Article
Studying the influence of the preparation of a new copolyamide as adhesive for wood-wood surfaces
دراسة تأثير تحضير بولي أمايد مشترك جديد كلاصق لسطوح خشب – خشب

Author: Mohammad N. AL-Baiati
Journal: journal of the college of basic education مجلة كلية التربية الاساسية ISSN: 18157467(print) 27068536(online) Year: 2011 Volume: 17 Issue: 72/ملحق Pages: 109-116
Publisher: Al-Mustansyriah University الجامعة المستنصرية

Loading...
Loading...
Abstract

In this research, a new copolyamid was prepared from reaction Aceglutamide with Formaldehyde by esterfication process, and used this copolymer as adhesive between wood – wood surface. Five different weight ( 0.2, 0.4 , 0.6, 0.8 & 1.0 gm ) from the prepared copolymer respectively, were used as adhesive to prepared the specimens of wood / adhesive . Four standard test methods were used to measured the adhesion properties which are; ASTM: D-790, ASTM: D- 695, ISO – 179 & ASTM: D-638 . The results obtained from these tests indicated that, the specimens of wood / adhesive containing 1.0 gm from the prepared copolymer have high values in all standard tests; Impact strength was 45 MPa, Compressive strength was 40 MPa, Flexural strength was 250 MPa and Tensile strength was 8150.41 MPa ; compared with the other specimens which contain on less weight from the prepared copolymer.

تم في هذا البحث تحضير بولي أمايد مشترك جديد من تفاعل Aceglutamide مع الفورمالديهايد بواسطة عملية الأسترة ، وأستخدام هذا البوليمر المشترك كلاصق بين سطوح خشب – خشب . خمسة أوزان مختلفة ( 0.2 ،o.4 ،o.6 ، 0.8 و 1.0 غرام ) من البوليمر المشترك المحضر على التوالي ، أستخدمت كلاصق لتحضير عينات خشب / لاصق . أربعة طرق قياسية ، أستخدمت لقياس الخواص اللصوقية وهي :ASTM : D- 790 ، ASTM:D- 659 ، ISO: 179 و ASTM:D- 638 .النتائج التي تم التوصل اليها تشير الى أن عينات خشب / لاصق الحاوية على 1.0 gm من البوليمر المشترك المحضر يمتلك قيم عالية في جميع الأختبارات القياسية ، قوة الصدمة 45 MPa ، قوة الأنضغاط 40 MPa ، قوة الأنحناء 250 MPa و قوة الشد 8150.41 MPa ، مقارنة مع العينات الأخرى الحاوية على أوزان أقل من البوليمر المشترك المحضر .

Keywords


Article
Studying the effect of a new polyamide as adhesive for wood-wood surfaces

Authors: Mohammad N. AL-Baiati --- Laith B. AL-Asady --- Hawraa H. AL-Zubadi --- Saja A. Abd-Alkareem
Journal: journal of kerbala university مجلة جامعة كربلاء ISSN: 18130410 Year: 2012 Volume: 1 Issue: المؤتمر العلمي الاول للتربية للعلوم الصرفة Pages: 15-21
Publisher: Kerbala University جامعة كربلاء

Loading...
Loading...
Abstract

In this research, a new copolyamid was prepared from reaction Aceglutamide with Formaldehyde by esterfication process, and used this copolymer as adhesive between wood – wood surface. Five different weight ( 0.2, 0.4 , 0.6, 0.8 & 1.0 gm ) from the prepared copolymer respectively, were used as adhesive to prepared the specimens of wood / adhesive . Four standard test methods were used to measured the adhesion properties which are; ASTM: D-790, ASTM: D- 695, ISO – 179 &ASTM: D-638 .The results obtained from these tests indicated that, the specimens of wood / adhesive containing 1.0 gm from the prepared copolymer have high values in all standard tests; Impact strength was 45 MPa, Compressive strength was 40 MPa, Flexural strength was 250 MPa and Tensile strength was 8150.41 MPa ; compared with the other specimens which contain on less weight from the prepared copolymer.


