Article
Studying Critical Flash Over of Different Types of High Voltage Insulator

Authors: Mokdad T.Younis --- Dr.Sami A.Ajeel
Journal: Engineering and Technology Journal مجلة الهندسة والتكنولوجيا ISSN: 16816900 24120758 Year: 2007 Volume: 25 Issue: 6 Pages: 815-827
Publisher: University of Technology الجامعة التكنولوجية

Loading...
Loading...
Abstract

The critical flashover CFO of an insulation structure is commonly used todescribe the insulation structure lightening impulse strength. In this work,first CFO of polymer and porcelain each alone was measured and then, a newstructural arrangement is represented to measure (CFO). This arrangementsconsists of three layers; fiberglass is placed between two layers of polymer andporcelain .All insulation materials are examined in dry and wet condition withpositive and negative lightening impulse under (15,25 and 35) KV. The criticalflashover voltage (CFO) of insulator is distributed on certain surface alongwith fiberglass distribution poles as an insulator. Also altitude of poles istaken into consideration in calculating critical flashover voltage for bothinsulator and structure. (CFO) voltages are added from fiberglassdistribution pole to basic insulation component and are calculated based onthe test result of the (CFO). The above measurements indicated that the totalCFO voltage of new arrangements insulator under dry condition is muchhigher than under wet condition for the same impulse polarity and tested polelength.

يستخدم الجهد الحرج للومضة اللحظية بشكل مالوف لوصف قوة الضوء النبضي للبنية العازلة.في هذا البحث تم قياس , اولا الجهد الحرج للومضة اللحظية لمواد عازلة من البوليمروالبورسلين كلا على حدة بعد ذلك تم القياس لترتيب بنية جديدة حيث يتالف هذا الترتيب م نثلاث طبقات ، طبقة من الليف الزجاجي وضعت بين طبقتين من البوليمر مرة والبورسلين مرةاخرى. كل المواد اعلاه اختبرت تحت ظروف جافة ورطبة مع نبضات اضاءة موجبة وسالبةتحت ( ١٥،٢٥،٣٥ كيلو فولت ) . يكون الجهد الحرج للومضة اللحظية للعازل متوزع علىالسطح المحدد بامتداد الاعمدة الموزعة للالياف الزجاجية . اخذ بنظر الاعتبار ارتفاع الاعمدةفي حساب الجهد الحرج للومضة اللحظية لكلا من العازل والبنية . اضيفت الجهود الحرجةللومضة اللحظية من عمود الالياف الزجاجية الموزعة الى مكون العازل الاساسي وتكونمحسوبة بالاستناد الى نتيجة الاخت بارات للجهد الحرج للومضة اللحظية . القياسات اعلاه تشيرالى ان الجهود الحرجة للومضة اللحظية لترتيب العازل الجديد تحت ظروف جافة يكون اعلىبكثير مقارنة مع الظروف الرطبة لنفس النبض القطبي ونفس طول عمود الاختبار .


Article
The Electrical Degradation of Fiberglass Poles
الانحلال الكهربائي لاقطاب الالياف الزجاجية

Authors: Sami .Ajeel --- Mokdad T.Younis --- Arkan A.Hussein
Journal: Engineering and Technology Journal مجلة الهندسة والتكنولوجيا ISSN: 16816900 24120758 Year: 2008 Volume: 26 Issue: 9 Pages: 1131-1142
Publisher: University of Technology الجامعة التكنولوجية

Loading...
Loading...
Abstract

This work involves fiberglass samples used in two kind of aging (45days aging, 45 days aging with AC of 25 kV). Five sets of fiberglasssamples were used in the accelerated aging tests and each set consists ofnine fiberglass samples. The tested insulation length of these samples waschosen as 0.3 m. Two metallic bands, upper and bottom, were used aselectrodes and tightly wrapped on the samples. The effect of surfacecondition on the materials electric degradation was studied and the ninesamples were divided into' three group. The external surfaces of the firstgroup of tested samples were kept intact, but some scratches were manuallyplaced on the external surfaces of the second group. For the third group, fiveholes, each with 2.5 cm in diameter, were manually drilled in each sample.The electric experimental using to identify the insulation strength offiberglass materials were (the lighting impulse test, AC wet flashover testsand, AC dry flashover test).The result show that the CFO voltage and ACflashover under dry condition were higher than under wet condition for allsamples. The leakage current has a linear relation ship with applied voltage.The electric degradation is significant when the sample were tested withelectric stress.

يتضمن البحث استخدام نماذج من عوازل الالياف الزجاجية في اختبارات ا لتعتيقالمسرع المتضمنن لنوعين من ( 45 يوم تعتيق ، 45 يوم تعتيق مع فولتية متناوبة من 25كيلو فولت ) استخدمت في هذة الاختبارات خمسة مجاميع من عوازل الالياف الزجاجية وكلمجموعة تتالف من 9 عينات طول كل عينة كان 0.3 متر نوعين من الاشر طة االفلزيةاستخدمت كاقطاب علوية وسفليه تناول البحث دراسة تاثبر الظروف السطحية للنماذج علىالانحلال الكهربائي للمواد قسمت العينات التسع الى ثلاث مجاميع حيث احتفظ بالسطح الخارجيللمجموعة الاولى بدون اي تاثير وعملت حزوز على السطح الخارجي للمجموعة الثانية بينماالمجموعة الثالثة تحتوي خمسة ثقوب قطر كل ثقب 2.5 سم. الاختبارات الكهربائية المستخدمةلتحديد متانة العوازل هي ( اختبارات النبضة الضوئية ، الاختبارات الجافة والرطبة للفو لتي ةالمتناوبة لتجاوز الومضة. تشير النتائج الى ان الفولتية الحرجة والتيار الحرج يكون اعلى فيالظروف الرطبه ولجميع النماذج والتيار الحرج يتناسب خطيا مع الفولتية المسلطة . الانح لالالكهربائي يظهر بوضوح عندما تكون النماذج تحت ضغط كهربائي