Article
NUMERICAL AND EXPERIMENTAL STUDY OF BENDING AND TENSILE BEHAVIOR FOR THEALUMINUM –SILICON COMPOSITE BEAM REINFORCED BY ALUMINA

Author: Mohamad K. Alwan
Journal: Iraqi journal of mechanical and material engineering المجلة العراقية للهندسة الميكانيكية وهندسة المواد ISSN: 20761819 Year: 2012 Volume: 12 Issue: 3 Pages: 508-520
Publisher: Babylon University جامعة بابل

Loading...
Loading...
Abstract

This research includes experimental and numerical analysis using finiteelement method by ANSYS11 package to study effect of reinforcement of Aluminum–Silicon with ceramic particles (Alumina) for different beam width (12, 14 and16mm) on the hardiness and bending properties. The composite material is produced using the vortex technique by cutting the base alloy to small pieces and put inside steel crucible. Put the steel crucible inside gas furnace in temperature (700oC). The electrical mixer used to vortex the mixtureand adding the aluminum oxide particles (Alumina) (5% and 10%) and after thatpouring the melting in metallic mold. The results of the study showed that Vickers micro hardness increased from(HV=105) for pure Aluminum –Silicon alloy to (HV=127) with (10%) Alumina, alsothe tensile strength increased from (95 Mpa) to (135 Mpa). The maximum flexuralstrength was (451 MPa) and the maximum shear stress was (33 MPa) at (width=16mm) with volume fraction (10 %) of Alumina. the maximum strain decrease withincrease volume fraction of Alumina. The experimental and finite element resultsobtained are approximately agreement.


Article
Bending Characteristics of Carburized Low Carbon Steel Experimental and Numerically Study

Author: Mohamad K. Alwan Alsaadi
Journal: Journal of University of Babylon مجلة جامعة بابل ISSN: 19920652 23128135 Year: 2017 Volume: 25 Issue: 2 Pages: 761-773
Publisher: Babylon University جامعة بابل

Loading...
Loading...
Abstract

This research includes experimental and numerical studies by using finite element method to study the effect of carburized low carbon steel for different beams width on the hardiness and bending properties.The back of carburization consists from hardwood charcoal mixed with barium carbonate as the Activator. The specimens were carburized using (30%) of Activator at temperature equal to (900ºC) for five hours.The modulus of elasticity obtained from experimental work used in FEM (ANSYS) to calculate flexural strength, maximum strain and maximum shear stress and these results increase with carburized low carbon steel. The results of the study showed that the Vickers micro hardness increased, the maximum flexural strength (1750 MPa) and maximum shear stress was (121.5 MPa) at width (16 mm) for the experimental results carburized low carbon steel. The experimental, finite element and analytical results obtained for the bending analysis are approximately agreement.

تضمنت الدراسة الجانب العملي و تقنية العناصر المحددة لمعرفة تاثير كربنة الفولاذ المنخفض الكربون على قيم الصلادة وخواص الانحناء لعرض اعمدة مختلف.أن وسط الكربنة مكون من مسحوق الفحم النباتي مع كاربونات الباريوم كمادة منشطة.وأن العينات يتم كربنتها بأستخدام نسبة (30%) من مادة التنشيط وعند درجة حرارة (900ºC) ولمدة خمسة ساعات .النتائج العملية لمعامل المرونة استخدمت في تقنية العناصر المحددة (برنامج انسيز) لحساب مقاومة الانحناء واكبر انفعال واكبر اجهاد قص بينت النتائج زيادة هذه القيم بعد كربنة الفولاذ منخفض الكربون.كذلك بينت النتائج أن الصلادة المجهرية للسطح المكربن تزداد, متانة الانحناء (1750 MPa) واكبر اجهاد قص (121.5 MPa) عند عرض عمود(16 mm) بعد الكربنة للنتائج العملية .و كذلك كانت نتائج العناصر المحددة مقاربة للنتائج العملية.


Article
Tensile and Buckling Analysis of the Polymer Composite Beam Reinforced by Natural Jute Fiber

Authors: Mohamad Ali Tariq --- Qahtan Adnan Hamad --- Mohamad K. Alwan
Journal: Engineering and Technology Journal مجلة الهندسة والتكنولوجيا ISSN: 16816900 24120758 Year: 2011 Volume: 29 Issue: 1 Pages: 129-140
Publisher: University of Technology الجامعة التكنولوجية

Loading...
Loading...
Abstract

This research focuses on the preparation of polymer matrix compositematerial by (hand lay – UP) method, where the material was prepared fromunsaturated polyester resin (up) as a matrix reinforced by natural jute fiber withdifferent volume fractions (3%, 4%, 5%, 6%).The experimental work and finiteelement techniques were used to analysis the tensile and the buckling analysis ofthe composite beam reinforced by natural jute fiber at different volume fraction.The results of experimental work of the modulus of elasticity were in therange of the theoretical results. The critical load increased with increase the fibervolume fraction that ( cr P =610N) at ( f V = 3%) and ( cr P =830N) at ( f V =6 %) forthe experimental results.While ( cr P =619N) at ( f V = 3%) and ( cr P =877N) at( f V =6 %) for the finite element results.