Article
The Inhibition Combustion of Polyester and Epoxy Resins by Using Some of Inorganic Phosphorus Salts
تثبيط الاحتراق لراتنجي البولي استر والأيبوكسي باستخدام بعض أملاح الفسفور اللاعضوية

Authors: Mohammad N. AL-Baiati محمد ناظم بهجت البياتي --- Harith I. Jaffer حارث إبراهيم جعفر
Journal: Albahir journal مجلة الباهر ISSN: 23125721 Year: 2015 Volume: 2 Issue: 3,4 Pages: 37-47
Publisher: AL-Abbas Holy Shrine العتبة العباسية المقدسة

Loading...
Loading...
Abstract

Abstract In this work, the effect of four types of inorganic phosphorus salts on flammability for polyester and epoxy resins has been studied in the weight ratios of (0.5, 1.5, 2.5 & 3.5%) by preparing films of (130×130×3) mm3 in diameter, Three standard tests method were used to measure the flame retardation which are; ASTM: D-2863, ASTM: D-635 & ASTM: D-3014. The results obtained from these tests indicated that additive IV has high efficiency as a flame retardant, self-extinguishing (S.E), occurred at the percentage 0.5% for unsaturated polyester resin and the percentage 1.5% for epoxy resin. Non-burning (N.B), occurred at the percentage 2.5% for unsaturated polyester resin and at the percentage 3.5% for epoxy resin. Additives I and II show low effect on retard combustion in both resins.

ﺍﳋﻼﺻﺔ ﰲ ﻫﺬﺍ ﺍﻟﻌﻤﻞ، ﺩﺭﺱ ﺗﺄﺛﲑ ﺍﺭﺑﻊ ﺍﻧﻮﺍﻉ ﻣﻦ ﺍﻣﻼﺡ ﺍﻟﻔﺴﻔﻮﺭ ﺍﻟﻼﻋﻀﻮﻳﺔ ﻋﲆ ﺗﺜﺒﻴﻂ ﺍﻟﻠﻬﻮﺑﻴﺔ ﻟﺮﺍﺗﻨﺠﻲ ﺍﻟﺒﻮﱄ ﺍﺳﱰ .3 ( ﻣﻠﻢ3×130×130) ( ﺑﻮﺍﺳﻄﺔ ﲢﻀﲑ ﴍﺍﺋﺢ ﺑﻘﻴﺎﺱ 3.5% ﻭ0.5, 1.5, 2.5)ﻭﺍﻻﻳﺒﻮﻛﴘ، ﻭﺑﻨﺴﺐ ﻣﺌﻮﻳﺔ ﻭﺯﻧﻴﺔ ، ﺍﻟﻄﺮﻳﻘﺔ ASTM: D-2863ﺍﺳﺘﺨﺪﻣﺖ ﺛﻼﺙ ﻃﺮﺍﺋﻖ ﻗﻴﺎﺳﻴﺔ ﻻﺧﺘﺒﺎﺭ ﺗﺜﺒﻴﻂ ﺍﻟﻠﻬﻮﺑﻴﺔ ﻭﻫﻲ: ﺍﻟﻄﺮﻳﻘﺔ ﺍﻟﻘﻴﺎﺳﻴﺔ IV. ﺃﻥ ﺍﻟﻨﺘﺎﺋﺞ ﺍﳌﺴﺘﺤﺼﻞ ﻋﻠﻴﻬﺎ ﺗﺸﲑ ﺍﱃ ﺍﻥ ﺍﳌﻀﺎﻑ ASTM: D-3014 ﻭﺍﻟﻄﺮﻳﻘﺔ ﺍﻟﻘﻴﺎﺳﻴﺔ ASTM: D-635ﺍﻟﻘﻴﺎﺳﻴﺔ ﻟﺮﺍﺗﻨﺞ ﺍﻟﺒﻮﱄ ﺃﺳﱰ ﻏﲑ ﺍﳌﺸﺒﻊ 0.5% (. ﻋﻨﺪ ﺍﻟﻨﺴﺒﺔ S.E)ﻳﻤﺘﻠﻚ ﺗﺄﺛﲑﺍ ﻛﺒﲑﺍ ﻛﻤﺜﺒﻂ ﳍﺐ، ﺣﻴﺚ ﳛﺪﺙ ﺍﻷﻃﻔﺎﺀ ﺍﻟﺬﺍﰐ 2.5% (. ﻋﻨﺪ ﺍﻟﻨﺴﺒﺔ N.B) ﻟﺮﺍﺗﻨﺞ ﺍﻷﻳﺒﻮﻛﴘ. ﻛﺬﻟﻚ ﳛﺪﺙ ﻋﺪﻡ ﺍﻷﺷﺘﻌﺎﻝ ﻟﻠﻌﻴﻨﺔ 1.5%ﻭﻛﺬﻟﻚ ﺣﺪﻭﺛﻪ ﻋﻨﺪ ﺍﻟﻨﺴﺒﺔ ، ﻓﻘﺪ ﺃﻇﻬﺮﺍ ﺗﺄﺛﲑﺍ ﻗﻠﻴﻼ ﻋﲆ II ﻭI ﻟﺮﺍﺗﻨﺞ ﺍﻷﻳﺒﻮﻛﴘ. ﺃﻣﺎ ﺍﳌﻀﺎﻓﺎﻥ 3.5%ﻟﺮﺍﺗﻨﺞ ﺍﻟﺒﻮﱄ ﺃﺳﱰ ﻏﲑ ﺍﳌﺸﺒﻊ ﻭﻋﻨﺪ ﺍﻟﻨﺴﺒﺔ ﺗﺜﺒﻴﻂ ﺍﻟﻠﻬﻮﺑﻴﺔ ﰲ ﻛﻼ ﺍﻟﺮﺍﺗﻨﺠﲔ.


