Article
Effect of Addition Of Copper and Copper –Nickel Elements on Structure and Properties of Low Carbon Steels
تأثير إضافة عنصر النحاس وعنصري النحاس والنيكل على التركيب والخواص للفولاذ المنخفض الكربون

Author: Munthir Mohammed Radhy
Journal: Engineering and Technology Journal مجلة الهندسة والتكنولوجيا ISSN: 16816900 24120758 Year: 2010 Volume: 28 Issue: 23 Pages: 6688-6702
Publisher: University of Technology الجامعة التكنولوجية

Loading...
Loading...
Abstract

The purpose of this study is to investigate the effect of adding different amounts(2, 4, 6% of Cu) on properties and microstructure of low carbon steel .Also studythe effect of the same amounts of Cu with half amount of Ni(1,2,3%Ni) are addedon properties of low carbon steels. All these alloys(Fe-Cu,Fe-Cu-Ni) appear anincrease of hardness and strength with increase of the amount of Cu or Cu-Ni. Themicrostructure obtained after heat treated(quenched and aging) of Fe-Cu and Fe-Cu-Ni alloys has been studied by optical microscopy, investigated by X-raydiffraction and hardness measurement. The microstructures obtained afterquenching depending on composition and cooling rate, the massive ferrite andmassive martensite appears on most of structures in above alloys. Themicrostructure after aging of above alloys shown some of precipitates appear asdash plates, rod and spheres in ferrite or martensite structure and this precipitatesappear as X-ray diffraction were identified the copper rich phase €.

الغرض من هذه الدراسة هو بحث تأثير إضافة كميات مختلفة من عنصر النحاس بنسبة2,4,6% ) على الخواص الميكانيكية والتركيب المجهري للفولاذ المنخفض الكاربون كذلك )دراسة تأثير إضافة عنصر النحاس بنفس النسبة اعلاة مع نصف كمية النحاس من عنصرالنيكل(% 3,2,1 ) على الخواص الميكانيكية والتركيب المجهري للفولاذ المنخفض الكاربون.جميعالسبائك تظهر زيادة في الصلادة ومقاومة الشد مع زيادة كمية النحاس او كمية النحاس والنيكل.التركيب المجهري الناتج بعد عملية المعاملة الحرارية(االاخماد والتعتيق) لسبائك الحديد- نحاسX والحديد- نحاس-نيكل يدرس بواسطة المايكروسكوب الضوئي ويفحص بواسطة اشعة الحيودوتقاس صلادتة. التركيب المجهري التي يظهر بعد عملية االاخماد فقط يعتمد على كمية النحاسوالنيكل في السبيكة وعلى معدل التبريد, حيث يلاحظ ظهور فرايت كتلي اومارتنسايت كتلي فياغلب السبائك اعلاة . التركيب المجهري الناتج بعد عملية التعتيق يظهر رواسب بشكل الواحمتقطعة وقضبان وكرات في قوام فيراتي او مارتنسايتي وهذه الرواسب هي على الاغلب تؤشرظهور النحاس بشكل طور.(€) X في فحص أشعة الحيود


Article
THE EFFECT OF HEAT TREATMENT TEMPERATURES (ANNEALING, AGING AND DOUBLE AGING) ON HARDNESS OF 16%NI CAST MARAGING STEELS
دراسة تاثير تغير درجات الحرارة للمعاملة الحرارية (التلدين -التعتيق) على صلادة الفولاذ المراجيني الحاوي على نيكل بنسبة16%

Author: MUNTHIR MOHAMMED RADHY منذر محمد راضي
Journal: Iraqi journal of mechanical and material engineering المجلة العراقية للهندسة الميكانيكية وهندسة المواد ISSN: 20761819 Year: 2011 Volume: 11 Issue: 2 Pages: 333-343
Publisher: Babylon University جامعة بابل

Loading...
Loading...
Abstract

AbstractThe primary purpose of the present work was to study the effect of different annealing and aging temperature on the mechanical properties of 16%Ni cast Maraging steels. In addition subsidiary studies were made of the hardening mechanism responsible for high strength. It was found the annealing temperature must be done above approximate 750C◦ but not exceed 1250C◦ to give the good hardness during aging.. Marked hardening occurred within several minutes during from 485oC to545 oC but only after several hours in the range between 325 to 375 oC Heat treatment of 3 hour at 485 oC of cast alloys was most satisfactory. While the aging at 485 oC for long time decrease this hardening caused softening due to the reversion of the body centered cubic matrix to austenite. The aging kinetics mechanism refer to that lattice defect were influencing the reaction rate. X-ray diffraction evident indicated the formation of any bcc structure of matrix as martensite and the appeared that hardness was due to coherent precipitate having concentration in matrix that formed as Fe2CoNi,Ni3Ti and Ni3Mo phases. The double aging of cast alloys in different temperature given normal hardening result.

ملخص البحثان الغرض الاساسي من هذا البحث هو دراسة تاثير تغير عدة درجات حرارية للمعاملة الحرارية(التلدين و التعتيق ) على صلادة مسبوكة الفولاذ المراجين ي (المارتنسايت المعتق ) الذي يحتوي على16% ). اضافة الى دراسات ثانوية تخص مبكانيكية استجابة السبائك المصلدة الى المتانة العالي ة . لقد وجد Ni)1250 )لاعطاء oC) 750 ) وان لاتتجاوز oC) ان درجات حرارة التلدين يجب ان تنجز فوق درجة حرارةصلادة جيدة ومقبولة خلال التعتيق كذلك وجد بداية ظهور الصلادة بعد عدة دقائق خلال التعتيق في(375oC) 545 ) بينما هذاالظهور يبدا بعد عدة ساعات في مدى درجات حرارة( 325 ) الى oC) 485 ) الى oC)485 ) للسبائك المسبوكة يكون مقنع في اعطاء قيم صلادة oC) 3) عند hr) . المعاملة الحرارية التعتيق لمدةجيدة ولكن التعتيق لفترة طويلة عند هذه الدرجة الحرارية ربما يسبب في انخفاض في قيمة الصلادة ناتجهالى اوستنايت . انة ميكانيكية الحركية (bcc) من تلين التركيب بسبب ظهور انعكاس تحول المارتنسايت(X) للتعتيق تشير الى ان العيوب الشبكية متاثرة بمعدل التفاعل خلال التعتيق حيث ان فحص حيود اشعةبشكل مارتنسايت اضافة الى ان ظهور زيادة في الصلادة ناتج (bcc) يوضح مؤشرا تشكيل تركيب قوام ذو.(Fe3CoNi,Ni3Ti and Ni3Mo) من تمركز رواسب التصاقية في القوام والتي تشكل بصيغة اطوار مثلالتعتيق المزدوج للسبائك المزدوج للسبائك المسبوكة عند عدة درجات حرارية مختلفة تعطي نتائج تصليداعتيادية .