineering and Technology Journal مجلة الهندسة والتكنولوجيا ISSN: 16816900 24120758 Year: 2011 Volume: 29 Issue: 16 Pages: 3320-3330
Publisher: University of Technology الجامعة التكنولوجية

Loading...
Loading...
Abstract

This research involves study effect of MnO-4 anion addition as inhibitor on the polarization behavior of (70%Cu-30%Zn) alloy in salt and basic medium ( 0.6 M NaCl & 0.6 M NaOH) by potentiostatic method where Tafel slopes and corrosion rate (Rmpy) and inhibition efficiency (El%) for each salt and basic environments were measured .Result of the tests shows that the values of Tafel slopes and corrosion rate decreases with adding the MnO-4 anion in two solutions, the Inhibition efficiency of 70%Cu-Zn30% alloy in NaOH solution more than that observed in NaCl solution. which means that the basic media is more corrosive Cu-Zn alloy even after the addition of inhibitor.


Article
Study of Mechanical Properties of (Al-Cu-Mg) Alloy Matrix Composite
دراسة الخواص الميكانيكية لمتراكبات ذات أساس سبيكة (Al-Cu-Mg)

Authors: Sahama E. Salih سهامة عيسى صالح --- Mervit M. Al-Jnabi ميرفت مهدي الجنابي
Journal: Al-Khwarizmi Engineering Journal مجلة الخوارزمي الهندسية ISSN: 18181171 23120789 Year: 2012 Volume: 8 Issue: 3 Pages: 95-107
Publisher: Baghdad University جامعة بغداد

Loading...
Loading...
Abstract

The present research had dealt with preparing bars with the length of about (13 cm) and adiametar of (1.5 cm) of composite materials with metal matrix represented by (Al-Cu-Mg) alloy cast enforced by (ZrO2) particles with chosen weight percentages (1.5, 2.5 ,3.5, 5.5 %). The base cast and the composite materials were prepared by casting method by uses vortex Technique inorder to fix up (ZrO2) particles in homogeneous way on the base cast. In addition to that, two main groups of composite materials were prepared depending on the particles size of (ZrO2) , respectively. The study also contained the effect of insolution heat treatment at (505 0C) and the following forming process in addition to aging process at (185 0C) during different periods for all the prepared models. Also we caried on the study of the effect of reinforcement the base cast process with zerconia particles (ZrO2) on some of its mechanical properties. The optical microscopy test should that the microstructures of the composite materials having fine grains as comparet with large grains more of the base cast. As for hardness test & tensile test results showed an increase in hardness & tensile strength in addition to the increase in (ZrO2) that was added to reach the highest values when the weighted percentage of 3.5% and the amount of(140H.V),(570MPa) respectively. It was noted that the ductile values are reducedcontinuously with the increase of the added (ZrO2) . The effect of particle size of (ZrO2) particles on the mechanical properties, it was noted that there was a little reduction in the values of hardness and tensile strength with an increase of the particle size of (ZrO2) bat remains higher than in the base cast and the amount of(110H.V),(210MPa) respectively. While there was an increase in the ductilevalues with increasing the particle size but they still less than in the base cast.

يتناول البحث الحالي تحضير قضبان طولها (13 cm) وقطرها (1.5 cm) من مواد متراكبة ذات أساس معدني والمتمثل بسبيكة (Al-Cu-Mg) مقواة بدقائق الزركونيا (ZrO2) بنسب وزنيه مختارة هي(5.5, and3.5, 2.5, 1.5%) .حضرت سبيكة الأساس والمواد المتراكبة بطريقة السباكة باستخدام تقنية الدوامة (Vortex Technique) لتشتيت دقائق الزركونيا في سبيكة الأساس، فضلا عن ذلك تم تحضير مجموعتين رئيسيتين من المواد المتراكبة بالاعتماد على الحجم الحبيبي لدقائق الزركونيا المتمثلة ( )و( )على التوالي .وتضمنت الدراسة تأثير المعاملة الحرارية المحلولية عند درجة (5050C) وعملية التشكيل اللاحقة فضلا عن عملية التعتيق عند درجة (185 0C) وخلال أزمنة مختلفة ودراسة تأثير تقوية سبيكة الأساس بدقائق الزركونيا على بعض خواصها الميكانيكية. وقد أظهرت نتائج الفحص المجهري أن البنية المجهرية للمادة المتراكبة ذات حبيبات انعم من السبيكة الأساس ، أما فيما يخص فحص الصلادة ومقاومة الشد فقد بينت النتائج ازدياد قيم كل من الصلادة ومقاومة الشد مع زيادة نسبة الزركونيا المضافة لتصل الى اعلى قيمة لها عند النسبة الوزنية 3.5% والبالغة (140H.V),(570H.V) على التوالي ثم تسلك المادة سلوكا مغايرا ولكنها تبقى عند قيم اعلى مما هي عليه في السبيكة الاساس في حين لوحظ إن قيم المطيلية تقل باستمرار مع زيادة نسبة الزركونيا المضافة. أما تأثير الحجم الحبيبي لدقائق الزركونيا على الخواص الميكانيكية فقد لوحظ أن هنالك انخفاض قليل في قيم الصلادة ومقاومة الشد مع زيادة الحجم الحبيبي لدقائق الزركونيا ولكن تبقى اعلى مما هي عليه في السبيكة الاساس والبالغة (110H.V),(210H.V) على التوالي بينما هنالك زيادة قليلة في قيم المطيلية مع زيادة الحجم الحبيبي ولكنها تبقى اقل مما هي عليه في السبيكة الأساس .