Article
Studying the synergistic effect of some organo-halogen antimony complexes with chlorinated rubber on retard combustion of unsaturated polyester and epoxy resins
دراسة التأثيرالتآزري لبعض معقدات الانتيمون العضوية الهالوجينية مع المطاط المكلورعلى تثبيط اللهوبية لراتنجي البولي استر غير المشبع والايبوكسي

Authors: Mohammad N. AL-Baiati --- Husam N. AL-Ibrahimy --- Rouaa H. AL-Zamely --- Lamia T. AL-Maiahy --- et al.
Journal: journal of kerbala university مجلة جامعة كربلاء ISSN: 18130410 Year: 2012 Volume: 1 Issue: المؤتمر العلمي الاول للتربية للعلوم الصرفة Pages: 162-173
Publisher: Kerbala University جامعة كربلاء

Loading...
Loading...
Abstract

Two groups of additives were used in this investigation, to measure the effect of these additives on retard combustion of unsaturated polyester and epoxy resins. The first group contains four complexes, from type organo-halogen antimonate compounds, and the second group, which prepared from blend 50% in weight percentage of each complex with 50% in weight percentage of chlorinated rubber. Three sheets from each resins were prepared with weight percentage ( 0.2, 0.4, 0.6 & 0.8 % ) of additives . Three standard test methods used to measure the flame retardation, which are: (ASTM:D -2863), (ASTM:D-635) and (ASTM:D-3014) . Results were obtained from these tests indicated that, additive VI has high efficiency as flame retardant, for both resins and additive III show low effect on flammability in both resins .

مجموعتين من المضافات أستخدمت في هذا البحث لقياس تأثيرها على تثبيط اللهوبية لراتنجي البولي أستر غير المشبع والأيبوكسي . المجموعة الأولى ، تحتوي على أربعة معقدات من نوع مركبات أنتيمونات الهالوجين العضوية ، و المجموعة الثانية ، حضرت بخلط فيزيائي من 50% نسبة وزنية من كل من المعقدات المحضرة مع 50% نسبة وزنية من المطاط المكلور . ثلاثة ألواح من كل من الراتنجيـــــــــن قد حضرت مع نسب مئوية وزنيه ( % 0.8 &0.6 ,0.4, 0.2) من المضافات . استخدمت ثلاثة طرق قياسية لقياس تثبيط اللهوبية هي ( ASTM:D-3014) ,(ASTM:D-635), (ASTM:D-2863) .إن النتائج التي تم الحصول عليها من هذه القياسات تشير الى ان المضاف VI يمتلك كفاءة عالية في تثبيط اللهوبية في كلا الراتنجين ، أما المضاف III فقد أظهر تأثير قليل على تثبيط اللهوبية في كلا الراتنجين .