Studing The Mechanical Properties And Morphology of Ternary Blends Of Polyethylene
دراسة الخواص الفيزياوية والبنية الشكلية لممزوجات ثلاثية من البولي اثيلين

Author: Nabeela A. Mohammed
Journal: Engineering and Technology Journal مجلة الهندسة والتكنولوجيا ISSN: 16816900 24120758 Year: 2009 Volume: 27 Issue: 6 Pages: 1197-1205
Publisher: University of Technology الجامعة التكنولوجية

Loading...
Loading...
Abstract

The mechanical properties and the morphology of the ternary blend ofLDPE/LLDPE/HDPE were studied.In the present work LDPE was mixed with equal amount of LLDPE and differentwt% of HDPE (0, 10, 20 and 30 %) using the two roll mills. The mechanical propertiesand the morphology were specified by measuring the (tensile, hardness, impactproperties) for the former, and photomicrograph for the later. From the tensile testresults it was found that the tensile strength at break of the ternary blend increased withincreasing the HDPE contain also the increases of wt% HDPE leads to decrease theelongation at break. For the hardness test it was found that the shore hardness of theternary blends increased with the increasing the HDPE contain .On the other hand theimpact test carried out also and it was found that the addition of HDPE leads todecrease the impact strength . Nevertheless, optical micrograph results that the HDPEserves as a compatabilizing agent for immiscible LDPE/LLDPE

في البحث الحالي قد تم درسة الخواص الميكانيكيه والبنيه الشكليه لممزوجات ثلاثيه المواد من البولياثيلين واطىء الكثافه / البولي اثيلين واطىء الكثافه الخطي/ البولي اثيلين عالي الكثافه.(LDPE/LLDPE/HDPE)تم استخدام ثلاث انواع من البولي اثيلين, فقد تم مزج البولي اثيلين الواطىء الكثافه مع كميه متساويه من البوليفي البحث الحالي قد تم دراسه اثيلين الواطىء الكثافه الخطي وقد تم اضافه نسب وزنيه مختلفه من البولي اثيلينعالي الكثافه ( 30,20,10,0 %) وذلك باستخدام الاسطوانات المدلفنه لهذا الغرض.تم تعيين الخواص الميكانيكيه والبنيه الشكليه وذلك بقياس ( الشد, الصلاده وخواص الصدم ) والتصويرالمجهري ,من نتائج اختبار الشد وجد بأن الاجهاد عند نقطه الكسر يزداد بزياده محتوى البولي اثيلين عاليالكثافه في الممزوجات , ايظا زياده نسبه البولي اثيلين عالي الكثافه ادى الى تقليل النسبه المئويه للاستطاله عندنقطه الكسر. بالنسبه الى فحص الصلاده وجد بأن قيم صلاده شور تزداد بزياده محتوى البولي اثيلين عاليالكثافه , من ناحيه اخرى تم اجراء فحص الصدم وقد وجد بأن اضافه البولي اثيلين عالي الكثافه ادى الى تقليلاجهاد الصدم , ومن نتائج التصوير المجهري يتضح جلياًً بأن البولي اثيلين عالي الكثافه ساعد على زيادهامتزاجيه الخليط الثنائي الغير ممتزج من البولي اثيلين واطىء الكثافه/ البولي اثيلين واطىء الكثافه الخطي .


Article
The Effect of Photo-Initiated Oxidation on Mechanical Properties ofHigh Density Polyethylene / Linear Low Density Polyethylene Blends

Authors: Nabeela A. Mohammed --- Najat J. Saleh
Journal: Iraqi Journal of Chemical and Petroleum Engineering المجلة العراقية للهندسة الكيمياوية وهندسة النفط ISSN: 19974884/E26180707 Year: 2007 Volume: 8 Issue: 4 Pages: 53-58
Publisher: Baghdad University جامعة بغداد