Keywords

jute fiber --- tensile --- buckling --- composite --- beam


Article
Numerically and Experimentally Studying of some Mechanical Properties of the Polyester Matrix Composite Material Reinforced by Jute Fibers
دراسة تحليلية وعملية لبعض الخصائص الميكانيكية لمادة متراكبة ذات أساس من البولي استر مقواة بألياف الجوت

Authors: Jawad Kadhim Oleiwi --- Mohamad K. Alwan --- Qahtan Adnan Hamad
Journal: Engineering and Technology Journal مجلة الهندسة والتكنولوجيا ISSN: 16816900 24120758 Year: 2014 Volume: 32 Issue: 9 Part (A) Engineering Pages: 2235-2247
Publisher: University of Technology الجامعة التكنولوجية

Loading...
Loading...
Abstract

This research focuses on the preparation of polymer matrix composite material by (hand lay – up) method, where the material (rectangular beam) was prepared from unsaturated polyester resin as a matrix reinforced by natural jute fiber with different volume fraction (3%, 4%, 5%, 6%). Numerical studies by using finite element method (Ansys 11 package) to study the effect of selected volume fractions of jute fibers on the bending properties. Results of this experimental research indicate that increasing the volume fraction of jute fibers lead to increase bending modulus of elasticity. The values of flexural strength and shear stress increase with the increase of jute fibers volume fraction while the values of deflection and maximum strain decreases for both experimental and numerical studies.

في هذا البحث تم تحضير مادة متراكبة ذات أساس بوليمري بطريقة الصب اليدوي من البولي استر غير المشبع كمادة أساس مقواة بألياف الجوت الطبيعية وبكسور حجميه مختلفة هي (3%, 4%, 5% و 6%) . تضمن البحث دراسة عملية وتحليلية باستخدام طريقة العناصر المحددة لدراسة تأثير الكسور الحجمية المختارة لألياف الجوت على خصائص الانحناء. أظهرت النتائج العملية للبحث بأن زيادة الكسر ألحجمي لألياف الجوت أدت إلى زيادة قيم معامل مرونة الانحناء.مع زيادة الكسر الحجمي لألياف الجوت, فان قيم متانة الانحناء واقصى إجهاد القص تزداد بينما انخفضت قيم الاستطالة والانفعال الأعظم ولكلا الدراستين العملية والتحليلية.


Article
Experimental And Numerical Study Of Buckling For Carburized Low Carbon Steel Columns
دراسة عملية عددية لانبعاج أعمدة الفولاذ منخفض الكربون المكربن

Authors: Mohamad K. Alwan محمد كشكول علوان --- Naseem Sabah abrahim نسيم صباح ابراهيم
Journal: Journal of Engineering and Sustainable Development مجلة الهندسة والتنمية المستدامة ISSN: 25200917 Year: 2014 Volume: 18 Issue: 2 Pages: 133-145
Publisher: Al-Mustansyriah University الجامعة المستنصرية

Loading...
Loading...
Abstract

Experimental work and finite element techniques were used to analyze the tensile and buckling characteristics of carburized low carbon steel columns for different diameters.The back of carburization consists of hardwood charcoal mixed with barium carbonate as the energizer. The specimens were carburized using (30%) of energizers at temperature equal to (900ºC) for 5 five hours.The modulus of elasticity as measured experimentally was used in FEM (ANSYS) to calculate the buckling load. The results of the study showed that the Vickers micro hardness increased from (HV=210) to (HV=525), the tensile strength increased from (708 MPa) to (1065 MPa) and critical buckling load increased from (18.37 kN) to (19.6 kN) for d=8mm. Also critical buckling load increased from (5.8 kN) to (19.2 kN) as the diameter of the carburized low carbon steel column increased from 6mm to 8mm respectively for FEA analysis.

تضمنت الدراسة الجانب العملي و تقنية العناصر المحددة لتحليل الشد و الانبعاج للفولاذ المنخفض الكربون المكربن وبأقطار مختلفة للعمود.أن وسط الكربنة مكون من مسحوق الفحم النباتي مع كاربونات الباريوم كمادة منشطة.وأن العينات يتم كربنتها باستخدام نسبة (30%) من مادة التنشيط وعند درجة حرارة (900ºC) ولمدة خمسة ساعات.النتائج العملية لمعامل المرونة استخدمت في تقنية العناصر المحددة (برنامج انسيز).بينت النتائج أن الصلادة المجهرية للسطح المكربن تزداد من (HV=210) الى (HV=525) ومقاومة الشد تزداد من (708 MPa) الى (1065MPa) والحمل الحرج للانبعاج يزداد من (18.37 kN) الى (19.6 kN) بعد الكربنة للنتائج العملية لقطر 6mm. و كذلك يزداد الحمل الحرج من (5.8 kN) الى (19.2 kN) بزيادة قطر العمود من 6 mm الى 8mm على التوالي.

Listing 1 - 5 of 5
Sort by
Narrow your search

Resource type

article (5)


Language

English (4)

Arabic and English (1)


Year
From To Submit

2017 (1)

2014 (2)

2012 (1)

2011 (1)