Loading...
Loading...
Abstract

The long – term behaviour of polyethylene products used out doors is affected by weathering. In the present work,weathering test was carried out to find the effect of the environment conditions on the mechanical properties of HDPE/LLDPE blends with different weight percents (0, 15, 30, and 45 %) relative to the LLDPE by increasing the exposure times to (100, 150, 200, 250, 300) hr.A series of tests (destructive), tensile, impact and hardness were carried out on the prepared samples, the results obtained declare the changes on the material behaviour from ductile to brittle and the polymer shows a decline in the mechanical properties with increasing the exposure times.In the present work empirical equations were reached which could be used to calculate one of the mechanical properties in terms of exposure time, weight percent of LLDPE content and to other mechanical properties.


Article
Studing The Mechanical Properties Of Ternary Blends Of Hdpe/Pp/Abs

Authors: Zanaib.Y.Shnea --- Nabeela A. Mohammed
Journal: Engineering and Technology Journal مجلة الهندسة والتكنولوجيا ISSN: 16816900 24120758 Year: 2008 Volume: 26 Issue: 7 Pages: 885-893
Publisher: University of Technology الجامعة التكنولوجية

Loading...
Loading...
Abstract

In this work a type of polymer blend has been prepared from mixing differentpercent (40,50,60, and 70) % of High-density polyethylene, polypropylene and adding 6%weight percent of acrylonitril-butadiene-styrene by using single-screw extruder. Theextrusion process concentrated on the homogeneous mixing manner among materialsthrough a regular selection of machine screw revolution per minute and temperature used inextrusion process. Some of mechanical properties such as impact strength, modulus ofelasticity and shore hardness of polymer blend, were determined at different weight fractionof blend. It was found that the addition (6%wt) of ABS to the binary blends HDPE/PP leadsto increase the modulus of elasticity, the impact strength and shore hardness.On the other hand increasing % HDPE content from 40 to 70wt% in HDPE/PPternary blends leads to increase the modulus of elasticity from 166.35 Mpa to 186.25 Mpa,and impact strength increase from o.o52 to o.o6 J/mm2 while decreases the shore hardnessfrom 89 to 69.

في البحث الحالي تم تحضير خلائط بوليمرية جديدة والتي هي عبارة عن مخلوط بوليمري،40,50 ) من البولي اثلين العالي الكثافة مع البولي , يتكون من مزج نسب وزنية مختلفة%( 60,70بروبلين مع إضافة نسبة وزنية%( 6) من اكريلونتريل-بيوتا دين-ستايرين(وذلك باستخدام جهاز الباثقةالمنفرد).تم استخدام عملية البثق في تحضير المواد المتراكبة وذلك بواسطة استخدام ماكنة البثق أحاديةاللولب حيث ركزت على أسلوب الخلط المتجانس بين المواد من خلال تحديد سرعة دوران اللولب الماكنةودرجات الحرارة المستخدمة في عملية البثق. وبعد ذلك جرت دراسة بعض الخصائص الميكانيكية مث لمقاومه الصدم ،معامل المرونة وصلادة شور ولجميع خلائط بوليميرية المحضرة. والنتائج التي تم الحصولعليها أوضحت عند إضافة%( 6) من اكريلونتريل-بيوتا دين-ستايرين الى خلائط ثنائي( البولي اثلين العاليالكثافة –البولي بروبلين) ادى الى زيادة معامل المرونة ,قوه الصدمة وصلادة شور. من ناحية أخرى وجدبأن زيادة اضافة البولي اثيلين عالي الكثافة من( 40 الى 70 )% إلى خلائط ثلاثية (البولي اثيلين عاليالكثافة-البولي بروبلين - اكريلونتريل-بيوتا دين-ستايرين) تحسنت الكثير من الخواص الميكانيكية حيثادى الى زيادة معامل المرونة م ن( 166,35 )إلى ( 186,25 )ميكاباسكال وقوه الصدمة م ن.( 0,053 الى 0,060 )جول/مليملتر 2 . بينما قلت صلادة شور من ( 89 ) إلى (


Article
The Effect Of Blending Of Linear Low –Density Polyethylene On Mechanical Properties Of High Density – Polyethylene
تأثير مزج البولي اثيلين الخطي على الخواص الميكانيكية للبولي اثيلين عالي الكثافة

Authors: Nabeela A. Mohammed --- Najat J.Saleh
Journal: Engineering and Technology Journal مجلة الهندسة والتكنولوجيا ISSN: 16816900 24120758 Year: 2009 Volume: 27 Issue: 3 Pages: 418-424
Publisher: University of Technology الجامعة التكنولوجية

Loading...
Loading...
Abstract

High – density polyethylene is an important commercial polymer and it is widelyused for different engineering applications. In the present work, polymer blends werefabricated by mixing two types of polyethylene, high – density polyethylene was mixedwith different weight percent of linear – low – density polyethylene using two – rollmill, the mixing machine was operated at a temperature of 135oC.A series of standard tests (destructive), tensile, impact, hardness, and compressionwere carried out on the prepared samples it was found that the addition of linear – low –density polyethylene to the high – density polyethylene leads to decrease in the modulusof elasticity, tensile strength, tensile strength at break and increase in the % elongation atbreak.For the impact test it was found that the addition of linear – low – densitypolyethylene caused an increase in the impact strength of the material, the polymer blendwith 45 % wt of linear – low – density polyethylene gave the highest value of impactstrength.On the other hand the hardness test was carried out and it was found that the additionof linear – low – density polyethylene leads to decrease the hardness of the polymerblends. Therefore, the neat high – density polyethylene gave the highest hardness value.

البولي اثيلين عالي الكثافة من البوليمرات المهمة تجارياً والذي له استخدامات واسعة فيمختلف مجالات التطبي قات الهندسية . في البحث الحالي تم تصنيع مخاليط بوليمرية بواسطة مزج نوعينمن انواع البولي اثيلين , تم مزج البولي اثيلين عالي الكثافة مع نسب وزنية مختلفة من البولي اثيلينواطئ الكثافة الخطي وذلك باستخدام الاسطوانات المدلفنة حيث تم تشغيلها عند درجة حرارية مقداره ام). o135)تم اجراء العديد من الفحوصات (الاتلافية) حيث تم اجراء فحص الشد , الصدم , الصلاد ة,والانضغاطية على النماذج المحضرة , ووجد ان اضافة البولي اثيلين واطئ الكثافة الخطي الى البولياثيلين عالي الكثافة قد ادى الى تقليل كل من معامل المرونة , اجهاد الشد , اجهاد الشد عند الكسر وزيادةالنسبة المئوية للاستطالة عند الكسر .اما بالنسبة الى فحص الصدم فقد وجد ان اضافة البولي اثيلينواطئ الكثافة الخطي قد ادى الى زيادة مقاومة المواد للصدم حيث ان المخاليط البوليمرية الحاوية على45 % من البولي اثيلين واطئ الكثافة الخطي اعطى اعلى مقاومة للصدم.من ناحية اخرى تم اجراء فحص الصلادة ووجد بأن اضافة البولي اثيلين واطئ الكثافة الخطي ادى الىتقليل صلادة المخاليط البوليمرية . لذلك فأن البولي اثيلين عالي الكثافة وبدون اي اضافة قد اعطى اعلىقيمة للصلادة.


Article
Studing Of Some Phisical Properties And Morphology Of Blends Of Hdpe /Lldpe After And Before Exposure To Uv Light
دراسة بعض الخواص الفيزياوية والبنية الشكلية لممزوجات HDPE/LLDPE قبل وبعد التعريض للاشعة الفوق بنفسجية

Authors: Najat J. Saleh --- Nabeela A. Mohammed --- Weam A. Abed
Journal: Engineering and Technology Journal مجلة الهندسة والتكنولوجيا ISSN: 16816900 24120758 Year: 2009 Volume: 27 Issue: 4 Pages: 820-830
Publisher: University of Technology الجامعة التكنولوجية

Loading...
Loading...
Abstract

Products made of polyethylene used out doors are subjected to UV-degradation. Infact, many polymers show changes in physical properties during service lifetime, whenthey are exposed to sun light and particularity to UV-light. In the present work, thephysical properties and the morphology of blends of high – density polyethylene(HDPE)/linear-low-density polyethylene (LLDPE) studied before and after exposure toUV –light.HDPE was mixed with different weight percent (0, 15, 30, and 45%) of LLDPE usingthe two roll mills; the mixing machine is operated at a temperature of 135 oC.Weathering test was carried out to find the effect of the environment condition on thephysical properties of the polymeric materials by increasing the exposure times to(100,200,300) hr. The physical properties and the morphology were specified bymeasuring the (absorption properties, and densities), for the former, andphotomicrograph for the latter. The results obtained in this work show that the density ofpure HDPE and HDPE/LLDPE blends increased with the increasing the exposure time,and that immersing the HDPE and HDPE/LLDPE blends in water can produce a varietyof damage and this damage increased with the increasing of the exposure times also, asthe amount of LLDPE is increased in the HDPE/LLDPE blends the amount of waterabsorbed and diffusivity coefficient, increase greatly, and from the optical micrographresults showed clearly the damage obtained due to exposure to UV light for 300 hr forpure HDPE and HDPE/LLDPE blends.

ان المنتجات المصنوعه من ماده البولي اثيلين والتي تستخدم في الهواء الطلق او العراء تتعرض ألى ألانحلاال نتيجه تعرضها للأشعه الفوق بنفسجيه .ألعديد من ألبوليمرات تشهد تغيرا ً واضحا فًي خواصها الفيزياويه مع مرور الوقت وذلك نتيجه ألتعرض الى أشعه ألشمس وبصوره خاصه ألى ألأشعه فوق ألبنفسجيه.في البحث الحالي تم دراسه ألخواص ألفيزياويه وكذلك دراسه ألبنيه أو ألشكل لممزوجات من قبل وبعد (LLDPE) بولي أثيلين واطىء ألكثافه ألخطي /(HDPE) ألبولي أثيل ين عالي ألكثافه تعريضها ألى ألأشعه فوق ألبنفسجيه .في بحثنا ألحالي تم مزج ألبولي أثيلين عالي ألكثافه مع نسب وزنيهمن ألبولي أثيلين واطىء ألكثافه ألخطي ( 45,30,15,0 ٪) وذلك باستخدام ألاسطوانات ألمدلفنه.تم اجراء فحص التجويه وذلك لأايجاد تأثير الضروف الجويه على المخاليط البوليمريه وذلك 200 , و 300 ) ساعة.الصفات الفيزياويه والبنيه الشكليه تم تعيينها وذلك , بزياده زمن التعريض ( 100 بقياس (الكثافه وخواص الامتصاصيه ) وعن طريق التصوير المجهري .النتائج تم الحصول عليه ا فيتزداد بزياده زمن HDPE/LLDPE هذه الدراسه توضح بأن كثافه ألبولي أثيلين ألنقي وممزوجات التعريض للأشعه فوق بنفسجيه , وكذلك عمليه غمس النماذج في الماء قد أدى ألىاحداث أضرار مختلفه وهذه الاضرار تزداد بزياده زمن التعريض ,وبزياده النسبه الوزنيه للبولي أثيلين و اطىء ألكثافه ألخطي تزداد كميه الماء الممتصه وكذلك يزداد معامل الامتصاصيه بصوره , HDPE/LLDPE في ممزوجاتكبيره ,ومن نتائج التصوير المجهري يتضح جليا ً مقدار الاذى الحاصل في المواد البوليمريه المحضره نتيجه تعرضها للأشعه ألفوق بنفسجيه ولحوالي 300 ساعه.

Listing 1 - 5 of 5
Sort by
Narrow your search

Resource type

article (5)


Language

English (5)


Year
From To Submit

2009 (3)

2008 (1)

2007 (1)